$ 1685/MT
- Elongation at Break: <= 18 %
- Tear Strength: 7.89 kN/m
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Aluminum
$ 2337/MT
- Density: 1.51 g/cc
- Water Absorption: 0.19 % @Time 86400 sec
- Water Absorption: 0.50 % @Time 173000 sec
- Deformation: 0.10 %
- Hardness, Rockwell E: 25 - 40
$ 1548/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1506/MT
- Density: 0.554 g/cc
- Water Absorption: 10 %
- Tensile Strength, Yield: 0.414 MPa
- Elongation at Break: 250 %
- Tensile Modulus: 0.000345 GPa
$ 2460/MT
- Density: 0.471 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 0.517 MPa
- Elongation at Break: 125 %
- Compressive Strength: 0.0689 MPa @Temperature 23.0 °C
$ 1543/MT
- Tear Strength: 2.80 kN/m
- Thermal Conductivity: 1.10 W/m-K
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -28.9 °C
- Color: White
- Thermal Impedance @ 10 psi: 0.30°C in^2/W
$ 1638/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 123.0 kV/mm
$ 1846/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 13.1 MPa
- Elongation at Break: >= 150 %
- CTE, linear: 90.0 µm/m-°C @Temperature 20.0 °C
$ 1717/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Copper
$ 1867/MT
- Specific Gravity: 1.48 g/cc
- Water Absorption: 0.13 %
- Deformation: 0.090 % @Pressure 13.8 MPa
- Outgassing - Total Mass Loss: 0.00 %
- Outgassing - Total Mass Loss: 0.69 %
$ 2330/MT
- Elongation at Break: 200 %
- Tear Strength: 13.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 96.9 kV/mm
$ 2035/MT
- Density: 2.25 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Hardness, Shore D: 75
- Tensile Strength: 10.3 MPa
$ 1521/MT
- Elongation at Break: 225 %
- Tear Strength: 3.51 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Color: Rose
$ 1906/MT
- Specific Gravity: 1.377 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 5.52 MPa
- Tear Strength Test: 39.6
- Tear Strength Test: 39.6
$ 1917/MT
- Density: 0.360 g/cc
- Hardness, Shore A: 30
- Tensile Strength, Yield: 0.896 MPa
- Elongation at Break: 105 %
- Compressive Modulus: 0.000110 GPa
$ 1536/MT
- Specific Gravity: 2.12 - 2.18 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.483 GPa
$ 1671/MT
- Elongation at Break: 75 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 112 kV/mm
$ 1553/MT
- Tensile Strength, Yield: 3.45 MPa
- Thermal Conductivity: 4.00 W/m-K
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -28.9 °C
- Color: Metallic Black
- Thermal Impedance @ 10 psi: 0.10°C in^2/W
$ 2553/MT
- Elongation at Break: 50 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 110 kV/mm
$ 1537/MT
- Elongation at Break: 250 %
- Tear Strength: 11.4 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 84.3 kV/mm
$ 1692/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.080 %
- Hardness, Shore A: 71
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 300 %
$ 1470/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 51.77 kV/mm
$ 2244/MT
- Density: 0.238 g/cc
- Water Absorption: 3.0 %
- Hardness, Shore OO: 45
- Tensile Strength, Yield: 0.379 MPa
- Elongation at Break: 140 %
$ 1686/MT
- Elongation at Break: 375 %
- Tear Strength: 3.51 kN/m
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 86.6 kV/mm
$ 1644/MT
- Density: 1.11 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 0.827 MPa
- Elongation at Break: 150 %
- Compressive Strength: 0.138 MPa @Temperature 23.0 °C
$ 1702/MT
- Specific Gravity: 2.145 g/cc
- Tear Strength Test: 7.0
- Tear Strength Test: 9.0
- Tear Strength: 39.4 kN/m
- Tear Strength: 57.0 kN/m
$ 1744/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 78.7 kV/mm
$ 1566/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Color: Tan
$ 1499/MT
- Density: 0.471 g/cc
- Water Absorption: 10 %
- Hardness, Shore O: 53
- Tensile Strength, Yield: 0.414 MPa
- Elongation at Break: 250 %
$ 1925/MT
- Elongation at Break: 275 %
- Tear Strength: 10.5 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 90.6 kV/mm
$ 1570/MT
- Density: 0.332 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 0.345 MPa
- Elongation at Break: 75 %
- Compressive Strength: 0.0345 MPa @Temperature 23.0 °C
$ 1837/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.49 %
- Hardness, Shore A: 57
- Tensile Strength, Yield: 12.5 MPa
- Elongation at Break: 310 %
$ 1578/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.29 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 40 @Time 15.0 sec
- Tensile Strength: 7.412 MPa
- Tensile Strength, Yield: 1.97 MPa @Strain 100 %
$ 1858/MT
- Maximum Service Temperature, Air: 85.0 °C
- Minimum Service Temperature, Air: -40.0 °C
$ 2236/MT
- Maximum Service Temperature, Air: 73.9 °C
- Minimum Service Temperature, Air: -28.9 °C
$ 1446/MT
- Specific Gravity: 0.980 g/cc
- Water Absorption: <= 0.010 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 61 @Time 15.0 sec
- Tensile Strength: 6.89 MPa
- Elongation at Break: 375 %
$ 1465/MT
- Specific Gravity: 0.980 g/cc
- Water Absorption: 0.30 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 61 @Time 15.0 sec
- Tensile Strength: 6.89 MPa
- Elongation at Break: 375 %
$ 1605/MT
- Specific Gravity: 1.31 g/cc
- Water Absorption: 0.19 %
- Hardness, Shore A: 64
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 350 %
$ 1447/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.22 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 66 @Time 15.0 sec
- Tensile Strength: 15.2 MPa
- Tensile Strength, Yield: 9.508 MPa @Strain 200 %
$ 1906/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.22 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 66 @Time 15.0 sec
- Tensile Strength: 15.2 MPa
- Tensile Strength, Yield: 9.501 MPa @Strain 200 %
$ 1451/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.21 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 56 @Time 15.0 sec
- Tensile Strength: 12.1 MPa
- Tensile Strength, Yield: 4.01 MPa @Strain 100 %
$ 2231/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.20 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 56 @Time 15.0 sec
- Tensile Strength: 12.4 MPa
- Tensile Strength, Yield: 3.79 MPa @Strain 100 %
$ 2118/MT
- Specific Gravity: 1.45 g/cc
- Water Absorption: <= 0.010 %
- Hardness, Shore A: 67
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 350 %
$ 1852/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.22 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 66 @Time 15.0 sec
- Tensile Strength: 15.2 MPa
- Tensile Strength, Yield: 9.501 MPa @Strain 200 %
$ 1984/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.21 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 56 @Time 15.0 sec
- Tensile Strength: 12.1 MPa
- Tensile Strength, Yield: 4.01 MPa @Strain 100 %
$ 1787/MT
- Specific Gravity: 0.880 g/cc
- Water Absorption: 0.040 %
- Hardness, Shore A: 69
- Tensile Strength, Yield: 5.52 MPa
- Elongation at Break: 500 %
$ 1719/MT
- Maximum Service Temperature, Air: 73.9 °C
- Minimum Service Temperature, Air: -28.9 °C
- FDA: Yes
- Color: Translucent Yellow
$ 1499/MT
- Specific Gravity: 0.900 g/cc
- Water Absorption: <= 0.010 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 75 @Time 15.0 sec
- Tensile Strength: 13.1 MPa
- Elongation at Break: 850 %
$ 2079/MT
- Specific Gravity: 0.900 g/cc
- Water Absorption: 0.070 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 60 @Time 15.0 sec
- Tensile Strength: 11.2 MPa
- Elongation at Break: 770 %
$ 2261/MT
- Tear Strength: 2.80 kN/m
- Thermal Conductivity: 0.400 W/m-K
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -28.9 °C
- Volume Resistivity: 3.80e+14 ohm-cm
$ 2155/MT
- Elongation at Break: 150 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 89.96 kV/mm
$ 2188/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.414 GPa
$ 1653/MT
- Elongation at Break: 150 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 101 kV/mm
$ 2328/MT
- Elongation at Break: 75 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 112 kV/mm
$ 2413/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 70.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 17.5 kV/mm
$ 1842/MT
- Elongation at Break: <= 10 %
- Tear Strength: 14.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Aluminum
$ 2246/MT
- Elongation at Break: <= 8.0 %
- Tear Strength: 3.51 kN/m
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Aluminum
$ 1770/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1694/MT
- Specific Gravity: 1.57 g/cc
- Water Absorption: 0.62 %
- Deformation: 0.35 % @Pressure 13.8 MPa
- Outgassing - Total Mass Loss: 0.00 %
- Outgassing - Total Mass Loss: 1.15 %
$ 1485/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Rockwell M: 85
- Hardness, Shore D: 80
- Tensile Strength: 54.3 MPa
- Elongation at Yield: 7.5 %
$ 1889/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1602/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 10.3 MPa
- Elongation at Break: >= 100 %
- CTE, linear: 90.0 µm/m-°C @Temperature 20.0 °C
$ 2122/MT
- Specific Gravity: 1.78 g/cc
- Tear Strength Test: 2.5
- Tear Strength Test: 5.5
- Tear Strength: 14.9 kN/m
- Tear Strength: 19.3 kN/m
$ 2265/MT
- Specific Gravity: 2.20 g/cc
- Tensile Strength, Yield: 38.6 MPa
- Elongation at Break: 300 %
- Dielectric Strength: 157 kV/mm
$ 2120/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 43.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 28.7 kV/mm
$ 1916/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 70.28 kV/mm
$ 1487/MT
- Density: 1.96 g/cc
- Hardness, Shore D: 65
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 40 %
- Tensile Modulus: 1.65 GPa
$ 2536/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 51.2 kV/mm
$ 1967/MT
- Specific Gravity: 0.980 g/cc
- Water Absorption: 0.30 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 62 @Time 15.0 sec
- Tensile Strength: 6.55 MPa
- Tensile Strength, Yield: 6.55 MPa @Strain 100 %
$ 1804/MT
- Elongation at Break: <= 10 %
- Compressive Strength: 0.103 MPa
- Tear Strength: 17.5 kN/m
- Compression Set: 25 % @Temperature 100 °C
- Color: Blue Gray
$ 1626/MT
- Density: 1.97 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Tensile Strength: 11.7 MPa
- Elongation at Break: 160 %
$ 1614/MT
- Tensile Strength, Yield: 0.827 MPa
- Elongation at Break: 900 %
- Maximum Service Temperature, Air: 93.3 °C
- Minimum Service Temperature, Air: -34.4 °C
- Color: Clear
$ 1925/MT
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Copper
$ 1627/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 29.5 kV/mm
$ 1835/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 24.1 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.552 GPa
$ 2431/MT
- Density: 2.10 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Tensile Strength: 12.4 MPa
- Elongation at Break: 70 %
$ 1565/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1908/MT
- Elongation at Break: 50 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 65.59 kV/mm
$ 1948/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 65.59 kV/mm
$ 1660/MT
- Specific Gravity: 0.980 g/cc
- Water Absorption: 0.30 %
- Hardness, Shore A: 61
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 375 %
$ 1633/MT
- Volatile Organic Compounds (VOC) Content: <= 0.50 g/l
- Hardness, Shore A: 81
- Elongation at Break: <= 10 %
- Flexural Strength: 5.17 MPa
- Tear Strength: 52.6 kN/m
$ 2419/MT
- Elongation at Break: 7.0 %
- Tear Strength: 35.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Aluminum
$ 1652/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.414 GPa
$ 1539/MT
- Volatile Organic Compounds (VOC) Content: 1.5 g/l
- Hardness, Shore A: 75
- Elongation at Break: <= 10 %
- Flexural Strength: 5.17 MPa
- Tear Strength: 52.6 kN/m
$ 2095/MT
- Specific Gravity: 1.896 g/cc
- Tear Strength Test: 7.0
- Tear Strength Test: 16
- Tear Strength: 40.3 kN/m
- Tear Strength: 57.8 kN/m
$ 1669/MT
- Specific Gravity: 1.335 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 3.45 MPa
- Tear Strength Test: 20
- Tear Strength Test: 22
$ 1782/MT
- Density: 0.471 g/cc
- Water Absorption: 5.0 %
- Tensile Strength, Yield: 0.896 MPa
- Elongation at Break: 275 %
- Maximum Service Temperature, Air: 93.3 °C
$ 1545/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 27.6 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.552 GPa
$ 1566/MT
- Specific Gravity: 2.20 g/cc
- Tensile Strength, Yield: 41.4 MPa
- Elongation at Break: 300 %
- Dielectric Strength: 110 kV/mm
$ 2063/MT
- Hardness, Shore A: 65 - 75
- Tensile Strength, Yield: 5.17 MPa
- Elongation at Break: 160 %
- Tear Strength: 11.4 kN/m
- Compression Set: 20 % @Temperature 160 °C
$ 1709/MT
- Specific Gravity: 1.65 g/cc
- Water Absorption: 0.010 %
- Tensile Strength: 130 MPa
- Elongation at Break: 0.50 %
- Flexural Strength: 170 MPa
$ 1540/MT
- Density: 0.241 g/cc
- Water Absorption: 15 %
- Hardness, Shore O: 28
- Tensile Strength, Yield: 0.841 MPa
- Elongation at Break: 485 %
$ 1754/MT
- Specific Gravity: 1.90 g/cc
- Water Absorption: 0.23 %
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: 9.65 MPa
- Elongation at Break: 300 %
$ 1764/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 23.6 kV/mm
$ 1719/MT
- Hardness, Shore A: 85
- Tensile Strength, Yield: 89.6 MPa
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Thermal Conductivity: 0.800 W/m-K
$ 1534/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 22.4 kV/mm
$ 1896/MT
- Density: 0.401 g/cc
- Water Absorption: 15 %
- Hardness, Shore O: 20
- Tensile Strength, Yield: 0.689 MPa
- Elongation at Break: 340 %
$ 1508/MT
- Specific Gravity: 2.20 g/cc
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 275 %
- Dielectric Strength: 157 kV/mm
$ 1470/MT
- Density: 2.03 g/cc
- Deformation: 8.3 % @Time 86400 sec
- Hardness, Shore D: 60
- Tensile Strength: 20.7 MPa
- Elongation at Break: 230 %
$ 1506/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 18.9 kV/mm
$ 2083/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 57.0 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1535/MT
- Elongation at Break: 15 %
- Tear Strength: 17.5 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 15.0 kV/mm
$ 1903/MT
- Tensile Strength, Yield: 1.72 MPa
- Elongation at Break: 600 %
- Maximum Service Temperature, Air: 93.3 °C
- Minimum Service Temperature, Air: -34.4 °C
- Color: Translucent
$ 2239/MT
- Hardness, Shore A: 45 - 55
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 600 %
- Tear Strength: 28.0 kN/m
- Compression Set: 30 % @Temperature 160 °C
$ 1983/MT
- Specific Gravity: 1.89 g/cc
- Tear Strength Test: 12
- Tear Strength Test: 18
- Tear Strength: 37.7 kN/m
- Tear Strength: 55.2 kN/m
$ 1661/MT
- Density: 0.144 g/cc
- Water Absorption: 2.5 %
- Hardness, Shore OO: 28
- Tensile Strength, Yield: 0.338 MPa
- Elongation at Break: 135 %
$ 1465/MT
- Specific Gravity: 2.20 g/cc
- Tensile Strength, Yield: 41.4 MPa
- Elongation at Break: 350 %
- Dielectric Strength: 78.7 kV/mm
$ 1897/MT
- Density: 0.471 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 0.621 MPa
- Elongation at Break: 150 %
- Compressive Strength: 0.0689 MPa @Temperature 23.0 °C
$ 2109/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.414 GPa
$ 1658/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 33.3 kV/mm
$ 1739/MT
- Elongation at Break: 5.0 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 154 °C
- Minimum Service Temperature, Air: -28.9 °C
- Color: Natural
$ 1488/MT
- Elongation at Break: 350 %
- Tear Strength: 7.01 kN/m
- Maximum Service Temperature, Air: 107 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1515/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: <= 0.25 %
- Tensile Strength, Yield: 145 MPa
- Elongation at Break: 100 %
- Tensile Modulus: 2.41 GPa
$ 1453/MT
- Elongation at Break: 50 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 102 kV/mm
$ 2443/MT
- Tear Strength: 31.6 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: White
$ 1523/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.414 GPa
$ 1642/MT
- Elongation at Break: 250 %
- Tear Strength: 2.63 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 87.8 kV/mm
$ 1770/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 43.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 47.83 kV/mm
$ 1667/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: <= 0.010 %
- Hardness, Shore A: 67 - 77
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 240 %
$ 1965/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 48.2 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1522/MT
- Density: 1.95 g/cc
- Deformation: 3.0 % @Time 86400 sec
- Hardness, Shore D: 60
- Tensile Strength: 13.8 MPa
- Elongation at Break: 180 %
$ 1837/MT
- Density: 0.332 g/cc
- Water Absorption: 13 %
- Hardness, Shore O: 7.0
- Tensile Strength, Yield: 0.241 MPa
- Elongation at Break: 250 %
$ 1887/MT
- Density: 0.692 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 0.896 MPa
- Elongation at Break: 200 %
- Compressive Strength: 0.110 MPa @Temperature 23.0 °C
$ 1595/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 70.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 34.4 kV/mm
$ 1733/MT
- Density: 2.19 g/cc
- Deformation: 7.0 % @Time 86400 sec
- Hardness, Shore D: 60
- Tensile Strength: 18.6 MPa
- Elongation at Break: 220 %
$ 1661/MT
- Density: 0.637 g/cc
- Hardness, Shore O: 65
- Tensile Strength, Yield: 3.07 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00172 GPa
$ 2270/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 24.1 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.552 GPa
$ 1570/MT
- Density: 1.51 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Hardness, Rockwell E: 50
- Tensile Strength: 37.9 MPa @Temperature 260 °C
- Tensile Strength: 65.5 MPa @Temperature 23.0 °C
$ 2003/MT
- Density: 3.11 g/cc
- Hardness, Shore D: 60
- Tensile Strength: 21.4 MPa
- Elongation at Break: 200 %
- Tensile Modulus: 1.59 GPa
$ 1610/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 29.3 kV/mm
$ 2463/MT
- Specific Gravity: 1.78 g/cc
- Tear Strength Test: 2.5
- Tear Strength Test: 5.0
- Tear Strength: 12.3 kN/m
- Tear Strength: 15.8 kN/m
$ 2249/MT
- Specific Gravity: 1.60 g/cc
- Tensile Strength, Yield: 2.59 MPa
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 300 %
$ 2357/MT
- Hardness, Shore A: 55 - 65
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 200 %
- Tear Strength: 11.4 kN/m
- Compression Set: 15 % @Temperature 160 °C
$ 2175/MT
- Thermal Conductivity: 0.400 W/m-K
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -28.9 °C
- Volume Resistivity: 2.10e+14 ohm-cm
- Dielectric Strength: 23.6 kV/mm
$ 1478/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 131.2 kV/mm
$ 1811/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 550 %
- Tensile Modulus: 0.379 GPa
$ 1457/MT
- Elongation at Break: 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 26.3 kV/mm
$ 1542/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 20.7 MPa
- Elongation at Break: >= 200 %
- Tensile Modulus: 0.552 GPa
$ 1673/MT
- Density: 2.25 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Hardness, Shore D: 60
- Tensile Strength: 13.8 MPa
$ 1809/MT
- Elongation at Break: 120 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 68.9 kV/mm
$ 1521/MT
- Volatile Organic Compounds (VOC) Content: 1.5 g/l
- Hardness, Shore A: 74
- Elongation at Break: <= 10 %
- Flexural Strength: 5.17 MPa
- Tear Strength: 52.6 kN/m
$ 1646/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.50 %
- Tensile Strength, Yield: 107 MPa
- Elongation at Break: 105 %
- Tensile Modulus: 2.59 GPa
$ 1452/MT
- Elongation at Break: 75 %
- Compressive Strength: 0.0207 MPa
- Tear Strength: 3.51 kN/m
- Compression Set: 5.0 % @Temperature 100 °C
- Color: Gray
$ 1593/MT
- Specific Gravity: 1.78 g/cc
- Water Absorption: <= 0.040 %
- Tensile Strength, Yield: 34.5 - 49.6 MPa
- Elongation at Break: 100 - 250 %
- Tensile Modulus: 2.48 GPa
$ 1891/MT
- Specific Gravity: 0.700 g/cc
- Tensile Strength, Yield: 0.862 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 75 %
$ 1800/MT
- Density: 2.25 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Tensile Strength: 13.8 MPa
- Elongation at Break: 175 %
$ 2354/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 43.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1505/MT
- Elongation at Break: 450 %
- Tear Strength: 10.5 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -40.0 °C
- Dielectric Strength: 66.9 kV/mm
$ 1594/MT
- Elongation at Break: 225 %
- Tear Strength: 3.51 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Rose
$ 1971/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.414 GPa
$ 2228/MT
- Volatile Organic Compounds (VOC) Content: <= 1.0 g/l
- Hardness, Shore A: 76
- Elongation at Break: <= 10 %
- Flexural Strength: 5.17 MPa
- Tear Strength: 52.6 kN/m
$ 2394/MT
- Specific Gravity: 1.53 g/cc
- Water Absorption: 0.18 %
- Deformation: 0.10 % @Pressure 13.8 MPa
- Outgassing - Total Mass Loss: 0.010 %
- Outgassing - Total Mass Loss: 0.50 %
$ 1952/MT
- Specific Gravity: 1.21 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 5.52 MPa
- Tear Strength Test: 39.6
- Tear Strength Test: 39.6
$ 1603/MT
- Specific Gravity: 1.942 g/cc
- Tear Strength Test: 4.0
- Tear Strength Test: 7.0
- Tear Strength: 40.3 kN/m
- Tear Strength: 57.8 kN/m
$ 1684/MT
- Density: 0.0969 g/cc
- Water Absorption: 4.0 %
- Hardness, Shore OO: 13
- Tensile Strength, Yield: 0.103 MPa
- Elongation at Break: 140 %
$ 1997/MT
- Density: 0.332 g/cc
- Water Absorption: 10 %
- Hardness, Shore O: 53
- Tensile Strength, Yield: 1.37 MPa
- Elongation at Break: 380 %
$ 2286/MT
- Elongation at Break: <= 8.0 %
- Tear Strength: 3.51 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Aluminum
$ 2070/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 78.7 kV/mm
$ 1563/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1566/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 65.59 kV/mm
$ 1947/MT
- Density: 0.554 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 0.862 MPa
- Elongation at Break: <= 10 %
- Compressive Strength: 0.103 MPa @Temperature 23.0 °C
$ 1780/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength: 133.59 MPa
- Elongation at Yield: 5.2 %
- Tensile Modulus: 3.83 GPa
- Flexural Strength: 222.5 MPa
$ 1674/MT
- Density: 0.940 g/cc
- Deformation: 10 % @Time 86400 sec
- Hardness, Shore D: 62
- Tensile Strength: 31.0 MPa
- Elongation at Break: 230 %
$ 1476/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 10.3 MPa
- Elongation at Break: >= 100 %
- CTE, linear: 90.0 µm/m-°C @Temperature 20.0 °C
$ 2472/MT
- Density: 0.637 g/cc
- Tensile Strength, Yield: 2.00 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.00110 GPa
- Compressive Strength: 0.241 MPa
$ 2261/MT
- Density: 0.443 g/cc
- Tensile Strength, Yield: 1.17 MPa
- Elongation at Break: 215 %
- Maximum Service Temperature, Air: 93.3 °C
- Minimum Service Temperature, Air: -34.4 °C
- Color: White
$ 1523/MT
- Density: 0.241 g/cc
- Water Absorption: 2.4 %
- Tensile Strength, Yield: 0.414 MPa
- Elongation at Break: 220 %
- Compressive Strength: 0.0455 MPa
$ 1540/MT
- Tear Strength: 2.80 kN/m
- Thermal Conductivity: 0.500 W/m-K
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -28.9 °C
- Volume Resistivity: 2.63e+15 ohm-cm
$ 1551/MT
- Elongation at Break: 325 %
- Tear Strength: 2.63 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -40.0 °C
- Dielectric Strength: 84.3 kV/mm
$ 1686/MT
- Specific Gravity: 1.256 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 3.45 MPa
- Tear Strength Test: 28.6
- Tear Strength Test: 28.6
$ 1661/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 33.3 kV/mm
$ 1708/MT
- Hardness, Shore A: 85
- Tensile Strength, Yield: 89.6 MPa
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Thermal Conductivity: 1.25 W/m-K
$ 1855/MT
- Elongation at Break: 75 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 103.0 kV/mm
$ 1752/MT
- Specific Gravity: 0.700 g/cc
- Tensile Strength, Yield: 1.03 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 75 %
$ 1727/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 65.59 kV/mm
$ 1496/MT
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Black
$ 1586/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 0.20 %
- Tensile Strength: 112 MPa
- Elongation at Yield: 1.2 %
- Tensile Modulus: 15.9 GPa
$ 1591/MT
- Tear Strength: 14.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Black
$ 1771/MT
- Specific Gravity: 0.970 g/cc
- Water Absorption: 0.30 %
- Hardness, Shore A: 64
- Tensile Strength, Yield: 7.24 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 100 %
$ 1901/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.14 %
- Hardness, Shore A: 65
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 450 %
$ 1667/MT
- Density: 1.89 g/cc
- Deformation: 3 % @Temperature 23.0 °C, Pressure 10.3 MPa
- Tensile Strength: 8.27 MPa
- Elongation at Break: 160 %
- Compressive Yield Strength: 6.89 MPa
$ 2385/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.030 %
- Tensile Strength, Yield: 24.1 - 30.16 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.496 GPa
$ 1507/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 78.7 kV/mm
$ 2510/MT
- Elongation at Break: 200 %
- Tear Strength: 7.89 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 81.69 kV/mm
$ 1679/MT
- Elongation at Break: 120 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 78.7 kV/mm
$ 1810/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 20.7 MPa
- Elongation at Break: >= 200 %
- Tensile Modulus: 0.552 GPa
$ 2229/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 24.1 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.552 GPa
$ 1564/MT
- Elongation at Break: <= 10 %
- Tear Strength: 39.4 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 29.9 kV/mm
$ 1455/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 2594/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 33.5 kV/mm
$ 1701/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 5.91 kV/mm
$ 1506/MT
- Elongation at Break: 400 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 82.7 kV/mm
$ 1727/MT
- Specific Gravity: 1.67 g/cc
- Water Absorption: 0.17 %
- Hardness, Rockwell E: 24
- Tensile Strength, Ultimate: 51.7 MPa
- Elongation at Break: 3.2 %
$ 2362/MT
- Specific Gravity: 1.863 g/cc
- Tear Strength Test: 2.5
- Tear Strength Test: 5.0
- Tear Strength: 12.3 kN/m
- Tear Strength: 15.8 kN/m
$ 2381/MT
- Specific Gravity: 0.930 - 1.00 g/cc
- Tensile Strength, Yield: 37.9 MPa
- Elongation at Break: 200 - 300 %
- CTE, linear: 198 µm/m-°C @Temperature 20.0 °C
- Melting Point: 135 °C
- Maximum Service Temperature, Air: 93.3 °C
$ 1974/MT
- Specific Gravity: 1.43 g/cc
- Water Absorption: 0.23 %
- Hardness, Rockwell E: 64
- Tensile Strength, Ultimate: 86.0 MPa
- Tensile Strength, Ultimate: 37.0 MPa @Temperature 260 °C
$ 1879/MT
- Hardness, Shore A: 65 - 75
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 160 %
- Tear Strength: 10.5 kN/m
- Compression Set: 15 % @Temperature 160 °C
$ 1468/MT
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 19.7 kV/mm
- Dielectric Breakdown: 5000 V
- Color: White
$ 1635/MT
- Elongation at Break: 150 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -40.0 °C
- Dielectric Strength: 101 kV/mm
$ 1502/MT
- Density: 1.65 g/cc
- Water Absorption: 0.25 % @Time 86400 sec
- Water Absorption: 0.48 % @Time 173000 sec
- Hardness, Rockwell E: 5.0 - 20
- Tensile Strength: 31.0 MPa @Temperature 260 °C
$ 1472/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Color: Tan
$ 1453/MT
- Hardness, Shore A: 55 - 65
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 200 %
- Tear Strength: 8.77 kN/m
- Compression Set: 20 % @Temperature 160 °C
$ 1561/MT
- Elongation at Break: 200 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 89.96 kV/mm
$ 2329/MT
- Specific Gravity: 1.34 g/cc
- Deformation: 0.10 %
- Deformation: 0.00 % @Temperature 260 °C
- Tensile Strength, Ultimate: 75.8 MPa
- Tensile Strength, Ultimate: 36.5 MPa @Temperature 300 °C
$ 1648/MT
- Elongation at Break: 150 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Dielectric Strength: 106 kV/mm
$ 1452/MT
- Elongation at Break: 275 %
- Tear Strength: 3.51 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 87.4 kV/mm
$ 1594/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 49.2 kV/mm
$ 1907/MT
- Specific Gravity: 1.468 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 2.07 MPa
- Tear Strength Test: 10
- Tear Strength Test: 13.2
$ 2590/MT
- Hardness, Shore A: 85
- Tensile Strength, Yield: 89.6 MPa
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Thermal Conductivity: 0.900 W/m-K
$ 1982/MT
- Hardness, Shore A: 85
- Tensile Strength, Yield: 89.6 MPa
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Thermal Conductivity: 0.900 W/m-K
$ 1460/MT
- Elongation at Break: 110 %
- Tear Strength: 7.89 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 103 kV/mm
$ 1609/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 24.1 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.552 GPa
$ 2399/MT
- Specific Gravity: 1.70 g/cc
- Water Absorption: <= 0.25 %
- Tensile Strength, Yield: 124 MPa
- Elongation at Break: 100 %
- Tensile Modulus: 1.72 GPa
$ 1604/MT
- Elongation at Break: 120 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 78.7 kV/mm
$ 1926/MT
- Density: 2.60 g/cc
- Tensile Strength: 12.9 MPa
- Elongation at Break: 190 %
- Compressive Yield Strength: 6.89 MPa
- Coefficient of Friction, Dynamic: 0.15 - 0.25
$ 1644/MT
- Elongation at Break: 200 %
- Tear Strength: 11.4 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 94.5 kV/mm
$ 1510/MT
- Specific Gravity: 0.835 g/cc
- Water Absorption: 0.010 %
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: 180 %
- Tensile Modulus: 1.03 GPa
$ 2401/MT
- Elongation at Break: 15 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 288 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Green
$ 1560/MT
- Elongation at Break: 150 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Dielectric Strength: 98.4 kV/mm
$ 1611/MT
- Elongation at Break: 7.0 %
- Tear Strength: 22.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Aluminum
$ 1484/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 78.7 kV/mm
$ 2444/MT
- Elongation at Break: <= 5.0 %
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Copper
$ 1753/MT
- Density: 1.95 g/cc
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 260 °C
- Maximum Service Temperature, Air: 288 °C
- Minimum Service Temperature, Air: -240 °C
$ 1718/MT
- Specific Gravity: 1.57 g/cc
- Water Absorption: 0.030 %
- Tensile Strength: 46.0 MPa @Temperature 204 °C
- Tensile Strength: 69.0 MPa @Temperature 149 °C
- Tensile Strength: 175 MPa @Temperature 25.0 °C
$ 2126/MT
- Specific Gravity: 2.00 g/cc
- Tensile Strength, Yield: 27.2 MPa
- Elongation at Break: 300 %
- Melting Point: 327 °C
- Maximum Service Temperature, Air: 260 °C
$ 1507/MT
- Volatile Organic Compounds (VOC) Content: <= 0.50 g/l
- Hardness, Shore A: 79
- Elongation at Break: <= 10 %
- Flexural Strength: 5.52 MPa
- Tear Strength: 70.1 kN/m
$ 1889/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1765/MT
- Tensile Strength, Yield: 0.448 MPa
- Elongation at Break: 150 %
- Compressive Strength: 0.0689 MPa
- Compression Set: 25 % @Temperature 100 °C
- Color: Orange-Tan
$ 2363/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 2117/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 13.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 2481/MT
- Density: 2.09 g/cc
- Hardness, Shore D: 60
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 60 %
- Tensile Modulus: 1.59 GPa
$ 1578/MT
- Elongation at Break: 400 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -40.0 °C
- Dielectric Strength: 78.7 kV/mm
$ 1539/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1633/MT
- Density: 1.56 g/cc
- Deformation: 0.15 %
- Deformation: <= 0.0020 % @Temperature 260 °C
- Tensile Strength: 27.6 MPa @Temperature 260 °C
- Tensile Strength: 49.6 MPa @Temperature 23.0 °C
$ 2005/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 72.8 kV/mm
$ 2441/MT
- Density: 1.95 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Hardness, Shore D: 60
- Tensile Strength: 13.8 MPa
$ 1977/MT
- Density: 2.10 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Hardness, Shore D: 60
- Tensile Strength: 17.2 MPa
$ 1574/MT
- Density: 0.241 g/cc
- Water Absorption: 8.0 %
- Hardness, Shore OO: 20
- Tensile Strength, Yield: 0.221 MPa
- Elongation at Break: 105 %
$ 2364/MT
- Hardness, Shore A: 25 - 35
- Tensile Strength, Yield: 5.86 MPa
- Elongation at Break: 500 %
- Tear Strength: 7.01 kN/m
- Compression Set: 15 % @Temperature 160 °C
$ 1784/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1999/MT
- Specific Gravity: 2.16 g/cc
- Tensile Strength, Yield: >= 177 MPa
- Elongation at Break: >= 275 %
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -200 °C
$ 1478/MT
- Specific Gravity: 1.70 - 1.76 g/cc
- Water Absorption: <= 0.030 %
- Tensile Strength, Yield: 48.3 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.965 GPa
$ 1629/MT
- Thermal Conductivity: 0.640 W/m-K
- Melting Point: 53.00 °C
- Volume Resistivity: 2.23e+13 ohm-cm
- Dielectric Strength: 25.6 kV/mm
- Color: Blue
- Thermal Resistance: 0.08°C/W
$ 1758/MT
- Elongation at Break: 120 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 72.4 kV/mm
$ 1448/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: <= 0.010 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 69 @Time 15.0 sec
- Tensile Strength: 15.9 MPa
- Tensile Strength, Yield: 6.83 MPa @Strain 100 %
$ 1514/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Brown
$ 1544/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1915/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 33.5 kV/mm
$ 1704/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Tan
$ 1646/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength: 50.7 MPa
- Elongation at Yield: 6.3 %
- Tensile Modulus: 1.27 GPa
- Flexural Strength: 69.6 MPa
$ 1444/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.414 GPa
$ 1451/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.22 % @Temperature 22.8 °C, Time 86400 sec
- Hardness, Shore A: 66 @Time 15.0 sec
- Tensile Strength: 15.2 MPa
- Tensile Strength, Yield: 9.508 MPa @Strain 200 %
$ 1660/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 43.8 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1661/MT
- Elongation at Break: 75 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 112 kV/mm
$ 1567/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 78.7 kV/mm
$ 1938/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Brown
$ 2180/MT
- Hardness, Shore A: 65
- Elongation at Break: 350 %
- Tear Strength: 35.1 kN/m
- Thermal Conductivity: 1.55 W/m-K
- Volume Resistivity: 1.00e+14 ohm-cm
$ 1618/MT
- Specific Gravity: 2.20 g/cc
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Break: 300 %
- Melting Point: 327 °C
- Maximum Service Temperature, Air: 260 °C
$ 1878/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1489/MT
- Hardness, Shore A: 35 - 45
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 400 %
- Tear Strength: 13.1 kN/m
- Compression Set: 15 % @Temperature 160 °C
$ 2122/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 78.7 kV/mm
$ 1598/MT
- Tear Strength: 27.2 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Aluminum
$ 1946/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1525/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 48.2 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 2051/MT
- Density: 0.471 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 0.517 MPa
- Elongation at Break: 125 %
- Compressive Strength: 0.0689 MPa @Temperature 23.0 °C
$ 2251/MT
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Black
$ 1780/MT
- Specific Gravity: 0.980 g/cc
- Water Absorption: 0.30 %
- Hardness, Shore A: 61
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 375 %
$ 1498/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 70.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 17.5 kV/mm
$ 2179/MT
- Elongation at Break: 100 %
- Tear Strength: 17.5 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 56.3 kV/mm
$ 1654/MT
- Elongation at Break: 50 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 110 kV/mm
$ 2452/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 43.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Brown
$ 1477/MT
- Elongation at Break: 100 %
- Tear Strength: 17.5 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 60.6 kV/mm
$ 2186/MT
- Density: 1.57 g/cc
- Water Absorption: 0.030 % @Time 86400 sec
- Tensile Strength, Yield: 176 MPa
- Elongation at Break: 100 %
- Tensile Modulus: 1.72 GPa
$ 2584/MT
- Density: 0.241 g/cc
- Water Absorption: 2.4 %
- Tensile Strength, Yield: 0.414 MPa
- Elongation at Break: 220 %
- Compressive Strength: 0.0455 MPa
$ 1763/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 2147/MT
- Specific Gravity: 1.735 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 2.07 MPa
- Tear Strength Test: 10
- Tear Strength Test: 13.2
$ 1823/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 1.12 %
- Hardness, Shore A: 82
- Tensile Strength, Yield: 41.7 MPa
- Elongation at Break: 500 %
$ 1785/MT
- Specific Gravity: 1.585 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 3.45 MPa
- Tear Strength Test: 28.6
- Tear Strength Test: 28.6
$ 1550/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 15.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1503/MT
- Elongation at Break: 150 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 89.96 kV/mm
$ 1697/MT
- Hardness, Shore A: 85
- Tensile Strength, Yield: 89.6 MPa
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Thermal Conductivity: 0.900 W/m-K
$ 1509/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Rd/Bl/Cl
$ 1458/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 78.7 kV/mm
$ 1472/MT
- Elongation at Break: 175 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 101 kV/mm
$ 1885/MT
- Tear Strength: 28.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 25.2 kV/mm
- Dielectric Breakdown: 4500 V
- Color: White
$ 2190/MT
- Specific Gravity: 1.68 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 55.2 MPa
- Elongation at Break: 250 %
- Tensile Modulus: 1.38 GPa
$ 1483/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 78.7 kV/mm
$ 1499/MT
- Elongation at Break: <= 16 %
- Tear Strength: 12.3 kN/m
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Copper
$ 1456/MT
- Hardness, Shore A: 85
- Tensile Strength, Yield: 75.8 MPa
- Elongation at Break: <= 5.0 %
- Tear Strength: 17.5 kN/m
- Thermal Conductivity: 1.25 W/m-K
$ 1858/MT
- Specific Gravity: 1.60 g/cc
- Tensile Strength, Yield: 2.41 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 150 %
$ 2030/MT
- Specific Gravity: 1.60 g/cc
- Tensile Strength, Yield: 1.72 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 75 %
$ 2181/MT
- Density: 2.22 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Hardness, Shore D: 75
- Tensile Strength: 13.8 MPa
$ 2533/MT
- Density: 0.554 g/cc
- Water Absorption: <= 5.0 %
- Tensile Strength, Yield: 1.24 MPa
- Elongation at Break: 125 %
- Compressive Strength: 0.103 MPa @Temperature 23.0 °C
$ 1888/MT
- Density: 0.498 g/cc
- Hardness, Shore A: 35
- Tensile Strength, Yield: 1.24 MPa
- Elongation at Break: 125 %
- Compressive Modulus: 0.000214 GPa
$ 1544/MT
- Elongation at Break: <= 5.0 %
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Copper
$ 1576/MT
- Volatile Organic Compounds (VOC) Content: 1.0 g/l
- Hardness, Shore A: 81
- Elongation at Break: <= 10 %
- Flexural Strength: 5.17 MPa
- Tear Strength: 52.6 kN/m
$ 1705/MT
- Density: 2.30 g/cc
- Hardness, Shore D: 65
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 130 %
- Flexural Strength: 4.14 MPa
$ 1504/MT
- Specific Gravity: 1.55 g/cc
- Water Absorption: 0.17 %
- Hardness, Rockwell E: 23
- Tensile Strength, Ultimate: 46.9 MPa
- Elongation at Break: 3.5 %
$ 1611/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 21.9 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Brown
$ 1501/MT
- Elongation at Break: <= 5.0 %
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Copper
$ 1485/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 28.0 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1681/MT
- Density: 1.43 g/cc
- Water Absorption: 0.23 % @Time 86400 sec
- Water Absorption: 0.64 % @Time 173000 sec
- Deformation: 0.10 %
- Hardness, Rockwell E: 40 - 55
$ 1450/MT
- Elongation at Break: 50 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 118 kV/mm
$ 1530/MT
- Density: 2.23 g/cc
- Deformation: 8.5 % @Time 86400 sec
- Hardness, Shore D: 58
- Tensile Strength: 23.4 MPa
- Elongation at Break: 230 %
$ 1609/MT
- Elongation at Break: 500 %
- Tear Strength: 25.4 kN/m
- Maximum Service Temperature, Air: 107 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 2373/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 70.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1549/MT
- Elongation at Break: 400 %
- Tear Strength: 14.0 kN/m
- Maximum Service Temperature, Air: 107 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 2073/MT
- Elongation at Break: 300 %
- Tear Strength: 3.51 kN/m
- Maximum Service Temperature, Air: 107 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1686/MT
- Tear Strength: 28.9 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 24.2 kV/mm
- Dielectric Breakdown: 4300 V
- Color: White
$ 1627/MT
- Hardness, Shore A: 25 - 35
- Tensile Strength, Yield: 5.52 MPa
- Elongation at Break: 550 %
- Tear Strength: 8.77 kN/m
- Compression Set: 15 % @Temperature 160 °C
$ 1525/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 78.7 kV/mm
$ 2543/MT
- Specific Gravity: 1.42 g/cc
- Deformation: 0.14 %
- Tensile Strength, Ultimate: 66.9 MPa
- Tensile Strength, Ultimate: 31.7 MPa @Temperature 300 °C
- Tensile Strength, Ultimate: 34.5 MPa @Temperature 260 °C
$ 1911/MT
- Elongation at Break: 350 %
- Tear Strength: 7.01 kN/m
- Maximum Service Temperature, Air: 107 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 2106/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 70.1 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1730/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 27.6 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.552 GPa
$ 1650/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 21.9 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Copper
$ 2449/MT
- Elongation at Break: 50 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 102 kV/mm
$ 1475/MT
- Hardness, Shore A: 84
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: <= 5.0 %
- Tear Strength: 20.2 kN/m
- Thermal Conductivity: 0.800 W/m-K
$ 1458/MT
- Density: 0.144 g/cc
- Water Absorption: 2.5 %
- Hardness, Shore OO: 28
- Tensile Strength, Yield: 0.276 MPa
- Elongation at Break: 100 %
$ 1782/MT
- Density: 1.53 g/cc
- Water Absorption: 0.23 % @Time 86400 sec
- Water Absorption: 0.46 % @Time 173000 sec
- Hardness, Rockwell E: 1.0 - 15
- Tensile Strength: 29.6 MPa @Temperature 260 °C
$ 1449/MT
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 650 %
- Compressive Strength: 0.310 MPa
- Compression Set: 30 % @Temperature 100 °C
- Color: Light Gray
$ 2024/MT
- Density: 0.0969 g/cc
- Water Absorption: 3.0 %
- Hardness, Shore OO: 18
- Tensile Strength, Yield: 0.117 MPa
- Elongation at Break: 125 %
$ 1823/MT
- Specific Gravity: 1.001 g/cc
- Tear Strength Test: 12
- Tear Strength Test: 20
- Tear Strength: 21.9 kN/m
- Tear Strength: 30.7 kN/m
$ 2285/MT
- Tensile Strength, Ultimate: 50.0 MPa
- Tensile Strength, Ultimate: 1471 MPa
- Modulus of Elasticity: 45.3 GPa
- Compressive Yield Strength: 838 MPa
- Compressive Modulus: 45.0 GPa
- Shear Strength: 86.5 MPa
$ 1526/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 29.3 kV/mm
$ 1572/MT
- Elongation at Break: 100 %
- Tear Strength: 6.14 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 78.7 kV/mm
$ 2507/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 16.5 MPa
- Elongation at Break: >= 175 %
- CTE, linear: 90.0 µm/m-°C @Temperature 20.0 °C
$ 1500/MT
- Elongation at Break: 120 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 8.27 kV/mm
$ 2569/MT
- Elongation at Break: 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Aluminum
$ 1664/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Color: Tan
$ 1480/MT
- Specific Gravity: 1.175 g/cc
- Elongation at Break: <= 10 %
- Flexural Strength: 5.52 MPa
- Tear Strength Test: 39.6
- Tear Strength Test: 39.6
$ 2026/MT
- Specific Gravity: 1.883 g/cc
- Tear Strength Test: 12
- Tear Strength Test: 18
- Tear Strength: 37.7 kN/m
- Tear Strength: 55.2 kN/m
$ 1753/MT
- Specific Gravity: 2.20 g/cc
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: 300 %
- Melting Point: 327 °C
- Maximum Service Temperature, Air: 260 °C
$ 1500/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 28.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1750/MT
- Specific Gravity: 2.063 g/cc
- Tear Strength Test: 4.0
- Tear Strength Test: 7.0
- Tear Strength: 40.3 kN/m
- Tear Strength: 57.8 kN/m
$ 1709/MT
- Specific Gravity: 2.00 g/cc
- Tensile Strength, Yield: >= 196 MPa
- Elongation at Break: >= 200 %
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -200 °C
$ 1564/MT
- Tensile Strength, Yield: 0.621 MPa
- Elongation at Break: 150 %
- Compressive Strength: 0.0689 MPa
- Compression Set: 25 % @Temperature 100 °C
- Color: Orange-Tan
$ 2035/MT
- Elongation at Break: 425 %
- Tear Strength: 14.0 kN/m
- Maximum Service Temperature, Air: 107 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 1514/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.379 GPa
$ 1496/MT
- Tear Strength: 30.7 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Black
$ 1878/MT
- Density: 1.96 g/cc
- Hardness, Shore D: 65
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 40 %
- Tensile Modulus: 1.38 GPa
$ 2573/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 57.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1887/MT
- Elongation at Break: 275 %
- Tear Strength: 1.40 kN/m
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 101 kV/mm
$ 2212/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 65.7 kV/mm
$ 2361/MT
- Elongation at Break: 150 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 89.96 kV/mm
$ 2075/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength: 23.0 MPa @Temperature 204 °C
- Tensile Strength: 38.0 MPa @Temperature 149 °C
- Tensile Strength: 86.0 MPa @Temperature 25.0 °C
- Elongation at Break: 4.5 %
$ 1766/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 48.2 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1454/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 43.8 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1516/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 20.7 MPa
- Elongation at Break: >= 200 %
- Tensile Modulus: 0.552 GPa
$ 1624/MT
- Density: 0.471 g/cc
- Water Absorption: 5.0 %
- Tensile Strength, Yield: 0.896 MPa
- Elongation at Break: 275 %
- Maximum Service Temperature, Air: 93.3 °C
$ 1666/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 78.7 kV/mm
$ 1534/MT
- Specific Gravity: 2.025 g/cc
- Tear Strength Test: 9.0
- Tear Strength Test: 10
- Tear Strength: 21.0 kN/m
- Tear Strength: 21.0 kN/m
$ 1778/MT
- Specific Gravity: 0.897 g/cc
- Tear Strength Test: 4.0
- Tear Strength Test: 5.0
- Tear Strength: 7.01 kN/m
- Tear Strength: 10.5 kN/m
$ 1988/MT
- Elongation at Break: 15 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Green
$ 1592/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 28.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1595/MT
- Density: 2.11 g/cc
- Tensile Strength: 17.2 MPa
- Elongation at Break: 175 %
- Compressive Yield Strength: 6.89 MPa
- Coefficient of Friction, Dynamic: 0.10 - 0.20
$ 1634/MT
- Specific Gravity: 2.12 - 2.17 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 300 %
- Tensile Modulus: 0.483 GPa
$ 1738/MT
- Tear Strength: 14.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: White
$ 2115/MT
- Specific Gravity: 1.65 g/cc
- Tensile Strength: 103.05 MPa
- Elongation at Yield: 6.6 %
- Tensile Modulus: 3.91 GPa
- Flexural Strength: 157 MPa
$ 1986/MT
- Density: 0.332 g/cc
- Water Absorption: 15 %
- Hardness, Shore O: 20
- Tensile Strength, Yield: 0.689 MPa
- Elongation at Break: 400 %
$ 2001/MT
- Specific Gravity: 1.39 g/cc
- Water Absorption: 0.13 %
- Deformation: 0.10 % @Pressure 13.8 MPa
- Outgassing - Total Mass Loss: 0.010 %
- Outgassing - Total Mass Loss: 1.04 %
$ 1570/MT
- Specific Gravity: 0.700 g/cc
- Tensile Strength, Yield: 1.03 MPa
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 100 %
$ 1776/MT
- Hardness, Shore A: 45 - 55
- Tensile Strength, Yield: 6.21 MPa
- Elongation at Break: 400 %
- Tear Strength: 13.1 kN/m
- Compression Set: 15 % @Temperature 160 °C
$ 2480/MT
- Elongation at Break: 275 %
- Tear Strength: 1.40 kN/m
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 101 kV/mm
$ 2194/MT
- Volatile Organic Compounds (VOC) Content: <= 0.50 g/l
- Hardness, Shore A: 74
- Elongation at Break: <= 10 %
- Flexural Strength: 3.45 MPa
- Tear Strength: 52.6 kN/m
$ 1932/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 27.6 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.552 GPa
$ 1802/MT
- Hardness, Shore A: 25 - 35
- Tensile Strength, Yield: 7.93 MPa
- Elongation at Break: 800 %
- Tear Strength: 26.3 kN/m
- Compression Set: 30 % @Temperature 160 °C
$ 1753/MT
- Specific Gravity: 0.567 g/cc
- Tear Strength: 3.51 kN/m
- Tear Strength: 7.01 kN/m
- Color: Orange/Yellow
- Weight (oz/yd^2): 6.8
$ 2257/MT
- Specific Gravity: 0.601 g/cc
- Color: Tan/White or Blue/White
- Weight (oz/yd^2): 9
$ 1527/MT
- Specific Gravity: 0.758 g/cc
- Tear Strength: 4.38 kN/m
- Tear Strength: 8.77 kN/m
- Color: Orange/White
- Weight (oz/yd^2): 10.5
$ 2200/MT
- Thermal Conductivity: 0.400 W/m-K
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -28.9 °C
- Volume Resistivity: 2.10e+14 ohm-cm
- Dielectric Strength: 23.6 kV/mm
$ 1527/MT
- Thermal Conductivity: 0.400 W/m-K
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -28.9 °C
- Volume Resistivity: 2.10e+14 ohm-cm
- Dielectric Strength: 23.6 kV/mm
$ 1605/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 13.1 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -40.0 °C
- Color: Natural
$ 2249/MT
- Density: 2.11 g/cc
- Tensile Strength: 26.9 MPa
- Elongation at Break: 450 %
- Compressive Yield Strength: 6.89 MPa
- Coefficient of Friction, Dynamic: 0.10 - 0.20
$ 1582/MT
- Specific Gravity: 2.20 g/cc
- Tensile Strength, Yield: 41.4 MPa
- Elongation at Break: 350 %
- Dielectric Strength: 66.9 kV/mm
$ 1691/MT
- Specific Gravity: 1.60 g/cc
- Tensile Strength, Yield: 1.90 MPa
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 125 %
$ 1521/MT
- Elongation at Break: 7.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Aluminum
$ 1457/MT
- Tensile Strength, Ultimate: 606 MPa
- Tensile Strength, Ultimate: 655 MPa
- Modulus of Elasticity: 22.0 GPa
- Flexural Strength: 764 MPa
- Compressive Yield Strength: 524 MPa
- Compressive Modulus: 23.4 GPa
$ 1962/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 48.2 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1499/MT
- Elongation at Break: 15 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 288 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Green
$ 1684/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 48.2 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1643/MT
- Hardness, Shore A: 35 - 45
- Tensile Strength, Yield: 6.21 MPa
- Elongation at Break: 500 %
- Tear Strength: 14.0 kN/m
- Compression Set: 15 % @Temperature 160 °C
$ 1853/MT
- Density: 2.20 g/cc
- Tensile Strength: 14.8 MPa
- Elongation at Break: 210 %
- Compressive Yield Strength: 6.89 MPa
- Coefficient of Friction, Dynamic: 0.10 - 0.20
$ 1474/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 57.0 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1720/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -28.9 °C
- Dielectric Strength: 16.9 kV/mm
$ 1501/MT
- Elongation at Break: 120 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -51.1 °C
- Dielectric Strength: 78.7 kV/mm
$ 1717/MT
- Specific Gravity: 0.700 g/cc
- Tensile Strength, Yield: 1.03 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 125 %
$ 1869/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1452/MT
- Specific Gravity: 2.15 g/cc
- Water Absorption: <= 0.010 %
- Tensile Strength, Yield: >= 11.0 MPa
- Elongation at Break: >= 125 %
- CTE, linear: 90.0 µm/m-°C @Temperature 20.0 °C
$ 1569/MT
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 650 %
- Compressive Strength: 0.310 MPa
- Compression Set: 30 % @Temperature 100 °C
- Color: Light Gray
$ 2031/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 78.7 kV/mm
$ 1571/MT
- Elongation at Break: 120 %
- Tear Strength: 8.77 kN/m
- Maximum Service Temperature, Air: 163 °C
- Minimum Service Temperature, Air: -17.8 °C
- Dielectric Strength: 74.4 kV/mm
$ 1705/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 26.3 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 18.9 kV/mm
$ 1890/MT
- Hardness, Shore A: 65 - 75
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 350 %
- Tear Strength: 26.3 kN/m
- Compression Set: 30 % @Temperature 160 °C
$ 1997/MT
- Density: 2.25 g/cc
- Water Absorption: 0.00 % @Time 86400 sec
- Water Absorption at Saturation: 0.00 %
- Tensile Strength: 15.2 MPa
- Elongation at Break: 200 %
$ 1922/MT
- Elongation at Break: <= 5.0 %
- Tear Strength: 70.1 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Color: Natural
$ 1672/MT
- Elongation at Break: 275 %
- Tear Strength: 5.26 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 78.7 kV/mm
$ 1938/MT
- Elongation at Break: 100 %
- Tear Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Dielectric Strength: 65.59 kV/mm
Delivery Polymer Saint-Gobain Perfomance Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
tankers for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.