$ 1587/MT
- Density: 0.940 g/cc
- Butyl Acrylate Content: 18 %
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 14.0 MPa
$ 1648/MT
- Density: 0.917 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 500 %
- Melt Temperature: 149 - 166 °C
$ 1978/MT
- Density: 0.942 g/cc
- Methyl Acrylate Content: 17 %
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 37
- Tensile Strength at Break: 12.0 MPa
$ 1531/MT
- Specific Gravity: 0.906 g/cc
- Viscosity: 3000 - 4800 cP @Temperature 150 °C
- Brookfield Viscosity: 1800 cP @Temperature 190 °C
- Brookfield Viscosity: 8950 cP @Temperature 125 °C
- Molecular Weight: 17000 g/mol
$ 2081/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Viscosity: 780 - 1280 cP @Temperature 125 °C
- Brookfield Viscosity: 1050 cP @Temperature 125 °C
- Molecular Weight: 9200 g/mol
- Flash Point: >= 343 °C
$ 2137/MT
- Specific Gravity: 0.890 - 0.920 g/cc
- Viscosity: 6300 - 10000 cP @Temperature 150 °C
- Brookfield Viscosity: 2850 cP @Temperature 190 °C
- Brookfield Viscosity: 16650 cP @Temperature 125 °C
- Molecular Weight: 26000 g/mol
$ 1981/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Viscosity: 75 - 200 cP @Temperature 125 °C
- Brookfield Viscosity: 150 cP @Temperature 125 °C
- Molecular Weight: 4000 g/mol
- Flash Point: >= 343 °C
$ 1556/MT
- Specific Gravity: 0.920 g/cc
- Viscosity: 150 - 700 cP @Temperature 190 °C
- Brookfield Viscosity: 300 cP @Temperature 190 °C
- Molecular Weight: 9100.0 g/mol
- Flash Point: >= 277 °C
$ 1506/MT
- Density: 0.950 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 24.5 MPa
- Elongation at Break: 10 %
- Vicat Softening Point: 115 °C
- Process: Coating
$ 1535/MT
- Density: 0.945 g/cc
- Methyl Acrylate Content: 24 %
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 34
- Tensile Strength at Break: 8.00 MPa
$ 2587/MT
- Density: 0.920 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 8.00 MPa
- Elongation at Break: 70 %
- 2% Secant Modulus: 0.221 GPa
$ 1625/MT
- Density: 0.926 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.60 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1150 %
$ 1935/MT
- Density: 0.920 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 800 %
$ 1683/MT
- Density: 0.950 g/cc
- Melt Flow: 10.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 10 %
- Flexural Modulus: 0.965 GPa
$ 1798/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Viscosity: 1200 - 1850 cP @Temperature 125 °C
- Brookfield Viscosity: 1500 cP @Temperature 125 °C
- Molecular Weight: 10000 g/mol
- Flash Point: >= 343 °C
$ 1624/MT
- Density: 0.910 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Processing Temperature: 216 - 232 °C
- Blow-up Ratio (BUR): 2.4
- Process: Blown Film
- Region: US & Canada
$ 2027/MT
- Density: 0.943 g/cc
- Methyl Acrylate Content: 17 %
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 37
- Tensile Strength at Break: 12.0 MPa
$ 2281/MT
- Density: 0.925 g/cc
- Thickness: 25.4 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 12.4 MPa
$ 1945/MT
- Density: 0.925 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.55 g/10 min
- Film Elongation at Break, MD: 950 %
- Film Elongation at Break, TD: 1000 %
$ 2510/MT
- Density: 0.913 - 0.919 g/cc
- Brookfield Viscosity: 19 cP @Load 0.00000220 kg, Temperature 190 °C
- Molecular Weight: 100000 g/mol
- Melt Flow: 16 - 24 g/10 min
- Flash Point: >= 343 °C
$ 1656/MT
- Density: 0.948 g/cc
- Methyl Acrylate Content: 22 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 37
- Tensile Strength at Break: 11.0 MPa
$ 1630/MT
- Specific Gravity: 0.890 - 0.920 g/cc
- Viscosity: 2400 - 6000 cP @Temperature 150 °C
- Brookfield Viscosity: 1750 cP @Temperature 190 °C
- Brookfield Viscosity: 7750 cP @Temperature 125 °C
- Molecular Weight: 15000 g/mol
$ 1687/MT
- Density: 0.910 g/cc
- Melt Flow: 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 120 °C
- Crystallization Temperature: 88.0 °C
$ 1670/MT
- Density: 0.918 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.1 g/10 min
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1525/MT
- Density: 0.9215 g/cc
- Melt Flow: 5.7 g/10 min
- Tensile Strength, Ultimate: 10.3 MPa
- Elongation at Break: 475 %
- Tensile Modulus: 0.138 GPa
$ 1946/MT
- Density: 0.940 g/cc
- Melt Flow: 2.5 g/10 min
- Dart Drop Test: 390 g
- Film Tensile Strength at Break, MD: 24.8 MPa
- Film Tensile Strength at Break, TD: 24.1 MPa
$ 1510/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 1558/MT
- Density: 0.916 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 9.00 MPa
- Elongation at Break: 300 %
- 2% Secant Modulus: 0.200 GPa
$ 1880/MT
- Density: 0.943 g/cc
- Brookfield Viscosity: 500 cP @Temperature 140 °C
- Brookfield Viscosity: 700 cP @Temperature 125 °C
- Molecular Weight: 1037 g/mol
- Molecular Weight: 4538 g/mol
$ 1562/MT
- Specific Gravity: 0.890 - 0.920 g/cc
- Viscosity: 2400 - 6000 cP @Temperature 150 °C
- Brookfield Viscosity: 1550 cP @Temperature 190 °C
- Brookfield Viscosity: 7750 cP @Temperature 125 °C
- Molecular Weight: 15000 g/mol
$ 1502/MT
- Density: 0.918 g/cc
- Melt Flow: 8.0 g/10 min
- Tensile Strength, Ultimate: 9.65 MPa
- Elongation at Break: 400 %
- Tensile Modulus: 0.138 GPa
$ 1654/MT
- Density: 0.926 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.60 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1150 %
$ 1732/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Viscosity: 250 - 450 cP @Temperature 150 °C
- Brookfield Viscosity: 600 cP @Temperature 125 °C
- Molecular Weight: 6500 g/mol
- Flash Point: >= 343 °C
$ 1988/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 2.5 %
- Thickness: 31.8 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 350 %
$ 2106/MT
- Specific Gravity: 0.930 - 0.960 g/cc
- Viscosity: 150 - 300 cP @Temperature 125 °C
- Brookfield Viscosity: 225 cP @Temperature 125 °C
- Molecular Weight: 3600 g/mol
- Flash Point: >= 204 °C
$ 2131/MT
- Density: 0.9265 g/cc
- Vinyl Acetate Content: 4.0 %
- Thickness: 31.8 microns
- Melt Flow: 1.4 g/10 min
- Film Elongation at Break, MD: 300 %
$ 1874/MT
- Vinyl Acetate Content: 6.0 %
- Thickness: 31.8 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 450 %
- Film Elongation at Break, TD: 770 %
$ 2054/MT
- Density: 0.941 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 39
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 600 %
$ 1521/MT
- Density: 0.920 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 122 °C
- Crystallization Temperature: 103 °C
$ 1824/MT
- Density: 0.909 g/cc
- Melt Flow: 200 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 6.20 MPa
- Elongation at Break: 100 %
- 2% Secant Modulus: 0.103 GPa
$ 2225/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 600 %
$ 2222/MT
- Density: 0.943 g/cc
- Methyl Acrylate Content: 24 %
- Melt Flow: 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 74.0 °C
- Crystallization Temperature: 43.0 °C
$ 1738/MT
- Density: 0.931 g/cc
- Methyl Acrylate Content: 9.0 %
- Melt Flow: 8.0 g/10 min
- Dart Drop: 4.45 g/micron
- Film Tensile Strength at Break, MD: 27.6 MPa
$ 1994/MT
- Density: 0.923 g/cc
- Melt Flow: 4.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 100 %
- 2% Secant Modulus: 0.310 GPa
$ 1473/MT
- Density: 0.940 g/cc
- Vinyl Acetate Content: 18.5 %
- Melt Flow: 2.5 g/10 min
- Hardness, Shore D: 32
- Tensile Strength at Break: 12.0 MPa
$ 1610/MT
- Density: 0.931 g/cc
- Melt Flow: 2.0 g/10 min
- Tensile Strength, Ultimate: 32.4 MPa
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 950 %
$ 1659/MT
- Density: 0.906 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.50 g/10 min
- Film Tensile Strength at Yield, TD: 7.58 MPa
- Film Elongation at Break, MD: 600 %
$ 1446/MT
- Density: 0.927 g/cc
- Butyl Acrylate Content: 22.5 %
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 13.0 MPa
$ 2165/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 180 %
- Film Elongation at Break, TD: 690 %
$ 2273/MT
- Bulk Density: 0.530 g/cc
- Particle Mesh Size: 40 Mesh
- Particle Mesh Size: 200 Mesh
- Viscosity Measurement: 0.68
- Viscosity Measurement: 1.85
$ 1517/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.50 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 900 %
$ 1581/MT
- Density: 0.921 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 800 %
$ 1621/MT
- Density: 0.941 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 37
- Tensile Strength at Break: 5.52 MPa
- Tensile Strength, Yield: 3.86 MPa
$ 2084/MT
- Density: 0.916 g/cc
- Thickness: 20.3 microns
- Melt Flow: 4.2 g/10 min
- Film Tensile Strength at Yield, MD: 8.62 MPa
- Film Tensile Strength at Yield, TD: 6.89 MPa
$ 2242/MT
- Density: 0.9235 g/cc
- Thickness: 31.8 microns
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 575 %
- Film Elongation at Break, TD: 750 %
$ 1537/MT
- Density: 0.930 g/cc
- Thickness: 33.0 microns
- Melt Flow: 1.6 g/10 min
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 800 %
$ 1924/MT
- Density: 0.917 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 400 %
- 2% Secant Modulus: 0.207 GPa
$ 1606/MT
- Density: 0.922 g/cc
- Melt Flow: 5.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 180 %
- 2% Secant Modulus: 0.255 GPa
$ 1536/MT
- Bulk Density: 0.560 g/cc
- Particle Mesh Size: 40 Mesh
- Particle Mesh Size: 200 Mesh
- Viscosity Measurement: 0.90
- Viscosity Measurement: 2.2 @Temperature 25.0 °C
$ 1846/MT
- Density: 0.916 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 9.00 MPa
- Elongation at Break: 300 %
- 2% Secant Modulus: 0.172 GPa
$ 1918/MT
- Density: 0.944 g/cc
- Methyl Acrylate Content: 24 %
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 37
- Tensile Strength at Break: 11.0 MPa
$ 2119/MT
- Density: 0.910 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 700 %
- Film Elongation at Break, TD: 1200 %
$ 1645/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Viscosity: 250 - 450 cP
- Flash Point: >= 343 °C
- Ring & Ball Softening Point: 104 - 112 °C
- Gardner Color Number: <= 2.0
$ 2291/MT
- Specific Gravity: 0.930 - 0.960 g/cc
- Viscosity: 300 - 400 cP @Temperature 125 °C
- Brookfield Viscosity: 375 cP @Temperature 125 °C
- Molecular Weight: 4000 g/mol
- Flash Point: >= 204 °C
$ 1617/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Viscosity: 350 - 550 cP @Temperature 125 °C
- Brookfield Viscosity: 450 cP @Temperature 125 °C
- Molecular Weight: 6200 g/mol
- Flash Point: >= 343 °C
$ 1783/MT
- Density: 0.941 g/cc
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 39
- Tensile Strength at Break: 12.7 MPa
- Elongation at Break: 735 %
$ 1597/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 2185/MT
- Density: 0.927 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.6 g/10 min
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 800 %
$ 1722/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 2043/MT
- Density: 0.922 g/cc
- Thickness: 31.8 microns
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 350 %
- Film Elongation at Break, TD: 700 %
$ 1447/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 122 °C
- Vicat Softening Point: 97.0 °C
$ 1724/MT
- Density: 0.940 g/cc
- Methyl Acrylate Content: 21.5 %
- Melt Flow: 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 32
- Tensile Strength at Break: 10.0 MPa
$ 2296/MT
- Density: 0.915 g/cc
- Melt Flow: 12.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 9.70 MPa
- Elongation at Break: 400 %
- 2% Secant Modulus: 0.172 GPa
$ 1802/MT
- Specific Gravity: 0.900 - 0.920 g/cc
- Viscosity: 6000 - 9000 cP @Temperature 150 °C
- Brookfield Viscosity: 3550 cP @Temperature 190 °C
- Brookfield Viscosity: 18600 cP @Temperature 125 °C
- Molecular Weight: 35000 g/mol
$ 1652/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 1690/MT
- Base Resin Density: 0.931 g/cc
- Melt Flow: 8.0 g/10 min
- Melting Point: 77.0 °C
- Melting Point: 94.0 °C
- Vicat Softening Point: 69.0 °C
$ 1589/MT
- Density: 0.950 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 20 %
- Flexural Modulus: 0.896 GPa
$ 1483/MT
- Specific Gravity: 0.920 g/cc
- Viscosity: 250 - 950 cP
- Brookfield Viscosity: 700 cP @Temperature 190 °C
- Molecular Weight: 12000 g/mol
- Flash Point: >= 277 °C
$ 1623/MT
- Vinyl Acetate Content: 6.5 %
- Thickness: 31.8 microns
- Melt Flow: 0.55 g/10 min
- Film Elongation at Break, MD: 380 %
- Film Elongation at Break, TD: 550 %
$ 2044/MT
- Density: 0.926 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.60 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 950 %
$ 1512/MT
- Density: 0.946 g/cc
- Methyl Acrylate Content: 20.5 %
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 35
- Tensile Strength at Break: 14.0 MPa
$ 1749/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 600 %
$ 1544/MT
- Density: 0.923 g/cc
- Melt Flow: 5.7 g/10 min
- Tensile Strength, Ultimate: 11.0 MPa
- Elongation at Break: 450 %
- Tensile Modulus: 0.165 GPa
$ 1826/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 4.0 g/10 min
- Film Elongation at Break, MD: 570 %
- Film Elongation at Break, TD: 840 %
$ 1563/MT
- Density: 0.911 g/cc
- Melt Flow: 80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 8.30 MPa
- Elongation at Break: 120 %
- 2% Secant Modulus: 0.138 GPa
$ 2376/MT
- Density: 0.950 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 30 %
- Flexural Modulus: 0.896 GPa
$ 2089/MT
- Density: 0.923 g/cc
- Thickness: 31.8 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 350 %
- Film Elongation at Break, TD: 700 %
$ 1778/MT
- Density: 0.9235 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 650 %
$ 1586/MT
- Viscosity: 150 - 700 cP @Temperature 190 °C
- Brookfield Viscosity: 300 cP @Temperature 190 °C
- Molecular Weight: 12000 g/mol
- Ring & Ball Softening Point: 157 °C
- Gardner Color Number: 9.0
$ 1450/MT
- Specific Gravity: 0.910 - 0.920 g/cc
- Brookfield Viscosity: 8.0 cP @Load 0.00000220 kg, Temperature 190 °C
- Molecular Weight: 65000 g/mol
- Melt Flow: 2.0 - 10 g/10 min
- Ring & Ball Softening Point: 122 °C
$ 2095/MT
- Density: 0.920 g/cc
- Melt Flow: 7.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 9.70 MPa
- Elongation at Break: 400 %
- Melt Temperature: 149 - 166 °C
$ 1706/MT
- Density: 0.924 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.80 g/10 min
- Film Elongation at Break, MD: 1100 %
- Film Elongation at Break, TD: 1100 %
$ 2505/MT
- Density: 0.933 g/cc
- Vinyl Acetate Content: 12 %
- Thickness: 33.0 microns
- Melt Flow: 2.5 g/10 min
- Film Elongation at Break, MD: 300 %
$ 1765/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 145 %
- Film Elongation at Break, TD: 680 %
$ 1917/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 2560/MT
- Specific Gravity: 0.900 - 0.920 g/cc
- Brookfield Viscosity: 19 cP @Load 2.16 kg, Temperature 190 °C
- Molecular Weight: 100000 g/mol
- Melt Flow: 16 - 24 g/10 min
- Flash Point: >= 343 °C
$ 1743/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.50 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 900 %
$ 1490/MT
- Specific Gravity: 0.930 - 0.960 g/cc
- Viscosity: 300 - 450 cP @Temperature 125 °C
- Brookfield Viscosity: 375 cP @Temperature 125 °C
- Molecular Weight: 4000 g/mol
- Flash Point: >= 204 °C
$ 1475/MT
- Specific Gravity: 0.900 - 0.920 g/cc
- Brookfield Viscosity: 190 cP @Load 2.16 kg, Temperature 190 °C
- Molecular Weight: 76000 g/mol
- Melt Flow: 160 - 240 g/10 min
- Flash Point: >= 343 °C
$ 2040/MT
- Specific Gravity: 0.930 - 0.960 g/cc
- Viscosity: 150 - 300 cP @Temperature 125 °C
- Brookfield Viscosity: 225 cP @Temperature 125 °C
- Molecular Weight: 3600 g/mol
- Flash Point: >= 204 °C
$ 1545/MT
- Density: 0.934 g/cc
- Vinyl Acetate Content: 14.5 %
- Thickness: 45.7 microns
- Melt Flow: 3.5 g/10 min
- Film Elongation at Break, MD: 675 %
$ 1481/MT
- Specific Gravity: 0.920 g/cc
- Viscosity: 250 - 950 cP @Temperature 190 °C
- Brookfield Viscosity: 700 cP @Temperature 190 °C
- Molecular Weight: 12000 g/mol
- Flash Point: >= 277 °C
$ 1719/MT
- Bulk Density: 0.530 g/cc
- Particle Mesh Size: 40 Mesh
- Particle Mesh Size: 200 Mesh
- Viscosity Measurement: 0.73
- Viscosity Measurement: 1.9
$ 1524/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.50 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 900 %
$ 1880/MT
- Density: 0.921 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 750 %
$ 2124/MT
- Density: 0.918 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1486/MT
- Density: 0.918 g/cc
- Melt Flow: 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 12.0 MPa
- Elongation at Break: 500 %
- 2% Secant Modulus: 0.200 GPa
$ 1515/MT
- Density: 0.919 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 670 %
- Film Elongation at Break, TD: 900 %
$ 1792/MT
- Vinyl Acetate Content: 7.5 %
- Thickness: 31.8 microns
- Melt Flow: 0.55 g/10 min
- Film Elongation at Break, MD: 380 %
- Film Elongation at Break, TD: 550 %
$ 1748/MT
- Density: 0.941 g/cc
- Methyl Acrylate Content: 20 %
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 36
- Tensile Strength at Break: 7.00 MPa
$ 1583/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Viscosity: 75 - 200 cP
- Brookfield Viscosity: 150 cP @Temperature 125 °C
- Molecular Weight: 4000 g/mol
- Flash Point: >= 343 °C
$ 1906/MT
- Density: 0.941 g/cc
- Methyl Acrylate Content: 20 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 39
- Tensile Strength at Break: 10.0 MPa
$ 1595/MT
- Density: 0.942 g/cc
- Methyl Acrylate Content: 20 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 37
- Tensile Strength at Break: 11.0 MPa
$ 2024/MT
- Vinyl Acetate Content: 4.0 %
- Thickness: 31.8 microns
- Melt Flow: 0.55 g/10 min
- Film Elongation at Break, MD: 225 %
- Film Elongation at Break, TD: 600 %
$ 1676/MT
- Density: 0.924 g/cc
- Thickness: 31.8 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 500 %
- Film Elongation at Break, TD: 700 %
$ 2064/MT
- Density: 0.915 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 9.00 MPa
- Elongation at Break: 300 %
- 2% Secant Modulus: 0.193 GPa
$ 1497/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 750 %
$ 1587/MT
- Density: 0.906 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 62.0 MPa
- Film Tensile Strength at Yield, TD: 8.00 MPa
$ 2268/MT
- Density: 0.942 g/cc
- Methyl Acrylate Content: 20 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 35
- Tensile Strength at Break: 10.0 MPa
$ 1463/MT
- Density: 0.906 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.50 g/10 min
- Film Tensile Strength at Yield, TD: 7.58 MPa
- Film Tensile Strength at Yield, TD: 8.00 MPa
$ 2462/MT
- Specific Gravity: 0.890 - 0.920 g/cc
- Viscosity: 2400 - 6000 cP @Temperature 150 °C
- Brookfield Viscosity: 1550 cP @Temperature 190 °C
- Brookfield Viscosity: 7750 cP @Temperature 125 °C
- Molecular Weight: 15000 g/mol
$ 1822/MT
- Specific Gravity: 0.906 g/cc
- Viscosity: 3000 - 4800 cP @Temperature 150 °C
- Brookfield Viscosity: 1800 cP @Temperature 190 °C
- Brookfield Viscosity: 8950 cP @Temperature 125 °C
- Molecular Weight: 17000 g/mol
$ 1611/MT
- Specific Gravity: 0.920 g/cc
- Viscosity: 100 - 750 cP @Temperature 190 °C
- Brookfield Viscosity: 300 cP @Temperature 190 °C
- Molecular Weight: 9100 g/mol
- Flash Point: >= 277 °C
$ 2294/MT
- Density: 0.917 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 9.00 MPa
- Elongation at Break: 300 %
- 2% Secant Modulus: 0.235 GPa
$ 1747/MT
- Density: 0.920 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 8.00 MPa
- Elongation at Break: 90 %
- 2% Secant Modulus: 0.228 GPa
$ 1717/MT
- Density: 0.931 g/cc
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 950 %
- Dart Drop: 6.89 g/micron
$ 1569/MT
- Methyl Acrylate Content: 9.0 %
- Melt Flow: 8.0 g/10 min
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 800 %
- Dart Drop: 6.69 g/micron
$ 1499/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 650 %
- Film Elongation at Break, TD: 900 %
$ 1825/MT
- Specific Gravity: 0.930 - 0.960 g/cc
- Viscosity: 1000 - 2000 cP @Temperature 125 °C
- Brookfield Viscosity: 1500 cP @Temperature 125 °C
- Molecular Weight: 7500 g/mol
- Flash Point: >= 204 °C
$ 1543/MT
- Density: 0.918 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.1 g/10 min
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1461/MT
- Density: 0.917 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 500 %
- 2% Secant Modulus: 0.207 GPa
$ 1487/MT
- Density: 0.950 g/cc
- Methyl Acrylate Content: 23 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 37
- Tensile Strength at Break: 9.00 MPa
$ 1888/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 9.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 575 %
- Film Elongation at Break, TD: 730 %
$ 1569/MT
- Density: 0.923 g/cc
- Thickness: 31.8 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 350 %
- Film Elongation at Break, TD: 700 %
$ 1663/MT
- Density: 0.919 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 700 %
- Film Elongation at Break, TD: 900 %
$ 1566/MT
- Density: 0.917 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 400 %
- 2% Secant Modulus: 0.200 GPa
$ 2333/MT
- Density: 0.925 g/cc
- Butyl Acrylate Content: 17.5 %
- Melt Flow: 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 10.0 MPa
$ 1722/MT
- Density: 0.940 g/cc
- Vinyl Acetate Content: 18.5 %
- Thickness: 31.75 microns
- Melt Flow: 2.5 g/10 min
- Film Elongation at Break, MD: 600 %
$ 1526/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1762/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 1450/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 1588/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 1000 %
$ 1556/MT
- Density: 0.931 g/cc
- Vinyl Acetate Content: 9.0 %
- Thickness: 31.8 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 300 %
$ 1632/MT
- Specific Gravity: 0.930 - 0.960 g/cc
- Viscosity: 1000 - 2500 cP @Temperature 125 °C
- Brookfield Viscosity: 1500 cP @Temperature 125 °C
- Molecular Weight: 7500 g/mol
- Flash Point: >= 204 °C
$ 1485/MT
- Density: 0.932 g/cc
- Vinyl Acetate Content: 6.5 %
- Thickness: 38.1 microns
- Melt Flow: 1.1 g/10 min
- Dart Drop: 7.09 g/micron
$ 2000/MT
- Density: 0.942 g/cc
- Methyl Acrylate Content: 20 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 96.0 °C
- Vicat Softening Point: 43.0 °C
$ 1763/MT
- Density: 0.920 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 750 %
$ 1495/MT
- Density: 0.921 g/cc
- Thickness: 38.1 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 700 %
$ 1567/MT
- Density: 0.923 g/cc
- Melt Flow: 4.5 g/10 min
- Tensile Strength, Ultimate: 11.0 MPa
- Elongation at Break: 450 %
- Melt Temperature: 302 - 329 °C
$ 1579/MT
- Density: 0.909 g/cc
- Melt Flow: 200 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 6.00 MPa
- Elongation at Break: 100 %
- Melt Temperature: 149 - 166 °C
- Process: Injection Molding
$ 1538/MT
- Density: 0.940 g/cc
- Vinyl Acetate Content: 18.5 %
- Thickness: 38.1 microns
- Melt Flow: 2.5 g/10 min
- Dart Drop: 10.2 g/micron
$ 1574/MT
- Density: 0.917 g/cc
- Melt Flow: 16 g/10 min
- Tensile Strength, Ultimate: 8.96 MPa
- Elongation at Break: 450 %
- Melt Temperature: 302 - 329 °C
$ 1457/MT
- Density: 0.918 g/cc
- Melt Flow: 13.7 g/10 min
- Tensile Strength, Ultimate: 8.96 MPa
- Elongation at Break: 450 %
- Melt Temperature: 302 - 329 °C
$ 1511/MT
- Specific Gravity: 0.900 - 0.920 g/cc
- Brookfield Viscosity: 190 cP @Load 0.00000220 kg, Temperature 190 °C
- Molecular Weight: 76000 g/mol
- Melt Flow: 160 - 240 g/10 min
- Flash Point: >= 343 °C
$ 1602/MT
- Density: 0.945 g/cc
- Methyl Acrylate Content: 24 %
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 34
- Tensile Strength at Break: 8.00 MPa
$ 2232/MT
- Density: 0.917 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 106 °C
- Vicat Softening Point: 87.0 °C
$ 1555/MT
- Density: 0.932 g/cc
- Melt Flow: 8.0 g/10 min
- Melting Point: 77.0 °C
- Melting Point: 94.0 °C
- Vicat Softening Point: 69.0 °C
- Flash Point: >= 343 °C
$ 1514/MT
- Density: 0.906 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.50 g/10 min
- Film Tensile Strength at Yield, TD: 6.89 MPa
- Film Elongation at Break, MD: 550 %
$ 1660/MT
- Density: 0.918 g/cc
- Thickness: 25.4 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 2559/MT
- Density: 0.942 g/cc
- Methyl Acrylate Content: 20 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 12.0 MPa
$ 1540/MT
- Specific Gravity: 0.910 - 0.950 g/cc
- Brookfield Viscosity: 450 cP @Temperature 125 °C
- Molecular Weight: 6200 g/mol
- Flash Point: >= 343 °C
- Ring & Ball Softening Point: 104 °C
- Penetration Hardness: 5 dmm
$ 1632/MT
- Density: 0.932 g/cc
- Melt Flow: 0.55 g/10 min
- VA Content (%: 12
$ 2010/MT
- Density: 0.926 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.80 g/10 min
- Film Elongation at Break, MD: 700 %
- Film Elongation at Break, TD: 900 %
$ 1562/MT
- Density: 0.943 g/cc
- Methyl Acrylate Content: 21.5 %
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 15.0 MPa
Delivery Polymer Westlake Chemical Corporation
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil chemical tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.