$ 1529/MT
- Density: 0.961 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 31.0 MPa
- Flexural Modulus: 1.552 GPa
$ 1678/MT
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.5 MPa @Temperature 23.0 °C
- Elongation at Break: 30 %
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.38 GPa @Temperature 23.0 °C
$ 1562/MT
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.6 MPa
- Flexural Modulus: 1.00 GPa
- Izod Impact, Notched: 5.23 J/cm @Diameter 3.17 mm
- Izod Impact, Notched: 0.747 J/cm @Diameter 3.17 mm, Temperature 4.00 °C
$ 1877/MT
- Density: 0.961 g/cc
- Environmental Stress Crack Resistance: 5.0 hour
- Melt Flow: 6.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 31.0 MPa
$ 1583/MT
- Density: 0.910 g/cc
- Melt Flow: 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: >= 200 %
- Elongation at Yield: 8.0 %
$ 1798/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.9 MPa @Temperature 23.0 °C
- Elongation at Yield: 7.0 %
- Flexural Modulus: 1.72 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 116 °C
$ 2313/MT
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.5 MPa
- Flexural Modulus: 1.13 GPa
- Izod Impact, Notched: 0.908 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 87.0 °C
- Process: Injection Molding
$ 1544/MT
- Density: 0.942 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Environmental Stress Crack Resistance: >= 5000 hour
- Environmental Stress Crack Resistance: >= 5000 hour
- Oxidative Induction Time (OIT): >= 20 min @Temperature 210 °C
$ 1697/MT
- Density: 0.909 g/cc
- Melt Flow: 7.53 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 102
- Tensile Strength at Break: 18.79 MPa
- Tensile Strength, Yield: 36.0 MPa
$ 1459/MT
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.8 MPa @Temperature 23.0 °C
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.68 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 93.3 °C
$ 2225/MT
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.3 MPa
- Flexural Modulus: 1.14 GPa
- Izod Impact, Notched: 1.39 J/cm @Temperature -20.0 °C
- Izod Impact, Notched: NB @Temperature 23.0 °C
$ 1773/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 5.0 hour
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.9 MPa
$ 1458/MT
- Density: 0.937 g/cc
- Environmental Stress Crack Resistance: >= 3000 hour
- Oxidative Induction Time (OIT): >= 100 min
- High Load Melt Index: 10 g/10 min
- Hardness, Shore D: 60
$ 1455/MT
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.9 MPa @Temperature 23.0 °C
- Elongation at Break: 20 %
- Elongation at Yield: 6.0 %
- Flexural Modulus: 1.55 GPa @Temperature 23.0 °C
$ 1816/MT
- Density: 0.945 g/cc
- Melt Flow: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 800 %
$ 1464/MT
- Melt Flow: 2.5 - 4.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1561/MT
- Density: 0.950 g/cc
- High Load Melt Index: 10 g/10 min
- Hardness, Shore D: 65
- Tensile Strength at Break: 30.3 MPa
- Tensile Strength, Yield: 26.2 MPa
$ 1519/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1447/MT
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 49
- Tensile Strength, Yield: 20.0 MPa @Temperature 23.0 °C
- Elongation at Break: 80 %
- Flexural Modulus: 1.17 GPa @Temperature 23.0 °C
$ 1963/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 10 hour
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 28.3 MPa
$ 1716/MT
- Density: 0.944 g/cc
- Environmental Stress Crack Resistance: >= 2000 hour
- Environmental Stress Crack Resistance: >= 5000 hour
- High Load Melt Index: 12.5 g/10 min
- PENT: >= 100 hour
$ 1852/MT
- Melt Flow: 19.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.2 MPa @Temperature 23.0 °C
- Elongation at Yield: 9.6 %
- Flexural Modulus, 1% Secant: 1500 MPa
- Deflection Temperature at 0.46 MPa (66 psi): 88.9 °C
$ 2009/MT
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1722/MT
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2349/MT
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1942/MT
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1573/MT
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2114/MT
- Density: 0.962 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: >= 800 %
$ 1498/MT
- Melt Flow: 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.40 MPa @Temperature 23.0 °C
- Flexural Modulus: 1.69 GPa @Temperature 23.0 °C
- Izod Impact, Notched: 0.374 J/cm @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 97.8 °C
$ 2004/MT
- Density: 1.15 g/cc
- Apparent Bulk Density: 0.670 g/cc
- Moisture Vapor Transmission: 3.00 cc-mm/m²-24hr-atm
- Oxygen Transmission: 0.600 cc-mm/m²-24hr-atm
- Linear Mold Shrinkage: 0.0035 cm/cm
$ 1546/MT
- Density: 0.955 g/cc
- Melt Flow: 0.22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: >= 700 %
$ 1689/MT
- Melt Flow: 38 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.75 MPa @Temperature 23.0 °C
- Elongation at Break: 20 %
- Elongation at Yield: 8.9 %
- Flexural Modulus: 1.58 GPa @Temperature 23.0 °C
$ 2527/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1567/MT
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.9 MPa @Temperature 23.0 °C
- Elongation at Break: >= 200 %
- Elongation at Yield: 9.0 %
- Flexural Modulus: 1.45 GPa @Temperature 23.0 °C
$ 1739/MT
- Melt Flow: 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 40.3 MPa @Temperature 23.0 °C
- Flexural Modulus: 2.02 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 120 °C
$ 1517/MT
- Density: 0.963 g/cc
- Melt Flow: 0.72 g/10 min
- Hardness, Shore D: 66
- Tensile Strength: 8.96 MPa
- Tensile Strength, Yield: 31.0 MPa
$ 1471/MT
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 38.6 MPa @Temperature 23.0 °C
- Elongation at Break: 30 %
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.65 GPa @Temperature 23.0 °C
$ 1872/MT
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 84
- Tensile Strength, Yield: 27.9 MPa @Temperature 23.0 °C
- Elongation at Yield: 13.8 %
- Flexural Modulus: 0.896 GPa @Temperature 23.0 °C
$ 1539/MT
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 71.8
- Tensile Strength, Yield: 23.6 MPa
- Elongation at Yield: 6.0 %
- Tensile Modulus: 1.32 GPa
$ 1752/MT
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: >= 50 %
$ 2165/MT
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.5 MPa
- Flexural Modulus: 1.64 GPa
- Deflection Temperature at 0.46 MPa (66 psi): 97.2 °C
- Process: Fiber
- Region: US & Canada
$ 1934/MT
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 75
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: >= 500 %
- Flexural Modulus: 1.34 GPa
$ 1504/MT
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.3 MPa @Temperature 23.0 °C
- Elongation at Yield: 12.7 %
- Flexural Modulus, 1% Secant: 1430 MPa @Temperature 23.0 °C
- Izod Impact, Notched: 0.481 J/cm @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 90.6 °C
$ 1499/MT
- Density: 0.955 g/cc
- Melt Flow: 0.35 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: 700 %
$ 1656/MT
- Density: 0.955 g/cc
- Melt Flow: 0.35 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: 700 %
$ 1910/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 12 hour
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.9 MPa
$ 1570/MT
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 33.1 MPa
- Elongation at Break: >= 25 %
- Flexural Modulus: 1.83 GPa
$ 1532/MT
- Density: 0.900 g/cc
- Melt Flow: 12.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 71
- Tensile Strength at Break: 24.1 MPa
- Tensile Strength, Yield: 38.6 MPa
$ 1577/MT
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 77
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: >= 500 %
- Flexural Modulus: 1.24 GPa
$ 2581/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1454/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 6.5 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.9 MPa
$ 1666/MT
- Density: 0.948 g/cc
- Environmental Stress Crack Resistance: >= 96 hour
- Environmental Stress Crack Resistance: >= 192 hour
- Oxidative Induction Time (OIT): >= 20 min
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2070/MT
- Density: 0.951 g/cc
- Environmental Stress Crack Resistance: 4.0 hour
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 25.5 MPa
$ 2278/MT
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 31.7 MPa
- Flexural Modulus: 1.31 GPa
- Izod Impact, Notched: 0.481 J/cm @Diameter 3.17 mm
- Deflection Temperature at 0.46 MPa (66 psi): 87.8 °C
$ 2325/MT
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 75
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: >= 200 %
- Flexural Modulus: 1.17 GPa
$ 1898/MT
- Density: 0.944 g/cc
- Environmental Stress Crack Resistance: >= 2000 hour
- Environmental Stress Crack Resistance: >= 5000 hour
- Melt Flow: 12.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- PENT: >= 30 hour
$ 1568/MT
- Density: 0.944 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 30 g/10 min
- Hardness, Shore D: 68
$ 1874/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 4.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1829/MT
- Density: 0.9485 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- High Load Melt Index: 8.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- PENT: >= 10000 hour
- Hardness, Shore D: 66
$ 1885/MT
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1819/MT
- Density: 0.904 - 0.908 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 68 - 108
- Tensile Strength, Yield: 32.8 MPa @Temperature 23.0 °C
$ 1952/MT
- Density: 0.9485 g/cc
- Density: 0.959 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Carbon Black Loading: 2.3 %
- Melt Flow: 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1701/MT
- Density: 0.900 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Tensile Strength at Break: 16.3 MPa
- Tensile Strength, Yield: 25.6 MPa
$ 1732/MT
- Density: 0.944 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- High Load Melt Index: 8.75 g/10 min
- PENT: >= 100 hour
- Hardness, Shore D: 66
$ 1511/MT
- Density: 0.898 g/cc
- Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: 18.6 MPa
- Tensile Strength, Yield: 28.3 MPa
$ 2457/MT
- Density: 0.938 g/cc
- Density: 0.940 g/cc
- Oxidative Induction Time (OIT): >= 20 min
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 0.85 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 2548/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 76
- Tensile Strength at Break: 13.8 MPa
- Tensile Strength, Yield: 35.9 MPa
- Elongation at Break: >= 250 %
$ 1560/MT
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 61
- Tensile Strength, Yield: 20.7 MPa @Temperature 23.0 °C
- Elongation at Yield: 5.9 %
- Flexural Modulus, 1% Secant: 965 MPa @Temperature 23.0 °C
$ 1472/MT
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.2 MPa @Temperature 23.0 °C
- Elongation at Yield: 12.8 %
- Flexural Modulus, 1% Secant: 1470 MPa @Temperature 23.0 °C
- Izod Impact, Notched: 0.534 J/cm @Temperature 23.0 °C
$ 2146/MT
- Density: 0.951 g/cc
- Melt Flow: 0.22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: >= 700 %
$ 1854/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 10 hour
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 28.3 MPa
$ 1689/MT
- Density: 0.898 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: 18.6 MPa
- Tensile Strength, Yield: 29.3 MPa
$ 1672/MT
- Melt Flow: 65 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 39.3 MPa @Temperature 23.0 °C
- Elongation at Yield: 7.0 %
- Flexural Modulus, 1% Secant: 1790 MPa
$ 2139/MT
- Density: 0.953 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.9 MPa
- Flexural Modulus: 1.276 GPa
$ 1760/MT
- Melt Flow: 2.25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 38.0 MPa @Temperature 23.0 °C
- Flexural Modulus: 1.71 GPa @Temperature 23.0 °C
- Izod Impact, Notched: 0.374 J/cm @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 112 °C
$ 2216/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1687/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 13.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1503/MT
- Density: 0.954 g/cc
- High Load Melt Index: 5.0 g/10 min
- Hardness, Shore D: 64
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Break: 900 %
$ 2353/MT
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus: 1.24 GPa
- Izod Impact, Notched: 0.694 J/cm @Temperature -20.0 °C
$ 1532/MT
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1564/MT
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 83.5
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: >= 200 %
- Flexural Modulus: 1.05 GPa
$ 1968/MT
- Melt Flow: 17 - 23 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2378/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 6.5 hour
- Environmental Stress Crack Resistance: 6.5 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
$ 1660/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: >= 500 %
- Flexural Modulus: 1.28 GPa
$ 1624/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 12 hour
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.9 MPa
$ 2282/MT
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 49
- Tensile Strength, Yield: 20.0 MPa @Temperature 23.0 °C
- Elongation at Break: 80 %
- Flexural Modulus: 1.17 GPa
$ 2038/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Break: >= 200 %
- Flexural Modulus: 1.45 GPa
$ 1470/MT
- Density: 0.961 g/cc
- Environmental Stress Crack Resistance: 3.0 hour
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 31.0 MPa
$ 2080/MT
- Density: 0.951 g/cc
- Environmental Stress Crack Resistance: 4.0 hour
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 25.5 MPa
$ 1993/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 5.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1963/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 72
- Tensile Strength, Yield: 23.6 MPa
- Elongation at Yield: 6.0 %
- Tensile Modulus: 1.32 GPa
$ 1999/MT
- Density: 0.951 g/cc
- Environmental Stress Crack Resistance: 4.0 hour
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 25.5 MPa
$ 1643/MT
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.7 MPa @Temperature 23.0 °C
- Flexural Modulus: 1.59 GPa @Temperature 23.0 °C
- Izod Impact, Notched: 0.374 J/cm @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 101 °C
$ 1833/MT
- Density: 0.904 - 0.908 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
- Tensile Strength, Yield: 31.6 MPa @Temperature 23.0 °C
$ 1660/MT
- Density: 0.949 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Oxidative Induction Time (OIT): >= 20 min @Temperature 210 °C
- High Load Melt Index: 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- PENT: >= 10000 hour
$ 2035/MT
- Density: 0.900 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 19.7 MPa
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 480 %
$ 2386/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- High Load Melt Index: 0.35 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 31.7 MPa
$ 1481/MT
- Density: 0.961 g/cc
- Environmental Stress Crack Resistance: 3.0 hour
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 31.0 MPa
$ 2018/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 31.0 MPa
$ 1491/MT
- Density: 0.911 g/cc
- Melt Flow: 47 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 26.2 MPa
- Tensile Strength, Yield: 37.2 MPa
$ 2205/MT
- Density: 0.940 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Environmental Stress Crack Resistance: >= 5000 hour
- Environmental Stress Crack Resistance: >= 5000 hour
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2081/MT
- Density: 0.947 g/cc
- High Load Melt Index: 12 g/10 min
- Hardness, Shore D: 64
- Tensile Strength, Yield: 23.8 MPa
- Elongation at Break: 850 %
$ 2467/MT
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.1 MPa @Temperature 23.0 °C
- Elongation at Break: 15 %
- Elongation at Yield: 11 %
- Flexural Modulus: 1.22 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 92.2 °C
$ 1826/MT
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.1 MPa @Temperature 23.0 °C
- Elongation at Break: 15 %
- Elongation at Yield: 11 %
- Flexural Modulus: 1.22 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 92.2 °C
$ 1886/MT
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.1 MPa @Temperature 23.0 °C
- Elongation at Break: 15 %
- Elongation at Yield: 11 %
- Flexural Modulus: 1.22 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 92.2 °C
$ 1611/MT
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 93
- Tensile Strength, Yield: 30.3 MPa @Temperature 23.0 °C
- Elongation at Yield: 6.3 %
- Flexural Modulus, 1% Secant: 1430 MPa @Temperature 23.0 °C
$ 1551/MT
- Melt Flow: 34 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: >= 50 %
- Flexural Modulus: 1.31 GPa
$ 1478/MT
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 52
- Tensile Strength, Yield: 8.96 MPa @Temperature 23.0 °C
- Elongation at Break: >= 300 %
- Flexural Modulus, 1% Secant: 172 MPa @Temperature 23.0 °C
- Izod Impact, Notched: NB @Temperature 23.0 °C
$ 1746/MT
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus: 1.31 GPa
- Deflection Temperature at 0.46 MPa (66 psi): 104 °C
$ 1915/MT
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.51 MPa @Temperature 23.0 °C
- Elongation at Yield: 13.4 %
- Flexural Modulus, 1% Secant: 1280 MPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 85.0 °C
$ 1665/MT
- Melt Flow: 2.5 - 4.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1911/MT
- Melt Flow: 53 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 41.3 MPa @Temperature 23.0 °C
- Elongation at Break: 33 %
- Elongation at Yield: 8.0 %
$ 1532/MT
- Density: 0.956 g/cc
- Environmental Stress Crack Resistance: >= 5000 hour
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
- Tensile Strength, Ultimate: 31.0 MPa
$ 1703/MT
- Density: 0.950 g/cc
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: 700 %
$ 1652/MT
- Melt Flow: 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 93
- Tensile Strength, Yield: 34.3 MPa @Temperature 23.0 °C
- Elongation at Break: 172 %
- Flexural Modulus: 1.40 GPa @Temperature 23.0 °C
$ 1773/MT
- Density: 0.937 g/cc
- Environmental Stress Crack Resistance: >= 3000 hour
- Oxidative Induction Time (OIT): >= 100 min
- Melt Flow: 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 22 g/10 min
$ 1446/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 63
- Tensile Strength, Yield: 22.6 MPa
- Elongation at Yield: 7.2 %
- Flexural Modulus: 1.020 GPa
$ 2288/MT
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.4 MPa
- Elongation at Yield: 4.3 %
- Flexural Modulus: 1.05 GPa
- Izod Impact, Notched: 1.33 J/cm
- Process: Injection Molding
$ 1540/MT
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.5 MPa @Temperature 23.0 °C
- Elongation at Yield: 12.9 %
- Flexural Modulus, 1% Secant: 1240 MPa @Temperature 23.0 °C
- Izod Impact, Notched: 0.534 J/cm @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 86.1 °C
$ 2165/MT
- Density: 0.946 g/cc
- High Load Melt Index: 4.2 g/10 min
- Hardness, Shore D: 64
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Break: 800 %
$ 2047/MT
- Oxidative Induction Time (OIT): >= 70 min @Temperature 200 °C
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 96
- Tensile Strength at Break: 23.4 MPa
- Tensile Strength, Yield: 33.1 MPa
$ 1935/MT
- Density: 0.951 g/cc
- Melt Flow: 47 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 25.5 MPa
- Flexural Modulus: 1.207 GPa
$ 1824/MT
- Density: 1.11 g/cc
- Apparent Bulk Density: 0.680 g/cc
- Linear Mold Shrinkage: 0.0035 cm/cm
- Melt Flow: 3.0 g/10 min @Load 12.5 kg, Temperature 200 °C
- Hardness, Rockwell M: 45
$ 1454/MT
- Density: 0.953 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.9 MPa
- Flexural Modulus: 1.276 GPa
$ 2188/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 14.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 1490/MT
- Density: 0.898 g/cc
- Melt Flow: 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 66
- Tensile Strength, Ultimate: 18.6 MPa
- Tensile Strength, Yield: 26.9 MPa
$ 1731/MT
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 50
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: >= 200 %
- Flexural Modulus: 0.862 GPa
$ 1553/MT
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.1 MPa @Temperature 23.0 °C
- Elongation at Break: 15 %
- Elongation at Yield: 11 %
- Flexural Modulus: 1.22 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 92.2 °C
$ 1598/MT
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.1 MPa @Temperature 23.0 °C
- Elongation at Break: 15 %
- Elongation at Yield: 11 %
- Flexural Modulus: 1.22 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 92.2 °C
$ 1837/MT
- Density: 0.947 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 27.0 MPa
- Tensile Strength, Yield: 23.0 MPa
$ 2039/MT
- Density: 0.951 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: >= 500 %
$ 1921/MT
- Melt Flow: 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 41.1 MPa
- Flexural Modulus: 2.16 GPa
- Deflection Temperature at 0.46 MPa (66 psi): 123 °C
- Process: Coating
$ 1760/MT
- Density: 0.953 g/cc
- Melt Flow: 36.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.9 MPa
- Flexural Modulus: 1.276 GPa
$ 2248/MT
- Melt Flow: 7.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.1 MPa @Temperature 23.0 °C
- Elongation at Break: >= 300 %
- Flexural Modulus, 1% Secant: 1280 MPa @Temperature 23.0 °C
- Izod Impact, Notched: 1.33 J/cm @Temperature -20.0 °C
$ 1499/MT
- Melt Flow: 0.50 g/10 min
- Tensile Strength, Yield: 27.0 MPa
- Flexural Modulus: 1.242 GPa
- Izod Impact, Notched: NB
- Deflection Temperature at 0.46 MPa (66 psi): 88.0 °C
$ 2132/MT
- Melt Flow: 55 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 84.4
- Tensile Strength, Yield: 29.3 MPa
- Flexural Modulus: 1.073 GPa
- Izod Impact, Notched: 0.486 J/cm
$ 1799/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 2580/MT
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.5 MPa @Temperature 23.0 °C
- Flexural Modulus: 1.63 GPa @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 114 °C
- Haze: 18.5 %
$ 2196/MT
- Density: 0.955 g/cc
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: >= 700 %
$ 1659/MT
- Density: 0.950 g/cc
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: >= 700 %
$ 2041/MT
- Density: 0.954 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: >= 600 %
$ 2273/MT
- Density: 0.904 - 0.908 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 68 - 108
- Tensile Strength, Yield: 37.8 MPa @Temperature 23.0 °C
$ 1625/MT
- Melt Flow: 80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79
- Tensile Strength, Yield: 23.35 MPa
- Flexural Modulus: 1.19 GPa
- Izod Impact, Notched: 0.625 J/cm @Temperature -20.0 °C
$ 2251/MT
- Density: 0.904 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
- Tensile Strength at Break: 15.9 MPa
$ 1954/MT
- Density: 0.900 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 74
- Tensile Strength, Ultimate: 20.7 MPa
- Tensile Strength, Yield: 35.8 MPa
$ 1663/MT
- Density: 0.886 - 0.926 g/cc
- Water Absorption: <= 0.010 %
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79 - 108
$ 2490/MT
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2566/MT
- Density: 0.948 g/cc
- Environmental Stress Crack Resistance: 24 hour
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 22.8 MPa
$ 1551/MT
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 77
- Tensile Strength, Yield: 29.04 MPa @Temperature 23.0 °C
- Elongation at Break: >= 200 %
- Flexural Modulus: 1.62 GPa @Temperature 23.0 °C
$ 2194/MT
- Density: 0.944 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Oxidative Induction Time (OIT): >= 20 min @Temperature 210 °C
- High Load Melt Index: 6.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- PENT: >= 100 hour
$ 1537/MT
- Density: 0.900 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 25.5 MPa
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 500 %
Delivery Polymer Ineos Olefins & Polymers USA
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
passenger ship for sale singapore. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.