$ 1684/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.1 %
- Tensile Modulus: 3.05 GPa
$ 2300/MT
- Specific Gravity: 1.14 g/cc
- Viscosity Measurement: 226
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 3.30 GPa
$ 1602/MT
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 20 %
- Tensile Modulus: 1.05 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1700/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.5 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 130 MPa
$ 2336/MT
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
- Comparative Tracking Index: 600 V
$ 1546/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption at Equilibrium: 1.6 %
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 5.1 %
$ 1453/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 30 %
- Tensile Modulus: 0.600 GPa
$ 1488/MT
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
- Comparative Tracking Index: 600 V
$ 2012/MT
- Specific Gravity: 1.32 g/cc
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 35 %
- Elongation at Yield: 8.5 %
- Tensile Modulus: 2.75 GPa
$ 2221/MT
- Specific Gravity: 1.39 g/cc
- Water Absorption: 7.3 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 3.2 %
$ 1513/MT
- Specific Gravity: 1.54 g/cc
- Water Absorption: 4.8 %
- Moisture Absorption at Equilibrium: 1.4 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 155 MPa
$ 1611/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 5.3 %
- Moisture Absorption at Equilibrium: 1.2 %
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 1.9 %
$ 1584/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 5.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 195 MPa
$ 2099/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 35 %
- Elongation at Yield: 3.9 %
- Tensile Modulus: 3.00 GPa
$ 1495/MT
- Specific Gravity: 1.40 g/cc
- Moisture Absorption at Equilibrium: 0.18 %
- Elongation at Break: 100 %
- Tensile Modulus: 6.20 GPa
- Flexural Strength: 150 MPa
$ 1727/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: 3.2 %
- Moisture Absorption at Equilibrium: 0.90 %
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 1.7 %
$ 1527/MT
- Specific Gravity: 1.31 g/cc
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 cm/cm
- Elongation at Break: 75 %
$ 2330/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.7 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 35.0 MPa
$ 1558/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.1 %
- Tensile Modulus: 2.80 GPa
$ 1477/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 7.9 %
- Moisture Absorption at Equilibrium: 2.3 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 120 MPa
$ 2137/MT
- Specific Gravity: 0.962 g/cc
- Hardness, Shore D: 61 @Time 3.00 sec
- Tensile Strength at Break: 40.0 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
- Melting Point: 132 °C
$ 1540/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 77
- Hardness, Shore D: 69 @Time 15.0 sec
$ 2138/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 7.9 %
- Moisture Absorption at Equilibrium: 2.2 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 125 MPa
$ 2286/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 7.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: >= 50 %
$ 2098/MT
- Specific Gravity: 1.38 g/cc
- Tensile Strength, Yield: 185 MPa
- Elongation at Break: 3.6 %
- Tensile Modulus: 10.55 GPa
- Flexural Strength: 270 MPa
$ 1681/MT
- Specific Gravity: 1.28 g/cc
- Tensile Strength, Yield: 165 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 10.3 GPa
- Flexural Strength: 240 MPa
$ 1702/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 35 %
$ 1535/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.5 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 135 MPa
$ 1521/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 1.7 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 185 MPa
$ 1628/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 7.5 %
- Moisture Absorption at Equilibrium: 2.2 %
- Viscosity Measurement: 145
- Charpy Impact Unnotched: 6.50 J/cm² @Temperature -30.0 °C
$ 2227/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 5.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 145 MPa
$ 1857/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.2 %
- Tensile Modulus: 3.25 GPa
$ 1911/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.5 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 190 MPa
$ 2225/MT
- Specific Gravity: 1.14 g/cc
- Viscosity Measurement: 225
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Melting Point: 217 °C
$ 2146/MT
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 30 %
- Tensile Modulus: 1.20 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1963/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 6.4 %
- Moisture Absorption at Equilibrium: 1.8 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 115 MPa
$ 2076/MT
- Specific Gravity: 1.45 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Elongation at Break: 120 %
- Tensile Modulus: 7.20 GPa
- Flexural Strength: 175 MPa
$ 1696/MT
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 17 %
- Elongation at Yield: 8.0 %
- Tensile Modulus: 4.20 GPa
- Charpy Impact Unnotched: 4.20 J/cm² @Temperature -30.0 °C
$ 1479/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 7.4 %
- Moisture Absorption at Equilibrium: 2.0 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 160 MPa
$ 1644/MT
- Specific Gravity: 1.36 g/cc
- Moisture Absorption at Equilibrium: 0.18 %
- Elongation at Break: 75 %
- Tensile Modulus: 4.40 GPa
- Flexural Strength: 125 MPa
$ 2023/MT
- Specific Gravity: 1.61 g/cc
- Tensile Strength, Yield: 155 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 12.35 GPa
- Flexural Strength: 240 MPa
$ 1450/MT
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 17 %
- Tensile Modulus: 0.750 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1886/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 5.6 %
- Moisture Absorption at Equilibrium: 1.3 %
- Viscosity Measurement: 270
- Tensile Strength at Break: 230 MPa
$ 2182/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 85.0 MPa
- Elongation at Break: 25 %
- Elongation at Yield: 6.5 %
- Tensile Modulus: 3.55 GPa
$ 2261/MT
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
- Comparative Tracking Index: 600 V
$ 1779/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 2.5 %
- Moisture Absorption at Equilibrium: 1.1 %
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 1.8 %
$ 1777/MT
- Specific Gravity: 1.65 g/cc
- Tensile Strength, Yield: 115 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 11.8 GPa
- Flexural Strength: 180 MPa
$ 2317/MT
- Specific Gravity: 1.51 g/cc
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 10.15 GPa
- Flexural Strength: 190 MPa
$ 1970/MT
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 14 %
- Tensile Modulus: 2.15 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1575/MT
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 14 %
- Tensile Modulus: 2.15 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 2202/MT
- Specific Gravity: 1.44 g/cc
- Water Absorption: 5.6 %
- Moisture Absorption at Equilibrium: 1.4 %
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 3.0 %
$ 1633/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 8.8 %
- Moisture Absorption at Equilibrium: 2.4 %
- Viscosity Measurement: 145
- Tensile Strength, Yield: 77.0 MPa
$ 1543/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
$ 1868/MT
- Specific Gravity: 1.57 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Elongation at Break: 110 %
- Tensile Modulus: 9.00 GPa
- Flexural Strength: 160 MPa
$ 2307/MT
- Specific Gravity: 1.35 g/cc
- Tensile Strength at Break: 123 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 6.65 GPa
- Flexural Modulus: 6.10 GPa
$ 1682/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 3.5 %
- Tensile Modulus: 1.65 GPa
$ 1507/MT
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 11.7 GPa
- Charpy Impact Unnotched: 4.00 J/cm² @Temperature -30.0 °C
- Charpy Impact Unnotched: 5.50 J/cm² @Temperature 23.0 °C
$ 2415/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 6.4 %
- Moisture Absorption at Equilibrium: 1.8 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 185 MPa
$ 1502/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 8.8 %
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 67.0 MPa
$ 2328/MT
- Tensile Strength at Break: 86.0 MPa
- Elongation at Break: 5.1 %
- Tensile Modulus: 5.70 GPa
- Charpy Impact Unnotched: 9.00 J/cm² @Temperature 23.0 °C
- Charpy Impact, Notched: 3.20 J/cm² @Temperature 23.0 °C
$ 1759/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 7.9 %
- Moisture Absorption at Equilibrium: 2.3 %
- Viscosity Measurement: 145
- Tensile Strength, Yield: 85.0 MPa
$ 1466/MT
- Specific Gravity: 1.62 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.10 %
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 1.4 %
$ 1821/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 6.4 %
- Moisture Absorption at Equilibrium: 1.8 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 115 MPa
$ 1823/MT
- Specific Gravity: 1.56 g/cc
- Water Absorption: 4.6 %
- Moisture Absorption at Equilibrium: 1.1 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 220 MPa
$ 1492/MT
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 28 %
- Tensile Modulus: 2.45 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1551/MT
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 30 %
- Tensile Modulus: 1.40 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1612/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 5.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 2.2 %
$ 1865/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption at Equilibrium: 1.6 %
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 3.2 %
$ 1523/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption at Equilibrium: 1.6 %
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 3.2 %
$ 1587/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption at Equilibrium: 1.6 %
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 3.2 %
$ 2301/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 8.7 %
- Moisture Absorption at Equilibrium: 2.3 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 90.0 MPa
$ 1582/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.7 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 70.0 MPa
$ 2099/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 6.7 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 4.2 %
$ 1494/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 6.7 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 4.2 %
$ 1923/MT
- Specific Gravity: 1.15 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 4.0 %
- Tensile Modulus: 3.35 GPa
$ 1741/MT
- Specific Gravity: 1.48 g/cc
- Water Absorption: 5.7 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 5.1 %
$ 1470/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 7.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: >= 50 %
$ 2422/MT
- Specific Gravity: 0.957 g/cc
- Hardness, Shore D: 64 @Time 3.00 sec
- Tensile Strength at Break: 31.0 MPa
- Tensile Strength, Yield: 21.5 MPa
- Elongation at Break: >= 50 %
- Melting Point: 130 °C
$ 2355/MT
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 6.25 GPa
- Charpy Impact Unnotched: 4.90 J/cm² @Temperature -30.0 °C
- Charpy Impact Unnotched: 5.20 J/cm² @Temperature 23.0 °C
$ 1930/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 5.6 %
- Moisture Absorption at Equilibrium: 1.3 %
- Viscosity Measurement: 270
- Tensile Strength at Break: 145 MPa
$ 1945/MT
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
$ 2071/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 65
$ 1493/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 30 %
$ 1502/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 20 %
$ 1537/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 30 %
$ 1898/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 32 %
$ 1768/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 30 %
$ 1645/MT
- Specific Gravity: 0.880 g/cc
- Hardness, Shore A: 55
$ 1491/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 55
$ 1489/MT
- Specific Gravity: 0.880 g/cc
- Hardness, Shore A: 55
- Transmission, Visible: 90 %
$ 2149/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 57
$ 1543/MT
- Specific Gravity: 1.02 g/cc
- Hardness, Shore A: 65
$ 1883/MT
- Specific Gravity: 0.950 g/cc
- Hardness, Shore A: 65
$ 2457/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 70
$ 1503/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 80
$ 1446/MT
- Specific Gravity: 0.900 g/cc
- Hardness, Shore A: 90
$ 1484/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 90
$ 1809/MT
- Specific Gravity: 0.980 g/cc
- Hardness, Shore D: 35
$ 1846/MT
- Specific Gravity: 0.900 g/cc
- Hardness, Shore A: 60
$ 1450/MT
- Specific Gravity: 1.16 g/cc
- Water Absorption: 0.45 % @Time 86400 sec
- Melt Flow: 34 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 47
- Hardness, Shore D: 43 @Time 15.0 sec
$ 1663/MT
- Specific Gravity: 1.19 g/cc
- Water Absorption: 0.29 % @Time 86400 sec
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 56
- Hardness, Shore D: 50 @Time 15.0 sec
$ 1447/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 77
- Hardness, Shore D: 69 @Time 15.0 sec
$ 1894/MT
- Specific Gravity: 0.980 g/cc
$ 1498/MT
- Specific Gravity: 0.960 g/cc
$ 1581/MT
- Specific Gravity: 0.970 g/cc
- Hardness, Shore D: 40 @Time 3.00 sec
- Minimum Service Temperature, Air: -30.0 °C
$ 1609/MT
- Specific Gravity: 0.890 g/cc
- Hardness, Shore D: 51 @Time 3.00 sec
- Minimum Service Temperature, Air: -30.0 °C
- Transmission, Visible: 90 %
$ 1985/MT
- Specific Gravity: 0.900 g/cc
- Hardness, Shore A: 40
$ 1719/MT
- Specific Gravity: 1.02 g/cc
- Hardness, Shore A: 60
$ 1542/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 65
$ 1990/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 70
$ 1589/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 80
$ 1697/MT
- Specific Gravity: 1.05 g/cc
- Hardness, Shore A: 80
$ 2282/MT
- Specific Gravity: 1.12 g/cc
- Water Absorption: 0.73 % @Time 86400 sec
- Melt Flow: 34 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 39
- Hardness, Shore D: 35 @Time 15.0 sec
$ 1563/MT
- Specific Gravity: 0.890 g/cc
- Hardness, Shore D: 40 @Time 3.00 sec
- Minimum Service Temperature, Air: -30.0 °C
$ 1990/MT
- Specific Gravity: 0.890 g/cc
- Hardness, Shore A: 35
$ 1909/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Melt Flow: 23 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Hardness, Shore D: 57 @Time 15.0 sec
$ 1976/MT
- Specific Gravity: 0.890 g/cc
- Hardness, Shore D: 55 @Time 3.00 sec
- Minimum Service Temperature, Air: -30.0 °C
$ 1450/MT
- Specific Gravity: 0.890 g/cc
- Hardness, Shore D: 46 @Time 3.00 sec
- Minimum Service Temperature, Air: -30.0 °C
- Transmission, Visible: 90 %
$ 1599/MT
- Specific Gravity: 1.41 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 30 %
$ 2089/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 8.8 %
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength, Yield: 38.0 MPa
- Elongation at Break: >= 50 %
$ 2022/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: >= 50 %
$ 2446/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 5.8 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 8.5 %
$ 1477/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 11 %
- Moisture Absorption at Equilibrium: 3.1 %
- Viscosity Measurement: 225
- Tensile Strength, Yield: 40.0 MPa
$ 1665/MT
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 25 %
- Tensile Modulus: 1.45 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1457/MT
- Specific Gravity: 1.46 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Elongation at Break: 130 %
$ 2405/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 1.7 %
- Tensile Strength at Break: 155 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 8.40 GPa
$ 1625/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 5.8 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: 30 %
$ 1806/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.0 %
- Tensile Modulus: 2.30 GPa
$ 2402/MT
- Specific Gravity: 1.14 g/cc
- Viscosity Measurement: 230
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 4.1 %
- Tensile Modulus: 2.80 GPa
$ 1549/MT
- Specific Gravity: 1.14 g/cc
- Viscosity Measurement: 200
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 2.90 GPa
$ 2357/MT
- Specific Gravity: 1.14 g/cc
- Viscosity Measurement: 234
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 2.80 GPa
$ 1815/MT
- Specific Gravity: 1.14 g/cc
- Viscosity Measurement: 245
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 2.95 GPa
$ 1738/MT
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 30 %
- Tensile Modulus: 0.800 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 2337/MT
- Specific Gravity: 1.45 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 3.10 GPa
- Flexural Strength: 90.0 MPa
$ 2166/MT
- Specific Gravity: 1.12 g/cc
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 3.50 GPa
- Flexural Strength: 110 MPa
$ 1507/MT
- Specific Gravity: 1.14 g/cc
- Viscosity Measurement: 225
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 8.0 %
$ 1539/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
$ 1552/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 7.9 %
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 140 MPa
$ 1465/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 8.8 %
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 80.0 MPa
$ 1515/MT
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 9.05 GPa
- Charpy Impact Unnotched: 5.90 J/cm² @Temperature -30.0 °C
- Charpy Impact Unnotched: 7.00 J/cm² @Temperature 23.0 °C
$ 1476/MT
- Specific Gravity: 1.11 g/cc
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.0 %
- Tensile Modulus: 2.60 GPa
$ 1754/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 8.20 GPa
- Flexural Strength: 145 MPa
$ 1718/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 14 %
$ 1984/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 6.4 %
- Moisture Absorption at Equilibrium: 1.8 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 180 MPa
$ 1456/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 20 %
- Tensile Modulus: 2.30 GPa
$ 2037/MT
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 30 %
- Tensile Modulus: 1.25 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1517/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 20 %
- Tensile Modulus: 2.30 GPa
$ 2030/MT
- Specific Gravity: 1.39 g/cc
- Water Absorption: 7.3 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 5.1 %
$ 1559/MT
- Specific Gravity: 1.28 g/cc
- Moisture Absorption at Equilibrium: 0.18 %
- Elongation at Break: 40 %
- Tensile Modulus: 2.00 GPa
- Flexural Strength: 65.0 MPa
$ 1605/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 3.5 %
- Tensile Modulus: 3.10 GPa
$ 1834/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 7.9 %
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 90.0 MPa
$ 1651/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 10.2 %
- Moisture Absorption at Equilibrium: 3.1 %
- Viscosity Measurement: 125
- Tensile Strength, Yield: 80.0 MPa
$ 1838/MT
- Specific Gravity: 1.44 g/cc
- Water Absorption: 5.6 %
- Moisture Absorption at Equilibrium: 1.4 %
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 2.5 %
$ 1868/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 2.0 %
- Viscosity Measurement: 160
- Melting Point: 220 °C
$ 1598/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 10.2 %
- Moisture Absorption at Equilibrium: 3.0 %
- Viscosity Measurement: 205
- Tensile Strength, Yield: 80.0 MPa
$ 1661/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 8.8 %
- Moisture Absorption at Equilibrium: 2.4 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 125 MPa
$ 1828/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 7.3 %
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 55.0 MPa
$ 1476/MT
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
- Comparative Tracking Index: 550 V
$ 2078/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 2.0 %
- Viscosity Measurement: 160
- Tensile Strength at Break: 165 MPa
$ 1594/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 50 %
$ 1732/MT
- Specific Gravity: 1.13 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.15 %
- Tensile Modulus: 2.55 GPa
$ 1601/MT
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
- Comparative Tracking Index: 600 V
$ 1475/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 8.8 %
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: >= 50 %
$ 2549/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 2.4 %
- Moisture Absorption at Equilibrium: 0.90 %
- Tensile Strength at Break: 155 MPa
- Elongation at Break: 2.3 %
$ 2307/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 20 %
- Elongation at Yield: 4.3 %
- Tensile Modulus: 3.50 GPa
$ 1640/MT
- Specific Gravity: 1.35 g/cc
- Tensile Strength, Yield: 180 MPa
- Elongation at Break: 3.7 %
- Tensile Modulus: 9.75 GPa
- Flexural Strength: 260 MPa
$ 1554/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 5.8 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 3.5 %
$ 1938/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 8.4 %
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Measurement: 240
- Tensile Strength, Yield: 60.0 MPa
$ 1642/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 8.4 %
- Moisture Absorption at Equilibrium: 2.1 %
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: >= 50 %
$ 1551/MT
- Specific Gravity: 1.38 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Elongation at Break: 110 %
$ 2124/MT
- Specific Gravity: 0.945 g/cc
- Hardness, Shore D: 55 @Time 3.00 sec
- Tensile Strength at Break: 18.5 MPa
- Tensile Strength, Yield: 11.5 MPa
- Elongation at Break: >= 50 %
- Melting Point: 115 °C
$ 1637/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.5 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 195 MPa
$ 1990/MT
- Specific Gravity: 1.11 g/cc
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 35 %
- Elongation at Yield: 4.5 %
- Tensile Modulus: 2.75 GPa
$ 1642/MT
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 4.9 %
- Tensile Modulus: 6.40 GPa
- Charpy Impact Unnotched: 8.00 J/cm² @Temperature -30.0 °C
- Charpy Impact Unnotched: 11.0 J/cm² @Temperature 23.0 °C
$ 2100/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 6.7 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 77.0 MPa
- Elongation at Break: 7.5 %
$ 1767/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 2.5 %
- Moisture Absorption at Equilibrium: 1.1 %
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 1.8 %
$ 2344/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore D: 61 @Time 3.00 sec
- Tensile Strength at Break: 40.0 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 50 %
- Melting Point: 132 °C
$ 1702/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
$ 1526/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 4.1 %
- Tensile Modulus: 3.00 GPa
$ 1984/MT
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 25 %
- Tensile Modulus: 1.15 GPa
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1601/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 5.8 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 2.8 %
$ 2341/MT
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
- Comparative Tracking Index: 600 V
$ 1852/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 5.8 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: 35 %
$ 1516/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 8.7 %
- Moisture Absorption at Equilibrium: 2.3 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 140 MPa
$ 1748/MT
- Specific Gravity: 1.48 g/cc
- Tensile Strength, Yield: 135 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 10.65 GPa
- Flexural Strength: 205 MPa
$ 2013/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 7.5 %
- Moisture Absorption at Equilibrium: 2.2 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 155 MPa
$ 1596/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 5.8 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 10 %
$ 2158/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 7.9 %
- Moisture Absorption at Equilibrium: 2.2 %
- Viscosity Measurement: 140
- Tensile Strength, Yield: 85.0 MPa
$ 1588/MT
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 6.50 GPa
- Volume Resistivity: 1.00e+11 ohm-cm
- Surface Resistance: 1.00e+14 ohm
- Comparative Tracking Index: 550 V
$ 2089/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: 3.2 %
- Moisture Absorption at Equilibrium: 0.90 %
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 1.7 %
$ 1584/MT
- Specific Gravity: 1.06 g/cc
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 7.0 %
- Tensile Modulus: 1.85 GPa
$ 2044/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 5.3 %
- Moisture Absorption at Equilibrium: 1.2 %
- Tensile Strength at Break: 210 MPa
- Elongation at Break: 1.8 %
$ 1486/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 1.7 %
- Viscosity Measurement: 145
- Tensile Strength at Break: 130 MPa
$ 1952/MT
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 7.50 GPa
- Charpy Impact Unnotched: 9.00 J/cm² @Temperature -30.0 °C
- Charpy Impact Unnotched: 11.0 J/cm² @Temperature 23.0 °C
$ 1679/MT
- Specific Gravity: 1.54 g/cc
- Water Absorption: 4.8 %
- Moisture Absorption at Equilibrium: 1.4 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 220 MPa
$ 1837/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 2.4 %
- Moisture Absorption at Equilibrium: 0.90 %
- Melting Point: 260 °C
- Volume Resistivity: 1.00e+11 ohm-cm
$ 1724/MT
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 8.0 %
- Tensile Modulus: 4.25 GPa
- Charpy Impact Unnotched: 4.50 J/cm² @Temperature -30.0 °C
- Charpy Impact Unnotched: 7.00 J/cm² @Temperature 23.0 °C
$ 2301/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 10.9 %
- Moisture Absorption at Equilibrium: 2.9 %
- Viscosity Measurement: 185
- Tensile Strength, Yield: 40.0 MPa
$ 2087/MT
- Specific Gravity: 1.35 g/cc
- Tensile Strength, Yield: 90.0 MPa
- Elongation at Break: 6.8 %
- Tensile Modulus: 5.05 GPa
- Flexural Strength: 135 MPa
$ 2165/MT
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 30 %
- Tensile Modulus: 1.20 GPa
- Volume Resistivity: 1.00e+11 ohm-cm
$ 2268/MT
- Specific Gravity: 1.35 g/cc
- Tensile Strength, Yield: 90.0 MPa
- Elongation at Break: 6.8 %
- Tensile Modulus: 5.05 GPa
- Flexural Strength: 135 MPa
$ 1635/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 8.4 %
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Measurement: 240
- Tensile Strength, Yield: 95.0 MPa
$ 1603/MT
- Specific Gravity: 1.16 g/cc
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 35 %
- Tensile Modulus: 1.00 GPa
$ 1615/MT
- Specific Gravity: 1.47 g/cc
- Water Absorption: 5.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 2.2 %
$ 1793/MT
- Specific Gravity: 1.36 g/cc
- Water Absorption: 6.7 %
- Moisture Absorption at Equilibrium: 2.0 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 175 MPa
$ 1448/MT
- Specific Gravity: 1.27 g/cc
- Tensile Strength, Yield: 130 MPa
- Elongation at Break: 3.9 %
- Tensile Modulus: 8.40 GPa
- Flexural Strength: 200 MPa
$ 2229/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: >= 50 %
$ 1957/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 8.4 %
- Moisture Absorption at Equilibrium: 2.1 %
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: >= 50 %
$ 1729/MT
- Specific Gravity: 1.36 g/cc
- Water Absorption: 6.7 %
- Moisture Absorption at Equilibrium: 2.0 %
- Viscosity Measurement: 140
- Tensile Strength at Break: 125 MPa
Delivery Polymer Radici Group Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.