$ 1959/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 52.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1696/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 52.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1463/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 44.0 MPa
$ 1644/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 53.0 MPa
$ 1481/MT
- Density: 1.27 g/cc
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 28.0 MPa
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 110 %
$ 1448/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 83
- Hardness, Shore D: 73
- Secant Modulus, MD: 1.87 GPa
- Secant Modulus, TD: 1.825 GPa
$ 1446/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 46.0 MPa
$ 1723/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 49.0 MPa
$ 1751/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 72
- Tensile Strength at Break: 31.0 MPa
$ 1481/MT
- Density: 1.17 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 40
- Tensile Strength, Ultimate: 33.8 MPa
$ 1512/MT
- Bulk Density: 0.817 g/cc
- Melt Density: 1.20 g/cc @Temperature 285 °C
- Viscosity Measurement: 0.78 - 0.82
- Melting Point: 240 °C
- Acetaldehyde: <3ppm
$ 1812/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1968/MT
- Specific Gravity: 1.33 g/cc
- Bulk Density: 0.715 g/cc
- Density: 1.31 g/cc
- Melt Density: 1.20 g/cc @Temperature 285 °C
- Water Vapor Transmission: 39.0 g/m²/day
$ 1605/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 88
- Tensile Strength at Break: 47.6 MPa
$ 1499/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.19 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 24.0 MPa
$ 1876/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 35.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 2553/MT
- Specific Gravity: 1.33 g/cc
- Bulk Density: 0.715 g/cc
- Density: 1.31 g/cc
- Melt Density: 1.20 g/cc @Temperature 285 °C
- Water Vapor Transmission: 39.0 g/m²/day
$ 1604/MT
- Density: 1.20 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 84
- Tensile Strength, Ultimate: 33.1 MPa
$ 1628/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.40 % @Time 86400 sec
- Water Vapor Transmission: 146 g/m²/day
- Oxygen Transmission Rate: 940 cc/m²/day @Pressure 0.101 MPa, Temperature 30.0 °C
- Viscosity Measurement: 1.23
$ 2324/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.40 %
- Tensile Strength at Break: 33.1 MPa
$ 2245/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 68
- Tensile Strength, Ultimate: 30.3 MPa
$ 1451/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 106
- Tensile Strength at Break: 29.0 MPa
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 109 %
$ 1857/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.15 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 104
- Tensile Strength at Break: 38.0 MPa
$ 1462/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Ultimate: 53.0 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 2031/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 0.16 %
- Thickness: 3000 microns
- Hardness, Rockwell R: 113
- Tensile Strength at Break: 25.0 MPa
$ 2319/MT
- Density: 1.13 g/cc
- Tensile Strength, Yield: 12.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 29 %
- Tensile Modulus: 0.156 GPa
$ 1495/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 1.3 %
- Collected Volatile Condensable Material: 0.90 %
- Hardness, Rockwell R: 26
- Tensile Strength at Break: 30.7 MPa
$ 1715/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1841/MT
- Density: 1.21 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 95
- Tensile Strength, Ultimate: 40.7 MPa
$ 1992/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 68
- Tensile Strength, Ultimate: 30.3 MPa
$ 2017/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 109
- Tensile Strength at Break: 32.0 MPa
- Tensile Strength, Yield: 58.0 MPa
$ 2330/MT
- Density: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 33.1 MPa
$ 1717/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1546/MT
- Density: 1.16 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Tensile Strength, Ultimate: 20.0 MPa
- Tensile Strength, Yield: 17.2 MPa
$ 2238/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 49.0 MPa
$ 1474/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 85
- Tensile Strength at Break: 35.8 MPa
$ 1819/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 3.9 %
$ 1686/MT
- Density: 1.17 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 40
- Tensile Strength, Ultimate: 33.8 MPa
$ 1860/MT
- Density: 1.31 g/cc
- Water Absorption: 2.1 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 112
- Tensile Strength, Ultimate: 47.0 MPa
$ 1497/MT
- Specific Gravity: 1.31 g/cc
- Density: 1.31 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 26.0 MPa
$ 1556/MT
- Density: 1.12 g/cc
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 34 %
- Tensile Modulus: 0.131 GPa
$ 1785/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 1566/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 85
- Tensile Strength at Break: 38.3 MPa
$ 2032/MT
- Density: 1.27 g/cc
- Hardness, Rockwell R: 106
- Tensile Strength, Ultimate: 29.0 MPa
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 109 %
$ 1549/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 106
- Tensile Strength at Break: 29.0 MPa
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 109 %
$ 2367/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Rockwell R: 106
- Tensile Strength at Break: 29.0 MPa
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 109 %
$ 1445/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1583/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.35 % @Time 86400 sec
- Water Vapor Transmission: 132 g/m²/day
- Oxygen Transmission Rate: 841 cc/m²/day @Pressure 0.101 MPa, Temperature 30.0 °C
- Viscosity Measurement: 1.05
$ 1495/MT
- Density: 0.890 g/cc
- Water Vapor Transmission: 38.2 g/m²/day
- Oxygen Transmission: 10.4 cc-mm/m²-24hr-atm @Temperature 30.0 °C
- Carbon Dioxide Transmission: 42.7 cc-mm/m²-24hr-atm @Temperature 30.0 °C
- Thickness: 63.5 microns
$ 1885/MT
- Density: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 88
- Tensile Strength, Ultimate: 47.6 MPa
$ 1592/MT
- Density: 1.32 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 3.8 %
- Tensile Modulus: 2.47 GPa
$ 1605/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 43.0 MPa
$ 1758/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 2466/MT
- Density: 1.21 g/cc
- Water Absorption: 1.8 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 98
- Tensile Strength, Ultimate: 42.7 MPa
$ 1740/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 1.7 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 95
- Tensile Strength at Break: 40.7 MPa
$ 2139/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 35.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1801/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength, Ultimate: 46.0 MPa
- Tensile Strength, Ultimate: 51.0 MPa
$ 1855/MT
- Density: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 33.1 MPa
$ 1579/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.19 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 24.0 MPa
$ 2266/MT
- Specific Gravity: 1.16 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 1.2 %
- Tensile Strength at Break: 20.0 MPa
$ 1603/MT
- Bulk Density: 0.800 g/cc
- Bulk Density: 0.870 g/cc
- Melt Density: 1.20 g/cc @Temperature 285 °C
- Viscosity Measurement: 0.78 - 0.82
- Melting Point: 240 °C
$ 1626/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 43.0 MPa
$ 1783/MT
- Specific Gravity: 1.27 g/cc
- Density: 1.27 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Water Vapor Transmission: 7.00 g/m²/day
- Oxygen Transmission: 10.0 cc-mm/m²-24hr-atm
$ 1728/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.40 %
- Tensile Strength at Break: 33.1 MPa
$ 1622/MT
- Density: 1.27 g/cc
- Water Absorption: 2.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 71
- Tensile Strength, Ultimate: 33.1 MPa
$ 2022/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.60 %
- Tensile Strength at Break: 36.5 MPa
$ 1487/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 54.0 MPa
- Tensile Strength, Yield: 44.0 MPa
$ 2060/MT
- Density: 1.20 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 94
- Tensile Strength, Ultimate: 37.9 MPa
$ 1514/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength, Ultimate: 46.0 MPa
- Tensile Strength, Ultimate: 51.0 MPa
$ 2106/MT
- Density: 1.16 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Tensile Strength, Ultimate: 20.0 MPa
- Tensile Strength, Yield: 17.2 MPa
$ 1834/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 20.0 g/m²/day
- Oxygen Transmission Rate: 71.0 cc/m²/day @Pressure 0.101 MPa, Temperature 30.0 °C
- Viscosity Measurement: 0.70
- Thickness: 50.0 microns
$ 1884/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 20.0 g/m²/day
- Oxygen Transmission Rate: 71.0 cc/m²/day @Pressure 0.101 MPa, Temperature 30.0 °C
- Viscosity Measurement: 0.70
- Thickness: 50.0 microns
$ 1707/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 20.0 g/m²/day
- Oxygen Transmission Rate: 71.0 cc/m²/day @Pressure 0.101 MPa, Temperature 30.0 °C
- Viscosity Measurement: 0.70
- Thickness: 50.0 microns
$ 1645/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 20.0 g/m²/day
- Oxygen Transmission Rate: 71.0 cc/m²/day @Pressure 0.101 MPa, Temperature 30.0 °C
- Viscosity Measurement: 0.70
- Thickness: 50.0 microns
$ 1921/MT
- Density: 1.28 g/cc
- Water Absorption: 0.15 % @Time 86400 sec
- CTE, linear: 75.2 µm/m-°C @Temperature -30.0 - 30.0 °C
- Specific Heat Capacity: 1.30 J/g-°C @Temperature 60.0 °C
- Specific Heat Capacity: 1.72 J/g-°C @Temperature 100 °C
$ 1786/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 54.0 MPa
- Tensile Strength, Yield: 44.0 MPa
$ 1982/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 1.0 %
- Tensile Strength at Break: 27.6 MPa
$ 1449/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 81
- Tensile Strength at Break: 34.5 MPa
$ 1650/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 7.60 g/m²/day
- Oxygen Transmission Rate: 23.0 cc/m²/day @Pressure 0.101 MPa, Temperature 30.0 °C
- Viscosity Measurement: 0.70
- Thickness: 250 microns
$ 2153/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 73
- Tensile Strength at Break: 31.7 MPa
$ 2584/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength at Break: 43.4 MPa
$ 1574/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 1.60 mm
- Hardness, Rockwell R: 106
$ 1880/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 55
- Tensile Strength, Ultimate: 27.6 MPa
$ 2584/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 55
- Tensile Strength, Ultimate: 27.6 MPa
$ 1656/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 26.0 MPa
- Tensile Strength, Yield: 56.0 MPa
$ 2046/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Hardness, Rockwell R: 26
- Tensile Strength at Break: 30.7 MPa
- Tensile Strength, Yield: 23.5 MPa
$ 1482/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 68
- Tensile Strength at Break: 30.3 MPa
$ 1763/MT
- Specific Gravity: 1.27 g/cc
- Density: 1.27 g/cc
- Water Absorption: 0.13 %
- Water Absorption: 0.13 %
- Hardness, Rockwell R: 106
$ 1908/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 44.0 MPa
$ 1614/MT
- Density: 1.19 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Water Vapor Transmission: 4.00 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 11.0 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission: 32.0 cc-mm/m²-24hr-atm
$ 1750/MT
- Density: 1.19 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Water Vapor Transmission: 4.00 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 10.0 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission: 44.0 cc-mm/m²-24hr-atm
$ 1958/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.18 % @Time 86400 sec
- Thickness: 2970 microns
- Hardness, Rockwell R: 114
- Tensile Strength at Break: 46.0 MPa
$ 1654/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 44.0 MPa
$ 1901/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1907/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1461/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 52.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1999/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 44.0 MPa
$ 2377/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1882/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 52.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 2291/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 52.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1445/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 44.0 MPa
$ 1477/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 51.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1672/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 43.0 MPa
$ 1484/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 1607/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 2.3 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 1.8 %
- Hardness, Rockwell R: 82
$ 2153/MT
- Density: 1.17 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 40
- Tensile Strength, Ultimate: 33.8 MPa
$ 1546/MT
- Density: 1.28 g/cc
- Water Absorption: 0.15 % @Time 86400 sec
- CTE, linear: 76.8 µm/m-°C @Temperature -30.0 - 30.0 °C
- Specific Heat Capacity: 1.30 J/g-°C @Temperature 60.0 °C
- Specific Heat Capacity: 1.72 J/g-°C @Temperature 100 °C
$ 1799/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1463/MT
- Density: 1.17 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 40
- Tensile Strength, Ultimate: 33.8 MPa
$ 2247/MT
- Density: 1.17 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 40
- Tensile Strength, Ultimate: 33.8 MPa
$ 1919/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.25 %
- Hardness, Rockwell R: 94
$ 2165/MT
- Hardness, Rockwell R: 117
- Tensile Strength, Ultimate: 26.0 MPa
- Tensile Strength, Yield: 51.0 MPa
- Elongation at Break: 72 %
- Elongation at Yield: 4.0 %
$ 2167/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.40 %
- Tensile Strength at Break: 38.9 MPa
$ 1682/MT
- Density: 1.18 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 59
- Tensile Strength, Ultimate: 39.3 MPa
$ 2211/MT
- Specific Gravity: 1.22 g/cc
- Water Vapor Transmission: 8.00 g/m²/day
- Oxygen Transmission: 18.0 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 87.0 cc-mm/m²-24hr-atm
- Thickness: 250 microns
$ 1516/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 28.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 2032/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.30 %
- Tensile Strength at Break: 37.9 MPa
$ 2101/MT
- Density: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 33.1 MPa
$ 1574/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 49.0 MPa
$ 1473/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.2 %
$ 1825/MT
- Density: 1.21 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 90
- Tensile Strength, Ultimate: 40.0 MPa
$ 1444/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.2 %
$ 1952/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 46.0 MPa
$ 2353/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 43.0 MPa
$ 1704/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 49.0 MPa
$ 2191/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 46.0 MPa
- Tensile Strength at Break: 51.0 MPa
$ 1814/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 46.0 MPa
- Tensile Strength at Break: 51.0 MPa
$ 1944/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 43.0 MPa
$ 2287/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 43.0 MPa
$ 1977/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.2 %
$ 2047/MT
- Density: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 80
- Tensile Strength, Ultimate: 36.5 MPa
$ 1484/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 92
- Tensile Strength at Break: 38.9 MPa
$ 1709/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 1.60 mm
- Hardness, Rockwell R: 106
$ 2132/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 1735/MT
- Specific Gravity: 1.23 g/cc
- Density: 1.23 g/cc
- Water Absorption: 0.13 %
- Water Absorption: 0.13 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
$ 2052/MT
- Density: 1.13 g/cc
- Elongation at Break: >= 50 %
- Tensile Modulus: 0.132 GPa
- Charpy Impact Unnotched: NB
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
$ 1516/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.35 %
- Viscosity Measurement: 1.05
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
$ 1830/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 24.0 MPa
- Tensile Strength, Yield: 57.0 MPa
$ 1988/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 6.70 g/m²/day
- Oxygen Transmission: 7.40 cc-mm/m²-24hr-atm @Temperature 30.0 °C
- Viscosity Measurement: 0.70
- Thickness: 250 microns
$ 2197/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 73
- Tensile Strength at Break: 31.7 MPa
$ 1931/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.40 %
- Hardness, Rockwell R: 78
$ 1922/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 51
- Tensile Strength, Ultimate: 33.1 MPa
$ 1962/MT
- Density: 1.28 g/cc
- Water Absorption: 0.15 % @Time 86400 sec
- CTE, linear: 76.1 µm/m-°C @Temperature -30.0 - 30.0 °C
- Specific Heat Capacity: 1.30 J/g-°C @Temperature 60.0 °C
- Specific Heat Capacity: 1.72 J/g-°C @Temperature 100 °C
$ 1572/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 1.0 %
- Hardness, Rockwell R: 55
$ 1712/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 2207/MT
- Density: 1.21 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 95
- Tensile Strength, Ultimate: 40.7 MPa
$ 2116/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 2115/MT
- Density: 1.20 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 33.1 MPa
$ 1820/MT
- Density: 1.28 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Water Vapor Transmission: 7.00 g/m²/day
- Oxygen Transmission: 7.00 cc-mm/m²-24hr-atm
- Viscosity Measurement: 0.71
$ 1548/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 2449/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 0.70 %
- Tensile Strength at Break: 31.0 MPa
$ 1937/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 68
- Tensile Strength at Break: 30.3 MPa
$ 1578/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 1.2 % @Time 86400 sec
- Hardness, Rockwell R: 12
- Tensile Strength at Break: 27.6 MPa
- Tensile Strength, Yield: 21.4 MPa
$ 1506/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.2 % @Time 86400 sec
- Hardness, Rockwell R: 60
- Tensile Strength at Break: 31.0 MPa
- Tensile Strength, Yield: 30.3 MPa
$ 1609/MT
- Density: 1.21 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 88
- Tensile Strength, Ultimate: 37.2 MPa
$ 1454/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 1.3 %
- Tensile Strength at Break: 30.3 MPa
$ 1947/MT
- Specific Gravity: 1.205 g/cc
- Water Absorption: 1.7 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 98
- Tensile Strength at Break: 52.4 MPa
$ 1459/MT
- Density: 1.27 g/cc
- Water Vapor Transmission: 7.00 g/m²/day
- Oxygen Transmission: 10.0 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 49.0 cc-mm/m²-24hr-atm
- Thickness: 250 microns
$ 1631/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.40 % @Time 86400 sec
- Viscosity Measurement: 1.16
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
$ 1627/MT
- Bulk Density: 0.827 g/cc
- Viscosity Measurement: 0.26 - 0.32
- Glass Transition Temp, Tg: 45.0 - 48.0 °C
- Color: Pale Amber
- Form: Pellets
$ 1783/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 55
- Tensile Strength, Ultimate: 27.6 MPa
$ 1892/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 0.490 g/m²/day
- Oxygen Transmission: 23.0 cc-mm/m²-24hr-atm
- Viscosity Measurement: 0.70
- Thickness: 254 microns
$ 1729/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Collected Volatile Condensable Material: 1.3 %
- Tensile Strength at Break: 30.3 MPa
$ 1740/MT
- Density: 1.30 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 106
- Tensile Strength, Ultimate: 27.0 MPa
$ 1521/MT
- Density: 1.27 g/cc
- Water Absorption: 2.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 59
- Tensile Strength, Ultimate: 29.6 MPa
$ 2379/MT
- Density: 1.17 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 40
- Tensile Strength, Ultimate: 33.8 MPa
$ 1911/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 106
- Tensile Strength at Break: 52.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1746/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 26.0 MPa
$ 2000/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 29.0 MPa
- Tensile Strength at Break: 30.0 MPa
$ 1457/MT
- Specific Gravity: 1.27 g/cc
- Density: 1.27 g/cc
- Water Absorption: 0.13 %
- Water Absorption: 0.13 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
$ 1513/MT
- Density: 1.19 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 72
- Tensile Strength, Ultimate: 31.0 MPa
$ 1938/MT
- Density: 1.20 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Ultimate: 56.0 MPa
$ 1812/MT
- Specific Gravity: 1.27 g/cc
- Density: 1.27 g/cc
- Water Absorption: 0.20 %
- Water Absorption: 0.20 %
- Thickness: 3000 microns
$ 1927/MT
- Bulk Density: 0.670 g/cc
- Bulk Density: 0.730 g/cc
- Density: 1.20 g/cc
- Water Vapor Transmission: 5.00 g/m²/day
- Oxygen Transmission: 13.0 cc-mm/m²-24hr-atm
$ 1833/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength at Break: 51.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 2088/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Break: 120 %
$ 1569/MT
- Specific Gravity: 1.27 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 106
- Tensile Strength at Break: 28.0 MPa
$ 2110/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength at Break: 33.1 MPa
$ 1807/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.40 %
- Viscosity Measurement: 1.16
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
$ 1542/MT
- Density: 1.19 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 43.4 MPa
$ 1640/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.19 % @Time 86400 sec
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 24.0 MPa
$ 1864/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.2 %
$ 1793/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 56.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 3.8 %
$ 1448/MT
- Density: 1.19 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 72
- Tensile Strength, Ultimate: 31.0 MPa
$ 1519/MT
- Density: 1.30 g/cc
- Water Vapor Transmission: 25.0 g/m²/day
- Oxygen Transmission: 3.90 cc-mm/m²-24hr-atm @Temperature 30.0 °C
- Viscosity Measurement: 0.70
- Thickness: 50.0 microns
$ 1531/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1543/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1448/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 24.0 MPa
- Tensile Strength, Yield: 48.0 MPa
$ 2316/MT
- Specific Gravity: 1.27 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 106
- Tensile Strength at Break: 28.0 MPa
Delivery Polymer Eastman Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.