$ 1600/MT
- Bulk Density: 2.30 g/cc @Temperature 1400 °C
- Bulk Density: 2.40 g/cc @Temperature 800 °C
- Bulk Density: 2.50 g/cc @Temperature 200 °C
- Porosity: 16 %
- Porosity: 17 %
$ 2204/MT
- Bulk Density: 0.900 g/cc @Temperature 200 °C
- Compressive Strength: 2.94 MPa @Temperature 800 °C
- Compressive Strength: 3.43 MPa @Temperature 200 °C
- Compressive Strength: 3.92 MPa @Temperature 1300 °C
- Thermal Conductivity: 0.232 W/m-K @Temperature 500 °C
$ 1556/MT
- Bulk Density: 1.50 g/cc @Temperature 200 °C
- Compressive Strength: 10.8 MPa @Temperature 800 °C
- Compressive Strength: 12.7 MPa @Temperature 1400 °C
- Compressive Strength: 19.6 MPa @Temperature 200 °C
- Thermal Conductivity: 0.488 W/m-K @Temperature 500 °C
$ 1989/MT
- Bulk Density: 2.80 g/cc @Temperature 1400 °C
- Bulk Density: 2.90 g/cc @Temperature 800 °C
- Bulk Density: 3.00 g/cc @Temperature 200 °C
- Porosity: 12 %
- Porosity: 13 %
$ 1570/MT
- Bulk Density: 0.400 g/cc @Temperature 200 °C
- Compressive Strength: 0.392 MPa @Temperature 800 °C
- Compressive Strength: 0.883 MPa @Temperature 200 °C
- Compressive Strength: 0.981 MPa @Temperature 1200 °C
- Thermal Conductivity: 0.139 W/m-K @Temperature 500 °C
$ 1958/MT
- Bulk Density: 2.30 - 2.40 g/cc
- Porosity: 23 %
- Compressive Strength: 39.2 MPa
- Maximum Service Temperature, Air: 1500 °C
- Al2O3: 56 - 58 %
$ 1553/MT
- Bulk Density: 1.25 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00834 GPa @Temperature 1500 °C
$ 1956/MT
- Bulk Density: 2.09 g/cc
- Porosity: 15 %
- Compressive Strength: 88.3 MPa
- Maximum Service Temperature, Air: 1700 °C
- Al2O3: >= 90 %
$ 1643/MT
- Bulk Density: >= 2.30 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 34.3 MPa @Temperature 110 °C
- Compressive Strength: 78.5 MPa @Temperature 1100 °C
- Compressive Strength: 88.3 MPa @Temperature 1500 °C
$ 1899/MT
- Bulk Density: 2.20 g/cc
- Porosity: 22 - 24 %
- Compressive Strength: 24.5 MPa
- Maximum Service Temperature, Air: 1400 °C
- Al2O3: 40 %
$ 1475/MT
- Bulk Density: 1.10 g/cc
- Porosity: 60 %
- Compressive Strength: 1.96 - 2.94 MPa
- Maximum Service Temperature, Air: 1500 °C
- Al2O3: 60 %
- Fe2O3: 1.5 %
$ 1952/MT
- Density: 0.0480 - 0.144 g/cc
- Thermal Conductivity: 0.0299 W/m-K @Temperature 24.0 °C
- Maximum Service Temperature, Air: 800 °C
$ 1721/MT
- Density: 0.620 g/cc
- Thermal Conductivity: 0.113 W/m-K @Temperature 600 °C
- Maximum Service Temperature, Air: 1600 °C
$ 1791/MT
- Bulk Density: 2.40 g/cc
- Porosity: 20 - 22 %
- Compressive Strength: 39.2 MPa
- Maximum Service Temperature, Air: 1520 °C
- Al2O3: 62 %
$ 1844/MT
- Bulk Density: 2.30 g/cc
- Porosity: 22 - 24 %
- Compressive Strength: 29.4 - 39.2 MPa
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: 50 %
$ 1457/MT
- Bulk Density: 2.40 g/cc
- Porosity: 16 %
- Compressive Strength: 88.3 MPa
- Maximum Service Temperature, Air: 1550 °C
- Al2O3: >= 60 %
$ 1673/MT
- Bulk Density: 1.45 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00490 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00980 GPa @Temperature 110 °C
- Modulus of Rupture: 0.01177 GPa @Temperature 1500 °C
$ 1775/MT
- Bulk Density: 2.80 g/cc
- Porosity: 15 %
- Compressive Strength: 88.3 MPa
- Maximum Service Temperature, Air: 1600 °C
- Al2O3: >= 80 %
$ 2053/MT
- Bulk Density: 2.20 g/cc
- Porosity: 16 %
- Compressive Strength: 78.5 MPa
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: >= 45 %
$ 2051/MT
- Bulk Density: 2.00 g/cc
- Porosity: 25 %
- Compressive Strength: 19.6 MPa
- Maximum Service Temperature, Air: 1300 °C
- Al2O3: 30 %
$ 1473/MT
- Bulk Density: >= 2.00 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 24.5 MPa @Temperature 1100 °C
- Compressive Strength: 34.3 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1300 °C
$ 1463/MT
- Density: 0.250 g/cc
- Grain Size: 800 - 1000 µm
- Thermal Conductivity: 0.0570 W/m-K @Temperature 200 °C
$ 1605/MT
- Bulk Density: <= 1.60 g/cc
- Modulus of Rupture: 0.00235 GPa
- Modulus of Rupture: 0.00177 GPa @Treatment Temp. 800 °C
- Modulus of Rupture: 0.00196 GPa @Treatment Temp. 1300 °C
- Compressive Strength: 7.35 MPa
$ 1786/MT
- Bulk Density: >= 2.75 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00588 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0103 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0113 GPa @Temperature 1500 °C
$ 1520/MT
- Density: 0.128 g/cc
- Maximum Service Temperature, Air: 1260 °C
$ 1609/MT
- Bulk Density: 0.850 g/cc
- Porosity: 65 - 70 %
- Compressive Strength: 3.92 MPa
- Maximum Service Temperature, Air: 1500 °C
- Al2O3: 60 %
- Fe2O3: 1.5 %
$ 2162/MT
- Bulk Density: 1.30 g/cc
- Porosity: 50 %
- Compressive Strength: 10.8 - 12.7 MPa
- Maximum Service Temperature, Air: 1400 °C
- Al2O3: 35 - 40 %
- Fe2O3: 2.0 %
$ 2472/MT
- Bulk Density: >= 1.25 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 6.86 MPa @Temperature 1100 °C
- Compressive Strength: 8.83 MPa @Temperature 1300 °C
- Compressive Strength: 13.7 MPa @Temperature 110 °C
$ 1629/MT
- Bulk Density: 2.10 g/cc
- Porosity: 18 - 20 %
- Compressive Strength: 24.5 MPa
- Maximum Service Temperature, Air: 1350 °C
- Al2O3: 34 %
$ 2088/MT
- Bulk Density: 2.80 g/cc
- Porosity: 16 - 18 % @Temperature 1300 °C
- Grain Size: <= 10000 µm
- Modulus of Rupture: 0.0180 GPa @Temperature 1000 °C
- Modulus of Rupture: 0.0200 GPa @Temperature 1100 °C
$ 1461/MT
- Coating Weight: 3000 g/m² @Thickness 1.00 mm
- Maximum Service Temperature, Air: 1550 °C
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: 2.54 %
- CaO: 1.5 %
$ 2104/MT
- Bulk Density: 2.30 g/cc
- Porosity: 16 % @Temperature 1300 °C
- Grain Size: <= 10000 µm
- Modulus of Rupture: 0.0150 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0150 GPa @Temperature 1000 °C
$ 1789/MT
- Grain Size: <= 1000 µm
- Maximum Service Temperature, Air: 1500 °C
- Al2O3: 50 %
- Fe2O3: 3.0 %
- Sintering Temperature: 1100 °C
$ 1503/MT
- Bulk Density: 2.50 g/cc
- Porosity: 22 - 24 %
- Compressive Strength: 29.4 - 39.2 MPa
- Maximum Service Temperature, Air: 1460 °C
- Al2O3: 60 %
$ 1677/MT
- Bulk Density: 1.10 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00883 GPa @Temperature 1500 °C
$ 1500/MT
- Bulk Density: 2.90 g/cc
- Porosity: 12 %
- Compressive Strength: 177 MPa
- Maximum Service Temperature, Air: 1600 °C
- Al2O3: >= 90 %
$ 1602/MT
- Bulk Density: 0.850 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00392 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00785 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00981 GPa @Temperature 1500 °C
$ 1603/MT
- Bulk Density: >= 2.75 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00490 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00987 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0118 GPa @Temperature 1500 °C
$ 1599/MT
- Bulk Density: 2.30 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 39.2 - 49.0 MPa
- Maximum Service Temperature, Air: 1460 °C
- Al2O3: 42 %
$ 2084/MT
- Bulk Density: 2.10 g/cc
- Porosity: 25 - 27 %
- Compressive Strength: 39.2 MPa
- Al2O3: 50 %
- Fe2O3: 0.30 %
$ 1649/MT
- Bulk Density: >= 2.75 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00343 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00735 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00883 GPa @Temperature 1500 °C
$ 1629/MT
- Bulk Density: 2.10 g/cc
- Grain Size: <= 8000 µm
- Modulus of Rupture: 0.0160 GPa @Temperature 1000 °C
- Modulus of Rupture: 0.0200 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0200 GPa @Temperature 1400 °C
$ 1523/MT
- Bulk Density: 1.45 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00588 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0103 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0113 GPa @Temperature 1500 °C
$ 1904/MT
- Bulk Density: 2.10 g/cc
- Porosity: 23 - 25 %
- Compressive Strength: 34.3 MPa
- Al2O3: 45 %
- Fe2O3: 1.5 %
$ 1953/MT
- Bulk Density: <= 2.05 g/cc
- Modulus of Rupture: 0.00245 GPa @Treatment Temp. 800 °C
- Modulus of Rupture: 0.00588 GPa @Treatment Temp. 800 °C
- Compressive Strength: 20.6 MPa
- Compressive Strength: 24.5 MPa
$ 1606/MT
- Bulk Density: >= 2.65 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 29.4 MPa @Temperature 110 °C
- Compressive Strength: 53.9 MPa @Temperature 1100 °C
- Compressive Strength: 78.5 MPa @Temperature 1500 °C
$ 1455/MT
- Bulk Density: >= 2.20 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00883 GPa @Temperature 1500 °C
$ 1659/MT
- Bulk Density: >= 2.60 g/cc
- Grain Size: <= 3000 µm
- Compressive Strength: >= 24.5 MPa @Temperature 110 °C
- Compressive Strength: >= 53.9 MPa @Temperature 1100 °C
- Maximum Service Temperature, Air: 1700 °C
$ 1861/MT
- Bulk Density: <= 1.10 g/cc
- Modulus of Rupture: 0.00118 GPa
- Modulus of Rupture: 0.000490 GPa @Treatment Temp. 1100 °C
- Modulus of Rupture: 0.000588 GPa @Treatment Temp. 800 °C
- Compressive Strength: 1.18 MPa
$ 2071/MT
- Bulk Density: 0.550 g/cc
- Porosity: 80 %
- Compressive Strength: 1.96 MPa
- Maximum Service Temperature, Air: 1400 °C
- Al2O3: 40 %
- Fe2O3: 2.0 %
$ 1489/MT
- Bulk Density: 2.60 g/cc
- Porosity: 16 %
- Compressive Strength: 88.3 MPa
- Maximum Service Temperature, Air: 1550 °C
- Al2O3: >= 70 %
$ 1526/MT
- Bulk Density: >= 2.80 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00441 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00932 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0108 GPa @Temperature 1500 °C
$ 1581/MT
- Bulk Density: 2.80 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 58.8 MPa
- Maximum Service Temperature, Air: 1600 °C
- Al2O3: 80 %
$ 1758/MT
- Bulk Density: <= 1.20 g/cc
- Modulus of Rupture: 0.00127 GPa
- Modulus of Rupture: 0.000980 GPa @Treatment Temp. 800 °C
- Modulus of Rupture: 0.00118 GPa @Treatment Temp. 1300 °C
- Compressive Strength: 2.94 MPa
$ 1524/MT
- Bulk Density: >= 2.10 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 24.5 MPa @Temperature 1100 °C
- Compressive Strength: 49.0 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1350 °C
$ 1796/MT
- Bulk Density: 1.35 g/cc
- Compressive Strength: 3.43 MPa
- Maximum Service Temperature, Air: 1750 °C
- Al2O3: 72 %
- Fe2O3: 0.50 %
- Permanent Linear Change: -0.5%
$ 2030/MT
- Bulk Density: >= 2.80 g/cc
- Grain Size: <= 3000 µm
- Compressive Strength: >= 58.8 MPa @Temperature 1100 °C
- Compressive Strength: >= 78.5 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1700 °C
$ 1742/MT
- Bulk Density: >= 2.80 g/cc
- Grain Size: <= 10000 µm
- Compressive Strength: 78.5 MPa @Temperature 110 °C
- Compressive Strength: 98.1 MPa @Temperature 1100 °C
- Compressive Strength: 118 MPa @Temperature 1500 °C
$ 1563/MT
- Bulk Density: <= 0.850 g/cc
- Modulus of Rupture: 0.000392 GPa
- Modulus of Rupture: 0.000294 GPa @Treatment Temp. 1100 °C
- Modulus of Rupture: 0.000294 GPa @Treatment Temp. 3400 °C
- Compressive Strength: 0.392 MPa
$ 2193/MT
- Bulk Density: >= 3.00 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.0118 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0196 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0255 GPa @Temperature 1500 °C
$ 1731/MT
- Bulk Density: >= 2.70 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 34.3 MPa @Temperature 110 °C
- Compressive Strength: 68.6 MPa @Temperature 1100 °C
- Compressive Strength: 88.3 MPa @Temperature 1500 °C
$ 1706/MT
- Bulk Density: >= 2.10 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00834 GPa @Temperature 1500 °C
$ 1817/MT
- Bulk Density: 2.60 g/cc
- Porosity: 18 %
- Compressive Strength: 78.5 MPa
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: >= 70 %
$ 2300/MT
- Bulk Density: 1.00 g/cc @Temperature 200 °C
- Compressive Strength: 3.43 MPa @Temperature 800 °C
- Compressive Strength: 4.41 MPa @Temperature 1300 °C
- Compressive Strength: 4.90 MPa @Temperature 200 °C
- Thermal Conductivity: 0.256 W/m-K @Temperature 500 °C
$ 1605/MT
- Bulk Density: 2.35 g/cc
- Grain Size: <= 10000 µm
- Modulus of Rupture: 0.00000157 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00000167 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00000196 GPa @Temperature 1500 °C
$ 1575/MT
- Bulk Density: 2.80 g/cc
- Grain Size: <= 10000 µm
- Modulus of Rupture: 0.0200 GPa @Temperature 1000 °C
- Modulus of Rupture: 0.0240 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0240 GPa @Temperature 1400 °C
$ 1963/MT
- Bulk Density: 2.90 g/cc
- Porosity: 12 %
- Compressive Strength: 118 MPa
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: >= 70 %
$ 1660/MT
- Bulk Density: 1.10 g/cc
- Porosity: 55 %
- Compressive Strength: 3.43 - 4.41 MPa
- Maximum Service Temperature, Air: 1400 °C
- Al2O3: 40 %
- Fe2O3: 2.0 %
$ 1728/MT
- Bulk Density: >= 2.40 g/cc
- Grain Size: <= 10000 µm
- Compressive Strength: 68.6 MPa @Temperature 110 °C
- Compressive Strength: 88.3 MPa @Temperature 1100 °C
- Compressive Strength: 118 MPa @Temperature 1500 °C
$ 2083/MT
- Bulk Density: 2.30 g/cc @Temperature 1400 °C
- Bulk Density: 2.40 g/cc @Temperature 800 °C
- Bulk Density: 2.50 g/cc @Temperature 200 °C
- Porosity: 20 %
- Porosity: 21 %
$ 1864/MT
- Bulk Density: 0.400 g/cc @Temperature 200 °C
- Compressive Strength: 0.392 MPa @Temperature 800 °C
- Compressive Strength: 0.883 MPa @Temperature 200 °C
- Compressive Strength: 0.981 MPa @Temperature 1200 °C
- Thermal Conductivity: 0.139 W/m-K @Temperature 500 °C
$ 1910/MT
- Bulk Density: 0.600 g/cc @Temperature 200 °C
- Compressive Strength: 0.588 MPa @Temperature 800 °C
- Compressive Strength: 1.47 MPa @Temperature 1300 °C
- Compressive Strength: 1.77 MPa @Temperature 200 °C
- Thermal Conductivity: 0.163 W/m-K @Temperature 500 °C
$ 1538/MT
- Bulk Density: 0.600 g/cc @Temperature 200 °C
- Compressive Strength: 0.588 MPa @Temperature 800 °C
- Compressive Strength: 1.47 MPa @Temperature 1300 °C
- Compressive Strength: 1.77 MPa @Temperature 200 °C
- Thermal Conductivity: 0.163 W/m-K @Temperature 500 °C
$ 1983/MT
- Bulk Density: 1.20 g/cc @Temperature 200 °C
- Compressive Strength: 4.90 MPa @Temperature 800 °C
- Compressive Strength: 6.86 MPa @Temperature 1350 °C
- Compressive Strength: 8.83 MPa @Temperature 200 °C
- Thermal Conductivity: 0.395 W/m-K @Temperature 500 °C
$ 2472/MT
- Bulk Density: 2.40 g/cc @Temperature 1400 °C
- Bulk Density: 2.50 g/cc @Temperature 800 °C
- Bulk Density: 2.60 g/cc @Temperature 200 °C
- Porosity: 16 %
- Porosity: 17 %
$ 1524/MT
- Bulk Density: 2.60 g/cc @Temperature 1400 °C
- Bulk Density: 2.70 g/cc @Temperature 800 °C
- Bulk Density: 2.80 g/cc @Temperature 200 °C
- Porosity: 15 %
- Porosity: 16 %
$ 1844/MT
- Bulk Density: 1.70 g/cc @Temperature 1400 °C
- Bulk Density: 1.80 g/cc @Temperature 800 °C
- Bulk Density: 1.90 g/cc @Temperature 200 °C
- Porosity: 17 %
- Porosity: 18 %
$ 1823/MT
- Bulk Density: 1.40 g/cc @Temperature 1400 °C
- Bulk Density: 1.45 g/cc @Temperature 800 °C
- Bulk Density: 1.50 g/cc @Temperature 200 °C
- Porosity: 38 %
- Porosity: 40 %
$ 2047/MT
- Bulk Density: >= 2.30 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00981 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0123 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0162 GPa @Temperature 1500 °C
$ 1768/MT
- Bulk Density: 2.50 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 58.8 MPa
- Maximum Service Temperature, Air: 1600 °C
- Al2O3: 62 %
$ 1555/MT
- Bulk Density: >= 2.65 g/cc
- Grain Size: <= 10000 µm
- Compressive Strength: 39.2 MPa @Temperature 110 °C
- Compressive Strength: 78.5 MPa @Temperature 1100 °C
- Compressive Strength: 98.1 MPa @Temperature 1500 °C
$ 1905/MT
- Bulk Density: 1.25 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00834 GPa @Temperature 1500 °C
$ 1567/MT
- Bulk Density: >= 2.80 g/cc
- Grain Size: <= 6000 µm
- Compressive Strength: 29.4 MPa @Temperature 110 °C
- Compressive Strength: 73.5 MPa @Temperature 1100 °C
- Compressive Strength: 88.3 MPa @Temperature 1500 °C
$ 2107/MT
- Bulk Density: 2.00 g/cc
- Grain Size: >= 5000 µm
- Compressive Strength: 22.1 MPa @Temperature 1300 °C
- Compressive Strength: 24.5 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1400 °C
$ 1812/MT
- Bulk Density: 2.10 g/cc
- Porosity: 23 - 25 %
- Compressive Strength: 19.6 - 24.5 MPa
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: 42 %
$ 2026/MT
- Bulk Density: 2.30 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 39.2 - 49.0 MPa
- Maximum Service Temperature, Air: 1480 °C
- Al2O3: 45 %
$ 1478/MT
- Bulk Density: 3.00 g/cc
- Porosity: 15 %
- Compressive Strength: 93.2 MPa
- Maximum Service Temperature, Air: 1800 °C
- Al2O3: >= 94 %
$ 1535/MT
- Density: 0.128 g/cc
- Thermal Conductivity: 0.126 W/m-K @Temperature 600 °C
- Maximum Service Temperature, Air: 1425 °C
$ 1534/MT
- Bulk Density: 0.700 - 0.800 g/cc
- Porosity: 65 %
- Compressive Strength: 0.981 - 1.47 MPa
- Maximum Service Temperature, Air: 1200 °C
- Al2O3: 30 %
- Fe2O3: 2.0 %
$ 1902/MT
- Density: 0.0650 g/cc
- Maximum Service Temperature, Air: 1260 °C
$ 1543/MT
- Bulk Density: 2.20 g/cc
- Porosity: 23 %
- Compressive Strength: 39.2 MPa
- Al2O3: 60 %
- Fe2O3: 1.0 %
$ 2077/MT
- Bulk Density: 2.10 g/cc
- Porosity: 25 %
- Compressive Strength: 19.6 MPa
- Maximum Service Temperature, Air: 1400 °C
- Al2O3: 40 %
$ 1499/MT
- Bulk Density: 1.60 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00312 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00735 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00883 GPa @Temperature 1500 °C
$ 2226/MT
- Bulk Density: <= 1.20 g/cc
- Modulus of Rupture: 0.00108 GPa
- Modulus of Rupture: 0.000686 GPa @Treatment Temp. 800 °C
- Modulus of Rupture: 0.00108 GPa @Treatment Temp. 1300 °C
- Compressive Strength: 2.45 MPa
$ 1672/MT
- Bulk Density: 2.30 g/cc
- Porosity: 22 - 24 %
- Compressive Strength: 29.4 - 39.2 MPa
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: 45 %
$ 1796/MT
- Bulk Density: 2.40 g/cc
- Grain Size: >= 5000 µm
- Compressive Strength: 34.3 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: 70 %
$ 1475/MT
- Bulk Density: >= 2.40 g/cc
- Grain Size: <= 3000 µm
- Compressive Strength: >= 19.6 MPa @Temperature 110 °C
- Compressive Strength: >= 49.0 MPa @Temperature 1100 °C
- Maximum Service Temperature, Air: 1550 °C
$ 2173/MT
- Bulk Density: >= 1.80 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 19.6 MPa @Temperature 800 °C
- Compressive Strength: 24.5 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 800 °C
$ 2073/MT
- Density: 0.100 - 0.150 g/cc
- Thermal Conductivity: 0.440 W/m-K @Temperature 200 °C
- Maximum Service Temperature, Air: 700 °C
$ 1624/MT
- Density: 0.200 g/cc
- Maximum Service Temperature, Air: 1260 °C
$ 2219/MT
- Density: 2.50 g/cc
- Density: 2.52 g/cc
- Grain Size: <= 4000 µm
- Compressive Strength: >= 9.81 MPa @Temperature 110 °C, Time 86400 sec
- Compressive Strength: 10.8 MPa @Temperature 110 °C, Time 86400 sec
$ 2470/MT
- Bulk Density: 2.60 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 78.5 MPa
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: 72 - 75 %
$ 2193/MT
- Bulk Density: 2.10 g/cc
- Grain Size: >= 5000 µm
- Compressive Strength: 29.4 MPa @Temperature 1300 °C
- Compressive Strength: 39.2 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1350 °C
$ 1491/MT
- Bulk Density: >= 2.00 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00883 GPa @Temperature 1500 °C
$ 1800/MT
- Bulk Density: 1.60 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00883 GPa @Temperature 1500 °C
$ 1541/MT
- Bulk Density: >= 2.60 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.0118 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0147 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0167 GPa @Temperature 1500 °C
$ 1491/MT
- Bulk Density: 1.10 g/cc
- Compressive Strength: 3.43 MPa
- Maximum Service Temperature, Air: 1550 °C
- Al2O3: 55 %
- Fe2O3: 1.0 %
- Permanent Linear Change: -1.0%
$ 2274/MT
- Bulk Density: 2.20 g/cc
- Porosity: 22 - 24 %
- Compressive Strength: 34.3 MPa
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: 50 %
$ 1966/MT
- Bulk Density: 2.60 g/cc
- Porosity: 22 - 24 %
- Compressive Strength: 39.2 - 58.8 MPa
- Maximum Service Temperature, Air: 1480 °C
- Al2O3: 70 %
$ 1493/MT
- Bulk Density: >= 2.70 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.0127 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0167 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0226 GPa @Temperature 1500 °C
$ 1615/MT
- Bulk Density: 2.50 g/cc
- Porosity: 20 - 22 %
- Compressive Strength: 58.8 MPa
- Maximum Service Temperature, Air: 1600 °C
- Al2O3: 72 %
$ 2089/MT
- Bulk Density: <= 0.900 g/cc
- Modulus of Rupture: 0.000785 GPa
- Modulus of Rupture: 0.000686 GPa @Treatment Temp. 800 °C
- Modulus of Rupture: 0.000785 GPa @Treatment Temp. 1300 °C
- Compressive Strength: 1.96 MPa
$ 2087/MT
- Bulk Density: >= 2.65 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00392 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00785 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00981 GPa @Temperature 1500 °C
$ 1606/MT
- Bulk Density: >= 3.10 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.0157 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0186 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0265 GPa @Temperature 1500 °C
$ 1559/MT
- Bulk Density: 2.20 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 29.4 - 39.2 MPa
- Maximum Service Temperature, Air: 1420 °C
- Al2O3: 40 %
$ 1448/MT
- Bulk Density: 2.20 g/cc
- Porosity: 18 - 22 %
- Compressive Strength: 24.5 - 29.4 MPa
- Maximum Service Temperature, Air: 1450 °C
- Al2O3: 42 %
$ 1610/MT
- Bulk Density: 0.500 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.00441 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00931 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0108 GPa @Temperature 1500 °C
$ 2303/MT
- Bulk Density: 2.60 g/cc
- Porosity: 16 %
- Compressive Strength: 137 MPa
- Maximum Service Temperature, Air: 1550 °C
- Al2O3: >= 60 %
$ 1712/MT
- Bulk Density: >= 2.90 g/cc
- Grain Size: <= 10000 µm
- Compressive Strength: 93.2 MPa @Temperature 110 °C
- Compressive Strength: 101 MPa @Temperature 1200 °C
- Compressive Strength: 142 MPa @Temperature 1100 °C
$ 1465/MT
- Bulk Density: >= 2.70 g/cc
- Grain Size: <= 10000 µm
- Compressive Strength: 34.3 MPa @Temperature 110 °C
- Compressive Strength: 73.5 MPa @Temperature 1100 °C
- Compressive Strength: 88.3 MPa @Temperature 1500 °C
$ 1540/MT
- Bulk Density: >= 2.90 g/cc
- Grain Size: <= 10000 µm
- Modulus of Rupture: 0.0137 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0177 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0216 GPa @Temperature 1500 °C
$ 1481/MT
- Bulk Density: >= 2.30 g/cc
- Grain Size: <= 3000 µm
- Compressive Strength: >= 68.6 MPa @Temperature 1100 °C
- Compressive Strength: >= 73.5 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1500 °C
$ 1949/MT
- Bulk Density: 3.00 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 88.3 MPa
- Maximum Service Temperature, Air: 1500 °C
- Al2O3: 88 %
$ 1844/MT
- Bulk Density: 0.900 g/cc
- Compressive Strength: 1.47 MPa
- Maximum Service Temperature, Air: 1400 °C
- Al2O3: 55 %
- Fe2O3: 1.0 %
- Permanent Linear Change: -1.0%
$ 1745/MT
- Bulk Density: 2.50 g/cc
- Porosity: 12 %
- Compressive Strength: 88.3 MPa
- Maximum Service Temperature, Air: 1500 °C
- Fe2O3: <= 1.0 %
$ 2392/MT
- Bulk Density: 3.00 g/cc
- Porosity: 16 - 18 %
- Compressive Strength: 58.8 MPa
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: 90 %
$ 1714/MT
- Bulk Density: >= 2.70 g/cc
- Grain Size: <= 3000 µm
- Compressive Strength: >= 39.2 MPa @Temperature 110 °C
- Compressive Strength: >= 68.6 MPa @Temperature 1100 °C
- Maximum Service Temperature, Air: 1750 °C
$ 2168/MT
- Bulk Density: >= 2.70 g/cc
- Grain Size: <= 10000 µm
- Compressive Strength: 68.6 MPa @Temperature 110 °C
- Compressive Strength: 98.1 MPa @Temperature 1100 °C
- Compressive Strength: 118 MPa @Temperature 1500 °C
$ 2334/MT
- Bulk Density: >= 2.00 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00294 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.00637 GPa @Temperature 110 °C
- Modulus of Rupture: 0.00834 GPa @Temperature 1500 °C
$ 1837/MT
- Bulk Density: >= 2.35 g/cc
- Grain Size: <= 10000 µm
- Modulus of Rupture: 0.0118 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0147 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0177 GPa @Temperature 1500 °C
$ 1563/MT
- Bulk Density: 2.50 g/cc
- Porosity: 16 - 18 % @Temperature 1300 °C
- Grain Size: <= 10000 µm
- Modulus of Rupture: 0.0130 GPa @Temperature 1000 °C
- Modulus of Rupture: 0.0150 GPa @Temperature 1100 °C
$ 2312/MT
- Bulk Density: >= 2.75 g/cc
- Grain Size: <= 10000 µm
- Compressive Strength: 98.1 MPa @Temperature 110 °C
- Compressive Strength: 118 MPa @Temperature 1100 °C
- Compressive Strength: 127 MPa @Temperature 1500 °C
$ 1528/MT
- Bulk Density: >= 2.50 g/cc
- Grain Size: <= 5000 µm
- Compressive Strength: 39.2 MPa @Temperature 110 °C
- Compressive Strength: 58.8 MPa @Temperature 110 °C
- Maximum Service Temperature, Air: 1400 °C
$ 2237/MT
- Bulk Density: >= 2.75 g/cc
- Grain Size: <= 5000 µm
- Modulus of Rupture: 0.00735 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0118 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0127 GPa @Temperature 1500 °C
$ 1746/MT
- Bulk Density: 2.00 g/cc
- Porosity: 18 %
- Compressive Strength: 68.6 MPa
- Maximum Service Temperature, Air: 1350 °C
- Al2O3: >= 40 %
$ 1590/MT
- Bulk Density: >= 3.00 g/cc
- Grain Size: <= 6000 µm
- Modulus of Rupture: 0.0137 GPa @Temperature 110 °C
- Modulus of Rupture: 0.0196 GPa @Temperature 1100 °C
- Modulus of Rupture: 0.0265 GPa @Temperature 1500 °C
$ 1648/MT
- Density: 0.180 g/cc
- Thermal Conductivity: 0.139 W/m-K @Temperature 600 °C
- Maximum Service Temperature, Air: 1600 °C
Delivery Ceramic Sharadaa Ceramics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
vessels for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.