$ 1754/MT
- Specific Gravity: 0.959 g/cc
- Carbon Black Loading: 2.0 - 2.5 %
- Melt Flow: 0.20 g/10 min @Load 5.00 kg, Temperature 90.0 °C
- Melt Temperature: 190 - 220 °C
- Melt Temperature: 200 - 260 °C
$ 1595/MT
- Specific Gravity: 0.938 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 20 g/10 min @Load 21.6 kg, Temperature 190 °C
- Charpy Impact, Notched: 0.800 J/cm² @Temperature -30.0 °C
- Processing Temperature: 180 - 220 °C
$ 1455/MT
- Specific Gravity: 0.960 g/cc
- Thickness: 20.0 microns
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 23.0 MPa
- Film Tensile Strength at Yield, TD: 24.0 MPa
$ 2013/MT
- Specific Gravity: 0.935 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Charpy Impact, Notched: 8.00 J/cm²
- Processing Temperature: 160 - 200 °C
- Processing Temperature: 180 - 220 °C
$ 1614/MT
- Specific Gravity: 0.958 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 22 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 34.0 MPa
- Film Tensile Strength at Yield, TD: 31.0 MPa
$ 2006/MT
- Density: 0.949 g/cc
- High Load Melt Index: 7.5 g/10 min @Load 21.6 kg
- PENT: >= 3000 hour
- Tensile Strength, Yield: >= 24.1 MPa
- Elongation at Break: >= 800 %
$ 2014/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.0 MPa
- Tensile Modulus: 1.00 GPa
- Melting Point: 131 °C
- Melt Temperature: <= 250 °C
$ 2011/MT
- Specific Gravity: 0.935 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 135 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength at Break: 11.0 MPa
- Tensile Strength, Yield: 18.0 MPa
$ 1795/MT
- Specific Gravity: 0.962 g/cc
- Environmental Stress Crack Resistance: 10 hour
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Charpy Impact, Notched: 1.00 J/cm²
- Processing Temperature: 180 - 220 °C
$ 1567/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3200 ppm
- Slip Level: 1500 ppm
$ 2379/MT
- Density: 0.949 g/cc
- Environmental Stress Crack Resistance: >= 360 hour
- Thermal Stress Crack Resistance: >= 250 hour
- High Load Melt Index: 8.0 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: 24.0 MPa
$ 1981/MT
- Specific Gravity: 0.947 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 24.0 MPa
- Film Tensile Strength at Yield, TD: 25.0 MPa
$ 2052/MT
- Specific Gravity: 0.923 g/cc
- Thickness: 40.0 microns
- Thickness: 25.0 - 150 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
$ 2039/MT
- Specific Gravity: 0.948 g/cc
- Carbon Black Loading: 2.0 - 2.5 %
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 190 °C
- Processing Temperature: 190 - 220 °C
- Processing Temperature: 200 - 260 °C
$ 1833/MT
- Density: 0.946 g/cc
- Melt Flow: 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.9 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: >= 500 %
$ 1781/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3200 ppm
- Slip Level: 1500 ppm
$ 1761/MT
- Density: 0.947 g/cc
- Water Vapor Transmission: 7.76 g/m²/day @Thickness 0.0254 mm
- Water Vapor Transmission: 10.9 g/m²/day @Thickness 0.0254 mm
- Thickness: 25.4 microns
- Melt Flow: 0.28 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1656/MT
- Density: 0.940 g/cc
- Viscosity: 1.30e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Environmental Stress Crack Resistance: >= 700 hour
- Oxidative Induction Time (OIT): >= 20 min
- Oxidative Induction Time (OIT): >= 30 min
$ 1737/MT
- Density: 0.947 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.28 g/10 min @Load 2.16 kg
- High Load Melt Index: 20 g/10 min @Load 21.6 kg
- Hardness, Shore D: 63
$ 2507/MT
- Density: 0.945 g/cc
- Environmental Stress Crack Resistance: 200 hour
- Melt Flow: 0.55 g/10 min @Load 2.16 kg
- Melt Flow: 1.9 g/10 min @Load 5.00 kg
- High Load Melt Index: 19 g/10 min @Load 21.6 kg
$ 1628/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 21.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: >= 800 %
$ 1723/MT
- Specific Gravity: 0.927 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.5 MPa
- Film Tensile Strength at Yield, TD: 14.0 MPa
$ 1820/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 0.000 ppm
- Slip Level: 0.000 ppm
$ 1825/MT
- Density: 0.938 g/cc
- Melt Flow: 0.15 g/10 min @Load 2.16 kg
- Melt Flow: 0.80 g/10 min @Load 5.00 kg
- High Load Melt Index: 14 g/10 min @Load 21.6 kg
- Dart Drop Test: 80.0 g
$ 2057/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 190 °C
- Processing Temperature: 190 - 220 °C
- Processing Temperature: 200 - 260 °C
- Pigment Dispersion Rating: = 3
$ 2207/MT
- Specific Gravity: 0.946 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: >= 1000 hour
- Melt Flow: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength at Break: 36.8 MPa
$ 1734/MT
- Density: 0.924 g/cc
- Melt Flow: 0.80 g/10 min
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength, Yield: 12.0 MPa
- Elongation at Break: 650 %
$ 1501/MT
- Specific Gravity: 0.953 g/cc
- Environmental Stress Crack Resistance: 10 hour
- Melt Flow: 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Charpy Impact, Notched: 2.00 J/cm² @Temperature -30.0 °C
- Processing Temperature: 180 - 220 °C
$ 2218/MT
- Specific Gravity: 0.938 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 60
$ 1803/MT
- Specific Gravity: 0.955 g/cc
- Thickness: >= 10.0 microns
- Thickness: 12.0 microns
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 11 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 2219/MT
- Density: 0.941 g/cc
- Viscosity: 1.30e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Environmental Stress Crack Resistance: >= 700 hour
- Oxidative Induction Time (OIT): >= 20 min
- Oxidative Induction Time (OIT): >= 30 min
$ 1548/MT
- Specific Gravity: 0.961 g/cc
- ESCR 10% Igepal®: >= 10 hour
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 29.6 MPa
$ 2311/MT
- Density: 0.947 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.28 g/10 min @Load 2.16 kg
- High Load Melt Index: 20 g/10 min @Load 21.6 kg
$ 1739/MT
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 190 °C
- Thermal Stability 200°C: > 20 min
- Water Content: = 300 ppm
$ 1698/MT
- Density: 0.958 g/cc
- ESCR 100% Igepal®: >= 800 hour
- ESCR 10% Igepal®: >= 300 hour
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 30.3 MPa
$ 1463/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 29.0 MPa
- Tensile Modulus: 1.30 GPa
- Melting Point: 133 °C
- Processing Temperature: <= 250 °C
$ 1771/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 50 hour
- Environmental Stress Crack Resistance: 100 hour
- Melt Flow: 0.35 g/10 min @Load 2.16 kg
- High Load Melt Index: 30 g/10 min @Load 21.6 kg
$ 1924/MT
- Specific Gravity: 0.918 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51
- Tensile Strength at Break: 8.00 MPa
- Tensile Strength, Yield: 8.00 MPa
$ 1476/MT
- Density: 0.950 g/cc
- Water Vapor Transmission: 12.4 g/m²/day
- Thickness: 20.3 microns
- Melt Flow: 0.070 g/10 min @Load 2.16 kg
- Melt Flow: 0.31 g/10 min @Load 5.00 kg
$ 1790/MT
- Specific Gravity: 0.950 g/cc
- Environmental Stress Crack Resistance: 27 hour
- Melt Flow: 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Charpy Impact, Notched: 2.00 J/cm² @Temperature -30.0 °C
- Processing Temperature: 180 - 220 °C
$ 2465/MT
- Specific Gravity: 0.949 g/cc
- Melt Flow: 7.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- PENT: >= 2500 hour
- Tensile Strength, Yield: >= 24.1 MPa
- Elongation at Break: >= 800 %
$ 1479/MT
- Specific Gravity: 0.958 g/cc
- Carbon Black Loading: 2.0 - 2.5 %
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Temperature: 190 - 220 °C
- Melt Temperature: 200 - 260 °C
$ 1668/MT
- Density: 0.927 g/cc
- Water Vapor Transmission: 14.0 g/m²/day
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 580 %
$ 1881/MT
- Specific Gravity: 0.958 g/cc
- Carbon Black Loading: 2.5 %
- Melt Flow: 0.20 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- PENT: >= 1000 hour
$ 1728/MT
- Specific Gravity: 0.955 g/cc
- Carbon Black Loading: >= 2.0 %
- Melt Flow: 1.8 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Temperature: 210 - 245 °C
- Carbon Black Dispersion, Rating: = 3
$ 1703/MT
- Density: 0.927 g/cc
- Water Vapor Transmission: 13.9 g/m²/day @Thickness 0.0254 mm
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1487/MT
- Density: 0.950 g/cc
- Environmental Stress Crack Resistance: >= 600 hour
- High Load Melt Index: 9.0 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 26.2 MPa
- Elongation at Break: 600 %
$ 1913/MT
- Density: 0.937 g/cc
- Water Vapor Transmission: 12.4 g/m²/day
- Melt Flow: 0.23 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 20 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.4 MPa
$ 1544/MT
- Specific Gravity: 0.923 g/cc
- Thickness: 40.0 microns
- Thickness: 20.0 - 150 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 750 ppm
$ 1703/MT
- Specific Gravity: 0.962 g/cc
- ESCR 10% Igepal®: >= 10 hour
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 33.1 MPa
- Elongation at Break: 300 %
$ 1583/MT
- Density: 0.924 g/cc
- Melt Flow: 0.80 g/10 min
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength, Yield: 12.0 MPa
- Elongation at Break: 650 %
$ 1628/MT
- Specific Gravity: 0.919 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 800 %
$ 1509/MT
- Density: 0.951 g/cc
- Water Vapor Transmission: 12.4 g/m²/day
- Thickness: 20.3 microns
- Melt Flow: 0.080 g/10 min @Load 2.16 kg
- Melt Flow: 0.32 g/10 min @Load 5.00 kg
$ 1536/MT
- Oxidative Induction Time (OIT): >= 20 min
- Melt Flow: 0.30 g/10 min @Load 5.00 kg
$ 1553/MT
- Density: 0.949 g/cc
- Thermal Stress Crack Resistance: >= 250 hour
- High Load Melt Index: 8.0 g/10 min @Load 21.6 kg
$ 1491/MT
- Specific Gravity: 1.02 g/cc
- Water Vapor Transmission: 3.00 - 5.00 g/m²/day @Thickness 0.300 mm, Temperature 38.0 °C
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength at Break: 22.0 MPa
- Elongation at Break: 80 %
$ 2294/MT
- Specific Gravity: 0.959 g/cc
- Environmental Stress Crack Resistance: >= 100 hour
- Flexural Modulus: 1.30 GPa
- Processing Temperature: 220 - 240 °C
$ 2015/MT
- Density: 0.995 g/cc
- Environmental Stress Crack Resistance: >= 250 hour
- Melt Flow: 4.5 g/10 min @Temperature 190 °C
- Flexural Modulus: 1.20 GPa
- Volume Resistivity: <= 10000 ohm-cm
- Surface Resistance: <= 10000 ohm
$ 2131/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 50 hour
- Environmental Stress Crack Resistance: 100 hour
- Melt Flow: 0.35 g/10 min @Load 2.16 kg
- High Load Melt Index: 30 g/10 min @Load 21.6 kg
$ 1618/MT
- Specific Gravity: 0.919 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 850 %
$ 1561/MT
- Specific Gravity: 0.958 g/cc
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 133 °C
- Processing Temperature: 200 - 260 °C
$ 2006/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 29.0 MPa
- Tensile Modulus: 1.30 GPa
- Melting Point: 133 °C
- Processing Temperature: <= 250 °C
$ 1580/MT
- Density: 0.950 g/cc
- Viscosity: 270000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 2.10e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Oxidative Induction Time (OIT): >= 20 min
- Oxidative Induction Time (OIT): >= 20 min
$ 1474/MT
- Density: 0.951 g/cc
- Water Vapor Transmission: 12.4 g/m²/day
- Thickness: 20.3 microns
- Melt Flow: 0.060 g/10 min @Load 2.16 kg
- Melt Flow: 0.32 g/10 min @Load 5.00 kg
$ 1532/MT
- Density: 0.948 g/cc
- Viscosity: 1.30e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Environmental Stress Crack Resistance: >= 1000 hour
- Oxidative Induction Time (OIT): >= 30 min
- Carbon Black Loading: 2.0 - 2.5 %
$ 1717/MT
- Specific Gravity: 0.921 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3200 ppm
- Slip Level: 1500 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1556/MT
- Specific Gravity: 0.961 g/cc
- ESCR 10% Igepal®: >= 10 hour
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 55 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 29.6 MPa
$ 1479/MT
- Density: 0.959 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.27 g/10 min @Load 2.16 kg
- High Load Melt Index: 26 g/10 min @Load 21.6 kg
- Tensile Strength at Break: 28.0 MPa
$ 1806/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: 35 hour
- Environmental Stress Crack Resistance: 50 hour
- Melt Flow: 0.35 g/10 min @Load 2.16 kg
- High Load Melt Index: 30 g/10 min @Load 21.6 kg
$ 1691/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 0.000 ppm
- Slip Level: 0.000 ppm
$ 1448/MT
- Specific Gravity: 0.927 g/cc
- Thickness: 20.0 microns
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 9.00 MPa
$ 2356/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.0 MPa
- Tensile Modulus: 1.00 GPa
- Melting Point: 131 °C
- Melt Temperature: <= 250 °C
$ 2041/MT
- Density: 0.934 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.90 g/10 min @Load 2.16 kg
- Melt Flow: 3.0 g/10 min @Load 5.00 kg
- High Load Melt Index: 25 g/10 min @Load 21.6 kg
$ 2380/MT
- Specific Gravity: 0.961 g/cc
- Environmental Stress Crack Resistance: 10 hour
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 52 g/10 min @Load 21.6 kg, Temperature 190 °C
- Charpy Impact, Notched: 1.00 J/cm²
- Processing Temperature: 180 - 220 °C
$ 2274/MT
- Specific Gravity: 0.918 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 0.000 ppm
- Slip Level: 0.000 ppm
$ 1915/MT
- Specific Gravity: 0.955 g/cc
- Thickness: 40.0 microns
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 27.5 MPa
- Film Tensile Strength at Yield, TD: 28.0 MPa
$ 2042/MT
- Density: 0.947 g/cc
- Water Vapor Transmission: 7.76 g/m²/day
- Thickness: 25.4 microns
- Melt Flow: 0.28 g/10 min @Load 2.16 kg
- High Load Melt Index: 20 g/10 min @Load 21.6 kg
$ 2014/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: >= 700 hour
- Oxidative Induction Time (OIT): >= 20 min
- Oxidative Induction Time (OIT): >= 30 min
- Carbon Black Loading: 2.0 - 2.5 %
$ 1655/MT
- Density: 0.958 g/cc
- Water Vapor Transmission: 10.9 g/m²/day @Thickness 0.0254 mm
- Thickness: 25.4 microns
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 31.0 MPa @Thickness 0.0254 mm
$ 1980/MT
- Specific Gravity: 0.938 g/cc
- Melt Flow: 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 14 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 20.0 MPa @Thickness 0.0400 mm
- Film Tensile Strength at Yield, MD: 21.0 MPa @Thickness 0.0200 mm
$ 1612/MT
- Specific Gravity: 0.934 g/cc
- Thickness: 20.0 microns
- Melt Flow: 3.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 11.5 MPa
$ 2437/MT
- Specific Gravity: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1634/MT
- Specific Gravity: 0.952 g/cc
- Environmental Stress Crack Resistance: >= 250 hour
- Melt Flow: 1.4 g/10 min @Load 21.6 kg, Temperature 190 °C
- Charpy Impact, Notched: 5.50 J/cm² @Temperature -30.0 °C
- Charpy Impact, Notched: 8.00 J/cm² @Temperature 23.0 °C
- Processing Temperature: 180 - 230 °C
$ 2202/MT
- Density: 0.950 g/cc
- Viscosity: 270000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 2.10e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Oxidative Induction Time (OIT): >= 20 min
- Oxidative Induction Time (OIT): >= 20 min
$ 1679/MT
- Density: 0.925 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 12 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 700 % @Thickness 0.0254 mm
$ 1606/MT
- Specific Gravity: 0.960 g/cc
- Flexural Modulus: 1.40 GPa
- Charpy Impact, Notched: 1.10 J/cm²
- Processing Temperature: 220 - 240 °C
$ 1457/MT
- Oxidative Induction Time (OIT): >= 20 min
- Melt Flow: 0.30 g/10 min @Load 5.00 kg
$ 1518/MT
- Specific Gravity: 0.918 g/cc
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 7.00 MPa
- Tensile Strength, Yield: 8.00 MPa
$ 1933/MT
- Specific Gravity: 0.955 g/cc
- Water Vapor Transmission: 10.9 g/m²/day @Temperature 37.8 °C
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 27.6 MPa
$ 1934/MT
- Specific Gravity: 0.927 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.5 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
$ 1519/MT
- Density: 0.959 g/cc
- Viscosity: 270000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 2.10e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Oxidative Induction Time (OIT): >= 20 min
- Oxidative Induction Time (OIT): >= 20 min
$ 2010/MT
- Density: 0.946 g/cc
- Melt Flow: 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.9 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: >= 500 %
$ 1814/MT
- Specific Gravity: 0.921 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3200 ppm
- Slip Level: 1500 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1645/MT
- Specific Gravity: 0.952 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 2.1 g/10 min @Load 21.6 kg, Temperature 190 °C
- Charpy Impact, Notched: 5.00 J/cm² @Temperature -30.0 °C
- Processing Temperature: 180 - 220 °C
$ 1805/MT
- Density: 0.945 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.080 g/10 min @Load 2.16 kg
- Melt Flow: 0.34 g/10 min @Load 5.00 kg
- High Load Melt Index: 7.0 g/10 min @Load 21.6 kg
$ 1579/MT
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 190 °C
- Thermal Stability 200°C: > 20 min
- Water Content: = 300 ppm
$ 2096/MT
- Specific Gravity: 0.946 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.0 MPa
- Elongation at Break: >= 600 %
$ 1485/MT
- Specific Gravity: 0.918 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength, Yield: 9.00 MPa
$ 1828/MT
- Density: 0.949 g/cc
- Environmental Stress Crack Resistance: >= 250 hour
- High Load Melt Index: 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength at Break: 37.0 MPa
- Tensile Strength, Yield: 24.0 MPa
$ 1529/MT
- Density: 0.935 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: >= 1000 hour
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1486/MT
- Oxidative Induction Time (OIT): >= 20 min
- Melt Flow: 0.30 g/10 min @Load 5.00 kg
$ 2122/MT
- Specific Gravity: 0.952 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Charpy Impact, Notched: 1.00 J/cm²
- Melt Temperature: 180 °C
$ 1466/MT
- Specific Gravity: 0.954 g/cc
- Environmental Stress Crack Resistance: 60 hour
- Melt Flow: 22 g/10 min @Load 21.6 kg, Temperature 190 °C
- Charpy Impact, Notched: 1.60 J/cm²
- Processing Temperature: 180 - 220 °C
$ 2257/MT
- Specific Gravity: 0.948 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 60
Delivery Polyethylene (PE) Total Atofina
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tanker ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.