$ 1630/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1593/MT
- Density: 0.952 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
$ 1460/MT
- Density: 0.952 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Melt Flow: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.0 MPa
$ 1756/MT
- Density: 0.929 g/cc
- Water Absorption: 0.10 %
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 14 %
$ 1629/MT
- Density: 0.931 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1681/MT
- Density: 1.05 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 7.0 %
- Flexural Modulus: 1.10 GPa
$ 1758/MT
- Density: 0.942 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 98
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength, Yield: 34.0 MPa
$ 1840/MT
- Density: 0.895 g/cc
- Brookfield Viscosity: 640000 cP @Temperature 117 °C
- Melt Flow: 45 g/10 min
- Tensile Strength, Ultimate: 24.1 MPa
- Tensile Strength, Yield: 3.74 MPa
$ 2489/MT
- Density: 0.930 g/cc
- Apparent Bulk Density: 0.490 - 0.510 g/cc
- Viscosity Test: 2000 cm³/g
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 40.0 MPa
$ 1489/MT
- Density: 0.895 g/cc
- ESCR 10% Igepal®: >= 15000 hour @Temperature 50.0 °C
- Melt Flow: 0.40 g/10 min
- Tensile Strength, Ultimate: >= 27.6 MPa
- Tensile Strength, Yield: 17.2 MPa
$ 2297/MT
- Density: 1.10 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 21.0 MPa
- Tensile Strength, Yield: 19.0 MPa
$ 1571/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Flow: 42 g/10 min
- Tensile Strength, Ultimate: 24.0 MPa
- Flexural Modulus: 1.30 GPa
- CTE, linear: 75.0 µm/m-°C @Temperature -30.0 - 80.0 °C
$ 2296/MT
- Density: 1.03 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 500 %
- Elongation at Yield: 12 %
$ 1793/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1455/MT
- Density: 0.930 g/cc
- Apparent Bulk Density: 0.470 - 0.470 g/cc
- Viscosity Test: 2900 cm³/g
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 40.0 MPa
$ 1457/MT
- Density: 0.892 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength, Yield: 9.03 MPa
$ 2093/MT
- Density: 1.03 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 67
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Break: 500 %
$ 1712/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 51.0 MPa
- Tensile Strength, Yield: 52.0 MPa
$ 1473/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 85.0 MPa
- Elongation at Break: 6.0 %
$ 1903/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 100 MPa
- Elongation at Break: 2.0 %
$ 1493/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 97.0 MPa
- Elongation at Break: 2.0 %
$ 1725/MT
- Density: 0.960 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Break: 9.0 %
$ 1999/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 66.0 MPa
- Elongation at Break: 8.0 %
$ 1489/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 92
- Hardness, Shore D: 64
$ 2489/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 83.0 MPa
- Elongation at Break: 3.0 %
$ 1794/MT
- Density: 0.930 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 25.0 MPa
$ 1624/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Flow: 29 g/10 min
- Tensile Strength, Yield: 18.6 MPa
$ 1937/MT
- Density: 0.932 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 96
- Tensile Strength at Break: 29.6 MPa
$ 1599/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
$ 2212/MT
- Density: 1.13 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Ultimate: 19.0 MPa
- Tensile Strength, Yield: 30.0 MPa
$ 2032/MT
- Density: 0.908 g/cc
- Melt Flow: 4.0 g/10 min
- Tensile Strength, Ultimate: >= 27.6 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: >= 350 %
$ 1765/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 70
- Tensile Strength, Yield: 15.0 MPa
$ 1727/MT
- Density: 0.930 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 84
- Tensile Strength, Yield: 23.0 MPa
$ 1610/MT
- Density: 0.890 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Heat Seal Strength Initiation Temperature: 106.1 °C
- Melting Point: 135 °C
- Haze: 1.5 %
$ 1465/MT
- Density: 1.05 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 12.0 MPa
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 55 %
$ 1741/MT
- Density: 0.936 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1474/MT
- Density: 0.952 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.024 cm/cm
$ 2130/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
$ 1647/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
$ 2152/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
$ 1758/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
$ 1564/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
$ 1729/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: >= 50 %
$ 1963/MT
- Density: 0.934 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: >= 50 %
$ 1623/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1870/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1671/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1594/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1659/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1613/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1971/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1734/MT
- Density: 0.929 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1741/MT
- Density: 0.932 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Break: >= 50 %
$ 2224/MT
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 180 µm/m-°C @Temperature 20.0 °C
- Melting Point: 114 °C
$ 1529/MT
- Density: 0.950 g/cc
- Water Absorption: 0.010 %
- Melt Flow: 0.285 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
$ 1640/MT
- Density: 0.938 g/cc
- Water Absorption: 0.010 %
- Melt Flow: 0.285 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
$ 1509/MT
- Density: 0.938 g/cc
- Water Absorption: 0.010 %
- Melt Flow: 0.26 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
$ 1451/MT
- Density: 0.952 g/cc
- Water Absorption: 0.010 %
- Melt Flow: 0.285 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Break: >= 50 %
$ 1480/MT
- Density: 0.945 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- High Load Melt Index: 0.10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.0 MPa
$ 1528/MT
- Density: 0.952 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.024 cm/cm
$ 1856/MT
- Density: 0.952 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.024 cm/cm
$ 2292/MT
- Density: 0.954 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- High Load Melt Index: 0.10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 27.0 MPa
$ 1693/MT
- Density: 0.954 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- High Load Melt Index: 0.10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.0 MPa
$ 1490/MT
- Density: 0.951 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- High Load Melt Index: 0.10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.0 MPa
$ 1952/MT
- Density: 0.952 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.024 cm/cm
$ 1687/MT
- Density: 0.963 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.050 %
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
$ 1488/MT
- Density: 0.934 g/cc
- Water Absorption: 0.10 %
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 14 %
$ 1683/MT
- Density: 0.926 g/cc
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 0.190 GPa
- Melting Point: 108 °C
$ 1558/MT
- Density: 0.931 g/cc
- Tensile Strength, Yield: 7.00 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 0.0650 GPa
- CTE, linear, Parallel to Flow: 160 µm/m-°C @Temperature 20.0 °C
$ 1618/MT
- Density: 0.931 g/cc
- Tensile Strength, Yield: 7.00 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 0.0650 GPa
- CTE, linear, Parallel to Flow: 160 µm/m-°C @Temperature 20.0 °C
$ 2227/MT
- Density: 0.933 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1623/MT
- Density: 0.900 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Heat Seal Strength Initiation Temperature: 112 °C
$ 1514/MT
- Density: 1.05 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 84
- Tensile Strength, Ultimate: 29.0 MPa
- Tensile Strength, Yield: 31.0 MPa
$ 1461/MT
- Density: 0.932 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 97
- Tensile Strength at Break: 29.0 MPa
$ 1802/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Hardness, Shore D: 67
$ 2417/MT
- Density: 0.890 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.65 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, TD: 15.2 MPa
- Film Elongation at Break, MD: 670 %
$ 2162/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 1.02 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 21.0 MPa
$ 1842/MT
- Density: 0.900 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Heat Seal Strength Initiation Temperature: 112 °C @Thickness 1.20 mm
- Melting Point: 140 °C
$ 1886/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 26.0 MPa
$ 2077/MT
- Density: 1.11 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: 550 %
$ 1896/MT
- Density: 0.928 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: >= 50 %
$ 1573/MT
- Density: 0.930 g/cc
- Apparent Bulk Density: 0.470 - 0.470 g/cc
- Viscosity Test: 2300 cm³/g
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 40.0 MPa
$ 2464/MT
- Density: 0.882 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 48
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 350 %
$ 1940/MT
- Density: 0.890 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Heat Seal Strength Initiation Temperature: 106 °C
- Melting Point: 135 °C
- Haze: 2.0 %
$ 1996/MT
- Density: 0.900 g/cc
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 75
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 15 %
$ 1926/MT
- Density: 0.900 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 52
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 500 %
$ 1663/MT
- Density: 0.916 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1914/MT
- Density: 1.10 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 17.0 MPa
- Tensile Strength, Yield: 15.0 MPa
$ 1881/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 10 %
$ 2468/MT
- Density: 1.04 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Ultimate: 13.0 MPa
- Tensile Strength, Yield: 30.0 MPa
$ 2202/MT
- Density: 0.925 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 700 %
- Film Elongation at Break, TD: 750 %
$ 1486/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 94
- Tensile Strength, Yield: 37.0 MPa
- Elongation at Yield: 9.0 %
$ 2047/MT
- Density: 0.912 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 12.4 MPa
- Film Elongation at Break, MD: 600 %
$ 1896/MT
- Density: 1.23 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Ultimate: 16.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 1475/MT
- Density: 0.930 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 67
- Tensile Strength, Yield: 19.0 MPa
$ 1465/MT
- Density: 0.970 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Yield: 10 %
$ 1750/MT
- Density: 0.940 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 97
- Tensile Strength, Ultimate: 19.0 MPa
- Tensile Strength, Yield: 34.0 MPa
$ 2020/MT
- Density: 0.880 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 44
- Tensile Strength, Yield: 6.00 MPa
- Elongation at Break: 670 %
$ 2281/MT
- Density: 1.06 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 49
- Hardness, Shore D: 58
- Tensile Strength, Yield: 17.0 MPa
$ 2199/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 57
- Tensile Strength, Yield: 14.0 MPa
$ 1467/MT
- Specific Gravity: 1.01 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 21 g/10 min
- Tensile Strength, Yield: 20.0 MPa
- Flexural Modulus: 1.38 GPa
- CTE, linear: 52.0 µm/m-°C @Temperature -30.0 - 80.0 °C
$ 1551/MT
- Density: 0.930 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 27.0 MPa
$ 1477/MT
- Density: 1.17 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Break: 70 %
$ 1661/MT
- Density: 0.900 g/cc
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.20 GPa
$ 1696/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.0 MPa
- Tensile Strength, Yield: 16.0 MPa
$ 1606/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 87
- Tensile Strength, Ultimate: 19.0 MPa
$ 2224/MT
- Density: 1.04 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 78
- Hardness, Shore D: 71
- Tensile Strength at Break: 16.0 MPa
$ 1499/MT
- Density: 0.900 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Yield: 13 %
- Flexural Modulus: 0.650 GPa
$ 1509/MT
- Density: 0.980 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 72
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: 200 %
$ 1632/MT
- Density: 0.900 g/cc
- Water Absorption: 0.010 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.018 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1653/MT
- Density: 0.900 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 77
- Hardness, Shore D: 68
- Tensile Strength, Yield: 23.0 MPa
$ 1463/MT
- Density: 0.902 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Yield: 13 %
- Flexural Modulus: 1.03 GPa
$ 1793/MT
- Density: 0.902 g/cc
- Melt Flow: 34 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2018/MT
- Density: 0.900 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 74
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 16 %
$ 1556/MT
- Density: 1.03 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 80 %
$ 1576/MT
- Density: 0.900 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Heat Seal Strength Initiation Temperature: 112 °C
- Melting Point: 140 °C
$ 1977/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Yield: 12 %
$ 2190/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 66
- Tensile Strength, Yield: 19.0 MPa
$ 2592/MT
- Density: 0.890 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Heat Seal Strength Initiation Temperature: 106 °C
- Melting Point: 135 °C
- Haze: 2.0 %
$ 1730/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.20 GPa
$ 1492/MT
- Density: 0.900 g/cc
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 6.00 MPa
- Elongation at Yield: 22 %
- Flexural Modulus: 0.100 GPa
$ 1669/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Melt Flow: 0.97 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 66
- Tensile Strength, Yield: 28.0 MPa
$ 1732/MT
- Density: 0.930 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 68
- Tensile Strength, Yield: 21.4 MPa
- Tensile Strength, Yield: 23.0 MPa
$ 2019/MT
- Density: 0.930 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 68
- Tensile Strength, Yield: 21.4 MPa
- Tensile Strength, Yield: 23.0 MPa
$ 1663/MT
- Density: 0.930 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 68
- Tensile Strength, Yield: 21.4 MPa
- Tensile Strength, Yield: 23.0 MPa
$ 2360/MT
- Density: 0.915 g/cc
- ESCR 10% Igepal®: >= 15000 hour @Temperature 50.0 °C
- Melt Flow: 200 g/10 min
- Tensile Strength, Ultimate: >= 22.0 MPa
- Tensile Strength, Yield: 13.8 MPa
$ 1622/MT
- Density: 0.970 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 70
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength, Yield: 20.0 MPa
$ 1745/MT
- Density: 1.24 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 87
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Yield: 25 %
$ 2392/MT
- Density: 0.915 g/cc
- ESCR 10% Igepal®: >= 15000 hour @Temperature 50.0 °C
- Melt Flow: 4.0 g/10 min
- Tensile Strength, Ultimate: >= 26.1 MPa
- Tensile Strength, Yield: 13.8 MPa
$ 1646/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength, Yield: 17.0 MPa
$ 1826/MT
- Density: 1.05 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 96
- Tensile Strength, Ultimate: 26.0 MPa
- Tensile Strength, Yield: 34.0 MPa
$ 2148/MT
- Density: 0.890 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength, Yield: 17.0 MPa
$ 2200/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 93
- Tensile Strength, Yield: 32.0 MPa
$ 1493/MT
- Density: 1.03 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 67
- Tensile Strength, Yield: 23.0 MPa
$ 1881/MT
- Density: 1.07 g/cc
- Melt Flow: 23 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Hardness, Shore D: 75
- Tensile Strength, Ultimate: 20.0 MPa
$ 1453/MT
- Density: 0.910 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Break: 380 %
- Elongation at Yield: 8.0 %
$ 1526/MT
- Density: 0.890 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Yield: 8.0 %
$ 1454/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.20 GPa
$ 2230/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 21.0 MPa
$ 1915/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1882/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 2160/MT
- Density: 1.00 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Yield: 10 %
$ 1470/MT
- Density: 0.910 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 11.0 MPa
- Tensile Strength, Yield: 18.0 MPa
$ 1785/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 67
- Tensile Strength, Yield: 22.0 MPa
$ 1487/MT
- Density: 0.900 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 94
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Break: 500 %
$ 1802/MT
- Density: 0.930 g/cc
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 95
- Hardness, Shore D: 64
- Tensile Strength, Yield: 33.0 MPa
$ 1593/MT
- Density: 1.23 g/cc
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 87
- Hardness, Shore D: 74
- Tensile Strength, Ultimate: 21.0 MPa
$ 1748/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 12 %
$ 2295/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 78.6 MPa
- Flexural Modulus: 4.55 GPa
$ 1509/MT
- Density: 1.02 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 70
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Break: 100 %
$ 1565/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 67
- Tensile Strength, Yield: 26.0 MPa
$ 1743/MT
- Density: 1.24 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 94
- Tensile Strength, Ultimate: 23.0 MPa
- Tensile Strength, Yield: 29.0 MPa
$ 1685/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 34.0 MPa
- Tensile Strength, Yield: 23.0 MPa
$ 1929/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.012 cm/cm
- Melt Flow: 14 g/10 min
- Tensile Strength, Yield: 19.0 MPa
$ 2096/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 2039/MT
- Density: 0.916 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1738/MT
- Density: 0.916 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1637/MT
- Density: 0.916 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1931/MT
- Density: 0.892 g/cc
- Melt Flow: 9.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 56
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 580 %
$ 2143/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 17.0 MPa
$ 2062/MT
- Density: 0.912 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 12.4 MPa
- Film Elongation at Break, MD: 600 %
$ 1561/MT
- Density: 1.11 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 55
- Hardness, Shore D: 69
- Tensile Strength at Break: 15.0 MPa
$ 1515/MT
- Density: 1.07 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Yield: 4.0 %
- Flexural Modulus: 2.90 GPa
$ 1731/MT
- Density: 0.900 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 93
- Hardness, Shore D: 73
$ 1510/MT
- Density: 0.902 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 6.6 %
- Flexural Modulus: 1.03 GPa
$ 1686/MT
- Density: 0.917 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 8.00 MPa
- Elongation at Break: >= 50 %
$ 2318/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.0 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.20 GPa
$ 1688/MT
- Density: 0.900 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Yield: 13 %
- Flexural Modulus: 0.650 GPa
$ 1507/MT
- Density: 0.912 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 12.4 MPa
- Film Elongation at Break, MD: 600 %
$ 1554/MT
- Density: 1.13 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 55.0 MPa
- Elongation at Break: 12 %
- Flexural Modulus: 3.60 GPa
$ 1765/MT
- Density: 0.890 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Heat Seal Strength Initiation Temperature: 106 °C
- Melting Point: 135 °C
- Haze: 2.0 %
$ 1516/MT
- Density: 0.900 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 2.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Yield: 7.0 %
$ 1507/MT
- Density: 1.04 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.0 MPa
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Break: 200 %
$ 1460/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.4 MPa
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Break: 50 %
$ 2353/MT
- Density: 0.902 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.4 MPa
- Elongation at Yield: 7.0 %
- Flexural Modulus: 1.59 GPa
$ 1758/MT
- Density: 0.900 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.00 GPa
$ 2271/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 67
- Tensile Strength, Ultimate: 25.0 MPa
$ 1886/MT
- Density: 1.03 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 65
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 4.0 %
$ 1647/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 81
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Yield: 13 %
$ 1895/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 6.0 %
- Flexural Modulus: 1.40 GPa
$ 2533/MT
- Density: 1.03 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 62
- Tensile Strength, Ultimate: 14.0 MPa
- Tensile Strength, Yield: 18.0 MPa
$ 2011/MT
- Density: 1.22 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 350 %
- Flexural Modulus: 1.70 GPa
$ 1498/MT
- Density: 0.916 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 2355/MT
- Density: 0.902 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.17 GPa
$ 1446/MT
- Density: 1.05 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 86
- Tensile Strength, Ultimate: 17.0 MPa
- Tensile Strength, Yield: 26.0 MPa
$ 1990/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 10 %
$ 1655/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1627/MT
- Density: 0.910 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Break: 400 %
- Elongation at Yield: 10 %
$ 1699/MT
- Density: 0.892 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.65 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 17.9 MPa
- Film Tensile Strength at Yield, TD: 15.2 MPa
$ 1481/MT
- Density: 0.900 g/cc
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 30.0 MPa
- Elongation at Yield: 12 %
- Flexural Modulus: 1.20 GPa
$ 1961/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1614/MT
- Density: 0.890 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 30
- Tensile Strength, Yield: 5.00 MPa
- Elongation at Break: >= 400 %
$ 1545/MT
- Density: 0.900 g/cc
- Thickness: 25.4 microns
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.0 MPa
- Film Elongation at Break, TD: 710 %
$ 1929/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1668/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 93
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 11 %
$ 2462/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 69
- Tensile Strength, Ultimate: 14.0 MPa
$ 1547/MT
- Density: 0.900 g/cc
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 11 %
- Flexural Modulus: 1.10 GPa
$ 1652/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 86
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 12 %
$ 1536/MT
- Density: 0.930 g/cc
- Apparent Bulk Density: 0.490 - 0.510 g/cc
- Viscosity Test: 2800 cm³/g
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 40.0 MPa
$ 1497/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 40
- Hardness, Shore D: 64
$ 1970/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 22.0 MPa
$ 1840/MT
- Density: 1.03 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 68
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Break: 450 %
$ 1856/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 17.0 MPa
$ 1872/MT
- Density: 0.910 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Break: 350 %
- Elongation at Yield: 8.0 %
$ 1884/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm @Thickness 3.18 mm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 68
- Hardness, Shore D: 70
$ 1596/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 59
- Tensile Strength, Ultimate: 16.0 MPa
$ 2129/MT
- Density: 1.11 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 78
- Tensile Strength, Ultimate: 17.0 MPa
- Tensile Strength, Yield: 18.0 MPa
$ 1511/MT
- Density: 0.940 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 600 %
$ 1973/MT
- Specific Gravity: 0.940 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 11 g/10 min
- Tensile Strength, Yield: 19.0 MPa
- Flexural Modulus: 0.860 GPa
- CTE, linear: 88.0 µm/m-°C @Temperature 20.0 °C
$ 1912/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Tensile Strength, Ultimate: 19.0 MPa
- Tensile Strength, Yield: 27.0 MPa
$ 1499/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 71
- Tensile Strength, Yield: 28.0 MPa
$ 2497/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 59
- Tensile Strength, Yield: 21.0 MPa
$ 1562/MT
- Density: 1.05 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.0 MPa
- Flexural Modulus: 2.80 GPa
- Izod Impact, Notched (ISO): 1.90 kJ/m² @Temperature -40.0 °C
$ 2502/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 8.00 MPa
$ 2518/MT
- Density: 0.900 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 16.0 MPa
$ 1483/MT
- Density: 0.900 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.0 MPa
- Tensile Strength, Yield: 35.2 MPa
- Elongation at Yield: 11 %
$ 1930/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 96
- Tensile Strength at Break: 18.0 MPa
$ 1450/MT
- Density: 0.892 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 57
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Yield: 23 %
$ 1775/MT
- Density: 0.912 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 31.0 MPa
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: 700 %
$ 1696/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 10 %
$ 2260/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 18.0 MPa
$ 2315/MT
- Density: 0.902 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 28.0 MPa
$ 2435/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1710/MT
- Density: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 9.65 MPa
$ 1640/MT
- Density: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 9.65 MPa
$ 2064/MT
- Density: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 9.65 MPa
$ 2034/MT
- Density: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 9.65 MPa
$ 2061/MT
- Density: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 9.65 MPa
$ 1458/MT
- Density: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 9.65 MPa
$ 1553/MT
- Density: 0.916 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1815/MT
- Density: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength, Yield: 17.0 MPa
- Tensile Modulus: 0.703 GPa
$ 1541/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min
- Tensile Strength, Yield: 18.0 MPa
- Flexural Modulus: 2.03 GPa
$ 1828/MT
- Density: 1.26 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 88
- Tensile Strength, Ultimate: 18.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 1811/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus: 1.10 GPa
$ 1904/MT
- Density: 1.05 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79
- Tensile Strength, Ultimate: 17.0 MPa
- Tensile Strength, Yield: 22.0 MPa
$ 1645/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 20.2 MPa
- Flexural Modulus: 1.413 GPa
- Impact Test: 17.5 J
- CTE, linear: 85.0 µm/m-°C @Temperature -30.0 - 80.0 °C
$ 1452/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.00 GPa
$ 1498/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 21.0 MPa
$ 1643/MT
- Density: 0.990 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 81
- Tensile Strength, Ultimate: 21.0 MPa
- Tensile Strength, Yield: 23.0 MPa
$ 1521/MT
- Density: 0.930 g/cc
- Apparent Bulk Density: 0.470 - 0.470 g/cc
- Viscosity Test: 2600 cm³/g
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 40.0 MPa
$ 1502/MT
- Density: 1.01 g/cc
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Break: 30 %
- Flexural Modulus: 1.60 GPa
$ 2564/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus: 1.40 GPa
$ 2013/MT
- Density: 1.00 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Yield: 13 %
- Flexural Modulus: 1.20 GPa
$ 1497/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 67
- Tensile Strength at Break: 17.2 MPa
$ 1607/MT
- Density: 0.908 g/cc
- Melt Flow: 1.0 g/10 min
- Tensile Strength, Ultimate: >= 27.6 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: >= 350 %
$ 1448/MT
- Density: 0.908 g/cc
- Melt Flow: 1.0 g/10 min
- Tensile Strength, Ultimate: >= 27.6 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: >= 350 %
$ 1759/MT
- Density: 0.908 g/cc
- Melt Flow: 1.0 g/10 min
- Tensile Strength, Ultimate: >= 27.6 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: >= 350 %
$ 1524/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 10 %
$ 1461/MT
- Density: 0.900 g/cc
- Melt Flow: 1.4 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.0 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.10 GPa
$ 1490/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 82
- Tensile Strength, Yield: 21.0 MPa
$ 1611/MT
- Density: 0.880 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 30
- Tensile Strength, Yield: 6.00 MPa
- Elongation at Break: 500 %
$ 1969/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1487/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 98
- Tensile Strength at Break: 26.0 MPa
$ 2141/MT
- Density: 0.902 g/cc
- Melt Flow: 100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Yield: 4.0 %
- Flexural Modulus: 1.45 GPa
$ 2333/MT
- Density: 0.900 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.0 MPa
- Elongation at Yield: 7.0 %
- Flexural Modulus: 1.00 GPa
$ 1553/MT
- Density: 0.892 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 67
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 550 %
$ 1524/MT
- Density: 0.924 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
$ 2566/MT
- Density: 0.902 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 33.8 MPa
- Elongation at Yield: 12 %
$ 2005/MT
- Density: 0.960 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength, Yield: 20.0 MPa
$ 1693/MT
- Density: 0.919 g/cc
- Water Absorption: 0.010 %
- Moisture Absorption at Equilibrium: 0.010 %
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 50 %
$ 1671/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 52
- Tensile Strength, Ultimate: 12.0 MPa
$ 1913/MT
- Density: 0.900 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus: 1.20 GPa
$ 1740/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 4.0 %
$ 1837/MT
- Density: 0.900 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Hardness, Shore D: 73
$ 2381/MT
- Density: 0.895 g/cc
- Melt Flow: 3.0 g/10 min
- Tensile Strength, Ultimate: 24.1 MPa
- Tensile Strength, Yield: 3.74 MPa
- Elongation at Break: 550 %
$ 1749/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Yield: 10 %
Delivery Polymer LyondellBasell
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
bulker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.