$ 1663/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.050 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1733/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 44.1 MPa
- Flexural Strength: 65.7 MPa
$ 1610/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.8 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ash: 9.7 %
- Hardness, Rockwell R: 114
$ 1590/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.8 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ash: 9.7 %
- Hardness, Rockwell R: 114
$ 1690/MT
- Density: 1.07 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 102
- Tensile Strength at Break: 43.4 MPa
- Elongation at Break: 66 %
$ 1613/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.050 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1584/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.3 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.1 MPa
- Elongation at Break: 35 %
$ 2306/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 40.2 MPa
- Flexural Strength: 58.8 MPa
$ 1585/MT
- Specific Gravity: 1.45 g/cc
- Water Absorption: 0.080 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0070 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 1707/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 93
- Tensile Strength at Break: 26.5 MPa
$ 1517/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 42 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 98.1 MPa
$ 1842/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Rockwell R: 95
- Tensile Strength at Break: 26.5 MPa
- Tensile Strength, Yield: 41.2 MPa
- Elongation at Break: 17 %
$ 2228/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 52.0 MPa
$ 2016/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 41.2 MPa
$ 1733/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 5.3 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 114
- Tensile Strength at Break: 39.2 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1547/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 79
- Tensile Strength at Break: 28.4 MPa
$ 1454/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 27 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 61.8 MPa
- Flexural Strength: 93.2 MPa
$ 1720/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 24 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 61.8 MPa
- Flexural Strength: 86.3 MPa
- Flexural Modulus: 2.40 GPa
$ 2083/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 40.2 MPa
$ 1460/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 33 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 56.9 MPa
- Flexural Strength: 87.3 MPa
$ 1516/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 8.9 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 109
- Tensile Strength at Break: 32.4 MPa
- Tensile Strength, Yield: 39.2 MPa
$ 1635/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 3.3 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 39.2 MPa
- Flexural Strength: 58.8 MPa
$ 1474/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 42.2 MPa
- Flexural Strength: 58.8 MPa
$ 1559/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 62.8 MPa
- Flexural Strength: 87.3 MPa
- Flexural Modulus: 2.45 GPa
$ 2246/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.4 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1494/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 88.3 MPa
$ 1878/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 97
- Flexural Strength: 53.9 MPa
- Flexural Modulus: 1.81 GPa
- Izod Impact, Notched: 0.981 J/cm @Thickness 3.17 mm
$ 1711/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
$ 2432/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 26 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 48.1 MPa
$ 1903/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.4 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ash: 31 %
- Hardness, Rockwell R: 112
$ 1544/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 40.2 MPa
- Elongation at Break: 40 %
$ 1486/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
- Tensile Strength at Break: 75.5 MPa
$ 2219/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 38.2 MPa
$ 1693/MT
- Density: 1.05 g/cc
- Water Absorption: 0.20 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 2.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 105
$ 2428/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 38.2 MPa
- Tensile Strength, Yield: 45.1 MPa
$ 1710/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.050 % @Temperature 23.0 °C
- Melt Flow: 29 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 45.1 MPa
$ 1581/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 10.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 51.0 MPa
- Flexural Strength: 76.5 MPa
$ 1458/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 116
- Tensile Strength at Break: 63.7 MPa
$ 2189/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 10.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 47.1 MPa
- Flexural Strength: 60.8 MPa
$ 1711/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 41.2 MPa
- Flexural Strength: 65.7 MPa
$ 1702/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 42.2 MPa
$ 1551/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.050 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1749/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.6 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 39.2 MPa
$ 2575/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 104
- Tensile Strength, Yield: 43.1 MPa
$ 1903/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.4 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 39.2 MPa
$ 1602/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 60.8 MPa
- Flexural Strength: 83.4 MPa
$ 1708/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 99
$ 1657/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 47 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 116
$ 1872/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 9.8 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 34.3 MPa
- Flexural Strength: 47.1 MPa
$ 1976/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 3.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 38.2 MPa
- Elongation at Break: 30 %
$ 2010/MT
- Density: 1.05 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 51.0 MPa @Thickness 3.17 mm
- Elongation at Break: 10 % @Thickness 3.17 mm
$ 1637/MT
- Specific Gravity: 1.15 g/cc
- Melt Flow: 50 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 45.1 MPa
- Tensile Strength, Yield: 56.9 MPa
$ 2247/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Melt Flow: 55 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 59.8 MPa
$ 1495/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 104
- Tensile Strength at Break: 40.7 MPa
$ 1757/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 40.2 MPa
- Flexural Strength: 57.9 MPa
$ 2281/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.3 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 48.1 MPa
$ 2263/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 111
$ 1631/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 63.7 MPa
- Flexural Strength: 88.3 MPa
$ 1851/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 113
- Tensile Strength at Break: 37.3 MPa
$ 1663/MT
- Specific Gravity: 1.28 g/cc
- Melt Flow: 24 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 88.3 MPa
- Flexural Strength: 137 MPa
- Flexural Modulus: 4.51 GPa
$ 1478/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 11.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 31.4 MPa
- Flexural Strength: 51.0 MPa
$ 1644/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 41.2 MPa
$ 1486/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 35.3 MPa
- Tensile Strength, Yield: 53.9 MPa
$ 1765/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 3.7 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 44.1 MPa
- Flexural Strength: 65.7 MPa
$ 1879/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.050 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1444/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 34.3 MPa
- Tensile Strength, Yield: 41.2 MPa
$ 1860/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.6 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ash: 20 %
- Hardness, Rockwell R: 112
$ 1825/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 94
- Tensile Strength, Yield: 39.2 MPa
$ 1828/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 90
$ 1501/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 83.4 MPa
$ 1781/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 33.3 MPa
- Tensile Strength, Yield: 43.1 MPa
$ 1976/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 39.2 MPa
$ 1555/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 63.6 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 48.1 MPa
$ 1851/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 48.0 MPa
$ 1991/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 31.4 MPa
$ 1522/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 28 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 1480/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 70.6 MPa
$ 2038/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 51.0 MPa
- Flexural Strength: 73.5 MPa
$ 2049/MT
- Density: 1.06 g/cc
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 99
- Tensile Strength at Break: 42.7 MPa
- Elongation at Break: 76 %
$ 1603/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 33.3 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 2008/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 32.4 MPa
$ 1507/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 38 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 49.0 MPa
$ 2517/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2123/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 31.4 MPa
$ 1525/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 101.6
- Tensile Strength, Yield: 41.2 MPa
- Izod Impact, Notched: 1.67 J/cm @Thickness 3.17 mm
- Vicat Softening Point: 86.0 °C
$ 2305/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 26 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
- Tensile Strength at Break: 32.4 MPa
$ 1681/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 31.4 MPa
- Tensile Strength, Yield: 39.2 MPa
$ 1703/MT
- Specific Gravity: 1.17 g/cc
- Melt Flow: 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 41.2 MPa
- Flexural Strength: 60.8 MPa
$ 1489/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.2 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 40.2 MPa
$ 1783/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2390/MT
- Specific Gravity: 1.07 g/cc
- Melt Flow: 3.7 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 39.2 MPa
- Flexural Strength: 60.8 MPa
$ 2504/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 0.080 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Melt Flow: 33 g/10 min @Load 5.00 kg, Temperature 250 °C
- Ash: 19 %
$ 1477/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 446 MPa
$ 2063/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 43.1 MPa
- Flexural Strength: 58.8 MPa
$ 1865/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 41.2 MPa
- Elongation at Break: 50 %
$ 1905/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0064 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Melt Flow: 2.9 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1582/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 98
- Tensile Strength, Yield: 37.3 MPa
$ 2449/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.7 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1809/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 46 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 43.1 MPa
$ 1807/MT
- Density: 1.06 g/cc
- Melt Flow: 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 95
- Tensile Strength at Break: 39.3 MPa
- Elongation at Break: 80 %
$ 2437/MT
- Density: 1.04 g/cc
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 49.0 MPa @Thickness 3.17 mm
- Flexural Strength: 70.3 MPa @Thickness 3.17 mm
$ 2212/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 116
- Tensile Strength at Break: 19.6 MPa
- Tensile Strength, Yield: 51.0 MPa
$ 1785/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 39.2 MPa
- Flexural Strength: 52.0 MPa
$ 1596/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 8.8 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 39.2 MPa
- Izod Impact, Notched: 2.16 J/cm @Thickness 6.35 mm
- Vicat Softening Point: 100 °C
$ 2586/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 83.4 MPa
- Flexural Strength: 108 MPa
$ 2355/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.4 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
- Tensile Strength at Break: 29.4 MPa
$ 1675/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 2165/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 51.0 MPa
$ 1627/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1604/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.1 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 94
- Tensile Strength, Yield: 38.2 MPa
$ 1840/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 90
- Tensile Strength at Break: 25.5 MPa
- Tensile Strength, Yield: 31.4 MPa
$ 1707/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 48.3 MPa @Thickness 3.17 mm
$ 2472/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 33.3 MPa
- Tensile Strength, Yield: 43.1 MPa
$ 1826/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 50.0 MPa
$ 1557/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 48 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 63.7 MPa
- Flexural Strength: 94.1 MPa
- Flexural Modulus: 2.75 GPa
$ 1486/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1973/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
- Tensile Strength at Break: 32.4 MPa
$ 1898/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 17.2 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 76.5 MPa
$ 1830/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength: 43.12 MPa @Thickness 3.17 mm
- Elongation at Break: 14 % @Thickness 3.17 mm
$ 2163/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 45.1 MPa
$ 2003/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 260 °C
- Melt Flow: 47 g/10 min @Load 10.0 kg, Temperature 250 °C
$ 1870/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 66.7 MPa
- Tensile Strength, Yield: 62.8 MPa
$ 2138/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Melt Flow: 35 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 103
$ 2163/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 40.2 MPa
$ 1574/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 1.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 96
- Tensile Strength at Break: 33.3 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1568/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 2176/MT
- Specific Gravity: 1.07 g/cc
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 39.2 MPa
- Flexural Strength: 51.0 MPa
- Flexural Modulus: 1.81 GPa
$ 1761/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 32 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 53.9 MPa
- Elongation at Break: 110 %
$ 2146/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
$ 1991/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 46 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 58.8 MPa
- Flexural Strength: 83.4 MPa
$ 1605/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 116
- Tensile Strength at Break: 61.8 MPa
- Tensile Strength, Yield: 59.8 MPa
$ 2225/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 68.6 MPa
$ 1882/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 70.6 MPa
- Flexural Strength: 108 MPa
$ 1884/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Melt Flow: 16 g/10 min
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 39.2 MPa
Delivery ABS Polymer Samsung, Cheil Industries
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.