AK Steel 409 ULTRA FORM® Stainless Steel price 1797 per MT

Physical Properties
Density
7.74 g/cc

Mechanical Properties
Hardness, Rockwell B
66.9
Hardness, Rockwell B
70
Hardness, Rockwell B
85.3
Hardness, Rockwell B
85.3
Hardness, Rockwell B
88.7
Hardness, Rockwell B
93.5
Hardness, Rockwell B
64 - 70 @Thickness 1.27 - 2.16 mm
Tensile Strength, Ultimate
434 MPa
Tensile Strength, Ultimate
490 MPa
Tensile Strength, Ultimate
545 MPa
Tensile Strength, Ultimate
657 MPa
Tensile Strength, Ultimate
730 MPa
Tensile Strength, Ultimate
32.0 MPa @Temperature 816 °C
Tensile Strength, Ultimate
73.0 MPa @Temperature 704 °C
Tensile Strength, Ultimate
145 MPa @Temperature 649 °C
Tensile Strength, Ultimate
246 MPa @Temperature 538 °C
Tensile Strength, Ultimate
320 MPa @Temperature 371 °C
Tensile Strength, Ultimate
340 MPa @Temperature 204 °C
Tensile Strength, Ultimate
418 MPa @Temperature 22.2 °C
Tensile Strength, Ultimate
379 - 455 MPa @Thickness 1.27 - 2.16 mm
Tensile Strength, Yield
186 - 262 MPa @Strain 0.200 %
Tensile Strength, Yield
352 MPa @Strain 0.200 %
Tensile Strength, Yield
486 MPa @Strain 0.200 %
Tensile Strength, Yield
541 MPa @Strain 0.200 %
Tensile Strength, Yield
652 MPa @Strain 0.200 %
Tensile Strength, Yield
721 MPa @Strain 0.200 %
Tensile Strength, Yield
22.0 MPa @Strain 0.200 %, Temperature 816 °C
Tensile Strength, Yield
47.0 MPa @Strain 0.200 %, Temperature 704 °C
Tensile Strength, Yield
89.0 MPa @Strain 0.200 %, Temperature 649 °C
Tensile Strength, Yield
127 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
152 MPa @Strain 0.200 %, Temperature 371 °C
Tensile Strength, Yield
154 MPa @Strain 0.200 %, Temperature 204 °C
Tensile Strength, Yield
225 MPa @Strain 0.200 %, Temperature 22.2 °C
Elongation at Break
3.5 %
Elongation at Break
4.0 %
Elongation at Break
9.5 %
Elongation at Break
17 %
Elongation at Break
31.9 %
Elongation at Break
36.3 %
Elongation at Break
33 - 43 % @Thickness 1.27 - 2.16 mm
Modulus of Elasticity
208 GPa
Fatigue Strength
10.0 MPa @# of Cycles 1.00e+7 , Temperature 816 °C
Fatigue Strength
34.0 MPa @# of Cycles 1.00e+7 , Temperature 704 °C

Component Elements Properties
Carbon, C
<= 0.020 %
Chromium, Cr
10.5 - 11.7 %
Iron, Fe
86 - 89.5 %
Manganese, Mn
<= 0.75 %
Nickel, Ni
<= 0.50 %
Phosphorous, P
<= 0.040 %
Silicon, Si
<= 1.0 %
Sulfur, S
<= 0.010 %

Electrical Properties
Electrical Resistivity
0.0000600 ohm-cm

Descriptive Properties
Typical rm value
1.5

Alternative products

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 85%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 16) accurate 85%

$ 1714/MT

Particle Size: 8.4 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-4 PH Stainless Steel Powder (Grade 95% - 16) accurate 70%

$ 1460/MT

Particle Size: 6.7 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.070 %
Chromium, Cr: 15.5 - 17.5 %
Copper, Cu: 3.0 - 5.0 %

SABIC Innovative Plastics Valox® K4560 PBT accurate 70%

$ 1742/MT

Specific Gravity: 1.50 g/cc
Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
Linear Mold Shrinkage, Transverse: 0.010 - 0.012 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 96.0 MPa
Tensile Strength at Break: 102 MPa

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 85%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-4 PH Stainless Steel Powder (Grade 95% - 16) accurate 70%

$ 1533/MT

Particle Size: 6.7 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.070 %
Chromium, Cr: 15.5 - 17.5 %
Copper, Cu: 3.0 - 5.0 %

Osprey Metals 17-4 PH Stainless Steel Powder (Grade 95% - 16) accurate 70%

$ 1878/MT

Particle Size: 6.7 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.070 %
Chromium, Cr: 15.5 - 17.5 %
Copper, Cu: 3.0 - 5.0 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 85%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 70%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, general cargo for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for AK Steel 409 ULTRA FORM® Stainless Steel

Seller from Shanghai – 2021-03-05:

Seller from Shanghai work with company: 3M, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1797 per MT