$ 1469/MT
- Density: 1.51 g/cc
- Filler Content: 40 %
- Hardness, Rockwell M: 99
- Tensile Strength: 77.2 MPa
- Elongation at Break: 1.1 %
$ 1503/MT
- Density: 1.44 g/cc
- Tensile Strength: 65.5 MPa
- Elongation at Break: 3.7 %
- Flexural Strength: 97.2 MPa
- Flexural Modulus: 3.03 GPa
$ 1659/MT
- Density: 0.919 g/cc
- Moisture Absorption at Equilibrium: 0.050 % @Temperature 22.8 °C
- Ball Indentation Hardness: 100 MPa
- Tensile Strength, Yield: 32.99 MPa
- Elongation at Break: >= 30 %
$ 1927/MT
- Specific Gravity: 1.12 g/cc
- Tensile Strength at Break: 142 MPa @Temperature 22.8 °C
- Elongation at Break: 5.94 % @Temperature 22.8 °C
- Flexural Strength: 266 MPa @Temperature 22.8 °C
- Flexural Modulus: 20.872 GPa @Temperature 22.8 °C
$ 1877/MT
- Density: 1.44 g/cc
- Filler Content: 15 %
- Tensile Strength: 103 MPa
- Elongation at Break: 3.8 %
- Flexural Strength: 150 MPa
$ 1853/MT
- Density: 1.59 g/cc @Temperature 23.0 °C
- Filler Content: 40 %
- Water Absorption: 1.2 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 2.18 % @Temperature 80.0 °C, Time 86400 sec
- Hardness, Shore D: 84 @Temperature 23.0 °C
$ 1581/MT
- Hardness, Rockwell R: 110
- Tensile Strength, Ultimate: 58.6 MPa
- Elongation at Break: 40 %
- Flexural Strength: 88.3 MPa
- Flexural Modulus: 2.76 GPa
$ 1792/MT
- Specific Gravity: 1.48 g/cc
- Density: 1.48 g/cc
- Water Absorption: <= 0.10 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 0.10 %
- Hardness, Rockwell M: 85
$ 1792/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 0.16 %
- Water Absorption at Saturation: 0.29 %
- Tensile Strength, Yield: 110 MPa
- Elongation at Break: 5.0 %
$ 1459/MT
- Density: 1.15 - 1.16 g/cc
- Water Absorption: 1.2 %
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 68.9 MPa
- Elongation at Break: 25 %
$ 1691/MT
- Density: 1.54 g/cc
- Water Absorption: 0.22 %
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 48.3 MPa
- Elongation at Break: 17.5 %
$ 1446/MT
- Density: 1.70 g/cc
- Filler Content: 40 %
- Water Absorption: 0.063 % @Time 86400 sec
- Hardness, Shore D: 88
- Tensile Strength: 42.7 MPa
$ 1675/MT
- Density: 1.44 g/cc
- Filler Content: 20 %
- Tensile Strength: 36.5 MPa
- Elongation at Break: 0.80 %
- Tensile Modulus: 7.58 GPa
$ 1761/MT
- Density: 1.38 g/cc
- Water Absorption: 0.64 % @Temperature 23.0 °C
- Water Absorption: 2.26 % @Temperature 80.0 °C
- Hardness, Shore D: 80 @Temperature 23.0 °C
- Tensile Strength: 54.4 MPa @Temperature 23.0 °C
$ 1542/MT
- Density: 1.31 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C
- Water Absorption: 2.58 % @Temperature 80.0 °C
- Hardness, Shore D: 80 @Temperature 23.0 °C
- Tensile Strength: 57.4 MPa @Temperature 23.0 °C
$ 1834/MT
- Specific Gravity: 1.78 g/cc
- Density: 1.77 g/cc
- Water Absorption: 0.020 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell R: 100
- Tensile Strength at Break: 53.8 MPa @Temperature 22.8 °C
$ 2085/MT
- Density: 1.14 g/cc
- Water Absorption: 1.2 %
- Water Absorption at Saturation: 8.5 %
- Hardness, Rockwell M: 90
- Tensile Strength, Yield: 80.0 MPa
$ 1552/MT
- Density: 1.71 g/cc
- Filler Content: 45 %
- Hardness, Rockwell M: 104
- Tensile Strength: 93.1 MPa
- Elongation at Break: 1.9 %
$ 1988/MT
- Filler Content: 64 %
- Tensile Strength: 14.5 MPa
- Elongation at Break: 1.3 %
- Tensile Modulus: 2.83 GPa
- Flexural Strength: 24.1 MPa
$ 1504/MT
- Specific Gravity: 1.64 g/cc
- Density: 1.64 g/cc
- Water Absorption at Saturation: 0.020 %
- Tensile Strength at Break: 184 MPa
- Elongation at Break: 1.9 %
$ 2566/MT
- Specific Gravity: 1.27 g/cc
- Water Absorption: 0.25 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 1.25 % @Temperature 22.8 °C
- Hardness, Rockwell M: 109
- Tensile Strength at Break: 105 MPa @Temperature 22.8 °C
$ 1541/MT
- Density: 1.45 g/cc @Temperature 23.0 °C
- Filler Content: 15 %
- Water Absorption: 0.44 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 1.55 % @Temperature 80.0 °C, Time 86400 sec
- Hardness, Shore D: 87 @Temperature 23.0 °C
$ 1630/MT
- Density: 1.36 g/cc
- Filler Content: 0.00 %
- Water Absorption: 0.050 % @Time 86400 sec
- Hardness, Rockwell M: 101
- Hardness, Shore D: 89
$ 1903/MT
- Specific Gravity: 1.42 g/cc
- Water Absorption: 0.25 % @Time 86400 sec
- Water Absorption at Saturation: 0.90 %
- Hardness, Rockwell M: 94
- Hardness, Rockwell R: 120
$ 1863/MT
- Specific Gravity: 1.38 g/cc
- Density: 1.38 g/cc
- Water Absorption: 0.10 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 0.50 % @Temperature 22.8 °C
- Hardness, Rockwell M: 94
$ 1523/MT
- Density: 1.41 g/cc
- Water Absorption: 0.43 % @Temperature 23.0 °C
- Water Absorption: 1.7 % @Temperature 80.0 °C
- Hardness, Shore D: 78 @Temperature 23.0 °C
- Tensile Strength: 44.1 MPa @Temperature 23.0 °C
$ 1663/MT
- Specific Gravity: 1.31 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Tensile Strength, Yield: 64.8 MPa
- Elongation at Break: 50 %
- Tensile Modulus: 2.93 GPa
$ 1619/MT
- Specific Gravity: 1.16 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Water Absorption at Saturation: 6.3 % @Temperature 22.8 °C
- Tensile Strength, Yield: 110 MPa
- Elongation at Break: 4.0 %
$ 2132/MT
- Density: 1.90 g/cc
- Hardness, Rockwell M: 104
- Tensile Strength: 84.8 MPa
- Elongation at Break: 1.1 %
- Elongation at Break: 1.8 %
$ 1553/MT
- Density: 1.57 g/cc @Temperature 23.0 °C
- Filler Content: 40 %
- Water Absorption: 0.42 % @Temperature 23.0 °C, Time 86400 sec
- Hardness, Shore D: 85 @Temperature 23.0 °C
- Tensile Strength, Yield: 65.0 MPa @Temperature 23.0 °C
$ 1539/MT
- Density: 1.49 g/cc
- Filler Content: 35 %
- Water Absorption: 0.17 % @Time 86400 sec
- Hardness, Shore D: 90
- Tensile Strength: 76.5 MPa
$ 1990/MT
- Specific Gravity: 1.56 g/cc
- Density: 1.49 g/cc
- Water Absorption: 0.15 % @Time 86400 sec
- Hardness, Rockwell M: 81
- Tensile Strength, Yield: 60.0 MPa
$ 2056/MT
- Specific Gravity: 1.08 g/cc
- Density: 0.830 g/cc
- Water Absorption: 0.23 % @Temperature 22.8 °C
- Tensile Strength at Break: 67.6 MPa @Temperature 22.8 °C
- Elongation at Break: 16.3 % @Temperature 22.8 °C
$ 1775/MT
- Density: 1.34 g/cc @Temperature 23.0 °C
- Water Absorption: 0.59 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 1.88 % @Temperature 80.0 °C, Time 86400 sec
- Hardness, Shore D: 90 @Temperature 23.0 °C
- Tensile Strength, Yield: 153 MPa @Temperature 23.0 °C
$ 1647/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.050 %
- Tensile Strength, Yield: 130 MPa
- Elongation at Yield: 11 %
$ 1600/MT
- Density: 1.35 g/cc
- Water Absorption: 1.04 % @Temperature 23.0 °C
- Water Absorption: 2.62 % @Temperature 80.0 °C
- Hardness, Shore D: 84 @Temperature 23.0 °C
- Tensile Strength: 77.0 MPa @Temperature 23.0 °C
$ 1653/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.19 % @Time 86400 sec
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 68.9 MPa
- Elongation at Break: 140 %
$ 2415/MT
- Density: 1.42 g/cc @Temperature 23.0 °C
- Filler Content: 15 %
- Water Absorption: 0.51 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 1.57 % @Temperature 80.0 °C, Time 86400 sec
- Hardness, Shore D: 88 @Temperature 23.0 °C
$ 1559/MT
- Density: 1.42 g/cc @Temperature 23.0 °C
- Filler Content: 15 %
- Water Absorption: 0.51 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 1.57 % @Temperature 80.0 °C, Time 86400 sec
- Hardness, Shore D: 88 @Temperature 23.0 °C
$ 1538/MT
- Density: 1.49 g/cc
- Water Absorption: 0.080 % @Temperature 23.0 °C
- Water Absorption: 0.53 % @Temperature 80.0 °C
- Hardness, Shore D: 86 @Temperature 23.0 °C
- Tensile Strength: 93.0 MPa @Temperature 23.0 °C
$ 1754/MT
- Density: 1.43 g/cc
- Filler Content: 35 %
- Hardness, Shore D: 88
- Tensile Strength: 35.9 MPa
- Elongation at Break: 1.5 %
$ 2226/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Water Absorption at Saturation: 0.020 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell M: 104
- Tensile Strength, Yield: 60.0 MPa @Temperature 22.8 °C
$ 1558/MT
- Density: 1.59 g/cc
- Filler Content: 20 %
- Hardness, Rockwell M: 85
- Tensile Strength: 57.9 MPa
- Elongation at Break: 3.0 %
$ 1461/MT
- Density: 1.45 g/cc
- Filler Content: 30 %
- Water Absorption: 0.070 % @Time 86400 sec
- Hardness, Rockwell M: 98
- Hardness, Shore D: 88
$ 1802/MT
- Density: 1.50 g/cc
- Filler Content: 30 %
- Tensile Strength: 51.7 MPa
- Elongation at Break: 3.8 %
- Elongation at Break: 4.0 %
$ 1669/MT
- Density: 1.47 g/cc
- Filler Content: 30 %
- Water Absorption: 0.050 % @Time 86400 sec
- Hardness, Rockwell M: 98
- Hardness, Shore D: 87
$ 1577/MT
- Filler Content: 40 %
- Tensile Strength: 84.1 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 8.27 GPa
- Flexural Strength: 119 MPa
$ 1807/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 0.020 % @Time 86400 sec
- Tensile Strength, Yield: 50.3 MPa
- Tensile Modulus: 2.83 GPa
- Flexural Strength: 103 MPa
$ 2203/MT
- Density: 1.32 g/cc
- Filler Content: 0.00 %
- Tensile Strength: 97.2 MPa
- Elongation at Break: 2.8 %
- Elongation at Break: 3.0 %
$ 1865/MT
- Density: 1.65 g/cc
- Filler Content: 30 %
- Hardness, Shore D: 86
- Tensile Strength: 36.5 MPa
- Elongation at Break: 1.1 %
$ 2050/MT
- Density: 1.47 g/cc
- Filler Content: 30 %
- Water Absorption: 0.060 % @Time 86400 sec
- Hardness, Rockwell M: 90
- Hardness, Shore D: 85
$ 1860/MT
- Density: 1.424 g/cc
- Hardness, Shore D: 90 @Temperature 23.0 °C
- Elongation at Yield: 2.6 % @Temperature 23.0 °C
- Flexural Strength: 136 MPa @Temperature 23.0 °C
- Flexural Modulus: 4.90 GPa @Temperature 23.0 °C
$ 1448/MT
- Density: 1.54 g/cc
- Filler Content: 40 %
- Hardness, Shore D: 82
- Tensile Strength: 45.5 MPa
- Elongation at Break: 1.2 %
$ 2069/MT
- Density: 1.38 g/cc @Temperature 23.0 °C
- Water Absorption: 0.47 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 1.65 % @Temperature 80.0 °C, Time 86400 sec
- Hardness, Shore D: 90 @Temperature 23.0 °C
- Tensile Strength, Yield: 118 MPa @Temperature 23.0 °C
$ 1615/MT
- Density: 1.49 g/cc
- Water Absorption: 0.11 %
- Hardness, Rockwell M: 103
- Tensile Strength, Yield: 157 MPa
- Elongation at Break: 2.2 %
$ 1559/MT
- Density: 1.44 g/cc
- Water Absorption: 0.060 %
- Hardness, Rockwell M: 107
- Tensile Strength, Yield: 186 MPa
- Elongation at Break: 1.1 %
$ 1700/MT
- Density: 1.35 g/cc
- Filler Content: 5.0 %
- Hardness, Rockwell M: 102
- Hardness, Shore D: 87
- Tensile Strength: 105 MPa
$ 1483/MT
- Density: 1.65 g/cc
- Water Absorption: 0.060 % @Temperature 23.0 °C
- Water Absorption: 0.26 % @Temperature 80.0 °C
- Hardness, Shore D: 90 @Temperature 23.0 °C
- Tensile Strength: 77.0 MPa @Temperature 23.0 °C
$ 2395/MT
- Density: 1.88 g/cc @Temperature 23.0 °C
- Filler Content: 20 %
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Hardness, Shore D: 65 @Temperature 23.0 °C
- Tensile Strength, Yield: 15.0 MPa @Temperature 23.0 °C
$ 1591/MT
- Specific Gravity: 0.900 g/cc
- Density: 0.913 g/cc
- Water Absorption: 0.010 - 0.030 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell R: 90
- Tensile Strength at Break: 32.4 MPa @Temperature 22.8 °C
$ 1570/MT
- Density: 1.28 g/cc
- Water Absorption: 1.62 % @Temperature 23.0 °C
- Water Absorption: 3.12 % @Temperature 80.0 °C
- Hardness, Shore D: 85 @Temperature 23.0 °C
- Tensile Strength: 88.0 MPa @Temperature 23.0 °C
$ 1719/MT
- Specific Gravity: 1.38 g/cc
- Density: 1.38 g/cc
- Hardness, Rockwell M: 99
- Tensile Strength at Break: 95.0 MPa
- Tensile Strength, Yield: 94.975 MPa @Temperature 22.8 °C
$ 1483/MT
- Density: 1.54 g/cc
- Hardness, Rockwell M: 106
- Tensile Strength: 62.1 MPa
- Elongation at Break: 1.0 %
- Elongation at Break: 2.1 %
$ 1848/MT
- Density: 1.51 g/cc
- Filler Content: 45 %
- Tensile Strength: 82.7 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 128 MPa
$ 2420/MT
- Density: 1.42 g/cc
- Water Absorption: 0.14 % @Temperature 23.0 °C
- Water Absorption: 0.66 % @Temperature 80.0 °C
- Hardness, Shore D: 89 @Temperature 23.0 °C
- Elongation at Yield: 2.9 % @Temperature 23.0 °C
$ 2112/MT
- Specific Gravity: 1.42 g/cc
- Water Absorption: 0.19 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 1.1 % @Temperature 22.8 °C
- Hardness, Rockwell M: 114
- Tensile Strength at Break: 139 MPa @Temperature 22.8 °C
$ 1778/MT
- Density: 1.51 g/cc @Temperature 23.0 °C
- Filler Content: 10 %
- Filler Content: 15 %
- Water Absorption: 0.35 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 1.5 % @Temperature 80.0 °C, Time 86400 sec
$ 1812/MT
- Density: 1.35 g/cc
- Filler Content: 10 %
- Hardness, Rockwell M: 98
- Tensile Strength: 117 MPa
- Elongation at Break: 3.5 %
$ 1639/MT
- Density: 1.14 - 1.15 g/cc
- Water Absorption: 0.75 %
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 60.7 MPa
- Elongation at Break: 25 %
$ 1514/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: <= 0.30 %
- Water Absorption at Saturation: 0.50 %
- Tensile Strength, Yield: 13.0 MPa
$ 1459/MT
- Filler Content: 60 %
- Hardness, Shore D: 65
- Tensile Strength: 12.4 MPa
- Elongation at Break: 1.6 %
- Flexural Strength: 18.6 MPa
- Color: Black
$ 1532/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 0.37 % @Time 86400 sec
- Water Absorption at Saturation: 1.1 %
- Hardness, Rockwell R: 123
- Tensile Strength, Yield: 69.6 MPa
$ 1707/MT
- Density: 1.67 g/cc @Temperature 23.0 °C
- Filler Content: 30 %
- Water Absorption: 0.72 % @Temperature 23.0 °C, Time 86400 sec
- Hardness, Shore D: 89 @Temperature 23.0 °C
- Tensile Strength, Yield: 82.0 MPa @Temperature 23.0 °C
$ 1635/MT
- Density: 1.42 g/cc
- Water Absorption: 0.96 % @Temperature 23.0 °C
- Water Absorption: 2.39 % @Temperature 80.0 °C
- Hardness, Shore D: 82 @Temperature 23.0 °C
- Tensile Strength: 38.0 MPa @Temperature 23.0 °C
$ 1618/MT
- Hardness, Rockwell R: 110 - 115
- Tensile Strength, Yield: 64.1 - 73.1 MPa @Temperature 22.8 °C
- Modulus of Elasticity: 2.55 - 2.93 GPa @Temperature 22.8 °C
- Compressive Strength: 79.3 - 89.6 MPa @Temperature 22.8 °C
- Shear Strength: 44.8 - 51.7 MPa @Temperature 22.8 °C
- Izod Impact, Notched: 0.427 - 0.534 J/cm @Temperature 22.8 °C
$ 1511/MT
- Specific Gravity: 1.47 g/cc
- Density: 1.47 g/cc
- Water Absorption at Saturation: 0.020 %
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 1.5 %
$ 1480/MT
- Density: 1.70 g/cc
- Filler Content: 45 %
- Hardness, Shore D: 83
- Tensile Strength: 26.2 MPa
- Elongation at Break: 0.80 %
$ 1907/MT
- Density: 1.71 g/cc
- Filler Content: 25 %
- Tensile Strength: 42.7 MPa
- Elongation at Break: 0.70 %
- Tensile Modulus: 6.89 GPa
$ 1731/MT
- Specific Gravity: 1.48 g/cc
- Water Absorption: 0.22 % @Time 86400 sec
- Water Absorption at Saturation: 0.65 %
- Hardness, Rockwell M: 86
- Tensile Strength, Yield: 64.0 MPa
$ 1547/MT
- Specific Gravity: 1.61 g/cc
- Hardness, Rockwell M: 89
- Tensile Strength, Yield: 58.3 MPa
- Elongation at Break: 7.9 %
- Tensile Modulus: 2.76 GPa
$ 1642/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.30 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell M: 119
- Tensile Strength at Break: 145 MPa @Temperature 22.8 °C
- Elongation at Break: 15 % @Temperature 22.8 °C
$ 1737/MT
- Density: 1.416 g/cc
- Water Absorption: 0.16 % @Temperature 23.0 °C
- Water Absorption: 0.60 % @Temperature 80.0 °C
- Hardness, Shore D: 88 @Temperature 23.0 °C
- Tensile Strength: 124 MPa @Temperature 23.0 °C
$ 1880/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Rockwell M: 109
- Tensile Strength at Break: 131 MPa @Temperature 22.8 °C
- Elongation at Break: 10 % @Temperature 22.8 °C
- Flexural Strength: 159 MPa @Temperature 22.8 °C
$ 1674/MT
- Density: 1.56 g/cc
- Filler Content: 30 %
- Tensile Strength: 84.8 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 7.58 GPa
$ 1550/MT
- Melting Point: 340 °C
- Maximum Service Temperature, Air: 260 °C
$ 1771/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.25 g/cc
- Water Absorption: 0.30 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 70.3 MPa @Temperature 22.8 °C
$ 2251/MT
- Specific Gravity: 0.920 g/cc
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 35.00 MPa
- Elongation at Break: 12 %
- Flexural Modulus: 1.45 GPa
$ 1673/MT
- Density: 1.32 g/cc
- Water Absorption: 0.50 %
- Water Absorption at Saturation: 0.50 %
- Hardness, Rockwell M: 99
- Tensile Strength, Yield: 110 MPa
$ 1445/MT
- Density: 1.08 g/cc
- Water Absorption: 1.2 %
- Water Absorption at Saturation: 6.7 %
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 49.6 MPa
$ 1533/MT
- Density: 1.51 g/cc @Temperature 23.0 °C
- Filler Content: 30 %
- Water Absorption: 0.46 % @Temperature 23.0 °C, Time 86400 sec
- Hardness, Shore D: 84 @Temperature 23.0 °C
- Tensile Strength, Yield: 82.0 MPa @Temperature 23.0 °C
$ 1859/MT
- Density: 1.43 g/cc
- Filler Content: 30 %
- Water Absorption: 0.050 % @Time 86400 sec
- Hardness, Rockwell M: 102
- Hardness, Shore D: 93
$ 1494/MT
- Specific Gravity: 1.08 g/cc
- Density: 0.830 g/cc
- Water Absorption: 0.23 % @Temperature 22.8 °C
- Tensile Strength at Break: 67.6 MPa @Temperature 22.8 °C
- Elongation at Break: 16.3 % @Temperature 22.8 °C
$ 1865/MT
- Density: 1.44 g/cc
- Tensile Strength, Yield: 100 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 4.30 GPa
- Flexural Modulus: 4.40 GPa
$ 1649/MT
- Density: 1.40 g/cc
- Filler Content: 15 %
- Hardness, Rockwell M: 119
- Tensile Strength: 96.5 MPa
- Elongation at Break: 3.0 %
$ 1507/MT
- Density: 1.54 g/cc
- Filler Content: 30 %
- Hardness, Rockwell M: 120
- Hardness, Shore D: 85
- Tensile Strength: 27.6 MPa
$ 1754/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.21 % @Time 86400 sec
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 62.1 MPa
- Elongation at Break: 80 %
$ 1812/MT
- Density: 1.51 g/cc
- Filler Content: 30 %
- Tensile Strength: 14.5 MPa
- Elongation at Break: 0.90 %
- Flexural Strength: 24.8 MPa
$ 2109/MT
- Density: 1.80 g/cc
- Filler Content: 35 %
- Tensile Strength: 32.4 MPa
- Elongation at Break: 0.70 %
- Tensile Modulus: 3.10 GPa
$ 1463/MT
- Density: 1.33 g/cc
- Filler Content: 0.00 %
- Tensile Strength: 114 MPa
- Elongation at Break: 2.6 %
- Elongation at Break: 4.0 %
$ 1870/MT
- Density: 1.34 g/cc
- Filler Content: 0.00 %
- Hardness, Shore D: 89
- Tensile Strength: 64.1 MPa
- Elongation at Break: 2.0 %
$ 2438/MT
- Specific Gravity: 1.65 g/cc
- Density: 1.65 g/cc
- Tensile Strength, Yield: 80.0 MPa @Temperature 22.8 °C
- Elongation at Break: 2.0 %
- Tensile Modulus: 5.00 GPa @Temperature 22.8 °C
$ 1573/MT
- Density: 1.49 g/cc
- Filler Content: 50 %
- Water Absorption: 0.13 % @Time 86400 sec
- Crystallinity: 17 %
- Hardness, Rockwell M: 110
$ 2595/MT
- Density: 1.49 g/cc
- Water Absorption: 1.81 % @Temperature 23.0 °C
- Water Absorption: 2.48 % @Temperature 80.0 °C
- Hardness, Shore D: 80 @Temperature 23.0 °C
- Tensile Strength: 40.0 MPa @Temperature 23.0 °C
$ 1685/MT
- Density: 1.38 g/cc
- Filler Content: 15 %
- Water Absorption: 0.060 % @Time 86400 sec
- Hardness, Rockwell M: 104
- Hardness, Shore D: 88
$ 1453/MT
- Specific Gravity: 1.36 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Tensile Strength, Yield: 49.6 MPa
- Elongation at Break: 40 %
- Tensile Modulus: 2.62 GPa
$ 1492/MT
- Density: 1.15 - 1.16 g/cc
- Water Absorption: 1.2 %
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 75.8 MPa
- Elongation at Break: 20 %
$ 2347/MT
- Density: 1.56 g/cc
- Filler Content: 30 %
- Crystallinity: 30 %
- Hardness, Shore D: 91
- Tensile Strength: 89.6 MPa
$ 1736/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 0.21 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 1.2 % @Temperature 22.8 °C
- Hardness, Rockwell M: 114
- Tensile Strength at Break: 114 MPa @Temperature 22.8 °C
$ 1528/MT
- Density: 1.39 g/cc
- Filler Content: 20 %
- Hardness, Shore D: 90
- Tensile Strength: 118 MPa
- Elongation at Break: 1.7 %
$ 2188/MT
- Density: 1.43 g/cc
- Filler Content: 15 %
- Hardness, Shore D: 85
- Tensile Strength: 62.1 MPa
- Elongation at Break: 1.8 %
$ 2234/MT
- Density: 1.34 g/cc
- Filler Content: 0.00 %
- Hardness, Shore D: 90
- Tensile Strength: 58.6 MPa
- Elongation at Break: 1.8 %
$ 1681/MT
- Density: 1.72 g/cc
- Filler Content: 25 %
- Hardness, Rockwell M: 97
- Hardness, Shore D: 90
- Tensile Strength: 42.1 MPa
$ 1951/MT
- Density: 1.43 g/cc
- Filler Content: 30 %
- Water Absorption: 0.050 % @Time 86400 sec
- Crystallinity: 35 %
- Hardness, Rockwell M: 102
$ 1586/MT
- Density: 1.41 g/cc
- Filler Content: 15 %
- Tensile Strength: 59.3 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 5.03 GPa
$ 2007/MT
- Density: 1.42 g/cc
- Filler Content: 25 %
- Tensile Strength: 122 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 183 MPa
$ 1955/MT
- Density: 1.77 g/cc
- Water Absorption: 0.070 % @Temperature 23.0 °C
- Water Absorption: 0.63 % @Temperature 80.0 °C
- Hardness, Shore D: 88 @Temperature 23.0 °C
- Elongation at Yield: 3.3 % @Temperature 23.0 °C
$ 1475/MT
- Density: 1.41 g/cc
- Water Absorption: 0.22 %
- Water Absorption at Saturation: 0.80 %
- Hardness, Rockwell M: 86
- Tensile Strength, Yield: 60.7 MPa
$ 1485/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.32 g/cc
- Water Absorption at Saturation: 0.10 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell M: 99
- Tensile Strength, Yield: 94.975 MPa @Temperature 22.8 °C
$ 1619/MT
- Density: 1.57 g/cc
- Filler Content: 38 %
- Hardness, Shore D: 89
- Tensile Strength: 46.9 MPa
- Elongation at Break: 0.60 %
$ 1471/MT
- Specific Gravity: 1.50 g/cc
- Density: 1.49 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Hardness, Rockwell M: 77
- Tensile Strength, Yield: 54.25 MPa
$ 1449/MT
- Density: 1.74 g/cc
- Filler Content: 47 %
- Hardness, Shore D: 73
- Tensile Strength: 18.6 MPa
- Elongation at Break: 1.3 %
$ 1572/MT
- Density: 1.42 g/cc
- Filler Content: 20 %
- Tensile Strength: 49.6 MPa
- Elongation at Break: 0.70 %
- Elongation at Break: 1.2 %
$ 1582/MT
- Density: 2.14 g/cc
- Filler Content: 0.00 %
- Hardness, Shore D: 76
- Tensile Strength: 42.1 MPa
- Elongation at Break: 37 %
$ 1920/MT
- Density: 1.06 g/cc
- Water Absorption: 0.25 %
- Water Absorption at Saturation: 3.0 %
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 55.2 MPa
$ 1513/MT
- Density: 1.15 - 1.16 g/cc
- Water Absorption: 1.2 %
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 68.9 MPa
- Elongation at Break: 25 %
$ 2097/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 0.15 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 0.15 %
- Tensile Strength, Yield: 62.1 MPa
- Elongation at Break: 8.0 %
$ 2516/MT
- Density: 1.52 g/cc
- Filler Content: 25 %
- Tensile Strength: 82.7 MPa
- Elongation at Break: 2.4 %
- Flexural Strength: 138 MPa
$ 2165/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Hardness, Rockwell M: 94
- Tensile Strength, Yield: 65.5 MPa
$ 1612/MT
- Specific Gravity: 1.14 - 1.15 g/cc
- Water Absorption at Saturation: 1.2 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell R: 110 - 115
- Tensile Strength, Yield: 64.1 - 73.1 MPa @Temperature 22.8 °C
- Tensile Modulus: 0.00255 - 0.00293 GPa
$ 2035/MT
- Density: 1.69 g/cc
- Filler Content: 25 %
- Hardness, Shore D: 86
- Tensile Strength: 33.1 MPa
- Elongation at Break: 0.50 %
$ 1459/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.29 g/cc
- Water Absorption: 0.37 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 1.1 % @Temperature 22.8 °C
- Hardness, Rockwell R: 123
$ 1517/MT
- Specific Gravity: 1.53 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 42.1 MPa
- Elongation at Yield: 20 %
$ 2414/MT
- Density: 1.44 g/cc
- Filler Content: 30 %
- Crystallinity: 35 %
- Hardness, Shore D: 90
- Tensile Strength: 98.6 MPa
$ 1548/MT
- Density: 1.14 - 1.15 g/cc
- Water Absorption: 0.75 %
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 60.7 MPa
- Elongation at Break: 25 %
$ 1628/MT
- Density: 2.03 g/cc
- Filler Content: 70 %
- Hardness, Shore D: 64
- Tensile Strength: 11.0 MPa
- Elongation at Break: 8.0 %
$ 1586/MT
- Density: 1.44 g/cc
- Filler Content: 40 %
- Hardness, Rockwell M: 123
- Hardness, Shore D: 89
- Tensile Strength: 122 MPa
$ 2457/MT
- Density: 1.49 g/cc
- Water Absorption: 0.54 % @Temperature 23.0 °C
- Water Absorption: 3.15 % @Temperature 80.0 °C
- Hardness, Shore D: 80 @Temperature 23.0 °C
- Tensile Strength: 41.6 MPa @Temperature 23.0 °C
$ 1623/MT
- Density: 1.88 g/cc
- Filler Content: 55 %
- Tensile Strength: 13.8 MPa
- Elongation at Break: 3.0 %
- Elongation at Break: 3.3 %
$ 1616/MT
- Density: 1.47 g/cc
- Filler Content: 25 %
- Hardness, Rockwell M: 96
- Tensile Strength: 51.7 MPa
- Elongation at Break: 1.3 %
$ 1605/MT
- Density: 1.60 g/cc
- Elongation at Break: 3.1 %
- Flexural Strength: 124 MPa
- Flexural Modulus: 4.62 GPa
- Color: Black
$ 1894/MT
- Density: 1.55 g/cc
- Filler Content: 45 %
- Tensile Strength: 40.0 MPa
- Elongation at Break: 1.1 %
- Elongation at Break: 1.1 %
$ 1730/MT
- Specific Gravity: 1.51 g/cc
- Water Absorption: 0.16 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 0.90 % @Temperature 22.8 °C
- Hardness, Rockwell M: 110
- Tensile Strength at Break: 121 MPa @Temperature 22.8 °C
$ 1732/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Rockwell M: 116
- Tensile Strength at Break: 117 MPa @Temperature 22.8 °C
- Elongation at Break: 2.0 % @Temperature 22.8 °C
- Flexural Strength: 145 MPa @Temperature 22.8 °C
$ 1680/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Hardness, Rockwell M: 91
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 70.60 MPa
$ 1535/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.25 % @Temperature 22.8 °C, Time 86400 sec
- Tensile Strength, Yield: 64.8 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 2.76 GPa
$ 1551/MT
- Density: 1.37 g/cc
- Filler Content: 15 %
- Tensile Strength: 84.8 MPa
- Elongation at Break: 4.3 %
- Tensile Modulus: 4.83 GPa
$ 1574/MT
- Density: 1.35 g/cc
- Water Absorption: 0.70 %
- Water Absorption at Saturation: 5.4 %
- Hardness, Rockwell M: 90
- Tensile Strength, Yield: 82.7 MPa
$ 1799/MT
- Density: 1.15 - 1.17 g/cc
- Water Absorption: 1.2 %
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 75.8 MPa
- Elongation at Break: 20 %
$ 2080/MT
- Density: 1.52 g/cc
- Filler Content: 25 %
- Hardness, Rockwell M: 105
- Tensile Strength: 104 MPa
- Elongation at Break: 2.8 %
$ 1601/MT
- Density: 1.47 g/cc
- Filler Content: 25 %
- Hardness, Rockwell M: 94
- Tensile Strength: 59.3 MPa
- Elongation at Break: 2.4 %
$ 1491/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 0.10 % @Temperature 22.8 °C, Time 86400 sec
- Tensile Strength, Yield: 65.5 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 2.07 GPa
$ 1775/MT
- Density: 1.57 g/cc @Temperature 23.0 °C
- Filler Content: 30 %
- Water Absorption: 3.13 % @Temperature 80.0 °C
- Water Absorption: 0.53 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 1.66 % @Temperature 80.0 °C, Time 86400 sec
$ 1808/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: <= 0.30 % @Temperature 22.8 °C
- Hardness, Rockwell M: 75
- Ball Indentation Hardness: 144.96 MPa
- Tensile Strength, Yield: 54.99 MPa
$ 2169/MT
- Density: 1.40 g/cc
- Filler Content: 15 %
- Hardness, Rockwell M: 93
- Hardness, Shore D: 88
- Tensile Strength: 79.3 MPa
$ 1577/MT
- Density: 1.38 g/cc @Temperature 23.0 °C
- Water Absorption: 4.17 % @Temperature 80.0 °C
- Water Absorption: 0.69 % @Temperature 23.0 °C, Time 86400 sec
- Water Absorption: 2.24 % @Temperature 80.0 °C, Time 86400 sec
- Hardness, Shore D: 91 @Temperature 23.0 °C
$ 1973/MT
- Density: 1.19 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1690/MT
- Density: 1.15 - 1.16 g/cc
- Water Absorption: 1.2 %
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 68.9 MPa
- Elongation at Break: 25 %
$ 1868/MT
- Density: 1.51 g/cc
- Filler Content: 40 %
- Tensile Strength: 42.7 MPa
- Elongation at Break: 0.60 %
- Flexural Strength: 62.1 MPa
$ 1898/MT
- Density: 1.43 g/cc
- Filler Content: 30 %
- Hardness, Rockwell M: 125
- Tensile Strength: 153.8 MPa
- Elongation at Break: 1.7 %
$ 2495/MT
- Density: 1.80 g/cc
- Filler Content: 50 %
- Hardness, Shore D: 88
- Tensile Strength: 36.5 MPa
- Elongation at Break: 0.80 %
$ 1827/MT
- Density: 1.46 g/cc
- Filler Content: 25 %
- Water Absorption: 0.040 % @Time 86400 sec
- Hardness, Rockwell M: 117
- Tensile Strength: 62.1 MPa
$ 1908/MT
- Tensile Strength, Yield: 728.8 MPa
- Tensile Strength, Yield: 820.8 MPa
- Tensile Modulus: 54.0 GPa
- Tensile Modulus: 55.79 GPa
- Flexural Strength: 803.79 MPa
$ 2437/MT
- Density: 1.51 g/cc
- Filler Content: 20 %
- Hardness, Shore D: 84
- Tensile Strength: 57.9 MPa
- Elongation at Break: 1.6 %
$ 1582/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.06 g/cc
- Water Absorption: 0.070 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 63.4 MPa @Temperature 22.8 °C
$ 1621/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.20 % @Temperature 22.8 °C, Time 86400 sec
- Water Absorption at Saturation: 0.20 %
- Tensile Strength, Yield: 45.5 MPa
- Elongation at Break: 45 %
$ 1723/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.06 g/cc
- Water Absorption: 0.070 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 63.4 MPa @Temperature 22.8 °C
$ 1713/MT
- Density: 1.53 g/cc
- Filler Content: 30 %
- Hardness, Rockwell M: 92
- Hardness, Shore D: 83
- Tensile Strength: 55.2 MPa
$ 1605/MT
- Density: 1.48 g/cc @Temperature 23.0 °C
- Filler Content: 10 %
- Filler Content: 15 %
- Water Absorption: 2.3 % @Temperature 80.0 °C
- Hardness, Shore D: 85 @Temperature 23.0 °C
$ 1460/MT
- Density: 1.40 g/cc
- Water Absorption: 0.22 %
- Water Absorption at Saturation: 0.80 %
- Hardness, Rockwell M: 86
- Tensile Strength, Yield: 60.7 MPa
Delivery Polymer Ensinger
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tanker ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.