$ 1571/MT
- Density: 1.30 g/cc
- Water Absorption: 0.070 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Modulus: 3.10 GPa
$ 2188/MT
- Density: 1.61 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 1.8 %
$ 1801/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
$ 1880/MT
- Density: 1.39 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 2.70 GPa
$ 1912/MT
- Density: 1.59 g/cc
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1512/MT
- Density: 1.68 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 2.0 %
$ 1691/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.039 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0010 cm/cm
- Hardness, Shore A: 25
- Tensile Strength at Break: 2.30 MPa
$ 1603/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.046 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Hardness, Shore A: 35
- Tensile Strength at Break: 3.40 MPa
$ 2328/MT
- Density: 1.67 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0042 cm/cm
- Tensile Strength at Break: 125 MPa
$ 2452/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 600 %
- Resin Type: TPE-V
$ 1748/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 55
- Tensile Strength at Break: 4.50 MPa
- Elongation at Break: 500 %
- Resin Type: TPE-V
$ 1594/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 8.50 GPa
- Charpy Impact Unnotched: 4.50 J/cm²
$ 1801/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 16.0 MPa
$ 1953/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.024 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Hardness, Shore A: 50
- Tensile Strength at Break: 4.80 MPa
$ 1516/MT
- Density: 1.65 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 10.5 GPa
$ 1805/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Shore A: 60
- Tensile Strength at Break: 5.70 MPa
$ 2226/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 8.20 MPa
- Elongation at Break: 600 %
- Resin Type: TPE-V
$ 1606/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1463/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.024 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Hardness, Shore A: 65
- Tensile Strength at Break: 7.00 MPa
$ 2023/MT
- Density: 2.30 g/cc
- Tensile Strength at Break: 36.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 3.00 GPa
- Charpy Impact Unnotched: 2.50 J/cm²
$ 2011/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Hardness, Shore D: 55
- Tensile Strength at Break: 35.0 MPa
$ 1862/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 9.90 MPa
$ 1467/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 9.20 MPa
$ 1499/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Shore A: 95
- Tensile Strength at Break: 15.3 MPa
$ 1743/MT
- Density: 1.50 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.60 GPa
$ 1459/MT
- Density: 1.52 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 145 MPa
$ 1527/MT
- Density: 1.62 g/cc
- Water Absorption: 0.040 %
- Linear Mold Shrinkage, Flow: 0.0016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0046 cm/cm
- Tensile Strength at Break: 136 MPa
$ 2434/MT
- Density: 1.62 g/cc
- Water Absorption: 0.040 %
- Linear Mold Shrinkage, Flow: 0.0016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0038 cm/cm
- Tensile Strength at Break: 145 MPa
$ 1450/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Hardness, Shore A: 40
- Tensile Strength at Break: 3.10 MPa
$ 2088/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 46.0 MPa
- Elongation at Break: 690 %
- Charpy Impact, Notched: NB
- Resin Type: TPU
$ 1537/MT
- Density: 1.94 g/cc
- Water Absorption: 0.020 %
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 0.80 %
- Tensile Modulus: 19.0 GPa
$ 1978/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 50
- Tensile Strength at Break: 4.00 MPa
- Elongation at Break: 500 %
- Resin Type: TPE-V
$ 1814/MT
- Density: 1.23 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 50 %
- Tensile Modulus: 1.80 GPa
$ 1986/MT
- Density: 1.29 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 235 °C
- Tensile Strength at Break: 58.0 MPa
- Elongation at Break: >= 25 %
$ 1877/MT
- Density: 0.940 g/cc
- Hardness, Shore D: 50
- Tensile Strength at Break: 22.0 MPa
- Elongation at Break: 700 %
- Resin Type: TPE-V
$ 1597/MT
- Density: 1.70 g/cc
- Moisture Absorption at Equilibrium: 0.10 %
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 1.8 %
- Tensile Modulus: 15.0 GPa
$ 1904/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 35
- Tensile Strength at Break: 3.00 MPa
- Elongation at Break: 450 %
- Resin Type: TPE-V
$ 1698/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 10.6 MPa
$ 1876/MT
- Density: 1.65 g/cc
- Water Absorption: 0.020 %
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 1.3 %
- Tensile Modulus: 14.5 GPa
$ 2582/MT
- Density: 1.40 g/cc
- Water Absorption: 0.040 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Modulus: 23.5 GPa
$ 1530/MT
- Density: 1.51 g/cc
- Water Absorption: 0.020 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Modulus: 11.8 GPa
$ 1481/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
$ 1580/MT
- Density: 3.40 g/cc
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 1.9 %
- Tensile Modulus: 10.0 GPa
- Melting Point: 178 °C
- Resin Type: PA 12 mod.
$ 2243/MT
- Density: 1.52 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 145 MPa
$ 2081/MT
- Density: 1.46 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 52.0 MPa
- Elongation at Yield: 8.0 %
$ 2285/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2265/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1528/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 115 MPa
$ 1719/MT
- Density: 1.59 g/cc
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2388/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1467/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
$ 2198/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1636/MT
- Density: 1.55 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 8.0 %
- Tensile Modulus: 5.10 GPa
$ 1616/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 60.0 MPa
$ 1627/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
$ 1872/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
$ 2434/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2058/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1764/MT
- Density: 1.37 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 57.0 MPa
- Elongation at Yield: 9.0 %
$ 1723/MT
- Density: 1.42 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 10.5 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2226/MT
- Density: 1.34 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 9.5 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1993/MT
- Density: 1.46 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 52.0 MPa
- Elongation at Yield: 8.0 %
$ 1675/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1587/MT
- Density: 1.43 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 6.60 GPa
$ 1612/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1736/MT
- Density: 1.51 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Yield: 7.0 %
$ 1973/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 50.0 MPa
$ 2015/MT
- Density: 1.44 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 52.0 MPa
- Elongation at Yield: 8.0 %
$ 1498/MT
- Density: 1.46 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 15.0 GPa
$ 2286/MT
- Density: 1.55 g/cc
- Moisture Absorption at Equilibrium: 0.19 %
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 44.0 MPa
- Elongation at Break: 6.0 %
$ 2008/MT
- Density: 1.40 g/cc
- Moisture Absorption at Equilibrium: 0.21 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1759/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 40.0 MPa
$ 1538/MT
- Density: 1.32 g/cc
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Yield: 19 %
- Tensile Modulus: 1.40 GPa
$ 2468/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1647/MT
- Density: 1.65 g/cc
- Water Absorption: 0.020 %
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 14.5 GPa
$ 1734/MT
- Density: 1.37 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 12 %
- Tensile Modulus: 2.05 GPa
$ 1765/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Shore A: 75
- Tensile Strength at Break: 8.50 MPa
$ 2027/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 7.40 MPa
- Elongation at Break: 550 %
- Resin Type: TPE-V
$ 1464/MT
- Density: 0.950 g/cc
- Hardness, Shore D: 40
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 620 %
- Resin Type: TPE-V
$ 1546/MT
- Density: 1.42 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 9.00 GPa
- Charpy Impact Unnotched: 5.50 J/cm²
$ 1458/MT
- Density: 1.55 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.80 GPa
$ 2530/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Shore A: 95
- Tensile Strength at Break: 23.7 MPa
$ 2075/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.028 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
- Hardness, Shore A: 45
- Tensile Strength at Break: 3.60 MPa
$ 1600/MT
- Density: 1.54 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 9.50 GPa
$ 1506/MT
- Density: 1.42 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 3.0 %
$ 2242/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Hardness, Shore D: 40
- Tensile Strength at Break: 25.0 MPa
$ 2016/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 25 %
$ 1502/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 42.0 MPa
- Elongation at Break: 900 %
- Charpy Impact, Notched: NB
- Resin Type: TPU
$ 1804/MT
- Density: 1.46 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 52.0 MPa
- Elongation at Yield: 8.0 %
$ 1863/MT
- Density: 1.81 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 260 °C
$ 1879/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 5.80 MPa
- Elongation at Break: 540 %
- Resin Type: TPE-V
$ 1560/MT
- Density: 1.65 g/cc
- Water Absorption: 0.020 %
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 1.8 %
- Tensile Modulus: 14.5 GPa
$ 2317/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1740/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.024 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Hardness, Shore A: 60
- Tensile Strength at Break: 6.20 MPa
$ 1466/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Shore A: 65
- Tensile Strength at Break: 9.70 MPa
$ 2082/MT
- Density: 1.38 g/cc
- Moisture Absorption at Equilibrium: 0.18 %
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength at Break: 85.0 MPa
$ 2098/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 60
- Tensile Strength at Break: 5.00 MPa
- Elongation at Break: 500 %
- Resin Type: TPE-V
$ 2066/MT
- Density: 1.68 g/cc
- Water Absorption: 0.020 %
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 140 MPa
$ 1547/MT
- Density: 1.65 g/cc
- Water Absorption: 0.020 %
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 1.2 %
- Tensile Modulus: 14.5 GPa
$ 1484/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 9.00 MPa
- Elongation at Break: 600 %
- Resin Type: TPE-V
$ 1511/MT
- Density: 1.62 g/cc
- Water Absorption: 0.20 %
- Moisture Absorption at Equilibrium: 0.40 %
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
Barlog Plastics KEBABLEND TC 170.13 PET functional compound, thermally conductive, electr. isolating
$ 1881/MT
- Density: 1.68 g/cc
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 1.2 %
- Tensile Modulus: 9.00 GPa
- Charpy Impact Unnotched: 1.30 J/cm²
$ 1771/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.026 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Hardness, Shore A: 60
- Tensile Strength at Break: 5.70 MPa
$ 1587/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Hardness, Shore A: 55
- Tensile Strength at Break: 7.70 MPa
$ 2006/MT
- Density: 1.94 g/cc
- Water Absorption: 0.020 %
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 1.0 %
- Tensile Modulus: 19.0 GPa
$ 2022/MT
- Density: 1.94 g/cc
- Water Absorption: 0.020 %
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 0.90 %
- Tensile Modulus: 20.0 GPa
$ 1851/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Hardness, Shore A: 55
- Tensile Strength at Break: 4.80 MPa
$ 2020/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Hardness, Shore D: 75
- Tensile Strength at Break: 39.0 MPa
$ 1695/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 45
- Tensile Strength at Break: 3.70 MPa
- Elongation at Break: 500 %
- Resin Type: TPE-V
$ 1969/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 650 %
- Charpy Impact, Notched: NB
- Resin Type: TPU
$ 1531/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.033 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Hardness, Shore A: 35
- Tensile Strength at Break: 2.40 MPa
$ 1754/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 8.50 MPa
$ 1825/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 40
- Tensile Strength at Break: 3.50 MPa
- Elongation at Break: 500 %
- Resin Type: TPE-V
Delivery Polymer Barlog Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.