$ 2109/MT
- Tensile Strength, Yield: 2300 MPa
- Tensile Modulus: 170 GPa
- Flexural Yield Strength: 1750 MPa
- Flexural Modulus: 155 GPa
- Compressive Yield Strength: 1250 MPa
$ 1699/MT
- Density: 1.21 g/cc
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 2.80 GPa
- Toughness: 100 J
$ 2429/MT
- Density: 1.30 g/cc
- Elongation at Yield: 1.7 %
- Fracture Toughness: 1.62 MPa-m½
- Maximum Service Temperature, Air: 121 °C
- Glass Transition Temp, Tg: 154 °C
$ 1661/MT
- Tensile Strength, Yield: 648 MPa @Temperature 23.0 °C
- Elongation at Yield: 3.5 % @Temperature 23.0 °C
- Tensile Modulus: 22.1 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 765 MPa @Temperature 23.0 °C
- Flexural Modulus: 20.7 GPa @Temperature 23.0 °C
$ 1477/MT
- Tensile Strength, Yield: 36.5 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 72.0 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 2365 MPa @Temperature 23.0 °C
- Tensile Modulus: 7.60 GPa @Temperature 23.0 °C
- Tensile Modulus: 196 GPa @Temperature 23.0 °C
$ 2348/MT
- Density: 1.16 g/cc
- Tensile Strength, Yield: 81.1 MPa
- Elongation at Yield: 3.7 %
- Tensile Modulus: 3.50 GPa
- Flexural Yield Strength: 140 MPa
$ 1691/MT
- Tensile Strength, Yield: 718 MPa
- Tensile Strength, Yield: 786 MPa
- Tensile Strength, Yield: 677 MPa @Temperature 175 °C
- Tensile Strength, Yield: 774 MPa @Temperature 175 °C
- Tensile Modulus: 67.0 GPa
$ 1528/MT
- Density: 1.29 g/cc
- Glass Transition Temp, Tg: 90.0 °C
- Glass Transition Temp, Tg: 105 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
- Tack Life (days): 30
$ 1493/MT
- Tensile Strength, Yield: 1337 MPa
- Tensile Modulus: 87.0 GPa
- Compressive Yield Strength: 369 MPa
- Compressive Yield Strength: 901 MPa
- Shear Strength: 71.0 MPa
$ 1829/MT
- Tensile Strength, Yield: 3017 MPa @Temperature 23.0 °C
- Tensile Modulus: 159 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 1510 MPa @Temperature 23.0 °C
- Compressive Modulus: 158 GPa @Temperature 23.0 °C
- Shear Strength: 111 MPa @Temperature 22.0 °C
$ 2058/MT
- Storage Temperature: 0.000 - 4.44 °C
- Shear Strength: 20.7 MPa @Temperature 71.1 °C
- Shear Strength: 31.0 MPa @Temperature 21.1 °C
- Shear Strength: 37.2 MPa @Temperature 21.1 °C
- Peel Strength: 10.5 kN/m @Temperature 21.1 °C
$ 1866/MT
- Density: 1.19 g/cc
- Hardness, Barcol: 33
- Glass Transition Temp, Tg: 90.0 °C
- Glass Transition Temp, Tg: 116 °C
$ 1608/MT
- Tensile Strength, Yield: 4.55 MPa @Temperature 71.1 °C
- Tensile Strength, Yield: 4.69 MPa @Temperature 21.1 °C
- Tensile Strength, Yield: 5.72 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 6.41 MPa @Temperature 71.1 °C
- Shear Strength: 4.69 MPa @Temperature 21.1 °C
$ 2359/MT
- Shelf Life: 6.00 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.02
- Carrier/Foil: None
$ 1484/MT
- Tensile Strength at Break: 300 MPa
- Tensile Modulus: 40.0 GPa
- Flexural Strength: 400 MPa
- Flexural Modulus: 30.0 GPa
- Compressive Strength: 350 MPa
$ 2006/MT
- Tensile Strength, Yield: 414 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 483 MPa @Temperature 23.0 °C
- Tensile Modulus: 27.6 GPa @Temperature 71.0 °C
- Tensile Modulus: 30.3 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 483 MPa @Temperature 71.0 °C
$ 2071/MT
- Outgassing - Total Mass Loss: 0.109 %
- Outgassing - Total Mass Loss: 1.168 %
- Collected Volatile Condensable Material: 0.00 %
- Shear Strength: 20.99 MPa @Temperature 150 °C
- Shear Strength: 32.0 MPa @Temperature 22.2 °C
$ 2074/MT
- Volatiles: 1.0 - 4.0 %
- Tensile Strength, Yield: 3.372 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 5.192 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 1269 MPa @Temperature -54.0 °C
- Tensile Strength, Yield: 1331 MPa @Temperature 24.0 °C
$ 1857/MT
- Tensile Strength, Yield: 4.523 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 5.833 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 319 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 393 MPa @Temperature 24.0 °C
- Tensile Modulus: 17.9 GPa @Temperature 93.0 °C
$ 1695/MT
- Density: 1.53 g/cc
- Tensile Strength, Yield: 1425 MPa @Temperature 23.0 °C
- Tensile Modulus: 89.0 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 925 MPa @Temperature 23.0 °C
- Shear Modulus: 4.70 GPa @Temperature 23.0 °C
$ 2016/MT
- Tensile Strength, Yield: 2027 MPa @Temperature 23.0 °C
- Tensile Modulus: 323 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 928 MPa @Temperature 23.0 °C
- Flexural Modulus: 263 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 896 MPa @Temperature 23.0 °C
$ 1555/MT
- Density: 1.23 g/cc
- Tensile Strength, Yield: 65.5 MPa
- Tensile Modulus: 3.39 GPa
$ 1502/MT
- Dry Resin Content (%): 37-41
- Fiber Volume (%): 0.009
- Flow (%): 4-16
- Wet Resin Content (%): 52
$ 1901/MT
- Outgassing - Total Mass Loss: 0.41 %
- Outgassing - Total Mass Loss: 1.74 %
- Collected Volatile Condensable Material: 0.00 %
- Tensile Strength, Yield: 6.00 MPa @Temperature 149 °C
- Tensile Strength, Yield: 8.00 MPa @Temperature 21.1 °C
$ 1546/MT
- Tensile Strength, Yield: 442 MPa
- Tensile Modulus: 33.0 GPa
- Compressive Yield Strength: 140 MPa
- Compressive Yield Strength: 278 MPa
- Shear Strength: 44.0 MPa
$ 1748/MT
- Tensile Strength, Yield: 7.03 MPa @Temperature 21.1 °C
- Shear Strength: 17.2 MPa @Temperature 98.9 °C
- Shear Strength: 35.2 MPa @Temperature 79.4 °C
- Shear Strength: 37.9 MPa @Temperature 71.1 °C
- Shear Strength: 41.4 MPa @Temperature 21.1 °C
$ 2292/MT
- Density: 1.17 g/cc
- Density: 1.48 g/cc
- Density: 1.79 g/cc
- Tensile Strength, Yield: 787 MPa
- Tensile Modulus: 67.0 GPa
$ 1535/MT
- Tensile Strength, Yield: 541 MPa @Temperature 177 °C
- Tensile Strength, Yield: 570 MPa @Temperature 24.0 °C
- Tensile Modulus: 57.7 GPa @Temperature 177 °C
- Tensile Modulus: 60.7 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 575 MPa @Temperature 71.0 °C
$ 1541/MT
- Volatiles: 0.40 - 1.2 %
- Tensile Strength, Yield: 419 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 507 MPa @Temperature 24.0 °C
- Tensile Modulus: 24.0 GPa @Temperature 24.0 °C
- Tensile Modulus: 26.3 GPa @Temperature 24.0 °C
$ 1685/MT
- Volatiles: 0.40 - 1.2 %
- Tensile Strength, Yield: 440 MPa @Temperature 24.0 °C
- Compressive Yield Strength: 324 MPa @Temperature 24.0 °C
- Shear Strength: 20.278 MPa @Temperature 82.0 °C
- Shear Strength: 31.757 MPa @Temperature 24.0 °C
$ 1855/MT
- Tensile Strength, Yield: 2170 MPa @Temperature 25.0 °C
- Elongation at Yield: 1.4 %
- Tensile Modulus: 145 GPa
- Flexural Yield Strength: 1700 MPa @Temperature 25.0 °C
- Flexural Modulus: 123 GPa @Temperature 25.0 °C
$ 1941/MT
- Tensile Strength, Yield: 400 MPa @Temperature 80.0 °C
- Tensile Strength, Yield: 410 MPa @Temperature 23.0 °C
- Flexural Yield Strength: 450 MPa @Temperature 80.0 °C
- Flexural Yield Strength: 520 MPa @Temperature 23.0 °C
- Flexural Modulus: 16.5 GPa @Temperature 80.0 °C
$ 1691/MT
- Tensile Strength, Yield: 20.0 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1841 MPa @Temperature 23.0 °C
- Tensile Modulus: 5.10 GPa @Temperature 23.0 °C
- Tensile Modulus: 538 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 366 MPa @Temperature 23.0 °C
- Shear Strength: 47.0 MPa @Temperature 22.0 °C
$ 2420/MT
- Tensile Strength, Yield: 579 MPa @Temperature 177 °C
- Tensile Strength, Yield: 610 MPa @Temperature 24.0 °C
- Tensile Modulus: 60.5 GPa @Temperature 177 °C
- Tensile Modulus: 63.7 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 585 MPa @Temperature 71.0 °C
$ 1523/MT
- Tensile Strength, Yield: 1247 MPa @Temperature 24.0 °C
- Tensile Modulus: 134.8 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 1260 MPa @Temperature 71.0 °C
- Compressive Yield Strength: 1420 MPa @Temperature 24.0 °C
- Shear Strength: 75.0 MPa @Temperature 132 °C
$ 1547/MT
- Tensile Strength, Yield: 600 MPa
- Tensile Modulus: 32.0 GPa
- Flexural Yield Strength: 380 MPa
- Flexural Modulus: 21.0 GPa
- Compressive Yield Strength: 240 MPa
$ 1753/MT
- Density: 1.18 g/cc
- Viscosity: >= 5000 cP
- Glass Transition Temp, Tg: 95.0 °C
- Glass Transition Temp, Tg: 120 °C
- Gel Time: 12.0 - 14.0 min @Temperature 120 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
$ 1517/MT
- Density: 1.17 g/cc
- Density: 1.77 g/cc
- Density: 2.54 g/cc
- Tensile Strength, Yield: 470 MPa
- Tensile Modulus: 25.0 GPa
$ 1452/MT
- Glass Transition Temp, Tg: 120 °C
- Gel Time: 80.0 - 120 min @Temperature 150 °C
- Shelf Life: 0.750 Month @Temperature 23.0 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
$ 1712/MT
- Tensile Strength, Yield: 1931 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1937 MPa @Temperature 71.0 °C
- Tensile Modulus: 103.4 GPa @Temperature 23.0 °C
- Tensile Modulus: 110.3 GPa @Temperature 71.0 °C
- Flexural Yield Strength: 1338 MPa @Temperature 71.0 °C
$ 2086/MT
- Volatiles: <= 1.5 %
- Maximum Service Temperature, Air: 121 °C
- Gel Time: 12.0 - 22.0 min
- Dry Resin Content (%): 36-42
- Fiber Volume (%): 58
- Flow (%): 8-22
$ 1462/MT
- Density: 1.50 g/cc
- Density: 1.78 g/cc
- Tensile Strength, Yield: 1500 MPa
- Flexural Yield Strength: 1400 MPa
- Flexural Modulus: 100 GPa
$ 2575/MT
- Shear Strength: 22.0 MPa @Temperature 149 °C
- Shear Strength: 42.0 MPa @Temperature 22.2 °C
- Peel Strength: 6.84 kN/m @Temperature 22.2 °C
- Shelf Life: 18.0 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.036
$ 2584/MT
- Density: 1.02 g/cc @Temperature 25.0 °C
- Density: 1.11 g/cc @Temperature 25.0 °C
- Density: 1.15 g/cc @Temperature 25.0 °C
- Viscosity: 4000 - 8000 cP @Temperature 25.0 °C
- Viscosity: 80000 - 90000 cP @Temperature 25.0 °C
$ 2369/MT
- Density: 1.29 g/cc
- Tensile Strength, Yield: 47.7 MPa
- Elongation at Yield: 1.5 %
- Tensile Modulus: 3.90 GPa
- Compressive Yield Strength: 180 MPa
$ 1993/MT
- Density: 1.26 g/cc
- Density: 2.25 g/cc
- Tensile Strength, Yield: 377 MPa
- Tensile Modulus: 28.0 GPa
- Compressive Yield Strength: 370 MPa @Temperature 150 °C
$ 1476/MT
- Storage Temperature: -17.8 °C
- Tensile Strength, Yield: 4.48 MPa
- Shear Strength: 31.0 MPa @Temperature 21.1 °C
- Shear Strength: 31.0 MPa @Temperature 48.9 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
$ 1791/MT
- Density: 1.28 g/cc
- Density: 1.53 g/cc
- Density: 1.78 g/cc
- Tensile Strength, Yield: 1022 MPa @Temperature 23.0 °C
- Tensile Modulus: 58.0 GPa @Temperature 23.0 °C
$ 1522/MT
- Tensile Strength, Yield: 5.52 MPa @Temperature 21.1 °C
- Shear Strength: 31.7 MPa @Temperature 71.1 °C
- Shear Strength: 31.7 MPa @Temperature 79.4 °C
- Shear Strength: 39.3 MPa @Temperature 21.1 °C
- Peel Strength: 9.12 kN/m @Temperature 21.1 °C
$ 1752/MT
- Flexural Yield Strength: 1280.9 MPa @Temperature 50.0 °C
- Flexural Yield Strength: 1381.0 MPa @Temperature 50.0 °C
- Flexural Yield Strength: 1531.0 MPa @Temperature 22.8 °C
- Flexural Yield Strength: 1611.1 MPa @Temperature 22.8 °C
- Flexural Modulus: 91.08 GPa @Temperature 50.0 °C
$ 1985/MT
- Tensile Strength, Yield: 379 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 448 MPa @Temperature 24.0 °C
- Tensile Modulus: 22.0 GPa @Temperature 71.0 °C
- Tensile Modulus: 22.4 GPa @Temperature 24.0 °C
- Flexural Yield Strength: 586 MPa @Temperature 24.0 °C
$ 1570/MT
- Density: 1.26 g/cc
- Density: 1.78 g/cc
- Tensile Strength, Yield: 850 MPa
- Tensile Strength, Yield: 750 MPa @Temperature 135 °C
- Tensile Modulus: 62.8 GPa
$ 2291/MT
- Tensile Strength, Yield: 28.9 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 40.0 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 2165 MPa @Temperature 23.0 °C
- Tensile Modulus: 6.20 GPa @Temperature 23.0 °C
- Tensile Modulus: 321 GPa @Temperature 23.0 °C
$ 1820/MT
- Density: 1.27 g/cc
- Compressive Yield Strength: 175 MPa
- Compressive Modulus: 3.06 GPa
- Glass Transition Temp, Tg: 150 °C
$ 1561/MT
- Tensile Strength, Yield: 1931 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1937 MPa @Temperature 71.0 °C
- Tensile Modulus: 103.4 GPa @Temperature 23.0 °C
- Tensile Modulus: 110.3 GPa @Temperature 71.0 °C
- Flexural Yield Strength: 1338 MPa @Temperature 71.0 °C
$ 1633/MT
- Tensile Strength, Yield: 1931 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1937 MPa @Temperature 71.0 °C
- Tensile Modulus: 103.4 GPa @Temperature 23.0 °C
- Tensile Modulus: 110.3 GPa @Temperature 71.0 °C
- Flexural Yield Strength: 1338 MPa @Temperature 71.0 °C
$ 1511/MT
- Tensile Strength, Yield: 1931 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1937 MPa @Temperature 71.0 °C
- Tensile Modulus: 103.4 GPa @Temperature 23.0 °C
- Tensile Modulus: 110.3 GPa @Temperature 71.0 °C
- Flexural Yield Strength: 1338 MPa @Temperature 71.0 °C
$ 1629/MT
- Tensile Strength, Yield: 6.481 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 848 MPa @Temperature 24.0 °C
- Tensile Modulus: 58.0 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 496 MPa @Temperature 71.0 °C
- Compressive Yield Strength: 904 MPa @Temperature 24.0 °C
$ 1461/MT
- Density: 1.26 g/cc
- Glass Transition Temp, Tg: 145 - 155 °C
$ 1750/MT
- Density: 1.26 g/cc
- Density: 2.60 g/cc
- Tensile Strength, Yield: 280 MPa
- Tensile Modulus: 17.0 GPa
- Shear Strength: 49.7 MPa
$ 1896/MT
- Tensile Strength, Yield: 400 MPa @Temperature 177 °C
- Tensile Strength, Yield: 455 MPa @Temperature 24.0 °C
- Tensile Modulus: 18.0 GPa @Temperature 177 °C
- Tensile Modulus: 21.0 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 296 MPa @Temperature 177 °C
$ 1519/MT
- Tensile Strength, Yield: 2151 MPa @Temperature 23.0 °C
- Tensile Modulus: 365 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 924 MPa @Temperature 23.0 °C
- Compressive Modulus: 343 GPa @Temperature 23.0 °C
- Shear Strength: 78.0 MPa @Temperature 22.0 °C
$ 1789/MT
- Tensile Strength, Yield: 450 MPa
- Tensile Modulus: 20.0 GPa
- Flexural Yield Strength: 550 MPa
- Flexural Modulus: 22.0 GPa
- Shear Strength: 55.0 MPa
$ 1554/MT
- Volatiles: 1.0 - 6.0 %
- Cured Thickness per Ply (cm): 0.021-0.024
- Dry Resin Content (%): 38-46
- Fiber Volume (%): 45-53
- Flow (%): <4.5
$ 1590/MT
- Specific Gravity: 1.286 g/cc
- Moisture Absorption at Equilibrium: 7.0 %
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: >= 9.5 %
- Tensile Modulus: 2.90 GPa
$ 2179/MT
- Tensile Strength, Yield: 400 MPa
- Tensile Modulus: 20.0 GPa
- Flexural Yield Strength: 670 MPa
- Flexural Modulus: 20.0 GPa
- Shear Strength: 53.0 MPa
$ 1667/MT
- Tensile Strength, Yield: 950 MPa
- Tensile Modulus: 70.0 GPa
- Flexural Yield Strength: 850 MPa
- Flexural Modulus: 60.0 GPa
- Compressive Yield Strength: 720 MPa
$ 1700/MT
- Tensile Strength, Yield: 710 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 765 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 765 MPa @Temperature 93.3 °C
- Tensile Strength, Yield: 793 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 800 MPa @Temperature 90.6 °C
$ 1854/MT
- Outgassing - Total Mass Loss: 0.109 %
- Outgassing - Total Mass Loss: 1.168 %
- Collected Volatile Condensable Material: 0.00 %
- Shear Strength: 18.0 MPa @Temperature 150 °C
- Shear Strength: 30.99 MPa @Temperature 22.2 °C
$ 1860/MT
- Tensile Strength, Yield: 820 MPa @Temperature 23.0 °C
- Tensile Modulus: 61.0 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 549 MPa @Temperature 90.0 °C
- Flexural Yield Strength: 934 MPa @Temperature 23.0 °C
- Flexural Modulus: 50.0 GPa @Temperature 23.0 °C
$ 2121/MT
- Density: 1.17 g/cc
- Density: 1.51 g/cc
- Density: 1.79 g/cc
- Tensile Strength, Yield: 2330 MPa
- Tensile Modulus: 141 GPa
$ 1792/MT
- Shear Strength: 11.7 MPa @Temperature 93.3 °C
- Shear Strength: 26.9 MPa @Temperature 60.0 °C
- Shear Strength: 41.4 MPa @Temperature 21.1 °C
- Peel Strength: 10.3 kN/m @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
$ 1575/MT
- Specific Gravity: 1.267 g/cc
- Moisture Absorption at Equilibrium: 4.8 %
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Yield: 2.4 %
- Tensile Modulus: 4.27 GPa
$ 1885/MT
- Specific Gravity: 1.34 g/cc
- Tensile Strength, Yield: 81.0 MPa
- Elongation at Yield: 3.7 %
- Tensile Modulus: 3.45 GPa
- Fracture Toughness: 1.41 MPa-m½
$ 1688/MT
- Thickness: 32.3 microns
- Thickness: 64.5 microns
- Tensile Strength at Break: 210 MPa @Temperature 180 °C
- Tensile Strength at Break: 260 MPa @Temperature 23.0 °C
- Tensile Modulus: 40.0 GPa @Temperature 180 °C
$ 2092/MT
- Storage Temperature: -17.8 °C
- Shelf Life: 6.00 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.03
- Roll Width (in): 49
- Standard Roll (ft2): 670
$ 1592/MT
- Tensile Strength, Yield: 2.965 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 3.896 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 4.682 MPa @Temperature -59.0 °C
- Tensile Strength, Yield: 4.806 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 419 MPa @Temperature 71.0 °C
$ 1863/MT
- Density: 1.24 g/cc
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Yield: 1.26 %
- Tensile Modulus: 5.10 GPa
- Poissons Ratio: 0.40
$ 1975/MT
- Tensile Strength, Yield: 1958 MPa @Temperature 23.0 °C
- Tensile Modulus: 352 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 1034 MPa @Temperature 23.0 °C
- Flexural Modulus: 290 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 869 MPa @Temperature 23.0 °C
$ 1575/MT
- Shear Strength: 31.0 MPa @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.06
- Roll Width (in): 49
- Standard Roll (ft2): 1075
- Support: None
$ 1534/MT
- Tensile Strength, Yield: 8.00 MPa @Temperature 21.1 °C
- Shear Strength: 20.0 MPa @Temperature 121 °C
- Shear Strength: 43.4 MPa @Temperature 71.1 °C
- Shear Strength: 46.9 MPa @Temperature 21.1 °C
- Peel Strength: 4.73 kN/m @Temperature 21.1 °C
$ 1719/MT
- Shear Strength: 17.2 MPa @Temperature 93.3 °C
- Shear Strength: 29.6 MPa @Temperature 60.0 °C
- Shear Strength: 43.4 MPa @Temperature 21.1 °C
- Peel Strength: 9.12 kN/m @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
$ 1770/MT
- Density: 1.28 g/cc
- Elongation at Yield: 5.0 %
- Flexural Yield Strength: 147 MPa
- Flexural Modulus: 3.50 GPa
- Glass Transition Temp, Tg: 185 °C
$ 1710/MT
- Tensile Strength, Yield: 365 MPa
- Tensile Strength, Yield: 384 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 2143 MPa @Temperature 23.0 °C
- Tensile Modulus: 140 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 204 MPa
$ 1762/MT
- Tensile Strength, Yield: 32.0 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 2289 MPa @Temperature 23.0 °C
- Tensile Modulus: 38.0 GPa @Temperature 23.0 °C
- Tensile Modulus: 391 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 476 MPa @Temperature 23.0 °C
$ 2360/MT
- Tensile Strength, Yield: 600 MPa
- Tensile Modulus: 21.0 GPa
- Flexural Yield Strength: 700 MPa
- Flexural Modulus: 20.0 GPa
- Compressive Yield Strength: 540 MPa
$ 2002/MT
- Tensile Strength, Yield: 903 MPa @Temperature 24.0 °C
- Tensile Modulus: 69.6 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 475 MPa @Temperature 71.0 °C
- Compressive Yield Strength: 655 MPa @Temperature 24.0 °C
- Shear Strength: 26.2 MPa @Temperature 71.0 °C
$ 1740/MT
- Shelf Life: >= 12.0 Month @Temperature -18.0 °C
$ 1763/MT
- Tensile Strength, Yield: 900 MPa
- Tensile Modulus: 37.0 GPa
- Flexural Yield Strength: 1000 MPa
- Flexural Modulus: 35.0 GPa
- Shear Strength: 65.0 MPa
$ 1726/MT
- Dry Resin Content (%): 57-63
- Fiber Volume (%): 0.011
- Flow (%): 24-36
- Wet Resin Content (%): 42
$ 1568/MT
- Density: 0.530 g/cc @Temperature 22.0 °C
- Density: 0.550 g/cc @Temperature 22.0 °C
- Density: 0.760 g/cc @Temperature 22.0 °C
- Density: 1.08 g/cc @Temperature 22.0 °C
- Compressive Yield Strength: 11.0 MPa @Temperature 22.0 °C
$ 1508/MT
- Tensile Strength, Yield: 600 MPa
- Tensile Modulus: 21.0 GPa
- Flexural Yield Strength: 700 MPa
- Flexural Modulus: 20.0 GPa
- Compressive Yield Strength: 540 MPa
$ 2133/MT
- Tensile Strength, Yield: 190 MPa @Temperature 177 °C
- Tensile Strength, Yield: 238 MPa @Temperature 177 °C
- Tensile Strength, Yield: 259 MPa @Temperature 132 °C
- Tensile Strength, Yield: 334 MPa @Temperature 132 °C
- Tensile Strength, Yield: 393 MPa @Temperature -54.0 °C
$ 1768/MT
- Density: 1.30 g/cc
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Yield: 2.4 %
- Elongation at Yield: 13 %
- Tensile Modulus: 3.80 GPa
$ 1558/MT
- Tensile Strength, Yield: 432 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 568 MPa @Temperature 23.0 °C
- Tensile Modulus: 52.0 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 225 MPa
- Compressive Yield Strength: 270 MPa
$ 1644/MT
- Tensile Strength, Yield: 365 MPa @Temperature 177 °C
- Tensile Strength, Yield: 424 MPa @Temperature 24.0 °C
- Tensile Modulus: 20.4 GPa @Temperature 177 °C
- Tensile Modulus: 27.2 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 276 MPa @Temperature 177 °C
$ 1691/MT
- Density: 1.26 g/cc
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Yield: 1.7 %
- Tensile Modulus: 3.54 GPa
- Flexural Yield Strength: 94.0 MPa
$ 1816/MT
- Density: 1.28 g/cc
- Density: 1.54 g/cc
- Density: 1.81 g/cc
- Tensile Strength, Yield: 991 MPa @Temperature 23.0 °C
- Tensile Modulus: 67.0 GPa @Temperature 23.0 °C
$ 1473/MT
- Tensile Strength, Yield: 253 MPa @Temperature 177 °C
- Tensile Strength, Yield: 259 MPa @Temperature 132 °C
- Tensile Strength, Yield: 281 MPa @Temperature 177 °C
- Tensile Strength, Yield: 349 MPa @Temperature 132 °C
- Tensile Strength, Yield: 392 MPa @Temperature -54.0 °C
$ 1474/MT
- Outgassing - Total Mass Loss: 0.41 %
- Outgassing - Total Mass Loss: 1.74 %
- Collected Volatile Condensable Material: 0.00 %
- Tensile Strength, Yield: 6.998 MPa @Temperature 149 °C
- Tensile Strength, Yield: 8.998 MPa @Temperature 21.1 °C
$ 1661/MT
- Outgassing - Total Mass Loss: 0.41 %
- Outgassing - Total Mass Loss: 1.74 %
- Collected Volatile Condensable Material: 0.00 %
- Tensile Strength, Yield: 5.00 MPa @Temperature 149 °C
- Tensile Strength, Yield: 6.998 MPa @Temperature 21.1 °C
$ 2026/MT
- Storage Temperature: -17.8 °C
- Shelf Life: 18.0 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.09
- Roll Width (in): 49
- Standard Roll (ft2): 1075
- Support: Woven Glass
$ 1795/MT
- Tensile Strength, Yield: 2230 MPa
- Tensile Modulus: 145 GPa
- Flexural Yield Strength: 1400 MPa
- Flexural Modulus: 132 GPa
- Compressive Yield Strength: 1530 MPa
$ 2465/MT
- Density: 1.33 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Yield: 2.4 %
- Tensile Modulus: 3.70 GPa
- Glass Transition Temp, Tg: 180 °C
$ 2389/MT
- Density: 1.24 g/cc
- Density: 1.75 g/cc
- Tensile Strength, Yield: 550 MPa
- Tensile Strength, Yield: 650 MPa
- Tensile Strength, Yield: 600 MPa @Temperature 75.0 °C
$ 1928/MT
- Tensile Strength, Yield: 1434 MPa
- Tensile Modulus: 87.0 GPa
- Compressive Yield Strength: 361 MPa
- Compressive Yield Strength: 912 MPa
- Shear Strength: 70.0 MPa
$ 2293/MT
- Tensile Strength, Yield: 1572 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1779 MPa @Temperature 71.0 °C
- Tensile Modulus: 90.3 GPa @Temperature 23.0 °C
- Tensile Modulus: 93.8 GPa @Temperature 71.0 °C
- Flexural Yield Strength: 1172 MPa @Temperature 71.0 °C
$ 2294/MT
- Tensile Strength, Yield: 2120 MPa @Temperature 23.0 °C
- Tensile Modulus: 391 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 858 MPa @Temperature 23.0 °C
- Flexural Modulus: 274 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 827 MPa @Temperature 23.0 °C
$ 1450/MT
- Cured Thickness per Ply (cm): 0.038
- Dry Resin Content (%): 40-44
- Fiber Volume (%): 51
- Flow (%): 4-16
$ 1689/MT
- Density: 1.29 g/cc
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Yield: 2.9 %
- Tensile Modulus: 3.20 GPa
- Glass Transition Temp, Tg: 110 - 130 °C
$ 1540/MT
- Tensile Strength, Yield: 4.55 MPa @Temperature 71.1 °C
- Tensile Strength, Yield: 5.79 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 6.41 MPa @Temperature 71.1 °C
- Tensile Strength, Yield: 6.62 MPa @Temperature 21.1 °C
- Shear Strength: 3.65 MPa @Temperature -55.0 °C
$ 1708/MT
- Density: 1.25 g/cc
- Outgassing - Total Mass Loss: 0.070 %
- Collected Volatile Condensable Material: 0.00 %
- Tensile Strength, Yield: 94.0 MPa @Temperature 23.0 °C
- Elongation at Yield: 2.52 % @Temperature 23.0 °C
$ 1614/MT
- Tensile Strength, Yield: 2326 MPa @Temperature 23.0 °C
- Tensile Modulus: 153 GPa @Temperature 23.0 °C
- Shear Strength: 44.0 MPa @Temperature 60.0 °C
- Shear Strength: 63.0 MPa @Temperature 90.0 °C
- Shear Strength: 92.0 MPa @Temperature 23.0 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
$ 1763/MT
- Tensile Strength, Yield: 385 MPa @Temperature 177 °C
- Tensile Strength, Yield: 461 MPa @Temperature 24.0 °C
- Tensile Modulus: 23.9 GPa @Temperature 177 °C
- Tensile Modulus: 29.7 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 353 MPa @Temperature 177 °C
$ 1469/MT
- Tensile Strength, Yield: 8.89 MPa @Temperature 22.2 °C
- Tensile Strength, Yield: 9.294 MPa @Temperature 22.2 °C
- Shear Strength: 26.0 MPa @Temperature 149 °C
- Shear Strength: 44.99 MPa @Temperature 22.2 °C
- Peel Strength: 7.01 kN/m @Temperature 22.2 °C
$ 2367/MT
- Density: 1.24 g/cc
- Maximum Service Temperature, Air: 120 - 130 °C
- Glass Transition Temp, Tg: 143 °C
- Glass Transition Temp, Tg: 155 °C
- Gel Time: 2.00 - 3.50 min @Temperature 140 °C
$ 1551/MT
- Tensile Strength, Yield: 1760 MPa
- Tensile Modulus: 215 GPa
- Compressive Yield Strength: 240 MPa
- Compressive Yield Strength: 894 MPa
- Shear Strength: 76.0 MPa
$ 2386/MT
- Density: 1.17 g/cc
- Density: 1.50 g/cc
- Density: 1.79 g/cc
- Tensile Strength, Yield: 897 MPa
- Tensile Modulus: 68.2 GPa
$ 1782/MT
- Volatiles: 1.0 - 4.0 %
- Cured Thickness per Ply (cm): 0.0097-0.011
- Dry Resin Content (%): 36-40
- Fiber Volume (%): 50-55
- Flow (%): 13-25
$ 2582/MT
- Density: 1.24 g/cc
- Density: 2.60 g/cc
- Tensile Strength, Yield: 415 MPa
- Tensile Strength, Yield: 510 MPa
- Tensile Strength, Yield: 270 MPa @Temperature 75.0 °C
$ 2369/MT
- Storage Temperature: -17.8 °C
- Shear Strength: 13.00 MPa @Temperature 100 °C
- Shear Strength: 19.00 MPa @Temperature 80.0 °C
- Shear Strength: 24.0 MPa @Temperature 50.0 °C
- Shear Strength: 30.0 MPa @Temperature 22.2 °C
$ 1875/MT
- Tensile Strength, Yield: 8.89 MPa @Temperature 22.2 °C
- Tensile Strength, Yield: 8.998 MPa @Temperature 22.2 °C
- Shear Strength: 0.152 MPa @Temperature 149 °C
- Shear Strength: 0.207 MPa @Temperature 22.2 °C
- Shear Strength: 16.0 MPa @Temperature 149 °C
$ 2571/MT
- Dry Resin Content (%): 37-41
- Fiber Volume (%): 0.019
- Flow (%): 4-16
- Wet Resin Content (%): 52
$ 1657/MT
- Tensile Strength, Yield: 19.0 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1799 MPa @Temperature 23.0 °C
- Tensile Modulus: 4.80 GPa @Temperature 23.0 °C
- Tensile Modulus: 556 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 365 MPa @Temperature 23.0 °C
$ 1579/MT
- Tensile Strength, Yield: 4.413 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 5.164 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 547 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 571 MPa @Temperature 24.0 °C
- Tensile Modulus: 26.9 GPa @Temperature 71.0 °C
$ 1824/MT
- Tensile Strength, Yield: 10.9 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 57.9 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 75.8 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 931 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 2760 MPa @Temperature 25.0 °C
$ 1459/MT
- Tensile Strength, Yield: 882 MPa @Temperature 23.0 °C
- Tensile Modulus: 56.0 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 515 MPa @Temperature 90.0 °C
- Flexural Yield Strength: 818 MPa @Temperature 23.0 °C
- Compressive Yield Strength: 422 MPa @Temperature 90.0 °C
$ 1489/MT
- Tensile Strength, Yield: 8.00 MPa @Temperature 177 °C
- Tensile Strength, Yield: 8.998 MPa @Temperature 149 °C
- Tensile Strength, Yield: 13.00 MPa @Temperature 22.2 °C
- Shear Strength: 14.0 MPa @Temperature 177 °C
- Shear Strength: 17.00 MPa @Temperature 149 °C
$ 1961/MT
- Tensile Strength, Yield: 1353 MPa @Temperature 24.0 °C
- Tensile Modulus: 131.8 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 1185 MPa @Temperature 71.0 °C
- Compressive Yield Strength: 1212 MPa @Temperature 24.0 °C
- Shear Strength: 76.0 MPa @Temperature 132 °C
$ 1693/MT
- Outgassing - Total Mass Loss: 0.41 %
- Outgassing - Total Mass Loss: 1.74 %
- Collected Volatile Condensable Material: 0.00 %
- Shear Strength: 20.99 MPa @Temperature 21.1 °C
- Shear Strength: 20.99 MPa @Temperature 149 °C
$ 1484/MT
- Tensile Strength, Yield: 2048 MPa @Temperature 23.0 °C
- Tensile Modulus: 324 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 1034 MPa @Temperature 23.0 °C
- Flexural Modulus: 255 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 896 MPa @Temperature 23.0 °C
$ 1473/MT
- Density: 1.24 g/cc
- Tensile Strength, Yield: 69.0 MPa @Temperature 23.0 °C
- Elongation at Break: 2.59 %
- Tensile Modulus: 3.00 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 82.0 MPa @Temperature 163 °C
$ 1975/MT
- Shear Strength: 30.99 MPa @Temperature 22.2 °C
- Peel Strength: 5.50 kN/m @Temperature 22.2 °C
- Shelf Life: 18.0 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.05
- Climbing Drum Peel (in-lb/3in): 44.8
$ 1558/MT
- Shelf Life: 6.00 Month @Temperature -17.8 °C
- Carrier/Foil: Perforated and expanded Copper foil
$ 1978/MT
- Tensile Strength, Yield: 39.0 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 2227 MPa @Temperature 23.0 °C
- Tensile Modulus: 5.50 GPa @Temperature 23.0 °C
- Tensile Modulus: 303 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 903 MPa @Temperature 23.0 °C
$ 1468/MT
- Shelf Life: 6.00 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.045
- Carrier/Foil: Stainless Steel foil
$ 1906/MT
- Thickness: 32.5 microns
- Tensile Strength at Break: 170 MPa @Temperature 120 °C
- Tensile Strength at Break: 175 MPa @Temperature 23.0 °C
- Tensile Modulus: 40.0 GPa @Temperature 120 °C
- Tensile Modulus: 43.0 GPa @Temperature 23.0 °C
$ 2528/MT
- Volatiles: 1.0 - 6.0 %
- Tensile Strength, Yield: 508 MPa @Temperature -54.0 °C
- Tensile Strength, Yield: 513 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 563 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 581 MPa @Temperature 71.0 °C
$ 1496/MT
- Storage Temperature: -17.8 °C
- Shelf Life: 6.00 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.06
- Roll Width (in): 49
- Standard Roll (ft2): 670
$ 1760/MT
- Tensile Strength, Yield: 741 MPa @Temperature 23.0 °C
- Tensile Modulus: 54.0 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 518 MPa @Temperature 90.0 °C
- Flexural Yield Strength: 921 MPa @Temperature 23.0 °C
- Flexural Modulus: 37.0 GPa @Temperature 90.0 °C
$ 1471/MT
- Tensile Strength, Yield: 2482 MPa @Temperature 23.0 °C
- Tensile Modulus: 129 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 1234 MPa @Temperature 23.0 °C
- Flexural Modulus: 101.4 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 1517 MPa @Temperature 23.0 °C
$ 1554/MT
- Tensile Strength, Yield: 2600 MPa
- Tensile Modulus: 183 GPa
- Flexural Yield Strength: 1570 MPa
- Flexural Modulus: 205 GPa
- Compressive Yield Strength: 1510 MPa
$ 1633/MT
- Density: 1.19 g/cc
- Tensile Strength, Yield: 56.0 MPa @Temperature 23.0 °C
- Elongation at Break: 1.9 %
- Tensile Modulus: 3.30 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 88.0 MPa @Temperature 23.0 °C
$ 1474/MT
- Tensile Strength, Yield: 1552 MPa @Temperature 24.0 °C
- Tensile Modulus: 126.2 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 924 MPa @Temperature 71.0 °C
- Compressive Yield Strength: 1158 MPa @Temperature 24.0 °C
- Compressive Modulus: 109.6 GPa @Temperature 24.0 °C
$ 1475/MT
- Shear Strength: 13.1 MPa @Temperature 93.3 °C
- Shear Strength: 29.6 MPa @Temperature 60.0 °C
- Shear Strength: 39.3 MPa @Temperature 21.1 °C
- Peel Strength: 12.6 kN/m @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
$ 1507/MT
- Shear Strength: 11.0 MPa @Temperature 93.3 °C
- Shear Strength: 24.1 MPa @Temperature 60.0 °C
- Shear Strength: 33.8 MPa @Temperature 21.1 °C
- Peel Strength: 8.59 kN/m @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
$ 1892/MT
- Tensile Strength, Yield: 1213 MPa @Temperature 23.0 °C
- Tensile Modulus: 558 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 476 MPa @Temperature 23.0 °C
- Flexural Modulus: 427 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 262 MPa @Temperature 23.0 °C
$ 2254/MT
- Tensile Strength, Yield: 4.544 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 5.509 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 6.026 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 330 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 363 MPa @Temperature 71.0 °C
$ 2171/MT
- Density: 1.11 g/cc @Temperature 25.0 °C
- Density: 1.14 g/cc @Temperature 25.0 °C
- Tensile Strength, Yield: 75.0 MPa
- Tensile Strength, Yield: 860 MPa
- Tensile Strength, Yield: 830 MPa @Temperature 80.0 °C
$ 1462/MT
- Tensile Strength, Yield: 627 MPa @Temperature 23.0 °C
- Elongation at Yield: 2.8 % @Temperature 23.0 °C
- Tensile Modulus: 28.3 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 848 MPa @Temperature 23.0 °C
- Flexural Modulus: 28.3 GPa @Temperature 23.0 °C
$ 1495/MT
- Tensile Strength, Yield: 1260 MPa @Temperature 177 °C
- Tensile Strength, Yield: 1362 MPa @Temperature 24.0 °C
- Tensile Modulus: 125.7 GPa @Temperature 177 °C
- Tensile Modulus: 132.3 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 1154 MPa @Temperature 71.0 °C
$ 1952/MT
- Tensile Strength, Yield: 4.62 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 1710 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 1834 MPa @Temperature 24.0 °C
- Tensile Modulus: 119 GPa @Temperature 71.0 °C
- Tensile Modulus: 126.2 GPa @Temperature 24.0 °C
$ 1663/MT
- Glass Transition Temp, Tg: 5.00 °C
- Gel Time: 5.50 min @Temperature 120 °C
- Shelf Life: 1.00 Month @Temperature 23.0 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
- Tack Life (days): 3
- Tack Life (days): 5
$ 2276/MT
- Specific Gravity: 1.283 g/cc
- Moisture Absorption at Equilibrium: 4.8 %
- Tensile Strength, Yield: 67.0 MPa
- Elongation at Yield: >= 2.1 %
- Tensile Modulus: 3.20 GPa
$ 1491/MT
- Tensile Strength, Yield: 2320 MPa
- Tensile Modulus: 125 GPa
- Flexural Yield Strength: 1320 MPa
- Flexural Modulus: 117 GPa
- Compressive Yield Strength: 1500 MPa
$ 1932/MT
- Glass Transition Temp, Tg: 87.0 °C
- Glass Transition Temp, Tg: 100 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
$ 1509/MT
- Storage Temperature: -17.8 °C
- Tensile Strength, Yield: 7.03 MPa
- Shear Strength: 15.2 MPa @Temperature 98.9 °C
- Shear Strength: 24.1 MPa @Temperature 21.1 °C
- Shear Strength: 24.1 MPa @Temperature 82.2 °C
$ 2033/MT
- Storage Temperature: -17.8 °C
- Tensile Strength, Yield: 5.86 MPa @Temperature 82.2 °C
- Tensile Strength, Yield: 7.58 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 8.27 MPa @Temperature 21.1 °C
- Shear Strength: 17.9 MPa @Temperature 100 °C
$ 1619/MT
- Flexural Yield Strength: 1050.7 MPa @Temperature 50.0 °C
- Flexural Yield Strength: 1060.8 MPa @Temperature 50.0 °C
- Flexural Yield Strength: 1080.8 MPa @Temperature 50.0 °C
- Flexural Yield Strength: 1150.8 MPa @Temperature 22.8 °C
- Flexural Yield Strength: 1150.8 MPa @Temperature 22.8 °C
$ 1951/MT
- Specific Gravity: 1.243 g/cc
- Moisture Absorption at Equilibrium: 2.8 %
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Yield: 2.2 %
- Tensile Modulus: 3.59 GPa
$ 1534/MT
- Specific Gravity: 1.20 g/cc
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Yield: >= 1.6 %
- Tensile Modulus: 3.10 GPa
- Glass Transition Temp, Tg: 124 °C
- Gel Time: <= 2.00 min @Temperature 135 °C
$ 2167/MT
- Tensile Strength, Yield: 2080 MPa
- Tensile Modulus: 130 GPa
- Flexural Yield Strength: 1450 MPa
- Flexural Modulus: 128 GPa
- Compressive Yield Strength: 1510 MPa
$ 2542/MT
- Tensile Strength, Yield: 2560 MPa
- Tensile Modulus: 184 GPa
- Flexural Yield Strength: 1330 MPa
- Flexural Modulus: 165 GPa
- Compressive Yield Strength: 1610 MPa
$ 1840/MT
- Density: 1.20 g/cc
- Density: 1.49 g/cc
- Density: 1.78 g/cc
- Tensile Strength, Yield: 751 MPa
- Tensile Modulus: 63.8 GPa
$ 1628/MT
- Tensile Strength, Yield: 4.137 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 5.516 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 400 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 427 MPa @Temperature 24.0 °C
- Tensile Modulus: 25.0 GPa @Temperature 71.0 °C
$ 1908/MT
- Storage Temperature: -17.8 °C
- Shear Strength: 17.00 MPa @Temperature 100 °C
- Shear Strength: 24.99 MPa @Temperature 80.0 °C
- Shear Strength: 28.0 MPa @Temperature 50.0 °C
- Shear Strength: 30.0 MPa @Temperature 22.2 °C
$ 1900/MT
- Tensile Strength, Yield: 2020 MPa @Temperature 23.0 °C
- Elongation at Yield: 0.91 % @Temperature 23.0 °C
- Elongation at Yield: 1.54 % @Temperature 23.0 °C
- Tensile Modulus: 121 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 1060 MPa @Temperature 23.0 °C
- Compressive Modulus: 117 GPa @Temperature 23.0 °C
$ 1989/MT
- Tensile Strength, Yield: 4.206 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 4.826 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 5.378 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 393 MPa @Temperature 93.0 °C
- Tensile Strength, Yield: 427 MPa @Temperature 71.0 °C
$ 1931/MT
- Shear Strength: 17.9 MPa @Temperature 93.3 °C
- Shear Strength: 35.9 MPa @Temperature 60.0 °C
- Shear Strength: 46.9 MPa @Temperature 21.1 °C
- Peel Strength: 8.77 kN/m @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
$ 2116/MT
- Density: 0.460 g/cc @Temperature 25.0 °C
- Density: 0.620 g/cc @Temperature 50.0 °C
- Density: 0.650 g/cc @Temperature 22.0 °C
- Density: 0.720 g/cc @Temperature 25.0 °C
- Hardness, Shore D: 74 @Temperature -5.56 °C
$ 1504/MT
- Specific Gravity: 1.10 g/cc
- Specific Gravity: 1.16 g/cc
- Specific Gravity: 1.20 g/cc
- Compressive Yield Strength: 98.0 MPa @Temperature 23.0 °C
- Shear Strength: 11.0 MPa @Temperature 150 °C
$ 1571/MT
- Tensile Strength, Yield: 263 MPa @Temperature 177 °C
- Tensile Strength, Yield: 368 MPa @Temperature 24.0 °C
- Tensile Modulus: 20.3 GPa @Temperature 177 °C
- Tensile Modulus: 23.9 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 345 MPa @Temperature 177 °C
$ 2293/MT
- Tensile Strength, Yield: 1900 MPa
- Tensile Modulus: 124 GPa
- Flexural Yield Strength: 2000 MPa
- Flexural Modulus: 116 GPa
- Compressive Yield Strength: 1250 MPa
$ 1661/MT
- Tensile Strength, Yield: 8.27 MPa @Temperature 21.1 °C
- Shear Strength: 20.0 MPa @Temperature 121 °C
- Shear Strength: 40.0 MPa @Temperature 71.1 °C
- Shear Strength: 46.2 MPa @Temperature 21.1 °C
- Peel Strength: 10.2 kN/m @Temperature 21.1 °C
$ 1730/MT
- Tensile Strength, Yield: 91.7 MPa @Temperature 104 °C
- Tensile Strength, Yield: 111 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 174 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 428 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 2540 MPa @Temperature 104 °C
$ 1828/MT
- Density: 1.272 g/cc
- Moisture Absorption at Equilibrium: 3.1 %
- Viscosity: 1900 cP @Temperature 129 - 149 °C
- Tensile Strength, Yield: 99.3 MPa
- Elongation at Yield: 4.4 %
$ 1832/MT
- Density: 1.27 g/cc
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Yield: 2.7 %
- Tensile Modulus: 2.90 GPa
- Poissons Ratio: 0.35
$ 1792/MT
- Density: 1.31 g/cc
- Tensile Strength, Yield: 105 MPa
- Elongation at Yield: 3.1 %
- Tensile Modulus: 3.60 GPa
- Flexural Yield Strength: 144 MPa
$ 1651/MT
- Volatiles: 0.40 - 1.2 %
- Tensile Strength, Yield: 308 MPa @Temperature 24.0 °C
- Compressive Yield Strength: 283 MPa @Temperature 24.0 °C
- Shear Strength: 26.676 MPa @Temperature 82.0 °C
- Shear Strength: 34.246 MPa @Temperature -54.0 °C
$ 1562/MT
- Tensile Strength, Yield: 2000 MPa
- Tensile Modulus: 130 GPa
- Flexural Yield Strength: 2000 MPa
- Flexural Modulus: 120 GPa
- Compressive Yield Strength: 1200 MPa
$ 1664/MT
- Density: 1.28 g/cc
- Density: 1.58 g/cc
- Density: 1.80 g/cc
- Tensile Strength, Yield: 2158 MPa @Temperature 23.0 °C
- Tensile Modulus: 154 GPa @Temperature 23.0 °C
$ 1619/MT
- Volatiles: <= 1.0 %
- Maximum Service Temperature, Air: 121 °C
- Gel Time: 12.0 - 22.0 min
- Dry Resin Content (%): 34-38
- Fiber Volume (%): 60
- Flow (%): 10-22
$ 2144/MT
- Tensile Strength, Yield: 940 MPa @Temperature 23.0 °C
- Tensile Modulus: 57.0 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 672 MPa @Temperature 90.0 °C
- Flexural Yield Strength: 946 MPa @Temperature 23.0 °C
- Flexural Modulus: 37.0 GPa @Temperature 90.0 °C
$ 1485/MT
- Tensile Strength, Yield: 517 MPa @Temperature 24.0 °C
- Tensile Modulus: 29.0 GPa @Temperature 24.0 °C
- Flexural Yield Strength: 110 MPa @Temperature 24.0 °C
- Flexural Yield Strength: 414 MPa @Temperature 24.0 °C
- Compressive Yield Strength: 117 MPa @Temperature 71.0 °C
$ 1760/MT
- Tensile Strength, Yield: 920 MPa @Temperature 23.0 °C
- Tensile Modulus: 60.0 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 935 MPa @Temperature 90.0 °C
- Flexural Yield Strength: 950 MPa @Temperature 23.0 °C
- Flexural Modulus: 40.0 GPa @Temperature 90.0 °C
$ 1503/MT
- Specific Gravity: 1.25 g/cc
- Viscosity: >= 15 cP @Temperature 156 °C
- Viscosity: 50 cP @Temperature 120 °C
- Viscosity: 67 cP @Temperature 120 °C
- Viscosity: 80 cP @Temperature 110 °C
$ 1764/MT
- Density: 1.30 g/cc
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: 1.4 %
- Elongation at Yield: 10.3 %
- Tensile Modulus: 4.17 GPa
$ 1445/MT
- Density: 1.26 g/cc
- Flexural Yield Strength: 120 MPa
- Flexural Modulus: 3.80 GPa
- Glass Transition Temp, Tg: 80.0 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
$ 1519/MT
- Density: 1.25 g/cc
- Glass Transition Temp, Tg: 85.0 °C
- Shelf Life: 12.0 Month @Temperature -18.0 °C
- Tack Life (days): 4
$ 1666/MT
- Shear Strength: 8.96 MPa @Temperature 93.3 °C
- Shear Strength: 19.3 MPa @Temperature 60.0 °C
- Shear Strength: 26.2 MPa @Temperature 21.1 °C
- Peel Strength: 9.12 kN/m @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
$ 1946/MT
- Shelf Life: 12.0 Month @Temperature -18.0 °C
$ 2594/MT
- Shear Strength: 31.7 MPa @Temperature 79.4 °C
- Shear Strength: 33.1 MPa @Temperature 71.1 °C
- Shear Strength: 37.2 MPa @Temperature 21.1 °C
- Shelf Life: 12.0 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.015
$ 1744/MT
- Density: 1.20 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Yield: 2.1 %
- Tensile Modulus: 3.00 GPa
- Glass Transition Temp, Tg: 95.0 °C
$ 1515/MT
- Tensile Strength, Yield: 1482 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 1717 MPa @Temperature 23.0 °C
- Tensile Modulus: 108.9 GPa @Temperature 71.0 °C
- Tensile Modulus: 110.3 GPa @Temperature 23.0 °C
- Flexural Yield Strength: 1289 MPa @Temperature 71.0 °C
$ 1555/MT
- Density: 1.22 g/cc
- Tensile Strength, Yield: 34.9 MPa
- Elongation at Yield: 7.4 %
- Elongation at Yield: 8.41 %
- Tensile Modulus: 3.76 GPa
$ 1830/MT
- Tensile Strength, Yield: 820 MPa @Temperature 24.0 °C
- Tensile Modulus: 72.4 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 655 MPa @Temperature 24.0 °C
- Compressive Modulus: 66.9 GPa @Temperature 24.0 °C
- Shear Strength: 63.4 MPa @Temperature 24.0 °C
$ 1489/MT
- Specific Gravity: 1.22 g/cc
- Volatiles: 3.92 %
- Moisture Absorption at Equilibrium: 4.2 %
- Tensile Strength, Yield: 60.4 MPa
- Elongation at Yield: 2.0 %
$ 1791/MT
- Density: 1.265 g/cc
- Tensile Strength, Yield: 56.0 MPa
- Elongation at Yield: 1.7 %
- Tensile Modulus: 4.05 GPa
- Flexural Yield Strength: 129 MPa
$ 1576/MT
- Density: 1.265 g/cc
- Tensile Strength, Yield: 56.0 MPa
- Elongation at Yield: 1.7 %
- Tensile Modulus: 4.05 GPa
- Flexural Yield Strength: 129 MPa
$ 2031/MT
- Tensile Strength, Yield: 391 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 862 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 945 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 979 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 979 MPa @Temperature 104 °C
$ 2587/MT
- Tensile Strength, Yield: 2270 MPa
- Tensile Modulus: 118 GPa
- Flexural Yield Strength: 1480 MPa
- Flexural Modulus: 114 GPa
- Compressive Yield Strength: 1650 MPa
$ 2562/MT
- Tensile Strength, Yield: 5.516 MPa
- Tensile Strength, Yield: 310 MPa @Temperature 71.0 °C
- Tensile Strength, Yield: 400 MPa @Temperature 23.0 °C
- Tensile Modulus: 20.7 GPa @Temperature 71.0 °C
- Tensile Modulus: 22.1 GPa @Temperature 23.0 °C
$ 1893/MT
- Glass Transition Temp, Tg: 100 °C
- Shelf Life: 6.00 Month @Temperature -18.0 °C
$ 1644/MT
- Density: 1.24 g/cc
- Density: 2.56 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Tensile Strength, Yield: 1560 MPa
- Tensile Strength, Yield: 16.0 MPa @Temperature 100 °C
$ 1613/MT
- Tensile Strength, Yield: 19.7 MPa @Temperature 24.0 °C
- Tensile Strength, Yield: 1758 MPa @Temperature -55.0 °C
- Tensile Strength, Yield: 1793 MPa @Temperature 71.0 °C
- Tensile Modulus: 131.7 GPa @Temperature 24.0 °C
- Tensile Modulus: 132.4 GPa @Temperature 71.0 °C
$ 1444/MT
- Tensile Strength, Yield: 75.2 MPa @Temperature 93.3 °C
- Tensile Strength, Yield: 80.7 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 438 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 738 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 1900 MPa @Temperature -55.0 °C
$ 1606/MT
- Tensile Strength, Yield: 330 MPa @Temperature 177 °C
- Tensile Strength, Yield: 438 MPa @Temperature 24.0 °C
- Tensile Modulus: 24.4 GPa @Temperature 177 °C
- Tensile Modulus: 27.7 GPa @Temperature 24.0 °C
- Compressive Yield Strength: 270 MPa @Temperature 177 °C
$ 2273/MT
- Dry Resin Content (%): 37-43
- Fiber Volume (%): 0.036
- Flow (%): 16-28
- Wet Resin Content (%): 45
$ 1652/MT
- Shelf Life: 6.00 Month @Temperature -17.8 °C
- Areal Weight (psf): 0.045
- Carrier/Foil: Woven Copper foil
$ 2227/MT
- Density: 1.53 g/cc
- Tensile Strength, Yield: 1017 MPa @Temperature 23.0 °C
- Tensile Modulus: 86.0 GPa @Temperature 23.0 °C
- Compressive Yield Strength: 904 MPa @Temperature 23.0 °C
- Compressive Modulus: 74.0 GPa
$ 1509/MT
- Density: 1.19 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.18 %
- Outgassing - Total Mass Loss: 0.20 %
- Outgassing - Total Mass Loss: 1.0 %
$ 2582/MT
- Tensile Strength, Yield: 9.10 MPa @Temperature 21.1 °C
- Shear Strength: 29.6 MPa @Temperature 98.9 °C
- Shear Strength: 39.3 MPa @Temperature 71.1 °C
- Shear Strength: 42.7 MPa @Temperature 21.1 °C
- Peel Strength: 9.12 kN/m @Temperature 21.1 °C
$ 1715/MT
- Tensile Strength, Yield: 780 MPa @Temperature 80.0 °C
- Tensile Strength, Yield: 790 MPa @Temperature 23.0 °C
- Flexural Yield Strength: 580 MPa @Temperature 80.0 °C
- Flexural Yield Strength: 900 MPa @Temperature 23.0 °C
- Flexural Modulus: 51.0 GPa @Temperature 80.0 °C
$ 2031/MT
- Cured Thickness per Ply (cm): 0.026
- Dry Resin Content (%): 36-40
- Fiber Volume (%): 45
- Flow (%): 8-20
$ 1986/MT
- Tensile Strength, Yield: 400 MPa
- Tensile Modulus: 35.0 GPa
- Flexural Yield Strength: 450 MPa
- Flexural Modulus: 35.0 GPa
- Shear Strength: 40.0 MPa
$ 1572/MT
- Tensile Strength, Yield: 900 MPa
- Tensile Modulus: 37.0 GPa
- Flexural Yield Strength: 900 MPa
- Flexural Modulus: 35.0 GPa
- Shear Strength: 60.0 MPa
Delivery Epoxy Hexcel
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ship sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.