$ 1531/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: >= 65
- Tensile Strength, Ultimate: 441 - 490 MPa
- Tensile Strength, Yield: 427 - 469 MPa
- Elongation at Break: >= 1.0 %
$ 1705/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: >= 61
- Tensile Strength, Ultimate: >= 359 MPa
- Tensile Strength, Yield: >= 352 MPa
- Elongation at Break: <= 3.0 %
$ 1506/MT
- Density: 8.89 g/cc
- Hardness, Rockwell 30T: 76 - 80
- Tensile Strength, Ultimate: 586 - 689 MPa
- Tensile Strength, Yield: 572 - 669 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1955/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 38 - 54
- Tensile Strength, Ultimate: 276 - 310 MPa
- Tensile Strength, Yield: 193 - 303 MPa
- Elongation at Break: 13 - 32 %
$ 1459/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 18 - 51
- Tensile Strength, Ultimate: 234 - 290 MPa
- Tensile Strength, Yield: 179 - 269 MPa
- Elongation at Break: 13 - 33 %
$ 1962/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 552 - 689 MPa
- Tensile Strength, Yield: >= 448 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 131 GPa
$ 1486/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 43 - 57
- Tensile Strength, Ultimate: 338 - 407 MPa
- Tensile Strength, Yield: 145 - 317 MPa
- Elongation at Break: 34 - 59 %
$ 1453/MT
- Density: 8.75 g/cc
- Hardness, Rockwell 30T: 63 - 68
- Tensile Strength, Ultimate: 393 - 462 MPa
- Tensile Strength, Yield: 352 - 414 MPa
- Elongation at Break: 4.0 - 12 %
$ 1970/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 76 - 80
- Tensile Strength, Ultimate: 655 - 758 MPa
- Tensile Strength, Yield: 634 - 745 MPa
- Elongation at Break: 1.0 - 3.0 %
$ 1477/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 42 - 57
- Tensile Strength, Ultimate: 331 - 400 MPa
- Tensile Strength, Yield: 124 - 276 MPa
- Elongation at Break: 18 - 35 %
$ 1716/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 46 - 57
- Tensile Strength, Ultimate: 290 - 359 MPa
- Tensile Strength, Yield: 255 - 352 MPa
- Elongation at Break: 5.0 - 29 %
$ 1628/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 71 - 78
- Tensile Strength, Ultimate: 552 - 565 MPa
- Tensile Strength, Yield: 483 - 586 MPa
- Elongation at Break: 18 - 32 %
$ 1518/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 16 - 60
- Tensile Strength, Ultimate: 310 - 421 MPa
- Tensile Strength, Yield: 68.9 - 228 MPa
- Elongation at Break: 40 - 67 %
$ 1469/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 621 - 724 MPa
- Tensile Strength, Yield: >= 517 MPa
- Elongation at Break: >= 6.0 %
- Tensile Modulus: 131 GPa
$ 1878/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: <= 393 MPa
- Elongation at Break: >= 25 %
- Tensile Modulus: 117 GPa
- CTE, linear: 17.3 µm/m-°C @Temperature 20.0 - 300 °C
$ 1724/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 67 - 72
- Tensile Strength, Ultimate: 455 - 552 MPa
- Tensile Strength, Yield: 414 - 538 MPa
- Elongation at Break: 3.0 - 10 %
$ 1584/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 43 - 57
- Tensile Strength, Ultimate: 255 - 317 MPa
- Tensile Strength, Yield: 207 - 303 MPa
- Elongation at Break: 8.0 - 32 %
$ 1563/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 66 - 74
- Tensile Strength, Ultimate: 462 - 565 MPa
- Tensile Strength, Yield: 441 - 552 MPa
- Elongation at Break: 6.0 - 15 %
$ 1680/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 76 - 80
- Tensile Strength, Ultimate: 662 - 752 MPa
- Tensile Strength, Yield: 634 - 717 MPa
- Elongation at Break: 1.0 - 4.0 %
$ 1495/MT
- Density: 8.89 g/cc
- Hardness, Rockwell 30T: 66 - 75
- Tensile Strength, Ultimate: 517 - 621 MPa
- Tensile Strength, Yield: 503 - 607 MPa
- Elongation at Break: 1.0 - 5.0 %
$ 1510/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 54 - 62
- Tensile Strength, Ultimate: 296 - 359 MPa
- Tensile Strength, Yield: 283 - 345 MPa
- Elongation at Break: 3.0 - 16 %
$ 1902/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 359 - 448 MPa
- Tensile Strength, Yield: 296 - 407 MPa
- Elongation at Break: >= 15 %
- Tensile Modulus: 117 GPa
$ 1889/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 324 - 414 MPa
- Tensile Strength, Yield: 303 - 407 MPa
- Elongation at Break: >= 5.0 %
- Tensile Modulus: 117 GPa
$ 2159/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 71 - 77
- Tensile Strength, Ultimate: 503 - 586 MPa
- Tensile Strength, Yield: 490 - 565 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1564/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 67 - 71
- Tensile Strength, Ultimate: 441 - 496 MPa
- Tensile Strength, Yield: 414 - 462 MPa
- Elongation at Break: 1.0 - 3.0 %
$ 1645/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 58 - 64
- Tensile Strength, Ultimate: 359 - 427 MPa
- Tensile Strength, Yield: 338 - 407 MPa
- Elongation at Break: 3.0 - 10 %
$ 1600/MT
- Density: 8.77 g/cc
- Hardness, Rockwell 30T: >= 76
- Tensile Strength, Ultimate: >= 634 MPa
- Tensile Strength, Yield: >= 600 MPa
- Elongation at Break: >= 1.0 %
$ 1685/MT
- Density: 8.77 g/cc
- Hardness, Rockwell 30T: 73 - 77
- Tensile Strength, Ultimate: 579 - 648 MPa
- Tensile Strength, Yield: 558 - 683 MPa
- Elongation at Break: 1.0 - 4.0 %
$ 1692/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 18 - 51
- Tensile Strength, Ultimate: 234 - 290 MPa
- Tensile Strength, Yield: 179 - 269 MPa
- Elongation at Break: 13 - 33 %
$ 1583/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 74 - 78
- Tensile Strength, Ultimate: 607 - 710 MPa
- Tensile Strength, Yield: 586 - 703 MPa
- Elongation at Break: 2.0 - 6.0 %
$ 2553/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 68 - 72
- Tensile Strength, Ultimate: 469 - 531 MPa
- Tensile Strength, Yield: 448 - 510 MPa
- Elongation at Break: 4.0 - 8.0 %
$ 1491/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 45 - 57
- Tensile Strength, Ultimate: 386 - 448 MPa
- Tensile Strength, Yield: 159 - 241 MPa
- Elongation at Break: 60 - 67 %
$ 1685/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 552 - 689 MPa
- Tensile Strength, Yield: >= 448 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 131 GPa
$ 1530/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 538 - 627 MPa
- Tensile Strength, Yield: 490 - 621 MPa
- Elongation at Break: >= 5.0 %
- Tensile Modulus: 117 GPa
$ 1864/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 414 - 483 MPa
- Tensile Strength, Yield: 400 - 483 MPa
- Elongation at Break: >= 2.0 %
- Tensile Modulus: 117 GPa
$ 1494/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 68 - 69
- Tensile Strength, Ultimate: 483 - 524 MPa
- Tensile Strength, Yield: 462 - 510 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 2220/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 67 - 69
- Tensile Strength, Ultimate: 462 - 503 MPa
- Tensile Strength, Yield: 441 - 490 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1454/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 34 - 51
- Tensile Strength, Ultimate: 255 - 324 MPa
- Tensile Strength, Yield: 103 - 317 MPa
- Elongation at Break: 15 - 45 %
$ 1603/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 69 - 70
- Tensile Strength, Ultimate: 503 - 552 MPa
- Tensile Strength, Yield: 483 - 531 MPa
- Elongation at Break: >= 1.0 %
$ 1510/MT
- Density: 8.77 g/cc
- Hardness, Rockwell 30T: 45 - 65
- Tensile Strength, Ultimate: 310 - 407 MPa
- Tensile Strength, Yield: 138 - 372 MPa
- Elongation at Break: 16 - 40 %
$ 2270/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: >= 455 MPa
- Tensile Strength, Yield: >= 441 MPa
- Elongation at Break: >= 1.0 %
- Tensile Modulus: 117 GPa
$ 1459/MT
- Density: 8.75 g/cc
- Hardness, Rockwell 30T: 42 - 57
- Tensile Strength, Ultimate: 303 - 372 MPa
- Tensile Strength, Yield: 159 - 331 MPa
- Elongation at Break: 15 - 39 %
$ 1695/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 63 - 75
- Tensile Strength, Ultimate: 476 - 579 MPa
- Tensile Strength, Yield: 352 - 517 MPa
- Elongation at Break: 25 - 49 %
$ 1498/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 60 - 66
- Tensile Strength, Ultimate: 345 - 400 MPa
- Tensile Strength, Yield: 331 - 393 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 1637/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 43 - 57
- Tensile Strength, Ultimate: 255 - 317 MPa
- Tensile Strength, Yield: 207 - 303 MPa
- Elongation at Break: 8.0 - 32 %
$ 1453/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 47 - 59
- Tensile Strength, Ultimate: 283 - 345 MPa
- Tensile Strength, Yield: 269 - 331 MPa
- Elongation at Break: 5.0 - 24 %
$ 1997/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 621 - 724 MPa
- Tensile Strength, Yield: >= 517 MPa
- Elongation at Break: >= 6.0 %
- Tensile Modulus: 131 GPa
$ 1767/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 43 - 63
- Tensile Strength, Ultimate: 338 - 421 MPa
- Tensile Strength, Yield: 152 - 359 MPa
- Elongation at Break: 32 - 50 %
$ 1558/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 71 - 75
- Tensile Strength, Ultimate: 524 - 627 MPa
- Tensile Strength, Yield: 510 - 607 MPa
- Elongation at Break: 7.0 - 11 %
$ 1656/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 73 - 78
- Tensile Strength, Ultimate: 579 - 683 MPa
- Tensile Strength, Yield: 558 - 655 MPa
- Elongation at Break: 1.0 - 6.0 %
$ 1905/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 56 - 64
- Tensile Strength, Ultimate: 324 - 386 MPa
- Tensile Strength, Yield: 317 - 379 MPa
- Elongation at Break: 3.0 - 5.0 %
$ 1683/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 53 - 69
- Tensile Strength, Ultimate: 400 - 503 MPa
- Tensile Strength, Yield: 324 - 469 MPa
- Elongation at Break: 10 - 38 %
$ 2438/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 78 - 83
- Tensile Strength, Ultimate: 724 - 820 MPa
- Tensile Strength, Yield: 689 - 779 MPa
- Elongation at Break: 3.0 - 9.0 %
$ 2530/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 621 - 758 MPa
- Tensile Strength, Yield: >= 586 MPa
- Elongation at Break: >= 4.0 %
- Tensile Modulus: 131 GPa
$ 1644/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 66 - 73
- Tensile Strength, Ultimate: 469 - 545 MPa
- Tensile Strength, Yield: 421 - 517 MPa
- Elongation at Break: 10 - 20 %
$ 1566/MT
- Density: 8.77 g/cc
- Tensile Strength, Ultimate: 483 - 641 MPa
- Tensile Strength, Yield: 476 - 627 MPa
- Elongation at Break: >= 8.0 %
- Tensile Modulus: 131 GPa
$ 1863/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 72 - 78
- Tensile Strength, Ultimate: 538 - 607 MPa
- Tensile Strength, Yield: >= 524 MPa
- Elongation at Break: >= 1.0 %
$ 1753/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 421 - 510 MPa
- Tensile Strength, Yield: 372 - 483 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 117 GPa
$ 1529/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 71 - 75
- Tensile Strength, Ultimate: 517 - 607 MPa
- Tensile Strength, Yield: 503 - 579 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 1642/MT
- Density: 8.77 g/cc
- Tensile Strength, Ultimate: 600 - 696 MPa
- Tensile Strength, Yield: 538 - 689 MPa
- Elongation at Break: >= 5.0 %
- Tensile Modulus: 131 GPa
$ 1770/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 51 - 72
- Tensile Strength, Ultimate: 400 - 496 MPa
- Tensile Strength, Yield: 379 - 490 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 1507/MT
- Density: 8.77 g/cc
- Tensile Strength, Ultimate: 696 - 779 MPa
- Tensile Strength, Yield: 655 - 779 MPa
- Elongation at Break: >= 2.0 %
- Tensile Modulus: 131 GPa
$ 1513/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 386 - 455 MPa
- Tensile Strength, Yield: 372 - 455 MPa
- Elongation at Break: >= 3.0 %
- Tensile Modulus: 117 GPa
$ 1527/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 60 - 66
- Tensile Strength, Ultimate: 345 - 400 MPa
- Tensile Strength, Yield: 331 - 393 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 2451/MT
- Density: 8.89 g/cc
- Hardness, Rockwell 30T: <= 72
- Tensile Strength, Ultimate: 379 - 517 MPa
- Tensile Strength, Yield: <= 500 MPa
- Elongation at Break: >= 5.0 %
$ 1704/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 50 - 59
- Tensile Strength, Ultimate: 296 - 352 MPa
- Tensile Strength, Yield: 276 - 345 MPa
- Elongation at Break: 4.0 - 21 %
$ 2100/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 34 - 47
- Tensile Strength, Ultimate: 317 - 386 MPa
- Tensile Strength, Yield: 131 - 200 MPa
- Elongation at Break: 48 - 62 %
$ 2010/MT
- Density: 8.91 g/cc
- Tensile Strength, Ultimate: 179 - 262 MPa
- Tensile Strength, Yield: 41.4 - 89.6 MPa
- Elongation at Break: 20 - 50 %
- Tensile Modulus: 117 GPa
$ 1795/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 724 - 827 MPa
- Tensile Strength, Yield: >= 655 MPa
- Elongation at Break: >= 2.0 %
- Tensile Modulus: 131 GPa
$ 1873/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 56 - 64
- Tensile Strength, Ultimate: 379 - 448 MPa
- Tensile Strength, Yield: 241 - 345 MPa
- Elongation at Break: 12 - 25 %
$ 2320/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 65 - 70
- Tensile Strength, Ultimate: 441 - 510 MPa
- Tensile Strength, Yield: 379 - 476 MPa
- Elongation at Break: 8.0 - 25 %
$ 1482/MT
- Density: 8.77 g/cc
- Hardness, Rockwell 30T: 70 - 74
- Tensile Strength, Ultimate: 483 - 565 MPa
- Tensile Strength, Yield: 462 - 552 MPa
- Elongation at Break: 4.0 - 10 %
$ 1492/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 56 - 64
- Tensile Strength, Ultimate: 324 - 386 MPa
- Tensile Strength, Yield: 317 - 379 MPa
- Elongation at Break: 3.0 - 5.0 %
$ 2079/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 52 - 70
- Tensile Strength, Ultimate: 352 - 462 MPa
- Tensile Strength, Yield: 290 - 448 MPa
- Elongation at Break: 3.0 - 21 %
$ 2069/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 72 - 76
- Tensile Strength, Ultimate: 552 - 634 MPa
- Tensile Strength, Yield: 538 - 607 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1524/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 365 - 455 MPa
- Tensile Strength, Yield: 276 - 379 MPa
- Elongation at Break: 35 - 55 %
- Tensile Modulus: 117 GPa
$ 1536/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 241 - 372 MPa
- Tensile Strength, Yield: 117 - 221 MPa
- Elongation at Break: >= 25 %
- Tensile Modulus: 117 GPa
$ 1636/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 62 - 66
- Tensile Strength, Ultimate: 386 - 441 MPa
- Tensile Strength, Yield: 379 - 434 MPa
- Elongation at Break: >= 2.0 %
$ 1537/MT
- Density: 8.89 g/cc
- Hardness, Rockwell 30T: 70 - 80
- Tensile Strength, Ultimate: 552 - 655 MPa
- Tensile Strength, Yield: 538 - 641 MPa
- Elongation at Break: 1.0 - 3.0 %
$ 1916/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 70 - 73
- Tensile Strength, Ultimate: 490 - 558 MPa
- Tensile Strength, Yield: 462 - 538 MPa
- Elongation at Break: 6.0 - 14 %
$ 1528/MT
- Density: 8.75 g/cc
- Hardness, Rockwell 30T: 74 - 76
- Tensile Strength, Ultimate: 538 - 593 MPa
- Tensile Strength, Yield: 476 - 524 MPa
- Elongation at Break: 3.0 - 4.0 %
$ 1831/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 57 - 62
- Tensile Strength, Ultimate: 345 - 407 MPa
- Tensile Strength, Yield: 338 - 400 MPa
- Elongation at Break: 2.0 - 8.0 %
$ 2135/MT
- Density: 8.89 g/cc
- Hardness, Rockwell 30T: 32 - 58
- Tensile Strength, Ultimate: 310 - 448 MPa
- Tensile Strength, Yield: 124 - 172 MPa
- Elongation at Break: 34 - 36 %
$ 1494/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 72 - 75
- Tensile Strength, Ultimate: 538 - 600 MPa
- Tensile Strength, Yield: 448 - 496 MPa
- Elongation at Break: 2.0 - 3.0 %
$ 1457/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 18 - 51
- Tensile Strength, Ultimate: 234 - 290 MPa
- Tensile Strength, Yield: 179 - 269 MPa
- Elongation at Break: 13 - 33 %
$ 1894/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 54 - 62
- Tensile Strength, Ultimate: 296 - 359 MPa
- Tensile Strength, Yield: 283 - 345 MPa
- Elongation at Break: 3.0 - 16 %
$ 1655/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 56 - 62
- Tensile Strength, Ultimate: 324 - 386 MPa
- Tensile Strength, Yield: 317 - 372 MPa
- Elongation at Break: 2.0 - 9.0 %
$ 1554/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 31 - 58
- Tensile Strength, Ultimate: >= 359 MPa
- Tensile Strength, Yield: >= 138 MPa
- Elongation at Break: >= 30 %
$ 1518/MT
- Density: 8.91 g/cc
- Tensile Strength, Ultimate: 490 - 558 MPa
- Tensile Strength, Yield: >= 414 MPa
- Elongation at Break: >= 10 %
- Tensile Modulus: 128 GPa
$ 1458/MT
- Density: 8.75 g/cc
- Hardness, Rockwell 30T: 75 - 77
- Tensile Strength, Ultimate: 565 - 621 MPa
- Tensile Strength, Yield: 503 - 552 MPa
- Elongation at Break: >= 2.0 %
$ 1864/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 77 - 81
- Tensile Strength, Ultimate: 689 - 786 MPa
- Tensile Strength, Yield: 676 - 758 MPa
- Elongation at Break: 1.0 - 3.0 %
$ 1472/MT
- Density: 8.91 g/cc
- Tensile Strength, Ultimate: >= 579 MPa
- Tensile Strength, Yield: >= 510 MPa
- Elongation at Break: >= 6.0 %
- Tensile Modulus: 128 GPa
$ 1767/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: >= 61
- Tensile Strength, Ultimate: >= 359 MPa
- Tensile Strength, Yield: >= 352 MPa
- Elongation at Break: <= 3.0 %
$ 1479/MT
- Density: 8.89 g/cc
- Hardness, Rockwell 30T: 75 - 80
- Tensile Strength, Ultimate: 621 - 724 MPa
- Tensile Strength, Yield: 607 - 703 MPa
- Elongation at Break: <= 1.0 %
$ 2327/MT
- Density: 8.75 g/cc
- Hardness, Rockwell 30T: 70 - 74
- Tensile Strength, Ultimate: 496 - 552 MPa
- Tensile Strength, Yield: 448 - 490 MPa
- Elongation at Break: 3.0 - 5.0 %
$ 1697/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 179 - 262 MPa
- Tensile Strength, Yield: 41.4 - 89.6 MPa
- Elongation at Break: 20 - 50 %
- Tensile Modulus: 117 GPa
$ 1721/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 63 - 68
- Tensile Strength, Ultimate: 421 - 490 MPa
- Tensile Strength, Yield: 331 - 400 MPa
- Elongation at Break: 6.0 - 15 %
$ 1936/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 47 - 59
- Tensile Strength, Ultimate: 283 - 345 MPa
- Tensile Strength, Yield: 269 - 331 MPa
- Elongation at Break: 5.0 - 24 %
$ 2067/MT
- Density: 8.77 g/cc
- Hardness, Rockwell 30T: 63 - 69
- Tensile Strength, Ultimate: 393 - 476 MPa
- Tensile Strength, Yield: 352 - 455 MPa
- Elongation at Break: 10 - 27 %
$ 2401/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 75 - 79
- Tensile Strength, Ultimate: 627 - 724 MPa
- Tensile Strength, Yield: 607 - 696 MPa
- Elongation at Break: 1.0 - 5.0 %
$ 1718/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 59 - 64
- Tensile Strength, Ultimate: 365 - 427 MPa
- Tensile Strength, Yield: 352 - 407 MPa
- Elongation at Break: 2.0 - 6.0 %
$ 2127/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 421 - 524 MPa
- Tensile Strength, Yield: 379 - 483 MPa
- Elongation at Break: 15 - 40 %
- Tensile Modulus: 117 GPa
$ 2038/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 38 - 53
- Tensile Strength, Ultimate: 276 - 345 MPa
- Tensile Strength, Yield: 131 - 324 MPa
- Elongation at Break: 15 - 40 %
$ 2272/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 73 - 80
- Tensile Strength, Ultimate: 586 - 689 MPa
- Tensile Strength, Yield: 538 - 655 MPa
- Elongation at Break: 12 - 30 %
$ 1697/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 76 - 78
- Tensile Strength, Ultimate: 627 - 689 MPa
- Tensile Strength, Yield: 565 - 627 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1628/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 77 - 79
- Tensile Strength, Ultimate: 655 - 717 MPa
- Tensile Strength, Yield: 593 - 641 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 2006/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 276 - 379 MPa
- Tensile Strength, Yield: 138 - 241 MPa
- Elongation at Break: >= 20 %
- Tensile Modulus: 117 GPa
$ 1496/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 52 - 71
- Tensile Strength, Ultimate: 379 - 483 MPa
- Tensile Strength, Yield: 290 - 483 MPa
- Elongation at Break: 12 - 31 %
$ 1468/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: >= 61
- Tensile Strength, Ultimate: >= 359 MPa
- Tensile Strength, Yield: >= 352 MPa
- Elongation at Break: <= 3.0 %
$ 2530/MT
- Density: 8.77 g/cc
- Hardness, Rockwell 30T: 66 - 71
- Tensile Strength, Ultimate: 427 - 510 MPa
- Tensile Strength, Yield: 400 - 483 MPa
- Elongation at Break: 5.0 - 20 %
$ 1965/MT
- Density: 8.75 g/cc
- Hardness, Rockwell 30T: 15 - 44
- Tensile Strength, Ultimate: 269 - 324 MPa
- Tensile Strength, Yield: 55.2 - 131 MPa
- Elongation at Break: 43 - 48 %
$ 1512/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 15 - 35
- Tensile Strength, Ultimate: 248 - 290 MPa
- Tensile Strength, Yield: 55.2 - 117 MPa
- Elongation at Break: 46 - 49 %
$ 1471/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 61 - 68
- Tensile Strength, Ultimate: 414 - 483 MPa
- Tensile Strength, Yield: 365 - 469 MPa
- Elongation at Break: 3.0 - 11 %
$ 1550/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 70 - 72
- Tensile Strength, Ultimate: 476 - 531 MPa
- Tensile Strength, Yield: 448 - 490 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1483/MT
- Density: 8.91 g/cc
- Tensile Strength, Ultimate: 517 - 593 MPa
- Tensile Strength, Yield: >= 441 MPa
- Elongation at Break: >= 8.0 %
- Tensile Modulus: 128 GPa
$ 1964/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 73 - 76
- Tensile Strength, Ultimate: 579 - 648 MPa
- Tensile Strength, Yield: 558 - 621 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1705/MT
- Density: 8.77 g/cc
- Tensile Strength, Ultimate: >= 758 MPa
- Tensile Strength, Yield: >= 738 MPa
- Elongation at Break: >= 1.0 %
- Tensile Modulus: 131 GPa
$ 1589/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 15 - 51
- Tensile Strength, Ultimate: 303 - 372 MPa
- Tensile Strength, Yield: 82.7 - 200 MPa
- Elongation at Break: 43 - 58 %
$ 1745/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 75 - 77
- Tensile Strength, Ultimate: 586 - 641 MPa
- Tensile Strength, Yield: 490 - 558 MPa
- Elongation at Break: 1.0 - 2.0 %
$ 1528/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 56 - 66
- Tensile Strength, Ultimate: 393 - 462 MPa
- Tensile Strength, Yield: 290 - 414 MPa
- Elongation at Break: 19 - 42 %
$ 2007/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 496 - 593 MPa
- Tensile Strength, Yield: 462 - 572 MPa
- Elongation at Break: 12 - 16 %
- Tensile Modulus: 117 GPa
$ 1710/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 43 - 57
- Tensile Strength, Ultimate: 255 - 317 MPa
- Tensile Strength, Yield: 207 - 303 MPa
- Elongation at Break: 8.0 - 32 %
$ 1737/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 676 - 779 MPa
- Tensile Strength, Yield: 662 - 765 MPa
- Elongation at Break: 1.0 - 3.0 %
- Tensile Modulus: 117 GPa
$ 1516/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: >= 586 MPa
- Tensile Strength, Yield: >= 538 MPa
- Tensile Modulus: 117 GPa
- CTE, linear: 17.3 µm/m-°C @Temperature 20.0 - 300 °C
$ 1602/MT
- Density: 8.66 g/cc
- Hardness, Rockwell 30T: 76 - 78
- Tensile Strength, Ultimate: 614 - 669 MPa
- Tensile Strength, Yield: 503 - 579 MPa
- Elongation at Break: <= 1.0 %
$ 1971/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 758 - 862 MPa
- Tensile Strength, Yield: >= 689 MPa
- Elongation at Break: >= 1.0 %
- Tensile Modulus: 131 GPa
$ 2058/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 71 - 73
- Tensile Strength, Ultimate: 496 - 552 MPa
- Tensile Strength, Yield: 462 - 510 MPa
- Elongation at Break: <= 1.0 %
$ 1670/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 52 - 61
- Tensile Strength, Ultimate: 324 - 393 MPa
- Tensile Strength, Yield: 290 - 365 MPa
- Elongation at Break: 5.0 - 20 %
$ 1592/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 359 - 427 MPa
- Tensile Strength, Yield: 345 - 427 MPa
- Elongation at Break: >= 4.0 %
- Tensile Modulus: 117 GPa
$ 1898/MT
- Density: 8.94 g/cc
- Tensile Strength, Ultimate: 476 - 565 MPa
- Tensile Strength, Yield: 441 - 552 MPa
- Elongation at Break: >= 7.0 %
- Tensile Modulus: 117 GPa
$ 1503/MT
- Density: 8.77 g/cc
- Tensile Strength, Ultimate: 634 - 738 MPa
- Tensile Strength, Yield: 579 - 731 MPa
- Elongation at Break: >= 3.0 %
- Tensile Modulus: 131 GPa
$ 1944/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 62 - 66
- Tensile Strength, Ultimate: 393 - 455 MPa
- Tensile Strength, Yield: 365 - 434 MPa
- Elongation at Break: 2.0 - 6.0 %
$ 1792/MT
- Density: 8.91 g/cc
- Tensile Strength, Ultimate: 462 - 531 MPa
- Tensile Strength, Yield: >= 345 MPa
- Elongation at Break: >= 12 %
- Tensile Modulus: 128 GPa
$ 2357/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 40 - 53
- Tensile Strength, Ultimate: 276 - 434 MPa
- Tensile Strength, Yield: 110 - 407 MPa
- Elongation at Break: 10 - 36 %
$ 1790/MT
- Density: 8.89 g/cc
- Hardness, Rockwell 30T: 62 - 75
- Tensile Strength, Ultimate: 448 - 552 MPa
- Tensile Strength, Yield: 407 - 538 MPa
- Elongation at Break: 3.0 - 17 %
$ 2281/MT
- Density: 8.91 g/cc
- Hardness, Rockwell 30T: 52 - 63
- Tensile Strength, Ultimate: 365 - 434 MPa
- Tensile Strength, Yield: 248 - 421 MPa
- Elongation at Break: 6.0 - 29 %
$ 1494/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 77 - 82
- Tensile Strength, Ultimate: 669 - 772 MPa
- Tensile Strength, Yield: 634 - 738 MPa
- Elongation at Break: 10 - 17 %
$ 1452/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 47 - 52
- Tensile Strength, Ultimate: 255 - 276 MPa
- Tensile Strength, Yield: 62.1 - 82.7 MPa
- Elongation at Break: 35 - 37 %
$ 1942/MT
- Density: 8.80 g/cc
- Hardness, Rockwell 30T: 79 - 83
- Tensile Strength, Ultimate: 758 - 841 MPa
- Tensile Strength, Yield: 724 - 800 MPa
- Elongation at Break: 2.0 - 6.0 %
$ 1543/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 54 - 62
- Tensile Strength, Ultimate: 296 - 359 MPa
- Tensile Strength, Yield: 283 - 345 MPa
- Elongation at Break: 3.0 - 16 %
$ 1909/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 15 - 45
- Tensile Strength, Ultimate: 296 - 345 MPa
- Tensile Strength, Yield: 89.6 - 172 MPa
- Elongation at Break: 33 - 37 %
$ 1684/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 29 - 46
- Tensile Strength, Ultimate: 317 - 372 MPa
- Tensile Strength, Yield: 110 - 193 MPa
- Elongation at Break: 45 - 49 %
$ 1557/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 538 - 641 MPa
- Tensile Strength, Yield: 503 - 621 MPa
- Elongation at Break: 8.0 - 11 %
- Tensile Modulus: 117 GPa
$ 2340/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 63 - 65
- Tensile Strength, Ultimate: 407 - 448 MPa
- Tensile Strength, Yield: 393 - 434 MPa
- Elongation at Break: >= 1.0 %
$ 1519/MT
- Density: 8.94 g/cc
- Hardness, Rockwell 30T: 60 - 66
- Tensile Strength, Ultimate: 345 - 400 MPa
- Tensile Strength, Yield: 331 - 393 MPa
- Elongation at Break: 2.0 - 4.0 %
$ 1665/MT
- Density: 8.53 g/cc
- Hardness, Rockwell 30T: 74 - 76
- Tensile Strength, Ultimate: 572 - 634 MPa
- Tensile Strength, Yield: 545 - 600 MPa
- Elongation at Break: 2.0 - 5.0 %
$ 1478/MT
- Density: 8.86 g/cc
- Hardness, Rockwell 30T: 35 - 65
- Tensile Strength, Ultimate: 317 - 400 MPa
- Tensile Strength, Yield: 138 - 345 MPa
- Elongation at Break: 25 - 47 %
$ 1978/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 331 - 414 MPa
- Tensile Strength, Yield: 193 - 276 MPa
- Elongation at Break: 50 - 60 %
- Tensile Modulus: 117 GPa
Delivery Copper Alloy Eagle Brass Company
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.