$ 2296/MT
- Bulk Density: 3.045 g/cc
- Porosity: 17 %
- Permeability: 4.0
- Deformation: 0.20 %
- Modulus of Rupture: 0.00965 GPa @Temperature 1540 °C
$ 1600/MT
- Specific Gravity: 3.30 - 3.50 g/cc
- Tensile Strength, Ultimate: 1000 - 2000 MPa
- Modulus of Elasticity: 296 - 324 GPa
- Al2O3: 96 - 97 %
- SiO2: 3.0 - 4.0 %
$ 1446/MT
- Density: 2.821 - 3.013 g/cc
- Modulus of Rupture: 0.00483 - 0.00827 GPa
- Modulus of Rupture: 0.00345 - 0.00552 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00689 - 0.00965 GPa @Treatment Temp. 1870 °C, Time 18000 sec
- Compressive Strength: 24.1 - 41.4 MPa
$ 1823/MT
- Density: >= 0.593 g/cc
- Solids Content: 43 %
- Modulus of Rupture: 0.00138 GPa
- Thermal Conductivity: 0.0749 W/m-K @Temperature 149 °C
- Thermal Conductivity: 0.105 W/m-K @Temperature 371 °C
$ 2288/MT
- Density: 0.192 g/cc
- Thickness: 3000 - 12000 microns
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.138 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.239 W/m-K @Temperature 816 °C
$ 1503/MT
- Loss On Ignition: 20 %
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1090 °C
- Al2O3: 47 %
- SiO2: 53 %
- Tensile Strength grip, lb: 63
$ 1910/MT
- Density: 0.0960 g/cc
- Loss On Ignition: 2.0 - 5.0 %
- Tensile Strength, Ultimate: 0.0345 MPa
- Tensile Strength, Ultimate: 0.0689 - 0.138 MPa
- Thermal Conductivity: 0.0548 W/m-K @Temperature 260 °C
$ 1694/MT
- Loss On Ignition: 20 %
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 982 °C
- Shrinkage: 2.0 %
- Al2O3: 47 %
- SiO2: 53 %
$ 1541/MT
- Density: 1.314 g/cc
- Deformation: 0.10 %
- Modulus of Rupture: 0.00310 GPa
- Compressive Strength: 6.20 MPa
- Thermal Conductivity: 0.793 W/m-K @Temperature 260 °C
$ 1937/MT
- Density: 0.0640 - 0.128 g/cc
- Thickness: 12500 - 50000 microns
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1320 °C
- Maximum Service Temperature, Air: 1430 °C
$ 1783/MT
- Density: 0.224 g/cc
- Loss On Ignition: 7.0 - 9.0 %
- Modulus of Rupture: 0.000862 GPa
- Compressive Yield Strength: 0.210 MPa
- Compressive Yield Strength: 0.240 MPa
$ 1529/MT
- Density: 2.019 - 2.179 g/cc
- Modulus of Rupture: 0.00689 - 0.00965 GPa
- Modulus of Rupture: 0.00276 - 0.00552 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00689 - 0.0103 GPa @Treatment Temp. 1320 °C, Time 18000 sec
- Compressive Strength: 24.1 - 41.4 MPa
$ 2076/MT
- Density: 1.33 - 1.426 g/cc
- Density: 1.346 - 1.506 g/cc
- Modulus of Rupture: 0.00276 - 0.00414 GPa
- Modulus of Rupture: 0.00259 - 0.00414 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00345 - 0.00517 GPa @Treatment Temp. 1370 °C, Time 18000 sec
$ 1966/MT
- Density: 0.768 - 0.897 g/cc
- Density: 0.849 - 1.04 g/cc
- Modulus of Rupture: 0.000345 - 0.000448 GPa
- Modulus of Rupture: 0.000331 - 0.000386 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.000338 - 0.000379 GPa @Treatment Temp. 1090 °C, Time 18000 sec
$ 1877/MT
- Density: 0.320 - 0.400 g/cc
- Density: 0.464 - 0.609 g/cc
- Modulus of Rupture: 0.000172 - 0.000276 GPa
- Modulus of Rupture: 0.000345 - 0.000689 GPa
- Modulus of Rupture: 0.000172 - 0.000276 GPa @Treatment Temp. 982 °C, Time 18000 sec
$ 1533/MT
- Density: 0.881 - 1.041 g/cc
- Density: 0.913 - 1.041 g/cc
- Modulus of Rupture: 0.000621 - 0.00103 GPa
- Modulus of Rupture: 0.000621 - 0.00110 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.000621 - 0.00117 GPa @Treatment Temp. 1090 °C, Time 18000 sec
$ 1600/MT
- Density: 0.881 - 1.041 g/cc
- Density: 0.913 - 1.041 g/cc
- Modulus of Rupture: 0.000621 - 0.00103 GPa
- Modulus of Rupture: 0.000621 - 0.00110 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.000621 - 0.00110 GPa @Treatment Temp. 1200 °C, Time 18000 sec
$ 1483/MT
- Density: 0.849 - 1.01 g/cc
- Density: 0.881 - 1.026 g/cc
- Modulus of Rupture: 0.000621 - 0.00103 GPa
- Modulus of Rupture: 0.000586 - 0.00103 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.000552 - 0.00138 GPa @Treatment Temp. 1200 °C, Time 18000 sec
$ 2316/MT
- Density: 1.089 - 1.25 g/cc
- Density: 1.153 - 1.282 g/cc
- Modulus of Rupture: 0.00207 - 0.00379 GPa
- Modulus of Rupture: 0.00138 - 0.00241 GPa @Treatment Temp. 1200 °C, Time 18000 sec
- Modulus of Rupture: 0.00110 - 0.00276 GPa @Treatment Temp. 816 °C, Time 18000 sec
$ 1450/MT
- Density: 1.074 - 1.25 g/cc
- Density: 1.09 - 1.25 g/cc
- Modulus of Rupture: 0.00172 - 0.00276 GPa
- Modulus of Rupture: 0.00103 - 0.00172 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00138 - 0.00207 GPa @Treatment Temp. 1200 °C, Time 18000 sec
$ 1510/MT
- Density: 0.897 - 1.025 g/cc
- Density: 0.865 - 1.058 g/cc
- Modulus of Rupture: 0.000689 - 0.00124 GPa
- Modulus of Rupture: 0.000621 - 0.00117 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.000896 - 0.00172 GPa @Treatment Temp. 1260 °C, Time 18000 sec
$ 2186/MT
- Density: 0.865 - 1.042 g/cc
- Density: 0.881 - 1.026 g/cc
- Modulus of Rupture: 0.000827 - 0.00138 GPa
- Modulus of Rupture: 0.000621 - 0.00103 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00103 - 0.00207 GPa @Treatment Temp. 1260 °C, Time 18000 sec
$ 1487/MT
- Density: 1.138 - 1.378 g/cc
- Density: 1.218 - 1.41 g/cc
- Modulus of Rupture: 0.00172 - 0.00276 GPa
- Modulus of Rupture: 0.00172 - 0.00276 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00276 - 0.00448 GPa @Treatment Temp. 1370 °C, Time 18000 sec
$ 2208/MT
- Density: 1.378 - 1.522 g/cc
- Modulus of Rupture: 0.00207 - 0.00345 GPa
- Modulus of Rupture: 0.00138 - 0.00241 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00689 - 0.0103 GPa @Treatment Temp. 1430 °C, Time 18000 sec
- Compressive Strength: 5.51 - 8.96 MPa
$ 1503/MT
- Density: 1.474 - 1.586 g/cc
- Modulus of Rupture: 0.00552 - 0.00827 GPa
- Modulus of Rupture: 0.00483 - 0.00724 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00689 - 0.0128 GPa @Treatment Temp. 1760 °C, Time 18000 sec
- Compressive Strength: 15.9 - 23.4 MPa
$ 1460/MT
- Density: 0.946 - 1.154 g/cc
- Density: 1.026 - 1.17 g/cc
- Modulus of Rupture: 0.00138 - 0.00207 GPa
- Modulus of Rupture: 0.000689 - 0.00155 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00138 - 0.00207 GPa @Treatment Temp. 1370 °C, Time 18000 sec
$ 1532/MT
- Density: 1.122 - 1.314 g/cc
- Density: 1.25 - 1.41 g/cc
- Modulus of Rupture: 0.00207 - 0.00345 GPa
- Modulus of Rupture: 0.000827 - 0.00138 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00483 - 0.00827 GPa @Treatment Temp. 1430 °C, Time 18000 sec
$ 1700/MT
- Density: 1.522 - 1.683 g/cc
- Modulus of Rupture: 0.00172 - 0.00276 GPa
- Modulus of Rupture: 0.00138 - 0.00207 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00586 - 0.00689 GPa @Treatment Temp. 1540 °C, Time 18000 sec
- Compressive Strength: 3.44 - 4.80 MPa
$ 1817/MT
- Specific Gravity: 2.56 g/cc
- Tensile Strength, Ultimate: 1030 MPa
- Tensile Modulus: 84.1 GPa
- Specific Heat Capacity: 1.089 J/g-°C @Temperature 982 °C
- Melting Point: 1760 °C
$ 2147/MT
- Density: 0.192 g/cc
- Thickness: 3000 - 12000 microns
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.138 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.239 W/m-K @Temperature 816 °C
$ 1602/MT
- Bulk Density: 2.772 g/cc
- Porosity: 19 %
- Permeability: 4.0
- Deformation: 0.20 %
- Modulus of Rupture: 0.00689 GPa @Temperature 1540 °C
$ 1729/MT
- Density: 0.0960 g/cc
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Loss On Ignition: 0.00 %
$ 1914/MT
- Density: 0.144 g/cc
- Thickness: 6300 microns
- Thickness: 13000 microns
- Thermal Conductivity: 0.0600 W/m-K @Temperature 149 °C
- Thermal Conductivity: 0.0800 W/m-K @Temperature 260 °C
$ 1888/MT
- Bulk Density: 0.240 - 0.304 g/cc
- Melting Point: 1500 °C
- Maximum Service Temperature, Air: 1200 °C
- CaO: 16 - 22 %
- MgO: 12 - 19 %
$ 1523/MT
- Specific Gravity: 2.54 g/cc
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 538 °C
- Al2O3: 10 - 12 %
- Alkalis: 0.00 - 1.0 %
$ 1774/MT
- Modulus of Rupture: 0.00176 GPa
- Melting Point: 1790 °C
- Maximum Service Temperature, Air: 1200 °C
- Shrinkage: 2.50 % @Temperature 1260 °C, Time 86400 sec
- Al2O3: 44 %
$ 1471/MT
- Bulk Density: 0.192 - 0.256 g/cc
- Melting Point: 1500 °C
- Maximum Service Temperature, Air: 1200 °C
- CaO: 16 - 22 %
- MgO: 12 - 19 %
$ 1778/MT
- Density: 0.176 - 0.208 g/cc
- Loss On Ignition: 2.0 - 5.0 %
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.241 - 0.345 MPa
- Thermal Conductivity: 0.0548 W/m-K @Temperature 260 °C
$ 1940/MT
- Specific Gravity: 2.54 g/cc
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 538 °C
- Al2O3: 10 - 12 %
- Alkalis: 0.00 - 1.0 %
$ 1622/MT
- Density: 1.025 - 1.17 g/cc
- Density: 1.025 - 1.17 g/cc
- Modulus of Rupture: 0.00103 - 0.00172 GPa
- Modulus of Rupture: 0.000827 - 0.00138 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00172 - 0.00276 GPa @Treatment Temp. 1370 °C, Time 18000 sec
$ 1481/MT
- Density: 0.144 g/cc
- Loss On Ignition: 5.0 %
- Thermal Conductivity: 0.125 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.146 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.189 W/m-K @Temperature 816 °C
$ 1605/MT
- Density: 0.320 - 0.400 g/cc
- Density: 0.496 - 0.625 g/cc
- Modulus of Rupture: 0.000310 - 0.000517 GPa
- Modulus of Rupture: 0.000483 - 0.000827 GPa
- Modulus of Rupture: 0.000172 - 0.000276 GPa @Treatment Temp. 816 °C, Time 18000 sec
$ 1555/MT
- Density: 0.4245 g/cc
- Density: 0.4806 g/cc @Temperature 1090 °C
- Loss On Ignition: 9.5 %
- Porosity: 91 %
- Modulus of Rupture: 0.000814 GPa
$ 1523/MT
- Density: 0.192 g/cc
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.138 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.239 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.353 W/m-K @Temperature 1090 °C
$ 1565/MT
- Density: 0.128 g/cc
- Thermal Conductivity: 0.0764 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.163 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.284 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.367 W/m-K @Temperature 982 °C
$ 1445/MT
- Bulk Density: 2.82 g/cc
- Porosity: 16 %
- Permeability: 4.0
- Deformation: 0.00 %
- Deformation: 0.30 %
$ 1977/MT
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1260 °C
- Flammability Test: 0.00
- Flammability Test: 0.00
- Flammability Test: 0.00
$ 2555/MT
- Density: 0.881 g/cc
- Loss On Ignition: 5.00 - 7.00 % @Temperature 538 °C
- Modulus of Rupture: 0.00448 - 0.00517 GPa
- Compressive Yield Strength: 0.340 - 0.510 MPa
- Compressive Yield Strength: 0.690 - 0.860 MPa
$ 1823/MT
- Density: 3.093 g/cc
- Deformation: -0.700 %
- Modulus of Rupture: 0.00552 GPa @Temperature 1430 °C
- Modulus of Rupture: 0.0138 GPa @Temperature 1260 °C
- Modulus of Rupture: 0.0290 GPa @Temperature 23.0 °C
$ 1516/MT
- Density: 0.321 - 0.353 g/cc
- Loss On Ignition: 4.0 - 7.0 %
- Modulus of Rupture: 0.00103 - 0.00138 GPa
- Compressive Yield Strength: 0.240 - 0.340 MPa
- Compressive Yield Strength: 0.340 - 0.450 MPa
$ 1897/MT
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 927 °C
- Shrinkage: 10 %
- Al2O3: 0.071 %
- B2O3: >= 0.016 %
$ 1536/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Density: 0.240 g/cc
- Thermal Conductivity: 0.0706 W/m-K @Temperature 260 °C
$ 2193/MT
- Bulk Density: 2.356 g/cc
- Porosity: 22 %
- Modulus of Rupture: 0.0143 GPa
- CTE, linear: 5.76 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 1.77 W/m-K @Temperature 1090 °C
$ 1872/MT
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 927 °C
- Shrinkage: 10 %
- Al2O3: 0.071 %
- B2O3: >= 0.016 %
$ 1537/MT
- Density: 1.554 - 1.715 g/cc
- Modulus of Rupture: 0.00138 - 0.00414 GPa
- Modulus of Rupture: 0.000689 - 0.00207 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00138 - 0.00276 GPa @Treatment Temp. 1200 °C, Time 18000 sec
- Compressive Strength: 2.80 - 5.50 MPa
$ 1561/MT
- Loss On Ignition: 8.0 %
- Thermal Conductivity: 0.03234 W/m-K @Temperature 23.9 °C
- Thermal Conductivity: 0.03437 W/m-K @Temperature 93.3 °C
- Thermal Conductivity: 0.04699 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0715 W/m-K @Temperature 538 °C
$ 2019/MT
- Density: 2.10 - 2.80 g/cc
- Solubility in Water: 0.00 %
- Loss On Ignition: 0.000 % @Temperature 799 °C, Time 7200 sec
- Melting Point: >= 2000 °C
- Maximum Service Temperature, Air: 1000 °C
$ 1909/MT
- Density: 0.160 - 0.208 g/cc
- Loss On Ignition: 5.0 - 10 %
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.517 - 0.689 MPa
- Thermal Conductivity: 0.0562 W/m-K @Temperature 260 °C
$ 1604/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Thermal Conductivity: 0.0793 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0821 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.143 W/m-K @Temperature 538 °C
$ 1521/MT
- Density: 3.30 - 3.50 g/cc
- Solubility in Water: 0.00 %
- Loss On Ignition: 0.000 % @Temperature 799 °C, Time 7200 sec
- Melting Point: >= 2000 °C
- Maximum Service Temperature, Air: 1600 °C
$ 2047/MT
- Density: 1.891 - 2.115 g/cc
- Modulus of Rupture: 0.00345 - 0.00621 GPa
- Modulus of Rupture: 0.00172 - 0.00310 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00689 - 0.0103 GPa @Treatment Temp. 1430 °C, Time 18000 sec
- Compressive Strength: 11.8 - 17.2 MPa
$ 1513/MT
- Density: 0.0500 g/cc
- Thermal Conductivity: 0.0893 W/m-K @Temperature 200 °C
- Thermal Conductivity: 0.140 W/m-K @Temperature 300 °C
- Thermal Conductivity: 0.220 W/m-K @Temperature 400 °C
- Thermal Conductivity: 0.320 W/m-K @Temperature 500 °C
$ 1614/MT
- Density: 0.385 g/cc
- Permeability: 3.0
- Thickness: 6250 microns
- Thickness: 12500 microns
- Thickness: 25000 microns
$ 2173/MT
- Density: 0.272 g/cc
- Loss On Ignition: 1.3 %
- Hardness, Shore A: 70 - 80
- Modulus of Rupture: 0.000517 GPa
- Compressive Yield Strength: 0.0600 MPa
$ 1473/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Thermal Conductivity: 0.0793 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0821 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.143 W/m-K @Temperature 538 °C
$ 2496/MT
- Bulk Density: 2.853 g/cc
- Porosity: 23 %
- Modulus of Rupture: 0.0276 GPa
- CTE, linear: 7.56 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 3.17 W/m-K @Temperature 1090 °C
$ 2002/MT
- Density: 0.321 - 0.369 g/cc
- Loss On Ignition: 4.0 - 7.0 %
- Modulus of Rupture: 0.00117 - 0.00138 GPa
- Compressive Yield Strength: 0.380 - 0.520 MPa
- Thermal Conductivity: 0.0692 W/m-K @Temperature 260 °C
$ 1763/MT
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: 41 %
- Alkalis: 2.1 %
- CaO: 0.20 %
- Fe2O3: 1.4 %
$ 2156/MT
- Bulk Density: 2.74 g/cc
- Porosity: 25 %
- Modulus of Rupture: 0.00655 GPa
- CTE, linear: 8.10 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 2.64 W/m-K @Temperature 1090 °C
$ 2571/MT
- Density: 0.0960 g/cc
- Loss On Ignition: <= 3.0 %
- Tensile Strength, Ultimate: 0.0345 MPa
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Thermal Conductivity: 0.0403 W/m-K @Temperature 100 °C
$ 1679/MT
- Density: 0.0640 g/cc
- Density: 0.0960 g/cc
- Density: 0.128 g/cc
- Thickness: 12500 - 50000 microns
- Thermal Conductivity: 0.0600 W/m-K @Temperature 260 °C
$ 1831/MT
- Specific Heat Capacity: 0.220 J/g-°C
- Thermal Conductivity: 0.127 W/m-K @Temperature 204 °C
- Thermal Conductivity: 0.157 W/m-K @Temperature 427 °C
- Thermal Conductivity: 0.189 W/m-K @Temperature 649 °C
- Thermal Conductivity: 0.225 W/m-K @Temperature 871 °C
$ 1867/MT
- Bulk Density: 2.869 g/cc
- Porosity: 17 %
- Permeability: 4.0
- Deformation: 3.6 %
- Modulus of Rupture: 0.00483 GPa @Temperature 1540 °C
$ 2328/MT
- Density: 0.160 - 0.192 g/cc
- Loss On Ignition: 7.0 - 10 %
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.517 - 0.689 MPa
- Thermal Conductivity: 0.0548 W/m-K @Temperature 260 °C
$ 1482/MT
- Density: 0.416 g/cc
- Loss On Ignition: 5.0 - 8.0 %
- Modulus of Rupture: 0.00103 - 0.00121 GPa
- Compressive Yield Strength: 0.340 - 0.480 MPa
- Compressive Yield Strength: 0.480 - 0.610 MPa
$ 1679/MT
- Density: 0.0480 g/cc
- Density: 0.0640 g/cc
- Tensile Strength, Ultimate: 0.0414 MPa
- Maximum Service Temperature, Air: 1180 °C
- Al2O3: 45 - 47 %
$ 1493/MT
- Bulk Density: 0.0950 - 0.961 g/cc
- Melting Point: 1470 °C
- Maximum Service Temperature, Air: 1000 °C
- CaO: 25 - 35 %
- MgO: 4.0 - 7.0 %
$ 2177/MT
- Density: 0.128 g/cc
- Density: 0.149 g/cc
- Density: 0.171 g/cc
- Thickness: 4000 - 12000 microns
- Thermal Conductivity: 0.0793 W/m-K @Temperature 260 °C
$ 1948/MT
- Density: 1.987 - 2.163 g/cc
- Compressive Strength: 3.10 - 5.52 MPa
- Compressive Strength: 10.3 - 17.2 MPa
- Compressive Strength: 17.2 - 24.1 MPa
- Thermal Conductivity: 0.908 W/m-K @Temperature 260 °C
$ 2502/MT
- Density: 1.891 - 2.115 g/cc
- Modulus of Rupture: 0.00758 - 0.0110 GPa
- Modulus of Rupture: 0.00310 - 0.00448 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00621 - 0.00827 GPa @Treatment Temp. 1430 °C, Time 18000 sec
- Compressive Strength: 24.1 - 41.4 MPa
$ 1762/MT
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: 40 %
- Alkalis: 3.7 %
- CaO: 0.20 %
- Fe2O3: 1.4 %
$ 1629/MT
- Density: 0.224 g/cc
- Loss On Ignition: 7.0 - 9.0 %
- Modulus of Rupture: 0.000483 GPa
- Compressive Yield Strength: 0.140 MPa
- Compressive Yield Strength: 0.170 MPa
$ 1761/MT
- Bulk Density: 3.045 g/cc
- Porosity: 17 %
- Permeability: 4.0
- Deformation: 0.00 %
- Deformation: 0.20 %
$ 1649/MT
- Density: 1.875 - 2.019 g/cc
- Modulus of Rupture: 0.00393 - 0.00576 GPa
- Modulus of Rupture: 0.00179 - 0.00307 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00517 - 0.0100 GPa @Treatment Temp. 1540 °C, Time 18000 sec
- Compressive Strength: 8.30 - 15.7 MPa
$ 1635/MT
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 982 °C
- Shrinkage: 2.0 %
- Al2O3: 0.071 %
- B2O3: >= 0.016 %
$ 1730/MT
- Bulk Density: 0.192 - 0.256 g/cc
- Melting Point: 1470 °C
- Maximum Service Temperature, Air: 1000 °C
- CaO: 25 - 35 %
- MgO: 4.0 - 7.0 %
$ 1800/MT
- Density: 0.128 g/cc
- Density: 0.149 g/cc
- Density: 0.171 g/cc
- Thickness: 4000 - 12000 microns
- Thermal Conductivity: 0.0793 W/m-K @Temperature 260 °C
$ 1632/MT
- Density: 0.208 g/cc
- Loss On Ignition: 7.0 - 9.0 %
- Modulus of Rupture: 0.000483 GPa
- Compressive Yield Strength: 0.140 MPa
- Compressive Yield Strength: 0.170 MPa
$ 1620/MT
- Specific Gravity: 2.54 g/cc
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 538 °C
- Al2O3: 10 - 12 %
- Alkalis: 0.00 - 1.0 %
$ 1714/MT
- Thermal Conductivity: 0.0663 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.140 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.238 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.301 W/m-K @Temperature 982 °C
- Flammability Test: 0.00
$ 1579/MT
- Density: 0.560 - 0.641 g/cc
- Loss On Ignition: 9.00 - 11.0 % @Temperature 538 °C
- Modulus of Rupture: 0.00448 - 0.00517 GPa
- Compressive Yield Strength: 0.0600 - 0.140 MPa
- Compressive Yield Strength: 0.380 - 0.480 MPa
$ 1821/MT
- Loss On Ignition: 20 %
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1090 °C
- Shrinkage: 0.401 %
- Al2O3: 47 %
$ 2112/MT
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Density: 0.240 g/cc
- Thickness: 3000 - 12000 microns
- Thermal Conductivity: 0.0706 W/m-K @Temperature 260 °C
$ 1954/MT
- Density: 0.0480 - 0.128 g/cc
- Thickness: 6250 - 50000 microns
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1180 °C
- Maximum Service Temperature, Air: 1320 °C
$ 1538/MT
- Density: 0.0640 g/cc
- Density: 0.0960 g/cc
- Density: 0.128 g/cc
- Thickness: 25000 - 50000 microns
- Thermal Conductivity: 0.0600 W/m-K @Temperature 260 °C
$ 1736/MT
- Density: 0.0960 g/cc
- Maximum Service Temperature, Air: 1540 °C
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: 95 - 97 %
- SiO2: 3.0 - 5.0 %
- Other Element Content: traces
$ 1681/MT
- Specific Gravity: 2.65 g/cc
- Specific Heat Capacity: 1.089 J/g-°C @Temperature 982 °C
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1180 °C
- Maximum Service Temperature, Air: 1320 °C
$ 1735/MT
- Density: 2.44 - 2.56 g/cc
- Porosity: 20 %
- Deformation: 0.50 %
- Modulus of Rupture: 0.0110 - 0.0179 GPa
- Modulus of Rupture: 0.00345 - 0.00621 GPa @Temperature 1370 °C
$ 2091/MT
- Specific Gravity: 0.385 g/cc
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Density: 0.288 g/cc
$ 2545/MT
- Specific Gravity: 0.385 g/cc
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.960 g/cc
- Loss On Ignition: 3.0 - 9.0 %
$ 2333/MT
- Density: 0.0640 g/cc
- Density: 0.0960 g/cc
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Thermal Conductivity: 0.0605 W/m-K @Temperature 260 °C
$ 1655/MT
- Density: 1.667 - 1.827 g/cc
- Density: 1.683 - 1.811 g/cc
- Modulus of Rupture: 0.00827 - 0.0124 GPa
- Modulus of Rupture: 0.00552 - 0.00724 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00552 - 0.00827 GPa @Treatment Temp. 1260 °C, Time 18000 sec
$ 2099/MT
- Density: 3.30 - 3.50 g/cc
- Solubility in Water: 0.00 %
- Loss On Ignition: 0.000 % @Temperature 799 °C, Time 7200 sec
- Melting Point: >= 2000 °C
- Maximum Service Temperature, Air: 1600 °C
$ 1535/MT
- Density: 0.0480 - 0.128 g/cc
- Thickness: 6250 - 50000 microns
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1180 °C
- Maximum Service Temperature, Air: 1320 °C
$ 1582/MT
- Density: 0.192 g/cc
- Loss On Ignition: 7.0 - 9.0 %
- Modulus of Rupture: 0.000793 GPa
- Compressive Yield Strength: 0.170 MPa
- Compressive Yield Strength: 0.210 MPa
$ 1538/MT
- Density: 2.564 - 2.724 g/cc
- Modulus of Rupture: 0.00689 - 0.00965 GPa
- Modulus of Rupture: 0.00621 - 0.00896 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.0103 - 0.0152 GPa @Treatment Temp. 1650 °C, Time 18000 sec
- Compressive Strength: 34.0 - 59.0 MPa
$ 1614/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Thermal Conductivity: 0.0793 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0821 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.143 W/m-K @Temperature 538 °C
$ 1632/MT
- Density: 0.288 - 0.320 g/cc
- Loss On Ignition: 4.00 - 6.00 % @Temperature 427 °C, Time 7200 sec
- Modulus of Rupture: 0.00101 GPa
- Compressive Yield Strength: 0.280 - 0.350 MPa
- Thermal Conductivity: 0.0692 W/m-K @Temperature 316 °C
$ 1466/MT
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 982 °C
- Shrinkage: 10 %
- Al2O3: 0.071 %
- B2O3: >= 0.016 %
$ 1665/MT
- Density: 2.276 - 2.452 g/cc
- Modulus of Rupture: 0.00345 - 0.00689 GPa
- Modulus of Rupture: 0.00207 - 0.00414 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.0103 - 0.0138 GPa @Treatment Temp. 1760 °C, Time 18000 sec
- Compressive Strength: 20.1 - 27.6 MPa
$ 2076/MT
- Density: 0.487 g/cc
- Density: 0.961 g/cc
- Density: 0.463 g/cc @Temperature 816 °C
- Compressive Strength: 0.451 MPa @Temperature 104 °C
- Compressive Strength: 1.35 MPa @Temperature 816 °C
$ 1765/MT
- Density: 1.939 - 2.131 g/cc
- Modulus of Rupture: 0.00414 - 0.00689 GPa
- Modulus of Rupture: 0.00138 - 0.00345 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00689 - 0.0103 GPa @Treatment Temp. 1540 °C, Time 18000 sec
- Compressive Strength: 11.8 - 20.1 MPa
$ 1522/MT
- Bulk Density: 2.468 g/cc
- Porosity: 20 %
- Permeability: 4.0
- Modulus of Rupture: 0.00896 GPa @Temperature 23.9 °C
- CTE, linear: 5.76 µm/m-°C @Temperature 20.0 °C
$ 1620/MT
- Density: 2.16 - 2.29 g/cc
- Porosity: 16 %
- Deformation: 1.9 %
- Modulus of Rupture: 0.00552 - 0.00827 GPa
- Modulus of Rupture: 0.00207 - 0.00345 GPa @Temperature 1370 °C
$ 2044/MT
- Density: 2.436 - 2.58 g/cc
- Deformation: -1.10 %
- Modulus of Rupture: 0.0117 - 0.0179 GPa
- Modulus of Rupture: 0.00414 - 0.00655 GPa @Temperature 1370 °C
- Modulus of Rupture: 0.00621 - 0.00896 GPa @Temperature 1230 °C
$ 1874/MT
- Density: 0.112 g/cc
- Thermal Conductivity: 0.124 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.153 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.209 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.303 W/m-K @Temperature 1090 °C
$ 1849/MT
- Density: 0.112 g/cc
- Thermal Conductivity: 0.124 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.153 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.209 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.303 W/m-K @Temperature 1090 °C
$ 1801/MT
- Density: 0.112 g/cc
- Thermal Conductivity: 0.124 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.153 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.209 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.303 W/m-K @Temperature 1090 °C
$ 1669/MT
- Density: 0.112 g/cc
- Thermal Conductivity: 0.124 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.153 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.209 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.303 W/m-K @Temperature 1090 °C
$ 1456/MT
- Maximum Service Temperature, Air: 1570 °C
- Al2O3: 36 %
- Alkalis: 4.0 %
- CaO: 0.20 %
- Fe2O3: 0.90 %
$ 2486/MT
- Density: 3.093 g/cc
- Modulus of Rupture: 0.00448 GPa @Temperature 1540 °C
- Modulus of Rupture: 0.00552 GPa @Temperature 1430 °C
- Modulus of Rupture: 0.0110 GPa @Temperature 1260 °C
- Modulus of Rupture: 0.0200 GPa @Temperature 1090 °C
$ 1448/MT
- Bulk Density: 0.128 - 0.192 g/cc
- Melting Point: 1470 °C
- Maximum Service Temperature, Air: 1000 °C
- CaO: 25 - 35 %
- MgO: 4.0 - 7.0 %
$ 1883/MT
- Specific Heat Capacity: 0.220 J/g-°C
- Thermal Conductivity: 0.127 W/m-K @Temperature 204 °C
- Thermal Conductivity: 0.157 W/m-K @Temperature 427 °C
- Thermal Conductivity: 0.189 W/m-K @Temperature 649 °C
- Thermal Conductivity: 0.225 W/m-K @Temperature 871 °C
$ 1571/MT
- Density: 2.933 g/cc
- Deformation: <= -0.500 %
- Deformation: -0.220 %
- Deformation: 0.10 %
- Deformation: <= 0.25 %
$ 1487/MT
- Bulk Density: 2.756 g/cc
- Porosity: 19 %
- Permeability: 4.0
- Modulus of Rupture: 0.00896 GPa @Temperature 23.9 °C
- CTE, linear: 6.66 µm/m-°C @Temperature 20.0 °C
$ 1693/MT
- Density: 2.901 - 3.061 g/cc
- Deformation: 0.60 %
- Modulus of Rupture: 0.0110 - 0.0165 GPa
- Modulus of Rupture: 0.0110 - 0.0165 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Compressive Strength: 69.0 - 90.0 MPa
$ 1576/MT
- Density: 0.160 - 0.208 g/cc
- Loss On Ignition: 2.0 - 5.0 %
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.207 - 0.345 MPa
- Thermal Conductivity: 0.0562 W/m-K @Temperature 260 °C
$ 1533/MT
- Density: 0.272 g/cc
- Loss On Ignition: 1.3 %
- Hardness, Shore A: 71 - 82
- Modulus of Rupture: 0.000386 GPa
- Compressive Yield Strength: 0.0500 MPa
$ 1572/MT
- Bulk Density: 2.868 g/cc
- Porosity: 17 %
- Permeability: 4.0
- Deformation: 3.6 %
- Modulus of Rupture: 0.00483 GPa @Temperature 1540 °C
$ 1498/MT
- Density: 0.272 g/cc
- Loss On Ignition: 1.3 %
- Modulus of Rupture: 0.000414 GPa
- Compressive Yield Strength: 0.0800 MPa
- Compressive Yield Strength: 0.100 MPa
$ 1583/MT
- Al2O3: 45 %
- Alkalis: 0.20 %
- B2O3: 0.080 %
- CaO: 0.10 %
- Fe2O3: 1.0 %
$ 1585/MT
- Bulk Density: 1.747 g/cc
- Porosity: 22 %
- Modulus of Rupture: 0.00352 GPa
- CTE, linear: 5.76 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 1.53 W/m-K @Temperature 1090 °C
$ 1935/MT
- Density: 0.144 - 0.160 g/cc
- Thickness: 6300 microns
- Thickness: 13000 microns
- Tensile Strength, Ultimate: 0.0552 - 0.0827 MPa
- Thermal Conductivity: 0.0600 W/m-K @Temperature 260 °C
$ 1619/MT
- Density: 0.288 - 0.321 g/cc
- Loss On Ignition: 4.0 - 7.0 %
- Modulus of Rupture: 0.000517 - 0.000689 GPa
- Compressive Yield Strength: 0.170 - 0.280 MPa
- Thermal Conductivity: 0.0677 W/m-K @Temperature 260 °C
$ 1769/MT
- Density: 0.464 g/cc
- Loss On Ignition: 6.0 - 9.0 %
- Modulus of Rupture: 0.00172 - 0.00207 GPa
- Compressive Yield Strength: 0.160 MPa
- Compressive Yield Strength: 0.220 MPa
$ 2370/MT
- Density: 3.50 g/cc
- Solubility in Water: 0.00 %
- Loss On Ignition: 0.000 % @Temperature 799 °C, Time 7200 sec
- Melting Point: >= 2000 °C
- Maximum Service Temperature, Air: 1600 °C
$ 1912/MT
- Density: 0.128 g/cc
- Density: 0.149 g/cc
- Density: 0.171 g/cc
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0728 W/m-K @Temperature 260 °C
$ 1842/MT
- Density: >= 0.625 g/cc
- Solids Content: 46 %
- Modulus of Rupture: 0.00138 GPa
- Thermal Conductivity: 0.0865 W/m-K @Temperature 149 °C
- Thermal Conductivity: 0.115 W/m-K @Temperature 371 °C
$ 2539/MT
- Density: 0.192 g/cc
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.138 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.239 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.353 W/m-K @Temperature 1090 °C
$ 1762/MT
- Bulk Density: 3.221 g/cc
- Porosity: 16 %
- Modulus of Rupture: 0.0253 GPa
- CTE, linear: 8.10 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 3.49 W/m-K @Temperature 1090 °C
$ 1758/MT
- Density: 0.0480 g/cc
- Density: 0.0640 g/cc
- Density: 0.0960 g/cc
- Density: 0.128 g/cc
- Thickness: 6250 - 50000 microns
$ 1501/MT
- Density: 0.0480 g/cc
- Density: 0.0640 g/cc
- Density: 0.0960 g/cc
- Density: 0.128 g/cc
- Density: 0.192 g/cc
$ 1496/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Density: 0.240 g/cc
- Thermal Conductivity: 0.0706 W/m-K @Temperature 260 °C
$ 1448/MT
- Density: 0.112 - 0.160 g/cc
- Loss On Ignition: 6.0 - 10 %
- Tensile Strength, Ultimate: 0.0345 MPa
- Tensile Strength, Ultimate: 0.172 - 0.276 MPa
- Thermal Conductivity: 0.0519 W/m-K @Temperature 260 °C
$ 1476/MT
- Density: 3.50 g/cc
- Solubility in Water: 0.00 %
- Loss On Ignition: 0.000 % @Temperature 799 °C, Time 7200 sec
- Melting Point: >= 2000 °C
- Maximum Service Temperature, Air: 1600 °C
$ 1841/MT
- Loss On Ignition: 20 %
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1090 °C
- Al2O3: 47 %
- SiO2: 53 %
$ 2014/MT
- Density: 0.272 g/cc
- Loss On Ignition: 4.0 - 7.0 %
- Modulus of Rupture: 0.000689 - 0.000896 GPa
- Compressive Yield Strength: 0.130 - 0.200 MPa
- Compressive Yield Strength: 0.200 - 0.270 MPa
$ 1487/MT
- Density: 0.256 g/cc
- Loss On Ignition: 1.3 %
- Hardness, Shore A: 51 - 62
- Modulus of Rupture: 0.000496 GPa
- Compressive Yield Strength: 0.130 MPa
$ 2105/MT
- Density: 0.320 g/cc
- Loss On Ignition: 5.0 - 8.0 %
- Modulus of Rupture: 0.00103 - 0.0124 GPa
- Compressive Yield Strength: 0.200 - 0.340 MPa
- Compressive Yield Strength: 0.340 - 0.410 MPa
$ 1924/MT
- Density: 0.336 g/cc
- Loss On Ignition: 7.0 - 9.0 %
- Modulus of Rupture: 0.00110 GPa
- Compressive Yield Strength: 0.430 MPa
- Compressive Yield Strength: 0.620 MPa
$ 1570/MT
- Bulk Density: 0.240 - 0.304 g/cc
- Melting Point: 1470 °C
- Maximum Service Temperature, Air: 1000 °C
- CaO: 25 - 35 %
- MgO: 4.0 - 7.0 %
$ 1987/MT
- Density: 0.288 - 0.320 g/cc
- Loss On Ignition: 4.00 - 6.00 % @Temperature 427 °C, Time 7200 sec
- Modulus of Rupture: 0.00101 GPa
- Compressive Yield Strength: 0.280 - 0.350 MPa
- Thermal Conductivity: 0.0692 W/m-K @Temperature 316 °C
$ 1469/MT
- Density: 1.25 - 1.41 g/cc
- Density: 1.282 - 1.41 g/cc
- Modulus of Rupture: 0.00207 - 0.00345 GPa
- Modulus of Rupture: 0.00121 - 0.00224 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00345 - 0.00621 GPa @Treatment Temp. 1370 °C, Time 18000 sec
$ 1688/MT
- Specific Gravity: 2.65 g/cc
- Specific Heat Capacity: 1.089 J/g-°C @Temperature 982 °C
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1370 °C
- Maximum Service Temperature, Air: 1430 °C
$ 2541/MT
- Bulk Density: 0.144 - 0.208 g/cc
- Melting Point: 1470 °C
- Maximum Service Temperature, Air: 1000 °C
- CaO: 25 - 35 %
- MgO: 4.0 - 7.0 %
$ 1614/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Density: 0.240 g/cc
- Thickness: 3000 - 12000 microns
$ 2085/MT
- Density: 2.147 - 2.308 g/cc
- Modulus of Rupture: 0.00621 - 0.00965 GPa
- Modulus of Rupture: 0.00689 - 0.0124 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00896 - 0.0131 GPa @Treatment Temp. 1540 °C, Time 18000 sec
- Compressive Strength: 34.5 - 55.2 MPa
$ 1620/MT
- Thermal Conductivity: 0.0303 W/m-K @Temperature 37.8 °C
- Thermal Conductivity: 0.0634 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.125 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.209 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.301 W/m-K @Temperature 1090 °C
$ 1551/MT
- Density: 0.176 - 0.224 g/cc
- Loss On Ignition: <= 0.50 %
- Tensile Strength, Ultimate: 0.207 - 0.310 MPa
- Thermal Conductivity: 0.0504 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0764 W/m-K @Temperature 538 °C
$ 2150/MT
- Density: 0.641 g/cc
- Loss On Ignition: 12.0 - 15.0 % @Temperature 538 °C
- Modulus of Rupture: 0.00276 - 0.00345 GPa
- Thermal Conductivity: 0.0764 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.102 W/m-K @Temperature 538 °C
$ 2187/MT
- Density: 0.256 g/cc
- Loss On Ignition: 1.3 %
- Hardness, Shore A: 36 - 47
- Modulus of Rupture: 0.000414 GPa
- Compressive Yield Strength: 0.0700 MPa
$ 1592/MT
- Maximum Service Temperature, Air: 1590 °C
- Al2O3: 38 %
- Alkalis: 2.8 %
- CaO: 0.20 %
- Fe2O3: 1.0 %
$ 2446/MT
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 982 °C
- Shrinkage: 10 %
- Al2O3: 0.071 %
- B2O3: >= 0.016 %
$ 1705/MT
- Bulk Density: 2.516 g/cc
- Porosity: 19 %
- Modulus of Rupture: 0.00862 GPa
- CTE, linear: 5.94 µm/m-°C @Temperature 20.0 °C
- Maximum Service Temperature, Air: 1600 °C
$ 1594/MT
- Hardness, Shore A: 71 - 82
- Modulus of Rupture: 0.000386 GPa
- Compressive Yield Strength: 0.0500 MPa
- Compressive Yield Strength: 0.0600 MPa
- Specific Heat Capacity: 1.13 J/g-°C
$ 1538/MT
- Specific Gravity: 2.60 g/cc
- Tensile Strength, Ultimate: 1030 - 1380 MPa
- Modulus of Elasticity: 82.7 - 117 GPa
- Al2O3: 45 - 49 %
- SiO2: 51 - 55 %
$ 1808/MT
- Bulk Density: 0.128 - 0.192 g/cc
- Melting Point: 1500 °C
- Maximum Service Temperature, Air: 1200 °C
- CaO: 16 - 22 %
- MgO: 12 - 19 %
$ 1944/MT
- Density: 0.673 g/cc
- Loss On Ignition: 5.0 - 8.0 %
- Modulus of Rupture: 0.00310 - 0.00379 GPa
- Compressive Yield Strength: 1.37 - 1.72 MPa
- Compressive Yield Strength: 1.72 - 2.06 MPa
$ 2387/MT
- Density: 2.612 - 2.804 g/cc
- Modulus of Rupture: 0.00896 - 0.00965 GPa
- Modulus of Rupture: 0.00689 - 0.0110 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00965 - 0.0131 GPa @Treatment Temp. 1820 °C, Time 18000 sec
- Compressive Strength: 41.0 - 62.0 MPa
$ 1470/MT
- Density: 2.612 - 2.804 g/cc
- Modulus of Rupture: 0.00896 - 0.00965 GPa
- Modulus of Rupture: 0.00689 - 0.0110 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00965 - 0.0131 GPa @Treatment Temp. 1820 °C, Time 18000 sec
- Compressive Strength: 41.0 - 62.0 MPa
$ 1551/MT
- Density: 1.041 g/cc
- Deformation: -0.300 %
- Modulus of Rupture: 0.00172 GPa
- Compressive Strength: 3.03 MPa
- Thermal Conductivity: 0.403 W/m-K @Temperature 260 °C
$ 2579/MT
- Density: 2.612 - 2.804 g/cc
- Modulus of Rupture: 0.00896 - 0.00965 GPa
- Modulus of Rupture: 0.00689 - 0.0110 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00965 - 0.0131 GPa @Treatment Temp. 1820 °C, Time 18000 sec
- Compressive Strength: 41.0 - 62.0 MPa
$ 1703/MT
- Density: 0.160 - 0.208 g/cc
- Loss On Ignition: 6.0 - 10 %
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.689 - 0.793 MPa
- Thermal Conductivity: 0.0533 W/m-K @Temperature 260 °C
$ 1961/MT
- Maximum Service Temperature, Air: 1650 °C
- Al2O3: 45 %
- Alkalis: 0.60 %
- B2O3: 0.70 %
- CaO: 0.20 %
$ 1925/MT
- Bulk Density: 2.933 g/cc
- Porosity: 21 %
- Permeability: 6.0
- Deformation: 0.50 %
- Modulus of Rupture: 0.00483 GPa @Temperature 1540 °C
$ 1492/MT
- Loss On Ignition: 8.0 %
- Thermal Conductivity: 0.03234 W/m-K @Temperature 23.9 °C
- Thermal Conductivity: 0.03437 W/m-K @Temperature 93.3 °C
- Thermal Conductivity: 0.04699 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0715 W/m-K @Temperature 538 °C
$ 1759/MT
- Density: 0.240 - 0.288 g/cc
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.517 - 0.689 MPa
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1150 °C
$ 1512/MT
- Density: 0.0480 - 0.128 g/cc
- Thickness: 12500 - 50000 microns
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1090 °C
- Maximum Service Temperature, Air: 1090 °C
$ 1814/MT
- Density: 0.256 g/cc
- Modulus of Rupture: 0.000621 - 0.000758 GPa
- Compressive Yield Strength: 0.138 - 0.207 MPa @Strain 5 %
- Compressive Yield Strength: 0.207 - 0.241 MPa @Strain 10 %
- Thermal Conductivity: 0.0432 W/m-K @Temperature 37.8 °C
$ 1663/MT
- Density: 0.112 g/cc
- Loss On Ignition: 6.0 %
- Thermal Conductivity: 0.0879 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.166 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.303 W/m-K @Temperature 816 °C
$ 1782/MT
- Density: 0.128 g/cc
- Density: 0.149 g/cc
- Density: 0.171 g/cc
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0728 W/m-K @Temperature 260 °C
$ 1596/MT
- Density: 1.875 - 2.019 g/cc
- Modulus of Rupture: 0.00276 - 0.00552 GPa
- Modulus of Rupture: 0.00138 - 0.00276 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00552 - 0.00965 GPa @Treatment Temp. 1430 °C, Time 18000 sec
- Compressive Strength: 9.60 - 14.5 MPa
$ 2392/MT
- Density: 1.699 - 1.811 g/cc
- Density: 1.667 - 1.859 g/cc
- Modulus of Rupture: 0.0103 - 0.0138 GPa
- Modulus of Rupture: 0.00552 - 0.00827 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00621 - 0.00896 GPa @Treatment Temp. 1320 °C, Time 18000 sec
$ 1956/MT
- Density: 0.448 g/cc
- Loss On Ignition: 6.0 - 9.0 %
- Modulus of Rupture: 0.00190 - 0.00224 GPa
- Compressive Yield Strength: 0.120 MPa
- Compressive Yield Strength: 0.160 MPa
$ 1689/MT
- Modulus of Rupture: 0.00141 GPa
- Melting Point: 1790 °C
- Maximum Service Temperature, Air: 1200 °C
- Shrinkage: 2.50 % @Temperature 1260 °C, Time 86400 sec
- Al2O3: 44 %
$ 2210/MT
- Density: 0.0960 g/cc
- Loss On Ignition: 2.0 - 5.0 %
- Tensile Strength, Ultimate: 0.0345 MPa
- Tensile Strength, Ultimate: 0.0689 - 0.138 MPa
- Thermal Conductivity: 0.0591 W/m-K @Temperature 260 °C
$ 2201/MT
- Bulk Density: 2.965 g/cc
- Porosity: 17.5 %
- Modulus of Rupture: 0.03507 GPa
- CTE, linear: 8.82 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 3.49 W/m-K @Temperature 1090 °C
$ 1663/MT
- Density: 2.179 - 2.356 g/cc
- Modulus of Rupture: 0.00827 - 0.0138 GPa
- Modulus of Rupture: 0.00621 - 0.00965 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00827 - 0.0138 GPa @Treatment Temp. 1540 °C, Time 18000 sec
- Compressive Strength: 45.5 - 62.1 MPa
$ 1537/MT
- Density: 3.30 - 3.50 g/cc
- Solubility in Water: 0.00 %
- Loss On Ignition: 0.000 % @Temperature 799 °C, Time 7200 sec
- Melting Point: >= 2000 °C
- Maximum Service Temperature, Air: 1600 °C
$ 1773/MT
- Density: 0.192 - 0.224 g/cc
- Loss On Ignition: 7.0 - 10 %
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.517 - 0.689 MPa
- Thermal Conductivity: 0.0620 W/m-K @Temperature 260 °C
$ 1727/MT
- Density: 0.0640 - 0.128 g/cc
- Thickness: 12500 - 50000 microns
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1320 °C
- Maximum Service Temperature, Air: 1430 °C
$ 1783/MT
- Density: 1.987 - 2.131 g/cc
- Modulus of Rupture: 0.00414 - 0.00552 GPa
- Modulus of Rupture: 0.00207 - 0.00310 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00345 - 0.00621 GPa @Treatment Temp. 1650 °C, Time 18000 sec
- Compressive Strength: 11.7 - 15.9 MPa
$ 2174/MT
- Density: 0.192 g/cc
- Thickness: 3000 - 12000 microns
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.138 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.239 W/m-K @Temperature 816 °C
$ 1614/MT
- Density: 0.881 g/cc
- Deformation: -0.100 %
- Modulus of Rupture: 0.00152 GPa
- Compressive Strength: 2.35 MPa
- Thermal Conductivity: 0.331 W/m-K @Temperature 260 °C
$ 1526/MT
- Specific Gravity: 3.30 g/cc
- Tensile Strength, Ultimate: 2000 MPa
- Tensile Modulus: 296 GPa
- Specific Heat Capacity: 1.047 J/g-°C @Temperature 982 °C
- Melting Point: 1760 °C
$ 1932/MT
- Bulk Density: 0.144 - 0.208 g/cc
- Melting Point: 1500 °C
- Maximum Service Temperature, Air: 1200 °C
- CaO: 16 - 22 %
- MgO: 12 - 19 %
$ 1463/MT
- Density: 0.192 g/cc
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.138 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.239 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.353 W/m-K @Temperature 1090 °C
$ 1545/MT
- Density: 0.0640 g/cc
- Density: 0.0960 g/cc
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Thermal Conductivity: 0.0605 W/m-K @Temperature 260 °C
$ 1566/MT
- Density: 0.240 - 0.272 g/cc
- Loss On Ignition: 2.0 - 4.0 %
- Modulus of Rupture: 0.00138 - 0.00172 GPa
- Compressive Yield Strength: 0.103 - 0.172 MPa
- Compressive Yield Strength: 0.172 - 0.276 MPa
$ 1741/MT
- Density: 2.612 - 2.804 g/cc
- Modulus of Rupture: 0.00896 - 0.00965 GPa
- Modulus of Rupture: 0.00689 - 0.0110 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00965 - 0.0131 GPa @Treatment Temp. 1820 °C, Time 18000 sec
- Compressive Strength: 41.0 - 62.0 MPa
$ 1556/MT
- Density: 0.464 g/cc
- Loss On Ignition: 6.0 - 9.0 %
- Modulus of Rupture: 0.00190 - 0.00224 GPa
- Compressive Yield Strength: 0.160 MPa
- Compressive Yield Strength: 0.220 MPa
$ 1808/MT
- Density: 1.106 g/cc
- Melting Point: 1870 °C
- Maximum Service Temperature, Air: 1540 °C
- Shrinkage: 0.300 % @Temperature 1302 °C, Time 86400 sec
- Shrinkage: 0.500 % @Temperature 1450 °C, Time 86400 sec
$ 1453/MT
- Density: 0.0960 g/cc
- Thermal Conductivity: 0.0602 W/m-K @Temperature 204 °C
- Thermal Conductivity: 0.0839 W/m-K @Temperature 316 °C
- Thermal Conductivity: 0.115 W/m-K @Temperature 427 °C
- Al2O3: 10 - 12 %
$ 1751/MT
- Density: 2.276 - 2.372 g/cc
- Compressive Strength: 3.45 - 5.52 MPa
- Compressive Strength: 17.2 - 27.6 MPa
- Compressive Strength: 27.6 - 41.4 MPa
- Thermal Conductivity: 1.27 W/m-K @Temperature 1090 °C
$ 1784/MT
- Bulk Density: 0.0950 - 0.961 g/cc
- Melting Point: 1500 °C
- Maximum Service Temperature, Air: 1200 °C
- CaO: 16 - 22 %
- MgO: 12 - 19 %
$ 2266/MT
- Density: 0.160 - 0.176 g/cc
- Thickness: 6300 microns
- Thickness: 13000 microns
- Tensile Strength, Ultimate: 0.124 - 0.172 MPa
- Thermal Conductivity: 0.0900 W/m-K @Temperature 316 °C
$ 2389/MT
- Density: 0.256 g/cc
- Loss On Ignition: 1.3 %
- Hardness, Shore A: 47 - 58
- Modulus of Rupture: 0.000455 GPa
- Compressive Yield Strength: 0.0700 MPa
$ 1906/MT
- Density: 0.176 - 0.224 g/cc
- Loss On Ignition: 5.0 - 10 %
- Tensile Strength, Ultimate: 0.0345 - 0.0689 MPa
- Tensile Strength, Ultimate: 0.414 - 0.621 MPa
- Thermal Conductivity: 0.0562 W/m-K @Temperature 260 °C
$ 1557/MT
- Bulk Density: 3.013 g/cc
- Porosity: 20 %
- Modulus of Rupture: 0.0283 GPa
- CTE, linear: 8.10 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 1.53 W/m-K @Temperature 1090 °C
$ 2308/MT
- Density: 0.256 g/cc
- Loss On Ignition: 4.0 - 7.0 %
- Modulus of Rupture: 0.00138 - 0.00172 GPa
- Compressive Yield Strength: 0.130 - 0.200 MPa
- Compressive Yield Strength: 0.200 - 0.270 MPa
$ 1954/MT
- Density: 2.628 - 2.804 g/cc
- Modulus of Rupture: 0.00965 - 0.0131 GPa
- Modulus of Rupture: 0.00758 - 0.0124 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.00965 - 0.0138 GPa @Treatment Temp. 1870 °C, Time 18000 sec
- Compressive Strength: 34.0 - 52.0 MPa
$ 1554/MT
- Bulk Density: 2.58 g/cc
- Porosity: 20 %
- Permeability: 4.0
- Deformation: 6.0 %
- Modulus of Rupture: 0.00552 GPa @Temperature 1540 °C
$ 1454/MT
- Bulk Density: 1.747 g/cc
- Porosity: 22 %
- Modulus of Rupture: 0.00352 GPa
- CTE, linear: 5.76 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 1.37 W/m-K @Temperature 1090 °C
$ 1489/MT
- Bulk Density: 0.144 - 0.208 g/cc
- Melting Point: 1470 °C
- Maximum Service Temperature, Air: 1000 °C
- CaO: 25 - 35 %
- MgO: 4.0 - 7.0 %
$ 1462/MT
- Specific Gravity: 2.54 g/cc
- Melting Point: 1650 °C
- Maximum Service Temperature, Air: 538 °C
- Al2O3: 10 - 12 %
- Alkalis: 0.00 - 1.0 %
$ 2177/MT
- Modulus of Rupture: 0.00124 GPa
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1180 °C
- Shrinkage: 3.20 % @Temperature 1260 °C, Time 86400 sec
- Al2O3: 39 %
$ 1733/MT
- Maximum Service Temperature, Air: 1790 °C
- Al2O3: 86.89 %
- Alkalis: 0.48 %
- CaO: 0.020 %
- Fe2O3: 0.32 %
$ 1926/MT
- Loss On Ignition: 20 %
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1090 °C
- Shrinkage: 0.321 %
- Al2O3: 47 %
$ 1825/MT
- Density: 0.448 g/cc
- Loss On Ignition: 5.0 - 8.0 %
- Modulus of Rupture: 0.00159 - 0.00179 GPa
- Compressive Yield Strength: 0.410 - 0.550 MPa
- Compressive Yield Strength: 0.550 - 0.680 MPa
$ 1951/MT
- Bulk Density: 0.128 - 0.192 g/cc
- Melting Point: 1470 °C
- Maximum Service Temperature, Air: 1000 °C
- CaO: 25 - 35 %
- MgO: 4.0 - 7.0 %
$ 2033/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Thermal Conductivity: 0.0720 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.0749 W/m-K @Temperature 260 °C
$ 1576/MT
- Density: 0.128 g/cc
- Density: 0.160 g/cc
- Density: 0.192 g/cc
- Density: 0.240 g/cc
- Thickness: 3000 - 12000 microns
$ 1680/MT
- Maximum Service Temperature, Air: 1760 °C
- Al2O3: 66 %
- Alkalis: 2.2 %
- CaO: 0.10 %
- Fe2O3: 1.2 %
$ 1484/MT
- Density: 0.416 g/cc
- Loss On Ignition: 6.0 - 9.0 %
- Modulus of Rupture: 0.00172 - 0.00193 GPa
- Compressive Yield Strength: 0.120 MPa
- Compressive Yield Strength: 0.160 MPa
$ 2332/MT
- Density: 0.240 g/cc
- Loss On Ignition: 7.0 - 9.0 %
- Modulus of Rupture: 0.000758 GPa
- Compressive Yield Strength: 0.210 MPa
- Compressive Yield Strength: 0.280 MPa
$ 1685/MT
- Density: 3.50 g/cc
- Solubility in Water: 0.00 %
- Loss On Ignition: 0.000 % @Temperature 799 °C, Time 7200 sec
- Melting Point: >= 2000 °C
- Maximum Service Temperature, Air: 1600 °C
$ 2391/MT
- Thermal Conductivity: 0.0663 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.140 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.238 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.301 W/m-K @Temperature 982 °C
- Flammability Test: 0.00
$ 1454/MT
- Thermal Conductivity: 0.0303 W/m-K @Temperature 37.8 °C
- Thermal Conductivity: 0.0634 W/m-K @Temperature 260 °C
- Thermal Conductivity: 0.125 W/m-K @Temperature 538 °C
- Thermal Conductivity: 0.209 W/m-K @Temperature 816 °C
- Thermal Conductivity: 0.301 W/m-K @Temperature 1090 °C
$ 1914/MT
- Bulk Density: 0.128 - 0.192 g/cc
- Melting Point: 1500 °C
- Maximum Service Temperature, Air: 1200 °C
- CaO: 16 - 22 %
- MgO: 12 - 19 %
$ 1791/MT
- Specific Gravity: 2.65 g/cc
- Specific Heat Capacity: 1.089 J/g-°C @Temperature 982 °C
- Melting Point: 1760 °C
- Maximum Service Temperature, Air: 1180 °C
- Maximum Service Temperature, Air: 1320 °C
$ 1786/MT
- Bulk Density: 2.179 g/cc
- Porosity: 20 %
- Permeability: 3.0
- Deformation: 0.40 %
- Modulus of Rupture: 0.00414 GPa @Temperature 1540 °C
$ 2198/MT
- Density: 2.196 - 2.372 g/cc
- Modulus of Rupture: 0.00483 - 0.00896 GPa
- Modulus of Rupture: 0.00276 - 0.00552 GPa @Treatment Temp. 816 °C, Time 18000 sec
- Modulus of Rupture: 0.0103 - 0.0138 GPa @Treatment Temp. 1650 °C, Time 18000 sec
- Compressive Strength: 27.6 - 38.0 MPa
$ 1757/MT
- Density: 0.128 g/cc
- Density: 0.149 g/cc
- Density: 0.171 g/cc
- Thickness: 4000 - 12000 microns
- Thermal Conductivity: 0.0793 W/m-K @Temperature 260 °C
$ 2332/MT
- Maximum Service Temperature, Air: 1760 °C
- Al2O3: 66 %
- Alkalis: 3.2 %
- CaO: 0.10 %
- Fe2O3: 1.2 %
Delivery Oxide Thermal Ceramics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
passenger boat for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.