$ 1454/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 63.4 MPa
- Elongation at Break: 30 %
$ 1618/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 40 %
$ 1759/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 20 %
$ 1480/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 87.6 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 110 MPa
$ 2270/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 148 MPa
- Elongation at Break: 2.2 %
- Flexural Strength: 170 MPa
$ 2110/MT
- Hardness, Rockwell R: 94
- Tensile Strength at Break: 46.2 MPa
- Elongation at Break: 130 %
- Flexural Strength: 34.5 MPa
- Flexural Modulus: 0.896 GPa
$ 1600/MT
- Specific Gravity: 1.15 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 64.8 MPa
- Elongation at Break: 10 %
$ 2288/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Yield: 93.1 MPa
- Elongation at Break: 1.0 %
$ 1880/MT
- Density: 1.49 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 6.0 %
$ 1850/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 148 MPa
- Elongation at Break: 2.2 %
- Flexural Strength: 170 MPa
$ 1939/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 150.0 MPa
$ 1480/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 53.8 MPa
- Elongation at Break: 60 %
$ 1870/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 2.0 %
$ 1560/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 4.0 %
$ 1682/MT
- Density: 1.18 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 89.6 MPa
$ 1548/MT
- Density: 1.20 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 96.5 MPa
$ 1699/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 83.0 MPa
- Elongation at Break: 10 %
$ 1925/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 85
$ 1519/MT
- Density: 1.49 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 87.6 MPa
$ 1742/MT
- Density: 1.49 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 88
- Tensile Strength at Break: 152 MPa
$ 1520/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 80
$ 1704/MT
- Density: 1.17 g/cc
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 51.7 MPa
- Flexural Yield Strength: 72.4 MPa
- Flexural Modulus: 1.86 GPa
$ 2094/MT
- Density: 1.18 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 8.0 %
$ 2362/MT
- Specific Gravity: 0.950 - 0.955 g/cc
- Melt Flow: 0.20 - 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 24.8 MPa
- Flexural Modulus: 1.24 GPa
$ 1885/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Melt Flow: 5.0 - 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 88
$ 1446/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.0 %
$ 1803/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 131 MPa
$ 1767/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 110
$ 2051/MT
- Density: 1.25 g/cc
- Melt Flow: 20 g/10 min @Load 3.80 kg, Temperature 250 °C
- Tensile Strength, Yield: 46.9 MPa
- Flexural Yield Strength: 72.4 MPa
- Flexural Modulus: 2.07 GPa
$ 1840/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 73.1 MPa
- Elongation at Break: 1.5 %
- Flexural Strength: 120 MPa
$ 1474/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 2.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 8.8 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 109
$ 1587/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.14 % @Time 7200 sec
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 85
$ 1601/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.2 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 260 °C
- Melt Flow: 15 g/10 min @Load 3.80 kg, Temperature 260 °C
$ 1618/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 85
$ 1666/MT
- Density: 1.38 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 98
- Tensile Strength at Break: 193 MPa
$ 2544/MT
- Density: 1.33 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 117 MPa
$ 2071/MT
- Density: 1.07 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 37.2 MPa
- Flexural Strength: 28.3 MPa
$ 1537/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 1523/MT
- Specific Gravity: 1.43 g/cc
- Water Absorption: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Melt Flow: 3.0 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 92
$ 1546/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 1.2 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 - 0.021 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 62.1 MPa
$ 1861/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 12 %
$ 2476/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 121
- Tensile Strength at Break: 141 MPa
$ 1554/MT
- Specific Gravity: 0.946 - 0.956 g/cc
- Melt Flow: 0.10 - 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.1 MPa
- Flexural Modulus: 1.21 GPa
$ 1531/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Yield: 75.8 MPa
- Elongation at Break: 2.0 %
$ 1478/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 63.4 MPa
- Elongation at Break: 30 %
$ 1528/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Tensile Strength, Yield: 68.9 MPa
- Flexural Strength: 117 MPa
$ 2192/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 65.5 MPa
- Elongation at Yield: 20 %
$ 1742/MT
- Density: 1.21 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Hardness, Rockwell R: 82
- Tensile Strength, Yield: 110 MPa
$ 1790/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 17 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 1679/MT
- Density: 1.22 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Hardness, Rockwell M: 95
- Tensile Strength at Break: 117 MPa
$ 1926/MT
- Density: 1.10 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 64.8 MPa
$ 1469/MT
- Specific Gravity: 0.950 - 0.955 g/cc
- Melt Flow: 4.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 24.8 MPa
- Flexural Modulus: 0.965 GPa
$ 1473/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 1453/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Tensile Strength, Yield: 68.9 MPa
- Flexural Strength: 117 MPa
$ 1603/MT
- Specific Gravity: 1.12 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 30 %
$ 1978/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 17 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 120 %
$ 1531/MT
- Density: 1.49 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 51.7 MPa
- Flexural Strength: 75.8 MPa
$ 2148/MT
- Specific Gravity: 1.17 g/cc
- Filler Content: 30 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 73.8 MPa
- Elongation at Yield: 3.0 %
$ 1450/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 58.6 MPa
- Elongation at Break: 5.0 %
- Flexural Strength: 84.1 MPa
$ 1781/MT
- Specific Gravity: 1.52 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 3.0 %
$ 2160/MT
- Specific Gravity: 0.952 - 0.960 g/cc
- Melt Flow: 0.20 - 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 24.1 MPa
- Flexural Modulus: 1.24 GPa
$ 1975/MT
- Density: 1.49 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Hardness, Rockwell M: 94
- Tensile Strength at Break: 96.5 MPa
$ 1617/MT
- Density: 1.33 g/cc
- Water Absorption: 0.90 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 131 MPa
$ 1781/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 130 %
$ 2137/MT
- Density: 1.49 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 89.6 MPa
$ 1739/MT
- Specific Gravity: 0.955 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 28 %
- Elongation at Yield: 7.0 %
$ 2557/MT
- Specific Gravity: 1.39 g/cc
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 160 MPa
- Tensile Strength at Break: 162 MPa
$ 1886/MT
- Density: 1.22 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Izod Impact, Notched: 1.12 J/cm
- Flammability, UL94: HB
$ 1608/MT
- Density: 1.07 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Yield: 55.2 MPa
$ 1560/MT
- Density: 1.17 g/cc
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 51.7 MPa
- Flexural Yield Strength: 72.4 MPa
- Flexural Modulus: 1.86 GPa
$ 1478/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 4.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 14 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 115
$ 1492/MT
- Density: 1.35 g/cc
- Water Absorption: 0.50 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 83
- Tensile Strength at Break: 103 MPa
$ 1608/MT
- Density: 1.14 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Hardness, Rockwell M: 87
- Tensile Strength at Break: 93.8 MPa
$ 1618/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Melt Flow: 4.0 - 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 91
$ 1589/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.5 MPa
- Elongation at Break: 60 %
$ 1767/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 5.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 13 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
$ 1780/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 46.9 MPa
$ 2353/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 2.5 %
- Flexural Strength: 160 MPa
$ 1520/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 43.4 MPa
- Elongation at Break: 240 %
$ 1453/MT
- Specific Gravity: 1.28 g/cc
- Filler Content: 40 %
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 92.4 MPa
- Elongation at Yield: 3.0 %
$ 1616/MT
- Density: 1.35 g/cc
- Water Absorption: 0.50 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 93
- Tensile Strength at Break: 128 MPa
$ 1591/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 1914/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 17 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 2429/MT
- Specific Gravity: 1.50 g/cc
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 84.8 MPa
- Tensile Strength at Break: 86.2 MPa
$ 1835/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 3.0 %
$ 2187/MT
- Density: 1.07 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.019 cm/cm
- Hardness, Rockwell R: 107
- Tensile Strength at Break: 51.7 MPa
$ 1800/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm
- Melt Flow: 26 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 54.5 MPa
$ 2087/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm
- Melt Flow: 34 g/10 min @Load 3.80 kg, Temperature 260 °C
- Tensile Strength, Yield: 57.2 MPa
- Flexural Yield Strength: 75.8 MPa
$ 1743/MT
- Density: 1.14 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 6.2 g/10 min @Load 2.16 kg, Temperature 260 °C
$ 1676/MT
- Density: 1.38 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 85
- Tensile Strength at Break: 138 MPa
$ 2246/MT
- Specific Gravity: 1.43 g/cc
- Water Absorption: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Melt Flow: 3.0 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 92
$ 1958/MT
- Density: 1.49 g/cc
- Water Absorption: 0.90 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 1495/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 32 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 1657/MT
- Density: 1.49 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 89.6 MPa
$ 1525/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 8.0 - 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ash: 16 - 24 %
- Tensile Strength: 24.0 MPa
- Flexural Modulus: 2.00 GPa
- Charpy Impact, Notched: 0.200 J/cm²
$ 2063/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 1.5 %
- Flexural Strength: 110.0 MPa
$ 1870/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 30 %
$ 1622/MT
- Density: 1.07 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Hardness, Rockwell R: 78
- Tensile Strength, Yield: 55.2 MPa
$ 1652/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 193 MPa
$ 1629/MT
- Density: 1.20 g/cc
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 61.4 MPa
- Flexural Modulus: 2.62 GPa
- Izod Impact, Notched: 7.21 J/cm
$ 2102/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 1490/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 78.0 MPa
- Elongation at Break: 10 %
$ 1466/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.3 MPa
- Elongation at Break: 30 %
$ 1540/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 48.3 MPa
- Elongation at Break: 30 %
$ 1627/MT
- Density: 1.19 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0080 cm/cm
- Tensile Strength, Yield: 93.1 MPa
- Elongation at Break: 3.5 %
$ 1655/MT
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.0090 cm/cm
- Tensile Strength, Yield: 51.7 MPa
- Flexural Strength: 75.8 MPa
- Flexural Modulus: 2.69 GPa
$ 1955/MT
- Density: 1.21 g/cc
- Melt Flow: 32 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 63.4 MPa
- Flexural Yield Strength: 96.5 MPa
- Flexural Modulus: 2.48 GPa
$ 1598/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 89.6 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 120 MPa
$ 1807/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 2196/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Melt Flow: 2.0 - 4.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 93
$ 1521/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.1 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 5.7 g/10 min @Load 2.16 kg, Temperature 260 °C
- Melt Flow: 14.8 g/10 min @Load 3.80 kg, Temperature 260 °C
$ 1923/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 32 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 80
$ 1514/MT
- Density: 1.14 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Hardness, Rockwell M: 64
- Tensile Strength at Break: 72.4 MPa
$ 1469/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 79
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: 45 %
$ 1474/MT
- Density: 1.33 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 117 MPa
$ 1803/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Water Absorption: 1.2 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 - 0.021 cm/cm
- Hardness, Rockwell R: 105
$ 2118/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 0.13 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Melt Flow: 5.0 - 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 91
$ 2248/MT
- Density: 1.03 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 1.3 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 102
$ 1728/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.14 % @Time 7200 sec
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 85
$ 1659/MT
- Density: 1.49 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Hardness, Rockwell M: 98
- Tensile Strength at Break: 131 MPa
$ 1974/MT
- Density: 1.33 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 60
- Tensile Strength at Break: 100 MPa
$ 1803/MT
- Density: 1.49 g/cc
- Water Absorption: 0.90 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 1511/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 5.6 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 109
$ 1736/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 1.75 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 101
- Tensile Strength, Yield: 44.1 MPa
$ 1494/MT
- Specific Gravity: 1.43 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 100 MPa
- Flexural Modulus: 5.100 GPa
$ 1545/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 57.2 MPa
- Elongation at Break: 110 %
$ 1888/MT
- Density: 1.03 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 8.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 102
$ 2073/MT
- Specific Gravity: 1.09 g/cc
- Filler Content: 20 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 59.0 MPa
- Elongation at Yield: 3.0 %
$ 1549/MT
- Density: 1.49 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 6.0 %
$ 1665/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.0 %
$ 1445/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 30 %
$ 1676/MT
- Density: 1.35 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 82
- Tensile Strength, Yield: 148 MPa
$ 2017/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 63.4 MPa
- Elongation at Break: 20 %
$ 1983/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 88.3 MPa
- Elongation at Break: 2.5 %
$ 1995/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 1.6 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 62.1 MPa
- Elongation at Break: 12 %
$ 1694/MT
- Density: 1.49 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 103
- Tensile Strength at Break: 221 MPa
$ 1817/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 51.7 MPa
$ 2124/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 57.2 MPa
- Elongation at Break: 110 %
$ 2127/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 82.7 MPa
- Elongation at Break: 2.5 %
$ 2011/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Elongation at Break: 130 %
$ 2040/MT
- Specific Gravity: 1.18 g/cc
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 21 g/10 min
$ 1724/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 40 %
$ 1816/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 44.8 MPa
- Elongation at Break: 40 %
$ 1446/MT
- Density: 1.20 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Hardness, Rockwell M: 76
- Tensile Strength at Break: 62.1 MPa
$ 1647/MT
- Density: 1.10 g/cc
- Water Absorption: 1.5 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 29.0 MPa
- Flexural Strength: 36.7 MPa
$ 2051/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 102 MPa
- Elongation at Break: 1.5 %
- Flexural Strength: 120 MPa
$ 2273/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 24.8 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.03 GPa
$ 1654/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm
- Melt Flow: 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength: 65.5 MPa
- Elongation at Break: 1.0 %
$ 1539/MT
- Specific Gravity: 1.15 g/cc
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 54.5 MPa
- Elongation at Break: 5.0 %
- Flexural Strength: 79.3 MPa
$ 1565/MT
- Density: 1.22 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 82.7 MPa
$ 1631/MT
- Density: 1.07 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage: 0.018 cm/cm
- Tensile Strength, Yield: 37.2 MPa
- Flexural Strength: 28.3 MPa
$ 1852/MT
- Density: 1.20 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 96.5 MPa
$ 2259/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Melt Flow: 5.0 - 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 88
$ 1540/MT
- Specific Gravity: 0.990 g/cc
- Filler Content: 10 %
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 48.0 MPa
- Elongation at Break: 5.0 %
$ 1552/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength at Break: 114 MPa
- Elongation at Break: 1.8 %
- Flexural Strength: 190 MPa
$ 1466/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 22 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 113
$ 1485/MT
- Density: 1.49 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell M: 103
- Tensile Strength at Break: 221 MPa
$ 1850/MT
- Density: 1.07 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.019 cm/cm
- Hardness, Rockwell R: 82
- Tensile Strength at Break: 34.5 MPa
$ 2220/MT
- Specific Gravity: 1.23 g/cc
- Density: 1.23 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00060 - 0.00090 cm/cm
- Hardness, Rockwell M: 95
Delivery Polymer Ravago Manufacturing Americas, LLC
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.