$ 1845/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength at Break: 26.9 MPa
- Flexural Strength: 24.8 MPa
- Flexural Modulus: 0.621 GPa
- Izod Impact, Notched: 52.9 J/cm
$ 1513/MT
- Specific Gravity: 1.58 g/cc
- Water Absorption: 0.18 %
- Tensile Strength at Break: 128 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 193 MPa
$ 1723/MT
- Specific Gravity: 1.22 g/cc
- Tensile Strength at Break: 62.1 MPa
- Flexural Strength: 86.9 MPa
- Flexural Modulus: 2.24 GPa
- Izod Impact, Notched: 1.60 J/cm
$ 1557/MT
- Density: 1.23 g/cc
- Filler Content: 10 %
- Water Absorption: 1.5 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Tensile Strength at Break: 110 MPa
$ 1777/MT
- Specific Gravity: 1.28 g/cc
- Tensile Strength at Break: 134 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 200 MPa
- Flexural Modulus: 6.21 GPa
$ 1661/MT
- Tensile Strength at Break: 67.0 MPa
- Flexural Strength: 115.4 MPa
- Flexural Modulus: 5.10 GPa
- Izod Impact, Notched: 1.60 J/cm
$ 2240/MT
- Specific Gravity: 1.39 g/cc
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 245 MPa
- Flexural Modulus: 8.62 GPa
$ 1749/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 56.5 MPa
- Flexural Strength: 37.2 MPa
- Flexural Modulus: 1.03 GPa
- Izod Impact, Notched: 1.49 J/cm
$ 1561/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 25 %
- Flexural Strength: 103 MPa
- Flexural Modulus: 2.86 GPa
$ 2118/MT
- Specific Gravity: 1.07 g/cc
- Tensile Strength at Break: 43.4 MPa
- Elongation at Break: 140 %
- Flexural Strength: 55.2 MPa
- Flexural Modulus: 1.38 GPa
$ 2171/MT
- Specific Gravity: 1.22 g/cc
- Tensile Strength at Break: 89.6 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 131 MPa
- Flexural Modulus: 4.34 GPa
$ 2057/MT
- Density: 1.41 g/cc
- Filler Content: 30 %
- Water Absorption: 0.60 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Hardness, Rockwell R: 120
$ 1981/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: >= 200 %
- Flexural Strength: 31.0 MPa
$ 1828/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength at Break: 32.4 MPa
- Flexural Strength: 20.0 MPa
- Flexural Modulus: 0.586 GPa
- Izod Impact, Notched: NB
$ 1720/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Hardness, Rockwell R: 123
- Tensile Strength at Break: 93.1 MPa
- Elongation at Break: 3.0 %
$ 1527/MT
- Density: 1.25 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Rockwell R: 124
- Tensile Strength, Yield: 58.6 MPa
$ 1538/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 179 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 262 MPa
- Flexural Modulus: 8.96 GPa
$ 1571/MT
- Specific Gravity: 1.28 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 96.5 MPa
- Flexural Modulus: 5.86 GPa
$ 1709/MT
- Tensile Strength at Break: 70.3 MPa
- Flexural Strength: 95.1 MPa
- Flexural Modulus: 2.48 GPa
- Izod Impact, Notched: 1.17 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 254 °C
- Deflection Temperature at 1.8 MPa (264 psi): 235 °C
$ 2161/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 26.9 MPa
- Elongation at Break: >= 200 %
- Flexural Strength: 34.5 MPa
$ 1866/MT
- Density: 1.30 g/cc
- Filler Content: 20 %
- Water Absorption: 1.5 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Tensile Strength at Break: 117 MPa
$ 1452/MT
- Density: 1.15 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Tensile Strength, Yield: 79.3 MPa
- Flexural Strength: 96.5 MPa
$ 1485/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 6.0 %
- Flexural Strength: 214 MPa
- Flexural Modulus: 6.55 GPa
$ 2139/MT
- Density: 1.56 g/cc
- Filler Content: 20 %
- Water Absorption: 0.24 %
- Hardness, Rockwell M: 89
- Tensile Strength at Break: 56.5 MPa
$ 1645/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 123
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 30 %
$ 1627/MT
- Specific Gravity: 1.50 g/cc
- Tensile Strength at Break: 155 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 221 MPa
- Flexural Modulus: 9.65 GPa
$ 1847/MT
- Density: 1.15 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Tensile Strength, Yield: 79.3 MPa
- Elongation at Break: 7.5 %
$ 1931/MT
- Density: 1.70 g/cc
- Filler Content: 60 %
- Water Absorption: 0.40 %
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Tensile Strength at Break: 269 MPa
$ 1546/MT
- Tensile Strength at Break: 78.6 MPa
- Flexural Strength: 95.8 MPa
- Flexural Modulus: 2.48 GPa
- Izod Impact, Notched: 1.33 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 254 °C
- Deflection Temperature at 1.8 MPa (264 psi): 235 °C
$ 2338/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 56.5 MPa
- Flexural Strength: 37.2 MPa
- Flexural Modulus: 1.03 GPa
- Izod Impact, Notched: 1.49 J/cm
$ 1722/MT
- Specific Gravity: 1.22 g/cc
- Tensile Strength at Break: 53.8 MPa
- Flexural Strength: 78.6 MPa
- Flexural Modulus: 2.17 GPa
- Izod Impact, Notched: 1.49 J/cm
$ 1555/MT
- Density: 1.41 g/cc
- Filler Content: 30 %
- Water Absorption: 0.60 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Hardness, Rockwell R: 120
$ 1671/MT
- Specific Gravity: 1.23 g/cc
- Tensile Strength at Break: 55.2 MPa
- Flexural Strength: 80.7 MPa
- Flexural Modulus: 2.24 GPa
- Izod Impact, Notched: 1.60 J/cm
$ 1520/MT
- Specific Gravity: 0.920 g/cc
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 10.3 MPa
- Elongation at Break: 600 %
- Flexural Modulus: 0.179 GPa
$ 1444/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength at Break: 143 MPa
- Flexural Strength: 230 MPa
- Flexural Modulus: 6.89 GPa
- Izod Impact, Notched: 1.60 J/cm
$ 1526/MT
- Density: 1.38 g/cc
- Filler Content: 33 %
- Water Absorption: 0.70 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Hardness, Rockwell M: 99
$ 1842/MT
- Specific Gravity: 1.22 g/cc
- Tensile Strength at Break: 103 MPa
- Elongation at Break: 4.0 %
- Flexural Strength: 152 MPa
- Flexural Modulus: 4.65 GPa
$ 1889/MT
- Density: 1.23 g/cc
- Filler Content: 10 %
- Water Absorption: 1.7 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Tensile Strength at Break: 96.5 MPa
$ 1887/MT
- Specific Gravity: 1.26 g/cc
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 15 %
- Flexural Strength: 103 MPa
- Flexural Modulus: 3.45 GPa
$ 1484/MT
- Density: 1.35 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Hardness, Rockwell R: 124
- Tensile Strength at Break: 107 MPa
$ 1480/MT
- Tensile Strength at Break: 60.7 MPa
- Elongation at Break: >= 100 %
- Flexural Modulus: 1.10 GPa
- Izod Impact, Notched: 1.60 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 232 °C
- Deflection Temperature at 1.8 MPa (264 psi): 82.2 °C
$ 1479/MT
- Tensile Strength at Break: 123 MPa
- Flexural Strength: 194 MPa
- Flexural Modulus: 6.10 GPa
- Izod Impact, Notched: 1.87 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 260 °C
- Deflection Temperature at 1.8 MPa (264 psi): 246 °C
$ 1535/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength at Break: 82.7 MPa
- Elongation at Break: 60 %
- Flexural Strength: 117 MPa
- Flexural Modulus: 3.10 GPa
$ 2519/MT
- Specific Gravity: 1.50 g/cc
- Tensile Strength at Break: 145 MPa
- Flexural Strength: 225 MPa
- Flexural Modulus: 7.58 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1502/MT
- Density: 1.09 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 79.3 MPa
$ 2285/MT
- Specific Gravity: 1.43 g/cc
- Tensile Strength at Break: 117 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 179 MPa
- Flexural Modulus: 6.89 GPa
$ 2343/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: >= 200 %
- Flexural Strength: 31.0 MPa
$ 1711/MT
- Density: 1.43 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Hardness, Rockwell R: 122
- Tensile Strength at Break: 128 MPa
$ 1900/MT
- Specific Gravity: 1.34 g/cc
- Tensile Strength at Break: 96.5 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 131 MPa
- Flexural Modulus: 5.17 GPa
$ 1491/MT
- Specific Gravity: 1.50 g/cc
- Tensile Strength at Break: 214 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 317 MPa
- Flexural Modulus: 11.0 GPa
$ 1661/MT
- Density: 1.50 g/cc
- Filler Content: 43 %
- Water Absorption: 0.60 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 100
$ 1810/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: >= 200 %
- Flexural Strength: 33.8 MPa
$ 1979/MT
- Density: 1.38 g/cc
- Filler Content: 33 %
- Water Absorption: 0.70 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Hardness, Rockwell M: 99
$ 2215/MT
- Specific Gravity: 1.22 g/cc
- Tensile Strength at Break: 117 MPa
- Elongation at Break: 4.0 %
- Flexural Strength: 165 MPa
- Flexural Modulus: 4.65 GPa
$ 2522/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 80.0 MPa
- Flexural Strength: 124 MPa
- Flexural Modulus: 4.41 GPa
- Izod Impact, Notched: 2.14 J/cm
$ 2196/MT
- Specific Gravity: 1.43 g/cc
- Tensile Strength at Break: 128 MPa
- Elongation at Break: 4.0 %
- Flexural Strength: 159 MPa
- Flexural Modulus: 8.27 GPa
$ 1721/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength at Break: 41.4 MPa
- Elongation at Break: 60 %
- Flexural Strength: 55.2 MPa
- Flexural Modulus: 1.72 GPa
$ 2439/MT
- Tensile Strength at Break: 39.3 MPa
- Elongation at Break: >= 100 %
- Flexural Strength: 36.2 MPa
- Flexural Modulus: 0.862 GPa
- Izod Impact, Notched: 6.41 J/cm
- Deflection Temperature at 1.8 MPa (264 psi): 71.1 °C
$ 2254/MT
- Tensile Strength at Break: 33.8 MPa
- Flexural Strength: 20.7 MPa
- Flexural Modulus: 0.621 GPa
- Izod Impact, Notched: NB
$ 1766/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength at Break: 207 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 310 MPa
- Flexural Modulus: 10.3 GPa
$ 1519/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 2559/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1673/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 2307/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 49.0 MPa
- Elongation at Break: 25 %
- Flexural Strength: 76.5 MPa
$ 1843/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Melt Flow: 7.95 g/10 min
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 61.4 MPa
$ 1684/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 45 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 49.0 MPa
- Elongation at Break: 15 %
- Flexural Strength: 79.3 MPa
$ 1531/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Melt Flow: 3.5 g/10 min
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 43.0 MPa
$ 1490/MT
- Specific Gravity: 1.07 g/cc
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 48.3 MPa
- Elongation at Break: 35 %
- Flexural Strength: 77.2 MPa
$ 1546/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 37.2 MPa
- Elongation at Break: 35 %
- Flexural Strength: 58.6 MPa
$ 1541/MT
- Density: 1.10 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 3.0 %
$ 1597/MT
- Density: 1.18 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength at Break: 72.4 MPa
- Elongation at Break: 3.0 %
$ 1445/MT
- Density: 1.27 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength at Break: 93.1 MPa
- Elongation at Break: 2.0 %
$ 1467/MT
- Specific Gravity: 1.18 g/cc
- Tensile Strength at Break: 72.4 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 117 MPa
- Flexural Modulus: 5.86 GPa
$ 1980/MT
- Specific Gravity: 1.28 g/cc
- Tensile Strength at Break: 89.6 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 138 MPa
- Flexural Modulus: 8.27 GPa
$ 1881/MT
- Specific Gravity: 1.05 g/cc
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 15 %
- Flexural Strength: 73.1 MPa
- Flexural Modulus: 2.40 GPa
$ 1541/MT
- Density: 1.41 g/cc
- Water Absorption: 0.16 %
- Linear Mold Shrinkage, Flow: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 9.0 g/10 min
$ 1503/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.22 %
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 62.7 MPa
- Elongation at Break: 65 %
$ 1950/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.22 %
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 62.7 MPa
- Elongation at Break: 65 %
$ 1482/MT
- Density: 1.58 g/cc
- Filler Content: 25 %
- Water Absorption: 0.26 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1874/MT
- Density: 1.41 g/cc
- Water Absorption: 0.20 %
- Linear Mold Shrinkage, Flow: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 10.5 g/10 min
$ 1528/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1665/MT
- Specific Gravity: 1.07 g/cc
- Tensile Strength at Break: 43.4 MPa
- Elongation at Break: 18 %
- Flexural Strength: 74.5 MPa
- Flexural Modulus: 2.25 GPa
$ 1470/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength at Break: 45.5 MPa
- Elongation at Break: 150 %
- Flexural Strength: 43.4 MPa
- Flexural Modulus: 0.889 GPa
$ 1786/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength at Break: 80.7 MPa
- Elongation at Break: 50 %
- Flexural Strength: 107 MPa
- Flexural Modulus: 2.76 GPa
$ 1506/MT
- Tensile Strength at Break: 45.5 MPa
- Elongation at Break: >= 100 %
- Flexural Strength: 43.4 MPa
- Flexural Modulus: 0.889 GPa
- Izod Impact, Notched: NB
$ 2387/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength at Break: 80.7 MPa
- Elongation at Break: 50 %
- Flexural Strength: 107 MPa
- Flexural Modulus: 2.76 GPa
$ 1683/MT
- Density: 1.15 g/cc
- Water Absorption: 1.9 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 13 %
$ 1922/MT
- Specific Gravity: 1.15 g/cc
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: >= 50 %
- Flexural Strength: 40.7 MPa
- Flexural Modulus: 0.993 GPa
$ 2465/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength at Break: 29.0 MPa
- Elongation at Break: >= 150 %
- Flexural Strength: 27.6 MPa
- Flexural Modulus: 0.621 GPa
$ 1929/MT
- Specific Gravity: 1.22 g/cc
- Tensile Strength at Break: 103 MPa
- Elongation at Break: 5.0 %
- Flexural Strength: 145 MPa
- Flexural Modulus: 4.48 GPa
$ 1517/MT
- Specific Gravity: 1.28 g/cc
- Tensile Strength at Break: 84.8 MPa
- Flexural Strength: 126 MPa
- Flexural Modulus: 3.59 GPa
- Izod Impact, Notched: 1.98 J/cm
$ 1490/MT
- Density: 1.30 g/cc
- Filler Content: 20 %
- Water Absorption: 1.4 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Tensile Strength at Break: 134 MPa
$ 1491/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1457/MT
- Density: 1.48 g/cc
- Filler Content: 40 %
- Water Absorption: 0.90 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Tensile Strength at Break: 110 MPa
$ 1837/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1971/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1777/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1786/MT
- Specific Gravity: 0.954 g/cc
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 24.8 MPa
- Elongation at Break: 350 %
- Flexural Strength: 40.7 MPa
$ 2299/MT
- Density: 1.08 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 64.1 MPa
$ 1677/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 68.9 MPa
- Elongation at Break: 25 %
- Flexural Strength: 103 MPa
- Flexural Modulus: 2.86 GPa
$ 1738/MT
- Density: 1.50 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Hardness, Rockwell E: 60
- Tensile Strength at Break: 193 MPa
$ 2124/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 133 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 131 MPa
- Flexural Modulus: 7.58 GPa
$ 1861/MT
- Tensile Strength at Break: 123 MPa
- Flexural Strength: 194 MPa
- Flexural Modulus: 6.10 GPa
- Izod Impact, Notched: 1.87 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 260 °C
- Deflection Temperature at 1.8 MPa (264 psi): 246 °C
$ 2265/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength at Break: 82.7 MPa
- Elongation at Break: 60 %
- Flexural Strength: 117 MPa
- Flexural Modulus: 3.10 GPa
$ 2065/MT
- Specific Gravity: 0.920 g/cc
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 300 %
- Flexural Modulus: 0.214 GPa
$ 1459/MT
- Specific Gravity: 1.39 g/cc
- Tensile Strength at Break: 134 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 207 MPa
- Flexural Modulus: 8.62 GPa
$ 1460/MT
- Specific Gravity: 1.39 g/cc
- Tensile Strength at Break: 97.2 MPa
- Flexural Strength: 153 MPa
- Flexural Modulus: 5.03 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1694/MT
- Specific Gravity: 1.50 g/cc
- Tensile Strength at Break: 93.1 MPa
- Flexural Strength: 132 MPa
- Flexural Modulus: 6.07 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1668/MT
- Specific Gravity: 1.16 g/cc
- Tensile Strength at Break: 93.1 MPa
- Elongation at Break: 10 %
- Flexural Strength: 138 MPa
- Flexural Modulus: 3.45 GPa
$ 1757/MT
- Density: 1.43 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Hardness, Rockwell R: 123
- Tensile Strength at Break: 110 MPa
$ 1884/MT
- Tensile Strength at Break: 69.6 MPa
- Flexural Strength: 104 MPa
- Flexural Modulus: 3.40 GPa
- Izod Impact, Notched: 1.76 J/cm
$ 1812/MT
- Density: 1.22 g/cc
- Filler Content: 13 %
- Water Absorption: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm
- Hardness, Rockwell M: 95
$ 1979/MT
- Specific Gravity: 1.20 g/cc
- Melt Index of Compound: 10 - 14 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 64.1 MPa
- Elongation at Break: 100 %
- Flexural Strength: 93.1 MPa
$ 1657/MT
- Specific Gravity: 1.26 g/cc
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 10 %
- Flexural Strength: 96.5 MPa
- Flexural Modulus: 3.31 GPa
$ 1638/MT
- Density: 1.50 g/cc
- Filler Content: 43 %
- Water Absorption: 0.80 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 100
$ 2119/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Flexural Strength: 167 MPa
- Flexural Modulus: 4.83 GPa
- Izod Impact, Notched: 2.40 J/cm
$ 1951/MT
- Density: 1.33 g/cc
- Filler Content: 33 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 141 MPa
$ 1505/MT
- Density: 1.09 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 62.1 MPa
$ 1570/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 66.9 MPa
- Elongation at Break: 25 %
- Flexural Strength: 96.5 MPa
- Flexural Modulus: 2.76 GPa
$ 1847/MT
- Specific Gravity: 1.15 g/cc
- Tensile Strength at Break: 48.3 MPa
- Elongation at Break: 35 %
- Flexural Strength: 75.8 MPa
- Flexural Modulus: 2.07 GPa
$ 1776/MT
- Specific Gravity: 1.20 g/cc
- Melt Index of Compound: 16 - 19 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 63.4 MPa
- Elongation at Break: 90 %
- Flexural Strength: 93.1 MPa
$ 2295/MT
- Specific Gravity: 1.39 g/cc
- Tensile Strength at Break: 81.4 MPa
- Flexural Strength: 128 MPa
- Flexural Modulus: 5.03 GPa
- Izod Impact, Notched: 2.14 J/cm
- Deflection Temperature at 1.8 MPa (264 psi): 204 °C
$ 1621/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 39.3 MPa
- Elongation at Break: >= 100 %
- Flexural Strength: 36.2 MPa
- Flexural Modulus: 0.862 GPa
$ 2023/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 66.9 MPa
- Elongation at Break: 25 %
- Flexural Strength: 96.5 MPa
- Flexural Modulus: 2.76 GPa
$ 2546/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength at Break: 207 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 310 MPa
- Flexural Modulus: 10.3 GPa
$ 1815/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 112 MPa
- Flexural Strength: 174 MPa
- Flexural Modulus: 6.10 GPa
- Izod Impact, Notched: 1.82 J/cm
$ 1454/MT
- Specific Gravity: 1.20 g/cc
- Melt Index of Compound: 16 - 23 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 45 %
- Flexural Strength: 89.6 MPa
$ 1712/MT
- Density: 1.13 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength at Break: 82.7 MPa
$ 1762/MT
- Specific Gravity: 1.34 g/cc
- Tensile Strength at Break: 107 MPa
- Elongation at Break: 5.0 %
- Flexural Strength: 138 MPa
- Flexural Modulus: 6.21 GPa
$ 2214/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 62.1 MPa
- Flexural Strength: 96.5 MPa
$ 1630/MT
- Tensile Strength at Break: 65.5 MPa
- Elongation at Break: >= 150 %
- Flexural Strength: 42.1 MPa
- Flexural Modulus: 1.10 GPa
- Izod Impact, Notched: 1.60 J/cm
$ 1471/MT
- Density: 1.40 g/cc
- Filler Content: 30 %
- Water Absorption: 1.4 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength at Break: 165 MPa
$ 1528/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 179 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 262 MPa
- Flexural Modulus: 8.96 GPa
$ 1661/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 32.4 MPa
- Elongation at Break: >= 200 %
- Flexural Modulus: 1.38 GPa
$ 1679/MT
- Specific Gravity: 1.07 g/cc
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: >= 250 %
- Flexural Strength: 20.7 MPa
- Flexural Modulus: 0.621 GPa
$ 2464/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 25.5 MPa
- Elongation at Break: >= 200 %
- Flexural Strength: 33.8 MPa
$ 1580/MT
- Specific Gravity: 1.20 g/cc
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 75 %
- Flexural Strength: 89.6 MPa
- Flexural Modulus: 2.28 GPa
$ 2376/MT
- Density: 1.23 g/cc
- Filler Content: 13 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength at Break: 117 MPa
$ 1849/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 34.5 MPa
- Elongation at Break: >= 200 %
- Flexural Modulus: 1.52 GPa
$ 1816/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 236 MPa
- Flexural Modulus: 8.96 GPa
$ 1570/MT
- Specific Gravity: 1.20 g/cc
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 75 %
- Flexural Strength: 89.6 MPa
- Flexural Modulus: 2.28 GPa
$ 1632/MT
- Specific Gravity: 1.20 g/cc
- Melt Index of Compound: 10 - 14 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 64.1 MPa
- Elongation at Break: 100 %
- Flexural Strength: 93.1 MPa
$ 1486/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength at Break: 75.8 MPa
- Elongation at Break: 50 %
- Flexural Strength: 103 MPa
- Flexural Modulus: 2.76 GPa
$ 2311/MT
- Density: 1.07 g/cc
- Water Absorption: 0.20 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Hardness, Rockwell R: 75
- Tensile Strength, Yield: 43.4 MPa
$ 2082/MT
- Tensile Strength at Break: 65.5 MPa
- Elongation at Break: >= 150 %
- Flexural Strength: 42.1 MPa
- Flexural Modulus: 1.10 GPa
- Izod Impact, Notched: 1.60 J/cm
Delivery Polymer Chase Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
used crude oil tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.