$ 2287/MT
- Density: 1.30 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 159 MPa
$ 2008/MT
- Density: 1.49 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 149 MPa
$ 1705/MT
- Density: 1.35 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 188 MPa
$ 1595/MT
- Density: 1.43 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 138 MPa
$ 1588/MT
- Density: 1.56 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 161 MPa
$ 2420/MT
- Density: 1.33 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 145 MPa
$ 1924/MT
- Density: 1.34 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 2178/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1746/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 165 MPa
$ 2495/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 186 MPa
$ 2069/MT
- Density: 1.46 g/cc
- Water Absorption: 0.58 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 162 MPa
$ 2106/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 94
- Tensile Strength, Yield: 154 MPa
$ 1945/MT
- Density: 1.54 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 124 MPa
$ 2188/MT
- Density: 1.51 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 123 MPa
$ 1451/MT
- Density: 1.67 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 159 MPa
$ 1727/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 2472/MT
- Density: 1.43 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength: 138 MPa
- Elongation at Yield: 4.5 %
$ 1762/MT
- Density: 1.38 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 172 MPa
$ 1448/MT
- Density: 1.38 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 145 MPa
$ 1826/MT
- Density: 1.38 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 186 MPa
$ 2565/MT
- Density: 1.50 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 149 MPa
$ 1503/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 190 MPa
$ 1471/MT
- Density: 1.41 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 155 MPa
$ 2242/MT
- Density: 1.31 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 99.3 MPa
$ 2143/MT
- Density: 1.62 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 138 MPa
$ 1643/MT
- Density: 1.34 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength: 176 MPa
$ 2334/MT
- Density: 1.46 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 135 MPa
$ 1731/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength at Break: 159 MPa
$ 1672/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 169 MPa
$ 1855/MT
- Density: 1.35 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 152 MPa
$ 1501/MT
- Density: 1.31 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 99.3 MPa
$ 1476/MT
- Density: 1.39 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1480/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 2132/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 94
- Tensile Strength, Yield: 152 MPa
$ 1465/MT
- Density: 1.31 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 145 MPa
$ 1658/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 124 MPa
$ 2145/MT
- Density: 1.38 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 159 MPa
$ 2480/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 172 MPa
$ 1872/MT
- Density: 1.35 g/cc
- Density: 1.37 g/cc
- Water Absorption: 0.85 % @Time 86400 sec
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
$ 1464/MT
- Density: 1.47 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 156 MPa
$ 1542/MT
- Density: 1.31 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 152 MPa
$ 2578/MT
- Density: 1.49 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 137 MPa
$ 1864/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1454/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1672/MT
- Density: 1.39 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 120 MPa
$ 1912/MT
- Density: 1.56 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 134 MPa
$ 1484/MT
- Density: 1.37 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 183 MPa
$ 1767/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 117 MPa
$ 1772/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1459/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1503/MT
- Density: 1.27 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 124 MPa
$ 1859/MT
- Density: 1.67 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 162 MPa
$ 1857/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 159 MPa
$ 1902/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1627/MT
- Density: 1.33 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 159 MPa
$ 1643/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 108
$ 1605/MT
- Density: 1.38 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 183 MPa
$ 1821/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 100 MPa
$ 1473/MT
- Density: 1.38 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Water Absorption at Saturation: 5.1 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
$ 1907/MT
- Density: 1.36 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 183 MPa
$ 2108/MT
- Density: 1.33 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 145 MPa
$ 1500/MT
- Density: 1.35 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 188 MPa
$ 1849/MT
- Density: 1.53 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 137 MPa
- Elongation at Break: 3.0 %
$ 1665/MT
- Density: 1.49 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 149 MPa
$ 2554/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 159 MPa
$ 2391/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 183 MPa
$ 1825/MT
- Density: 1.35 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 152 MPa
$ 1480/MT
- Density: 1.36 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 183 MPa
$ 1641/MT
- Density: 1.31 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 152 MPa
$ 1995/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 172 MPa
$ 1505/MT
- Density: 1.35 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 145 MPa
$ 1476/MT
- Density: 1.40 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 186 MPa
$ 2060/MT
- Density: 1.62 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 108 MPa
$ 1877/MT
- Density: 1.43 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 138 MPa
- Elongation at Break: 4.5 %
$ 1551/MT
- Density: 1.50 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 149 MPa
$ 1755/MT
- Density: 1.38 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Water Absorption at Saturation: 5.1 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
$ 1512/MT
- Density: 1.46 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 170 MPa
$ 1555/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 2594/MT
- Density: 1.37 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 119 MPa
$ 1487/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 172 MPa
- Elongation at Break: 6.0 %
$ 1642/MT
- Density: 1.49 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 149 MPa
$ 1592/MT
- Density: 1.46 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 170 MPa
$ 2050/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 165 MPa
$ 1650/MT
- Density: 1.33 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 165 MPa
$ 1578/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1448/MT
- Density: 1.24 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 108 MPa
- Elongation at Break: 3.0 %
$ 2232/MT
- Density: 1.36 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1723/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 149 MPa
$ 1964/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 4.5 %
$ 1466/MT
- Density: 1.35 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 172 MPa
$ 1650/MT
- Density: 1.30 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 165 MPa
$ 2595/MT
- Density: 1.49 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 156 MPa
$ 1832/MT
- Density: 1.62 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 115 MPa
$ 1798/MT
- Density: 1.51 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 120 MPa
$ 1468/MT
- Density: 1.30 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 165 MPa
$ 1892/MT
- Density: 1.31 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 145 MPa
$ 1608/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1715/MT
- Density: 1.38 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 190 MPa
$ 1619/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1605/MT
- Specific Gravity: 1.49 g/cc
- Water Absorption: 0.50 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 162 MPa
$ 1459/MT
- Density: 1.38 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 192 MPa
$ 1573/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 165 MPa
$ 1663/MT
- Density: 1.75 g/cc
- Water Absorption: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength: 128 MPa
$ 2261/MT
- Density: 1.33 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 145 MPa
$ 1453/MT
- Density: 1.32 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 141 MPa
$ 1742/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 96.5 MPa
$ 2330/MT
- Density: 1.31 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 148 MPa
$ 2252/MT
- Density: 1.37 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 172 MPa
$ 2174/MT
- Density: 1.62 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 115 MPa
$ 2509/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 179 MPa
$ 1576/MT
- Density: 1.40 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 141 MPa
$ 2504/MT
- Density: 1.35 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 145 MPa
$ 1507/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 159 MPa
$ 2371/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 186 MPa
$ 2280/MT
- Density: 1.62 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 115 MPa
$ 1605/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 4.5 %
$ 1903/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1729/MT
- Density: 1.67 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 162 MPa
$ 1478/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 141 MPa
$ 1862/MT
- Density: 1.38 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Water Absorption at Saturation: 5.1 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
$ 1655/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 179 MPa
- Flexural Yield Strength: 248 MPa
$ 1846/MT
- Density: 1.44 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 72.4 MPa
$ 1457/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 159 MPa
$ 1516/MT
- Density: 1.53 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 134 MPa
- Elongation at Break: 3.0 %
$ 1524/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1903/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1839/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1655/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1537/MT
- Density: 1.54 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength: 124 MPa
$ 1682/MT
- Density: 1.51 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 137 MPa
$ 1561/MT
- Density: 1.33 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0012 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 100 MPa
- Elongation at Break: 8.0 %
$ 2116/MT
- Density: 1.24 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 108 MPa
- Elongation at Break: 3.0 %
$ 1782/MT
- Density: 1.36 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 121 MPa
$ 1910/MT
- Density: 1.32 g/cc
- Water Absorption: 0.97 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 132 MPa
$ 1683/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 100 MPa
$ 1738/MT
- Density: 1.36 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 183 MPa
$ 1445/MT
- Density: 1.40 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 207 MPa
$ 1524/MT
- Density: 1.38 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 179 MPa
$ 1737/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 165 MPa
$ 2354/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 100 MPa
$ 1763/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1610/MT
- Density: 1.37 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 186 MPa
$ 1672/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 172 MPa
$ 1712/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 148 MPa
$ 1917/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 149 MPa
$ 2100/MT
- Density: 1.26 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 93.1 MPa
$ 2052/MT
- Density: 1.50 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 148 MPa
$ 2148/MT
- Density: 1.38 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Water Absorption at Saturation: 5.1 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
$ 1481/MT
- Density: 1.40 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 163 MPa
$ 1566/MT
- Density: 1.68 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 162 MPa
Delivery 30% Glass Fiber Filled Techmer ES
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale listing. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.