$ 2400/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 2155/MT
- Density: 0.923 g/cc
- Thickness: 76.0 microns
- Melt Flow: 0.22 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1520/MT
- Density: 0.924 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 7.58 MPa
$ 2351/MT
- Density: 0.926 g/cc
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 14.0 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
- Film Elongation at Break, MD: 615 %
$ 1665/MT
- Density: 0.922 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 3000 ppm
- Slip Level: 1200 ppm
$ 2081/MT
- Density: 0.952 g/cc
- Melt Index of Compound: 66 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 59
- Tensile Strength at Break: 28.3 MPa
- Tensile Strength, Yield: 17.2 MPa
$ 1820/MT
- Density: 0.935 g/cc
- Viscosity: 37000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 64000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 79000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 40 g/10 min @Load 2.16 kg
$ 2245/MT
- Density: 0.923 g/cc
- Viscosity: 40000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 93000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 161000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 7.0 g/10 min @Load 2.16 kg
$ 2296/MT
- Density: 0.9534 g/cc
- ESCR 100% Igepal®: 50 hour @Temperature 50.0 °C
- High Load Melt Index: 23 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 59
$ 2367/MT
- Density: 0.915 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.96 MPa
- Film Tensile Strength at Yield, TD: 8.41 MPa
$ 1763/MT
- Density: 0.919 g/cc
- Viscosity: 82000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 300000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 6.0 g/10 min @Load 2.16 kg
$ 1840/MT
- Density: 0.918 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.98 MPa
- Film Tensile Strength at Yield, TD: 15.42 MPa
$ 1682/MT
- Density: 0.917 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 8.80 MPa
- Film Elongation at Break, MD: 460 %
$ 1451/MT
- Density: 0.916 g/cc
- Viscosity: 34000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 76000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 130000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 8.0 g/10 min @Load 2.16 kg
$ 2248/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.47 g/10 min
- Film Tensile Strength at Yield, MD: 13.30 MPa
- Film Tensile Strength at Yield, TD: 10.73 MPa
$ 1505/MT
- Density: 0.926 g/cc
- ESCR 100% Igepal®: 10 hour @Temperature 50.0 °C
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51
- Tensile Strength at Break: 7.58 MPa
$ 1473/MT
- Density: 0.963 g/cc
- Thickness: 25.0 microns
- Melt Flow: 5.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 27.5 MPa
- Film Tensile Strength at Yield, TD: 28.3 MPa
$ 1668/MT
- Density: 0.917 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 9.218 MPa
- Film Tensile Strength at Yield, TD: 9.501 MPa
$ 1738/MT
- Density: 0.913 g/cc
- Moisture Vapor Transmission: 0.0300 cc-mm/m²-24hr-atm
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Coefficient of Friction: 0.14
$ 1686/MT
- Density: 0.884 g/cc
- High Load Melt Index: 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 83
- Hardness, Shore A: 83
$ 2248/MT
- Density: 0.948 g/cc
- Viscosity: 47000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 87000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 132000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 42 g/10 min @Load 2.16 kg
$ 2462/MT
- Density: 0.947 g/cc
- Melt Flow: 42 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.3 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 300 %
$ 1453/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1605/MT
- Density: 0.916 g/cc
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 20.0 MPa
- Film Tensile Strength at Yield, MD: 7.60 MPa
- Film Tensile Strength at Yield, TD: 6.90 MPa
$ 1733/MT
- Density: 0.924 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 7.58 MPa
$ 1816/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1907/MT
- Density: 0.923 g/cc
- Viscosity: 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 32000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 40000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 55 g/10 min @Load 2.16 kg
$ 1560/MT
- Density: 0.930 g/cc
- Viscosity: 23000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 50000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 77000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 150 g/10 min @Load 2.16 kg
$ 2085/MT
- Density: 0.920 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 10.31 MPa
- Film Tensile Strength at Yield, TD: 11.16 MPa
$ 2469/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.8 MPa
- Film Tensile Strength at Yield, TD: 11.6 MPa
$ 1623/MT
- Density: 0.916 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.3 MPa
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: 600 %
$ 1517/MT
- Density: 0.886 g/cc
- High Load Melt Index: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 82
- Hardness, Shore A: 85
$ 1722/MT
- Density: 0.932 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1200 ppm
$ 1528/MT
- Density: 0.917 g/cc
- Thickness: 20.3 microns
- Melt Flow: 2.3 g/10 min
- Film Tensile Strength at Yield, MD: 8.791 MPa
- Film Tensile Strength at Yield, TD: 8.163 MPa
$ 2342/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Elmendorf Tear Strength MD: 385 g
- Elmendorf Tear Strength TD: 499 g
$ 1958/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 1515/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 13.1 MPa
- Film Tensile Strength at Yield, MD: 7.60 MPa
$ 1653/MT
- Density: 0.935 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 15.23 MPa
- Film Tensile Strength at Yield, TD: 16.72 MPa
$ 1583/MT
- Density: 0.920 g/cc
- High Load Melt Index: 52 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 121 °C
$ 1450/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 2006/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 1511/MT
- Density: 0.926 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.9 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.0 MPa
- Film Tensile Strength at Yield, MD: 12.4 MPa
$ 1467/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1617/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1676/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1547/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1661/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 2105/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1456/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1792/MT
- Density: 0.922 g/cc
- Thickness: 30.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1637/MT
- Density: 0.911 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1452/MT
- Density: 0.954 g/cc
- Viscosity: 90000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 220000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 360000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 7.0 g/10 min @Load 2.16 kg
$ 1474/MT
- Density: 0.912 g/cc
- Thickness: 38.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Elmendorf Tear Strength MD: 650 g
- Elmendorf Tear Strength TD: 826 g
$ 1880/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 2012/MT
- Density: 0.956 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 11.0 MPa
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Break: 440 %
$ 1676/MT
- Density: 0.928 g/cc
- Thickness: 38.0 microns
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 13.0 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
$ 1526/MT
- Density: 0.9525 g/cc
- Environmental Stress Crack Resistance: 48 hour
- High Load Melt Index: 21 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1870/MT
- Density: 0.905 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.50 g/10 min
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1726/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 13.1 MPa
- Film Tensile Strength at Yield, MD: 7.60 MPa
$ 1813/MT
- Density: 0.955 g/cc
- ESCR 100% Igepal®: 40 hour @Temperature 50.0 °C
- High Load Melt Index: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 63
$ 2295/MT
- Density: 0.920 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- High Load Melt Index: 44 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
$ 1880/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1744/MT
- Density: 0.916 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg
- Vicat Softening Point: 88.0 °C
$ 1751/MT
- Density: 0.904 g/cc
- Thickness: 20.3 microns
- Melt Flow: 4.0 g/10 min
- Film Tensile Strength at Yield, MD: 6.998 MPa
- Film Tensile Strength at Yield, TD: 4.92 MPa
$ 1903/MT
- Density: 0.952 g/cc
- Melt Flow: 60 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 225 %
$ 1766/MT
- Density: 0.929 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 100 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
$ 1705/MT
- Density: 0.923 g/cc
- Viscosity: 27000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 44000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 60000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 35 g/10 min @Load 2.16 kg
$ 2033/MT
- Density: 0.921 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 14.5 MPa
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 720 %
$ 2198/MT
- Density: 0.961 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- High Load Melt Index: 47 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 58
$ 1486/MT
- Density: 0.922 g/cc
- Thickness: 38.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1477/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 11.4 MPa
$ 1930/MT
- Density: 0.929 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 100 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
$ 1603/MT
- Density: 0.913 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Coefficient of Friction: 0.14
- Elmendorf Tear Strength MD: 363 g
$ 1563/MT
- Density: 0.950 g/cc
- Viscosity: 33000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 40000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 95000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 50 g/10 min @Load 2.16 kg
$ 1605/MT
- Density: 0.920 g/cc
- ESCR 100% Igepal®: >= 1500 hour @Temperature 50.0 °C
- High Load Melt Index: 48 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 49
$ 2317/MT
- Density: 0.923 g/cc
- Thickness: 76.0 microns
- Melt Flow: 0.22 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 2395/MT
- Density: 0.933 g/cc
- Viscosity: 34000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 54000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 77000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 80 g/10 min @Load 2.16 kg
$ 1785/MT
- Density: 0.923 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg
- Vicat Softening Point: 95.0 °C
$ 1533/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 11.4 MPa
$ 2061/MT
- Density: 0.905 g/cc
- Thickness: 38.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Elmendorf Tear Strength MD: 502 g
- Elmendorf Tear Strength TD: 925 g
$ 1470/MT
- Density: 0.918 g/cc
- Thickness: 50.8 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.64 MPa
- Film Tensile Strength at Yield, TD: 11.02 MPa
$ 1464/MT
- Density: 0.926 g/cc
- Thickness: 30.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 24.1 MPa
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 1902/MT
- Density: 0.912 g/cc
- Water Vapor Transmission: 10.5 g/m²/day
- Oxygen Transmission: 280 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 1235 cc-mm/m²-24hr-atm
- Thickness: 50.8 microns
$ 1959/MT
- Density: 0.917 g/cc
- Thickness: 58.4 microns
- Melt Flow: 2.3 g/10 min
- Film Tensile Strength at Yield, MD: 9.080 MPa
- Film Tensile Strength at Yield, TD: 8.846 MPa
$ 1894/MT
- Density: 0.916 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg
- Vicat Softening Point: 84.0 °C
$ 1711/MT
- Density: 0.904 g/cc
- Water Vapor Transmission: 16.7 g/m²/day
- Oxygen Transmission: 445.7 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 2022 cc-mm/m²-24hr-atm
- Thickness: 50.8 microns
$ 1649/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 80 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
$ 1619/MT
- Density: 0.952 g/cc
- ESCR 100% Igepal®: >= 1500 hour @Temperature 50.0 °C
- High Load Melt Index: 14 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength at Break: 34.5 MPa
$ 1455/MT
- Density: 0.922 g/cc
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Coefficient of Friction: 0.17
$ 1624/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.2 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 12.4 MPa
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 1476/MT
- Density: 0.9055 g/cc
- High Load Melt Index: 20 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 91
- Hardness, Shore A: 95
$ 1608/MT
- Density: 0.920 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.50 g/10 min
- Antiblock Level: 5100 ppm
- Slip Level: 900 ppm
$ 2206/MT
- Density: 0.931 g/cc
- Melt Index of Compound: 127.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 2301/MT
- Density: 0.8985 g/cc
- Melt Index of Compound: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 91
- Hardness, Shore A: 93
- Tensile Strength at Break: 11.4 MPa
$ 2247/MT
- Density: 0.921 g/cc
- Thickness: 76.0 microns
- Melt Flow: 0.22 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1965/MT
- Density: 0.918 g/cc
- Water Vapor Transmission: 26.4 g/m²/day
- Thickness: >= 7.62 microns
- Melt Index of Compound: 8.0 g/10 min
- Neck In: 5.10 cm
$ 1771/MT
- Density: 0.930 g/cc
- Viscosity: 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 29000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 31000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 105 g/10 min @Load 2.16 kg
$ 2006/MT
- Density: 0.930 g/cc
- Viscosity: 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 29000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 31000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 105 g/10 min @Load 2.16 kg
$ 1548/MT
- Density: 0.924 g/cc
- Thickness: 30.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.9 MPa
- Film Tensile Strength at Yield, TD: 12.1 MPa
$ 2448/MT
- Density: 0.917 g/cc
- Viscosity: 47000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 86000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 110000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg
$ 1566/MT
- Density: 0.920 g/cc
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 11.5 MPa
- Film Elongation at Break, MD: 645 %
$ 1543/MT
- Density: 0.922 g/cc
- Thickness: 13.0 microns
- Melt Flow: 6.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.1 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1902/MT
- Density: 0.9265 g/cc
- Thickness: 19.0 microns
- Melt Flow: 0.50 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 650 ppm
$ 1774/MT
- Density: 0.9255 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 13.89 MPa
- Film Tensile Strength at Yield, TD: 14.58 MPa
$ 2164/MT
- Density: 0.952 g/cc
- Viscosity: 75000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 160000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 250000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 12 g/10 min @Load 2.16 kg
$ 1966/MT
- Density: 0.912 g/cc
- Oxygen Transmission: 282 cc-mm/m²-24hr-atm
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.832 MPa
$ 1626/MT
- Density: 0.941 g/cc
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 125 °C
$ 1788/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 1486/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 2385/MT
- Density: 0.9178 g/cc
- Thickness: 20.3 microns
- Melt Flow: 2.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.22 MPa
- Film Tensile Strength at Yield, TD: 10.5 MPa
$ 1533/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: 290 hour @Temperature 50.0 °C
- High Load Melt Index: 25 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 60
$ 1503/MT
- Density: 0.9218 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 3000 ppm
- Film Tensile Strength at Yield, MD: 10.5 MPa
$ 1895/MT
- Density: 0.916 g/cc
- Thickness: 20.3 microns
- Melt Flow: 4.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.549 MPa
- Film Tensile Strength at Yield, TD: 8.55 MPa
$ 1640/MT
- Density: 0.920 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 10.89 MPa
- Film Tensile Strength at Yield, TD: 12.29 MPa
$ 2454/MT
- Density: 0.9188 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.37 MPa
- Film Tensile Strength at Yield, TD: 12.98 MPa
$ 1601/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 1472/MT
- Density: 0.926 g/cc
- ESCR 100% Igepal®: 5.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 7.58 MPa
$ 1456/MT
- Density: 0.922 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1629/MT
- Density: 0.9289 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Film Tensile Strength at Yield, MD: 16.22 MPa
$ 1959/MT
- Density: 0.920 g/cc
- Thickness: 30.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 1496/MT
- Density: 0.911 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1734/MT
- Density: 0.965 g/cc
- ESCR 100% Igepal®: 2.0 hour @Temperature 50.0 °C
- High Load Melt Index: 180 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 8.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
$ 1560/MT
- Density: 0.950 g/cc
- Melt Flow: 90 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 150 %
$ 1538/MT
- Density: 0.960 g/cc
- Viscosity: 50000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 82000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 153000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 9.0 g/10 min @Load 2.16 kg
$ 1643/MT
- Density: 0.955 g/cc
- Viscosity: 55000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 110000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg
$ 1744/MT
- Density: 0.931 g/cc
- Melt Index of Compound: 127.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1604/MT
- Density: 0.884 g/cc
- High Load Melt Index: 5.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.090 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 81
- Hardness, Shore A: 82
$ 2348/MT
- Density: 0.952 g/cc
- Viscosity: 38000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 80000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 38 g/10 min @Load 2.16 kg
$ 1730/MT
- Density: 0.944 g/cc
- Density: 0.954 g/cc
- High Load Melt Index: 8.3 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- PENT: 200 hour
$ 1729/MT
- Density: 0.920 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 2365/MT
- Density: 0.912 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 68.3 MPa
- Film Tensile Strength at Yield, TD: 66.9 MPa
- Film Elongation at Break, MD: 605 %
$ 1693/MT
- Density: 0.922 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1681/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.9 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1647/MT
- Density: 0.921 g/cc
- Viscosity: 56000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 99000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 265000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
$ 1757/MT
- Density: 0.941 g/cc
- Thickness: 25.0 microns
- Melt Flow: 4.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 13.1 MPa
- Film Tensile Strength at Yield, MD: 16.5 MPa
$ 1913/MT
- Density: 0.9215 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 1000 ppm
$ 2372/MT
- Density: 0.950 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 129 °C
$ 2280/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 11.6 MPa
$ 1448/MT
- Density: 0.925 g/cc
- Viscosity: 28000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 50000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 76000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg
$ 1588/MT
- Density: 0.9215 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.85 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 1200 ppm
$ 1475/MT
- Density: 0.930 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 125 °C
$ 1498/MT
- Density: 0.952 g/cc
- ESCR 100% Igepal®: 12 hour @Temperature 50.0 °C
- Melt Index of Compound: 6.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 59
- Tensile Strength at Break: 22.8 MPa
$ 2333/MT
- Density: 0.928 g/cc
- Thickness: 50.8 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.58 MPa
- Film Tensile Strength at Yield, TD: 14.60 MPa
$ 1583/MT
- Density: 0.905 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.50 g/10 min
- Film Tensile Strength at Yield, MD: 10.7 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1581/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.7 MPa
- Film Tensile Strength at Yield, TD: 10.7 MPa
$ 1458/MT
- Density: 0.905 g/cc
- High Load Melt Index: 24 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 91
- Hardness, Shore A: 94
$ 1564/MT
- Density: 0.920 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 1446/MT
- Density: 0.941 g/cc
- Thickness: 25.4 microns
- Melt Flow: 4.0 g/10 min
- Film Tensile Strength at Yield, MD: 16.22 MPa
- Film Tensile Strength at Yield, TD: 10.76 MPa
$ 1522/MT
- Density: 0.924 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.6 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 22.1 MPa
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 1643/MT
- Density: 0.952 g/cc
- ESCR 100% Igepal®: 1100 hour @Temperature 50.0 °C
- High Load Melt Index: 16 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 37.9 MPa
$ 1544/MT
- Density: 0.962 g/cc
- Viscosity: 80000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 260000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 10 g/10 min @Load 2.16 kg
$ 2066/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: 180 hour @Temperature 50.0 °C
- High Load Melt Index: 25 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 57
$ 2570/MT
- Density: 0.960 g/cc
- Viscosity: 48000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 73000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 105000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 30 g/10 min @Load 2.16 kg
$ 1463/MT
- Density: 0.923 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 55 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 6.21 MPa
$ 1538/MT
- Density: 0.9175 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 1000 ppm
$ 1829/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 2374/MT
- Density: 0.916 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.818 MPa
- Film Tensile Strength at Yield, TD: 10.17 MPa
$ 1494/MT
- Density: 0.919 g/cc
- Viscosity: 76000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 176000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 305000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
$ 1612/MT
- Density: 0.924 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.1 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1618/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 10.28 MPa
- Film Tensile Strength at Yield, TD: 10.03 MPa
$ 1533/MT
- Density: 0.905 g/cc
- Moisture Vapor Transmission: 0.0714 cc-mm/m²-24hr-atm
- Thickness: 51.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Coefficient of Friction: 0.53
$ 1946/MT
- Density: 0.927 g/cc
- ESCR 100% Igepal®: 5.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 55 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 7.58 MPa
$ 1973/MT
- Density: 0.952 g/cc
- Melt Index of Compound: 80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 17.9 MPa
- Tensile Strength, Yield: 19.3 MPa
$ 2123/MT
- Density: 0.930 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 14.5 MPa
$ 2272/MT
- Density: 0.9178 g/cc
- Thickness: 20.3 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.60 MPa
- Film Tensile Strength at Yield, TD: 11.29 MPa
$ 1619/MT
- Density: 0.9255 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 16.28 MPa
- Film Tensile Strength at Yield, TD: 19.73 MPa
$ 1666/MT
- Density: 0.917 g/cc
- Water Vapor Transmission: 27.9 g/m²/day
- Thickness: >= 7.62 microns
- Melt Index of Compound: 10 g/10 min
- Neck In: 3.50 cm
$ 2388/MT
- Density: 0.933 g/cc
- Melt Index of Compound: 155 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 16.5 MPa
$ 1844/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.4 MPa
$ 1939/MT
- Density: 0.935 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.5 g/10 min
- Film Tensile Strength at Yield, MD: 16.9 MPa
- Film Tensile Strength at Yield, TD: 17.59 MPa
$ 1601/MT
- Density: 0.952 g/cc
- Viscosity: 39000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 80000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 40 g/10 min @Load 2.16 kg
$ 1499/MT
- Density: 0.926 g/cc
- Viscosity: 22000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 33000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 39000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 85 g/10 min @Load 2.16 kg
$ 2292/MT
- Density: 0.923 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
- Film Elongation at Break, MD: 360 %
$ 1472/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 9.90 MPa
- Film Tensile Strength at Yield, TD: 10.1 MPa
$ 1956/MT
- Density: 0.918 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 9.65 MPa
$ 1896/MT
- Density: 0.930 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 15.2 MPa
- Film Tensile Strength at Yield, TD: 15.2 MPa
$ 1931/MT
- Density: 0.949 g/cc
- Density: 0.959 g/cc
- High Load Melt Index: 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.080 g/10 min @Load 2.16 kg, Temperature 190 °C
- PENT: >= 6000 hour
$ 1524/MT
- Density: 0.914 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.501 MPa
- Film Tensile Strength at Yield, TD: 8.439 MPa
$ 2305/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 2494/MT
- Density: 0.910 g/cc
- Melt Index of Compound: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 120 °C
- Vicat Softening Point: 90.0 °C
$ 1476/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: >= 1500 hour @Temperature 50.0 °C
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 57
- Tensile Strength at Break: 36.5 MPa
$ 1465/MT
- Density: 0.935 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 15.2 MPa
- Film Tensile Strength at Yield, MD: 17.9 MPa
$ 1654/MT
- Density: 0.926 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 24.8 MPa
- Film Tensile Strength at Yield, MD: 12.7 MPa
$ 1538/MT
- Density: 0.920 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- High Load Melt Index: 44 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
$ 1651/MT
- Density: 0.920 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.85 g/10 min
- Antiblock Level: 5000 ppm
- Slip Level: 900 ppm
$ 1495/MT
- Density: 0.953 g/cc
- Viscosity: 32000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 46000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 54000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 65 g/10 min @Load 2.16 kg
$ 1521/MT
- Density: 0.951 g/cc
- Melt Index of Compound: 44 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 26.9 MPa
- Tensile Strength, Yield: 26.9 MPa
$ 1960/MT
- Density: 0.920 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 11.80 MPa
- Film Tensile Strength at Yield, TD: 12.5 MPa
$ 1608/MT
- Density: 0.9245 g/cc
- Thickness: 50.8 microns
- Melt Flow: 6.4 g/10 min
- Antiblock Level: 2900 ppm
- Slip Level: 2640 ppm
$ 2024/MT
- Density: 0.919 g/cc
- Thickness: 30.0 microns
- Melt Flow: 6.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 15.9 MPa
- Film Tensile Strength at Yield, MD: 9.00 MPa
$ 1455/MT
- Density: 0.930 g/cc
- Viscosity: 27000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 44000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 53000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 125 g/10 min @Load 2.16 kg
$ 1633/MT
- Density: 0.919 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.27 MPa
- Film Tensile Strength at Yield, TD: 11.2 MPa
$ 1617/MT
- Density: 0.961 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- High Load Melt Index: 57 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
$ 1540/MT
- Density: 0.905 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 94
- Tensile Strength at Break: 19.3 MPa
$ 2083/MT
- Density: 0.947 g/cc
- Melt Index of Compound: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 22.1 MPa
- Tensile Strength, Yield: 23.4 MPa
$ 1688/MT
- Density: 0.949 g/cc
- Density: 0.959 g/cc
- High Load Melt Index: 8.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.080 g/10 min @Load 2.16 kg, Temperature 190 °C
- PENT: >= 4000 hour
Delivery Polyethylene (PE) Dow Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
tankers for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.