$ 1730/MT
- Density: 1.90 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 90
$ 2509/MT
- Elongation at Break: 120 %
- Tenacity: 0.0250 N/tex
- Shrinkage: 18 % @Temperature 150 °C
- Diameter (mm): 0.23
- Rigidity index (cN/dtex): 0.38
- Yarn Count (dtex): 500
$ 1827/MT
- Elongation at Break: 110 %
- Tenacity: 0.0210 N/tex
- Shrinkage: 15 % @Temperature 150 °C
- Diameter (mm): 0.4
- Rigidity index (cN/dtex): 0.55
- Yarn Count (dtex): 1670
$ 2207/MT
- Specific Gravity: 1.46 g/cc
- Filler Content: 43 %
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 1.6 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm
$ 1561/MT
- Density: 1.29 g/cc
- Moisture Absorption at Equilibrium: 0.28 %
- Linear Mold Shrinkage: 0.018 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 10 g/10 min @Temperature 230 °C
- Hardness, Shore A: 99
$ 1849/MT
- Density: 1.55 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Rockwell M: 95
$ 1455/MT
- Specific Gravity: 1.37 g/cc
- Filler Content: 30 %
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 1.7 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 1.00 mm
$ 1571/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.48 %
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 10 g/10 min @Temperature 190 °C
- Hardness, Shore A: 89
$ 1495/MT
- Density: 1.21 g/cc
- Moisture Absorption at Equilibrium: 0.40 %
- Linear Mold Shrinkage: 0.012 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 17 g/10 min @Temperature 230 °C
- Hardness, Shore A: 96
$ 2156/MT
- Density: 1.59 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1477/MT
- Density: 1.59 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 2203/MT
- Density: 1.23 g/cc
- Moisture Absorption at Equilibrium: 0.36 %
- Linear Mold Shrinkage: 0.013 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 20 g/10 min @Temperature 230 °C
- Hardness, Shore A: 98
$ 2018/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 30 %
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 1.7 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm @Thickness 1.00 mm
$ 2247/MT
- Density: 1.12 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 39.0 MPa
- Tensile Strength, Yield: 4.30 MPa @Strain 100 %
- Elongation at Break: 510 %
- Tear Strength: 88.0 kN/m
$ 1582/MT
- Specific Gravity: 1.36 g/cc
- Filler Content: 30 %
- Water Absorption: 1.3 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm
$ 1597/MT
- Density: 1.23 g/cc
- Hardness, Shore D: 64
- Tensile Strength, Ultimate: 44.0 MPa
- Tensile Strength, Yield: 22.6 MPa @Strain 100 %
- Elongation at Break: 400 %
$ 1566/MT
- Density: 1.12 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 39.0 MPa
- Tensile Strength, Yield: 5.40 MPa @Strain 100 %
- Elongation at Break: 510 %
$ 2124/MT
- Density: 1.90 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 90
$ 1884/MT
- Density: 1.42 g/cc
- Water Absorption: 0.67 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 120
$ 2471/MT
- Density: 1.65 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 90
$ 1493/MT
- Density: 1.43 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Hardness, Rockwell M: 90
$ 1554/MT
- Density: 1.96 g/cc
- Water Absorption: 0.020 %
- Linear Mold Shrinkage: 0.0015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm
- Hardness, Rockwell R: 121
$ 1992/MT
- Density: 1.59 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1615/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 1.8 %
- Moisture Absorption at Equilibrium: 3.5 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm @Thickness 3.00 mm
$ 1829/MT
- Density: 1.17 g/cc
- Filler Content: 15 %
- Water Absorption: 0.50 %
- Water Absorption: 2.1 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 1.00 mm
$ 1663/MT
- Density: 1.65 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1459/MT
- Specific Gravity: 1.12 g/cc
- Water Absorption: 1.1 %
- Moisture Absorption at Equilibrium: 2.4 %
- Linear Mold Shrinkage: 0.0060 - 0.012 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.015 - 0.022 cm/cm @Thickness 3.00 mm
$ 1585/MT
- Density: 1.28 g/cc
- Moisture Absorption at Equilibrium: 0.30 %
- Linear Mold Shrinkage: 0.017 cm/cm @Thickness 2.00 mm
- Melt Flow: 12 g/10 min @Temperature 230 °C
- Hardness, Shore A: 99
$ 1754/MT
- Density: 1.24 g/cc
- Moisture Absorption at Equilibrium: 0.38 %
- Linear Mold Shrinkage: 0.013 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 12 g/10 min @Temperature 230 °C
- Hardness, Shore A: 97
$ 2207/MT
- Density: 1.45 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 120
$ 1883/MT
- Specific Gravity: 1.48 g/cc
- Filler Content: 45 %
- Water Absorption: 1.1 %
- Moisture Absorption at Equilibrium: 1.9 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm
$ 2288/MT
- Density: 1.44 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1780/MT
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.40 %
- Linear Mold Shrinkage: 0.011 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 3.0 g/10 min @Temperature 230 °C
- Hardness, Shore A: 96
$ 1474/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 0.45 %
- Linear Mold Shrinkage: 0.0070 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 22 g/10 min @Temperature 230 °C
- Hardness, Shore A: 94
$ 1776/MT
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 0.43 %
- Linear Mold Shrinkage: 0.010 cm/cm @Thickness 2.00 mm
- Melt Flow: 20 g/10 min @Temperature 230 °C
- Hardness, Shore A: 96
$ 1461/MT
- Density: 0.970 g/cc
- Water Absorption: 0.00 %
- Tensile Strength, Ultimate: 3500 MPa
- Modulus of Elasticity: 110 GPa
- Tenacity: 3.53 N/tex
- Maximum Service Temperature, Air: 150 °C
$ 2229/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 64
- Tensile Strength, Ultimate: 47.0 MPa
- Tensile Strength, Yield: 22.6 MPa @Strain 100 %
- Elongation at Break: 440 %
$ 1999/MT
- Density: 1.59 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1660/MT
- Density: 1.29 g/cc
- Moisture Absorption at Equilibrium: 0.28 %
- Linear Mold Shrinkage: 0.018 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 8.0 g/10 min @Temperature 230 °C
- Hardness, Shore A: 99
$ 2454/MT
- Density: 1.48 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 120
$ 1770/MT
- Elongation at Break: 280 %
- Tenacity: 0.0160 N/tex
- Shrinkage: 32 % @Temperature 150 °C
- Diameter (mm): 0.48
- Rigidity index (cN/dtex): 0.1
- Yarn Count (dtex): 2220
$ 2129/MT
- Density: 1.26 g/cc
- Moisture Absorption at Equilibrium: 0.34 %
- Linear Mold Shrinkage: 0.015 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 10 g/10 min @Temperature 230 °C
- Hardness, Shore A: 98
$ 1670/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 1.0 %
- Moisture Absorption at Equilibrium: 2.9 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm @Thickness 3.00 mm
$ 1866/MT
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.36 %
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 2.00 mm
- Melt Flow: 20 g/10 min @Temperature 230 °C
- Hardness, Shore A: 96
$ 1607/MT
- Density: 1.28 g/cc
- Moisture Absorption at Equilibrium: 0.38 %
- Linear Mold Shrinkage: 0.013 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 12 g/10 min @Temperature 230 °C
- Hardness, Shore A: 98
$ 1899/MT
- Specific Gravity: 1.17 g/cc
- Filler Content: 15 %
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 2.1 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 1.00 mm
$ 1782/MT
- Specific Gravity: 1.59 g/cc
- Filler Content: 30 %
- Water Absorption: 1.1 %
- Moisture Absorption at Equilibrium: 1.9 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 1.00 mm
$ 1469/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 1.2 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.0060 - 0.012 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.015 - 0.022 cm/cm @Thickness 3.00 mm
$ 1666/MT
- Specific Gravity: 1.62 g/cc
- Filler Content: 35 %
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 1.5 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm
$ 1568/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 2.3 %
- Moisture Absorption at Equilibrium: 3.5 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm @Thickness 3.00 mm
$ 2084/MT
- Density: 1.14 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 39.0 MPa
- Tensile Strength, Yield: 8.30 MPa @Strain 100 %
- Elongation at Break: 500 %
- Tear Strength: 118 kN/m
$ 2396/MT
- Density: 1.65 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 2595/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 95
- Tensile Strength, Ultimate: 44.0 MPa
- Tensile Strength, Yield: 13.3 MPa @Strain 100 %
- Elongation at Break: 500 %
- Tear Strength: 147 kN/m
$ 1567/MT
- Density: 1.81 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1984/MT
- Density: 1.65 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1538/MT
- Density: 1.28 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage: 0.0070 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 118
$ 1627/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 34.0 MPa
- Tensile Strength, Yield: 5.40 MPa @Strain 100 %
- Elongation at Break: 500 %
- Tear Strength: 93.0 kN/m
$ 1508/MT
- Density: 1.22 g/cc
- Water Absorption: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 3.00 mm
- Tensile Strength at Break: 66.0 MPa
$ 1479/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 34.0 MPa
- Tensile Strength, Yield: 4.40 MPa @Strain 100 %
- Elongation at Break: 650 %
- Tear Strength: 93.0 kN/m
$ 2305/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 0.45 %
- Linear Mold Shrinkage: 0.0070 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 22 g/10 min @Temperature 230 °C
- Hardness, Shore A: 94
$ 1655/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 71
- Tensile Strength, Ultimate: 51.0 MPa
- Tensile Strength, Yield: 25.5 MPa @Strain 100 %
- Elongation at Break: 380 %
$ 2209/MT
- Elongation at Break: 290 %
- Tenacity: 0.0160 N/tex
- Shrinkage: 38 % @Temperature 150 °C
- Diameter (mm): 0.25
- Rigidity index (cN/dtex): 0.086
- Yarn Count (dtex): 550
$ 1722/MT
- Density: 1.65 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 2118/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 90
$ 1761/MT
- Density: 1.21 g/cc
- Moisture Absorption at Equilibrium: 0.40 %
- Linear Mold Shrinkage: 0.012 cm/cm @Thickness 2.00 mm
- Melt Flow: 18 g/10 min @Temperature 190 °C
- Hardness, Shore A: 96
$ 1727/MT
- Density: 1.56 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1643/MT
- Density: 1.59 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Rockwell M: 95
$ 1591/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 0.45 %
- Linear Mold Shrinkage: 0.0070 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 0.50 g/10 min @Temperature 230 °C
- Hardness, Shore A: 97
$ 1582/MT
- Elongation at Break: 180 %
- Tenacity: 0.0200 N/tex
- Shrinkage: 25 % @Temperature 150 °C
- Diameter (mm): 0.46
- Rigidity index (cN/dtex): 0.22
- Yarn Count (dtex): 2080
$ 1648/MT
- Elongation at Break: 160 %
- Tenacity: 0.0200 N/tex
- Shrinkage: 20 % @Temperature 150 °C
- Diameter (mm): 0.46
- Rigidity index (cN/dtex): 0.35
- Yarn Count (dtex): 2080
$ 1940/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 30 %
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 1.7 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm @Thickness 1.00 mm
$ 1773/MT
- Density: 2.09 g/cc
- Water Absorption: 0.020 %
- Linear Mold Shrinkage: 0.0013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 cm/cm
- Hardness, Rockwell R: 121
$ 1936/MT
- Density: 1.54 g/cc
- Moisture Absorption at Equilibrium: 2.0 %
- Moisture Absorption at Equilibrium: 3.5 %
- Tensile Strength, Ultimate: 5800 MPa
- Elongation at Break: 3.5 %
$ 1673/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 0.56 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 10 g/10 min @Temperature 190 °C
- Hardness, Shore A: 82
$ 2590/MT
- Specific Gravity: 1.28 g/cc
- Filler Content: 20 %
- Water Absorption: 0.50 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm @Thickness 3.00 mm
$ 1556/MT
- Density: 1.65 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Hardness, Rockwell M: 93
$ 1885/MT
- Elongation at Break: 230 %
- Tenacity: 0.0190 N/tex
- Shrinkage: 19 % @Temperature 150 °C
- Diameter (mm): 0.32
- Rigidity index (cN/dtex): 0.15
- Yarn Count (dtex): 1000
$ 1838/MT
- Density: 1.59 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell M: 91
$ 1953/MT
- Density: 1.26 g/cc
- Moisture Absorption at Equilibrium: 0.30 %
- Linear Mold Shrinkage: 0.016 cm/cm @Thickness 2.00 mm
- Melt Flow: 13 g/10 min @Temperature 230 °C
- Hardness, Shore A: 99
$ 1558/MT
- Density: 1.29 g/cc
- Water Absorption: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm @Thickness 3.00 mm
- Tensile Strength at Break: 87.0 MPa
$ 1626/MT
- Density: 1.33 g/cc
- Moisture Absorption at Equilibrium: 0.38 %
- Linear Mold Shrinkage: 0.013 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 12 g/10 min @Temperature 230 °C
- Hardness, Shore A: 98
$ 2062/MT
- Specific Gravity: 1.36 g/cc
- Filler Content: 30 %
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 1.7 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm
$ 2582/MT
- Elongation at Break: 330 %
- Tenacity: 0.0120 N/tex
- Shrinkage: 30 % @Temperature 150 °C
- Diameter (mm): 0.45
- Rigidity index (cN/dtex): 0.072
- Yarn Count (dtex): 2220
$ 1819/MT
- Elongation at Break: 140 %
- Tenacity: 0.0220 N/tex
- Shrinkage: 16 % @Temperature 150 °C
- Diameter (mm): 0.45
- Rigidity index (cN/dtex): 0.5
- Yarn Count (dtex): 2080
$ 1755/MT
- Density: 1.59 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 90
$ 2332/MT
- Density: 1.30 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Hardness, Rockwell M: 80
$ 2105/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1532/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2538/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2216/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1861/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1498/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1543/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1810/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1534/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1905/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1885/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1528/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1784/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2073/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1676/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1999/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2372/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2147/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2264/MT
- Density: 1.14 g/cc
- Water Absorption: 1.2 %
- Water Absorption: 2.5 %
- Linear Mold Shrinkage: 0.0060 - 0.012 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.015 - 0.022 cm/cm @Thickness 3.00 mm
$ 1473/MT
- Density: 1.42 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell M: 80
$ 1530/MT
- Density: 1.91 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell M: 90
$ 1764/MT
- Density: 1.17 g/cc
- Filler Content: 15 %
- Water Absorption: 0.50 %
- Water Absorption: 2.1 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm @Thickness 1.00 mm
$ 1677/MT
- Specific Gravity: 1.57 g/cc
- Filler Content: 50 %
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 1.2 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm
$ 2198/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 1.3 %
- Moisture Absorption at Equilibrium: 3.0 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm @Thickness 3.00 mm
$ 1803/MT
- Specific Gravity: 1.48 g/cc
- Filler Content: 40 %
- Water Absorption: 0.90 %
- Moisture Absorption at Equilibrium: 2.0 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm @Thickness 1.00 mm
$ 1488/MT
- Density: 1.24 g/cc
- Moisture Absorption at Equilibrium: 0.38 %
- Linear Mold Shrinkage: 0.013 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 16 g/10 min @Temperature 230 °C
- Hardness, Shore A: 97
$ 1449/MT
- Density: 1.55 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 cm/cm
- Hardness, Rockwell R: 120
$ 1569/MT
- Density: 1.56 g/cc
- Moisture Absorption at Equilibrium: 0.60 %
- Moisture Absorption at Equilibrium: 1.0 %
- Tensile Strength, Ultimate: 5800 MPa
- Elongation at Break: 2.5 %
$ 1669/MT
- Density: 1.38 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 90
$ 2166/MT
- Specific Gravity: 1.26 g/cc
- Filler Content: 15 %
- Water Absorption: 1.0 %
- Moisture Absorption at Equilibrium: 2.1 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm @Thickness 1.00 mm
$ 1499/MT
- Density: 1.36 g/cc
- Moisture Absorption at Equilibrium: 0.40 %
- Linear Mold Shrinkage: 0.0080 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 22 g/10 min @Temperature 230 °C
- Hardness, Shore A: 96
$ 1872/MT
- Density: 1.28 g/cc
- Moisture Absorption at Equilibrium: 0.25 %
- Linear Mold Shrinkage: 0.017 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 10 g/10 min @Temperature 230 °C
- Hardness, Shore A: 99
$ 1632/MT
- Density: 1.65 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell R: 122
$ 1638/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: 0.58 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 2.00 mm
- Melt Flow: 14 g/10 min @Temperature 190 °C
- Hardness, Shore A: 70
$ 1538/MT
- Specific Gravity: 1.43 g/cc
- Filler Content: 37 %
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.0080 - 0.013 cm/cm @Thickness 3.00 mm
$ 1629/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 92
- Tensile Strength, Ultimate: 42.0 MPa
- Tensile Strength, Yield: 7.40 MPa @Strain 100 %
- Elongation at Break: 500 %
- Tear Strength: 118 kN/m
$ 1784/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 0.56 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 10 g/10 min @Temperature 190 °C
- Hardness, Shore A: 82
$ 1772/MT
- Specific Gravity: 1.64 g/cc
- Filler Content: 55 %
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 1.00 mm
$ 1791/MT
- Elongation at Break: 250 %
- Tenacity: 0.0160 N/tex
- Shrinkage: 24 % @Temperature 150 °C
- Diameter (mm): 0.48
- Rigidity index (cN/dtex): 0.14
- Yarn Count (dtex): 2220
$ 1538/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.48 %
- Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 18 g/10 min @Temperature 230 °C
- Hardness, Shore A: 93
$ 1595/MT
- Specific Gravity: 1.33 g/cc
- Filler Content: 25 %
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 2.7 %
- Linear Mold Shrinkage: 0.0020 - 0.0030 cm/cm @Thickness 1.00 mm
$ 1806/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1717/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2340/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1877/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2090/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1618/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 2407/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1797/MT
- Density: 1.45 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Hardness, Rockwell M: 90
$ 1526/MT
- Density: 1.39 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0055 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 120
$ 1725/MT
- Specific Gravity: 1.74 g/cc
- Filler Content: 60 %
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 1.4 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 1.00 mm
$ 2069/MT
- Density: 1.70 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell M: 95
$ 1463/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 34.0 MPa
- Tensile Strength, Yield: 4.40 MPa @Strain 100 %
- Elongation at Break: 650 %
$ 2265/MT
- Density: 1.68 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 95
$ 1791/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 1.3 %
- Moisture Absorption at Equilibrium: 2.4 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1542/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 1.9 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 3.00 mm
$ 1568/MT
- Specific Gravity: 1.81 g/cc
- Filler Content: 55 %
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm
$ 1531/MT
- Density: 1.32 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell M: 80
$ 2446/MT
- Density: 1.59 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell M: 90
$ 1685/MT
- Density: 1.17 g/cc
- Hardness, Shore D: 64
- Tensile Strength, Ultimate: 44.0 MPa
- Tensile Strength, Yield: 20.6 MPa @Strain 100 %
- Elongation at Break: 400 %
$ 1716/MT
- Density: 1.48 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Hardness, Rockwell M: 95
$ 1743/MT
- Density: 1.42 g/cc
- Water Absorption: 0.67 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 120
$ 1926/MT
- Density: 1.42 g/cc
- Water Absorption: 0.67 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 120
$ 1529/MT
- Density: 1.42 g/cc
- Water Absorption: 0.67 %
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell R: 120
$ 1831/MT
- Density: 1.14 g/cc
- Water Absorption: 1.2 %
- Water Absorption: 2.5 %
- Linear Mold Shrinkage: 0.0060 - 0.012 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.015 - 0.022 cm/cm @Thickness 3.00 mm
$ 2104/MT
- Density: 1.14 g/cc
- Moisture Absorption at Equilibrium: 0.45 %
- Linear Mold Shrinkage: 0.0080 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 17 g/10 min @Temperature 230 °C
- Hardness, Shore A: 95
$ 1558/MT
- Density: 1.65 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell M: 93
$ 1646/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 34.0 MPa
- Tensile Strength, Yield: 5.40 MPa @Strain 100 %
- Elongation at Break: 500 %
$ 1725/MT
- Specific Gravity: 1.56 g/cc
- Filler Content: 23 %
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 1.8 %
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm @Thickness 1.00 mm
$ 1742/MT
- Tensile Strength, Ultimate: 2700 MPa
- Tensile Modulus: 140 GPa
- Flexural Yield Strength: 550 MPa
- Flexural Modulus: 70.0 GPa
- Poissons Ratio: 0.30
$ 1972/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 1.1 %
- Moisture Absorption at Equilibrium: 2.4 %
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.014 - 0.018 cm/cm @Thickness 3.00 mm
$ 1607/MT
- Density: 1.58 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 3.00 mm
- Hardness, Rockwell M: 90
$ 1588/MT
- Density: 1.64 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.0023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Hardness, Rockwell R: 122
$ 1752/MT
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.40 %
- Linear Mold Shrinkage: 0.011 cm/cm @Thickness 2.00 mm
- Melt Index of Compound: 20 g/10 min @Temperature 230 °C
- Hardness, Shore A: 96
$ 1462/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 2.0 %
- Linear Mold Shrinkage: 0.0090 - 0.012 cm/cm @Thickness 1.00 mm
- Linear Mold Shrinkage: 0.018 - 0.023 cm/cm @Thickness 3.00 mm
$ 1985/MT
- Specific Gravity: 1.25 g/cc
- Filler Content: 15 %
- Water Absorption: 1.4 %
- Moisture Absorption at Equilibrium: 3.0 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm @Thickness 1.00 mm
$ 1453/MT
- Density: 1.75 g/cc
- Water Absorption: 0.020 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 cm/cm
- Hardness, Rockwell R: 123
$ 2096/MT
- Density: 1.35 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Hardness, Rockwell M: 90
$ 1904/MT
- Density: 1.59 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell M: 90
Delivery Polymer Toyobo
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.