Akro-Plastic Akromid® T1 GF 30 (3466) PPA Dry, 30% Glass Filled price 2376 per MT

Physical Properties
Density
1.40 g/cc @Temperature 23.0 °C
Filler Content
30 %
Water Absorption
1.25 % @Temperature 70.0 °C
Linear Mold Shrinkage, Flow
0.0040 cm/cm
Linear Mold Shrinkage, Transverse
0.0090 cm/cm

Mechanical Properties
Ball Indentation Hardness
290 MPa
Tensile Strength at Break
215 MPa
Tensile Strength at Break
107.5 MPa @Temperature 170 - 180 °C, Time 1.80e+7 sec
Tensile Strength at Break
107.5 MPa @Temperature 150 - 160 °C, Time 7.20e+7 sec
Elongation at Break
2.2 %
Elongation at Break
3.0 %
Tensile Modulus
12.5 GPa
Flexural Strength
300 MPa
Flexural Modulus
11.0 GPa
Charpy Impact Unnotched
6.00 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
313 °C
Deflection Temperature at 0.46 MPa (66 psi)
310 °C
Deflection Temperature at 1.8 MPa (264 psi)
285 °C
Deflection Temperature at 8.0 MPa
165 °C
Flammability, UL94
HB @Thickness 0.800 mm

Electrical Properties
Comparative Tracking Index
600 V

Processing Properties
Feed Temperature
80.0 - 95.0 °C
Nozzle Temperature
325 - 335 °C
Zone 1
315 - 325 °C
Zone 2
320 - 330 °C
Zone 3
325 - 340 °C
Zone 4
325 - 340 °C
Melt Temperature
330 - 340 °C
Mold Temperature
135 - 160 °C
Drying Temperature
90.0 °C
Dry Time
2 - 16.0 hour
Hold Pressure
30.0 - 80.0 MPa
Back Pressure
0.200 - 0.650 MPa

Descriptive Properties
Acetic acid
Fail
Acetone
Pass
Cresol
Fail
Diesel fuel (DIN 51601)
Pass
Drying, Moisture (%)
<0.1
Engine oil
Pass
Ethanol
Pass
Ethylene glycol/water
Pass
Formic acid
Fail
Hydraulic oil
Pass
Injection Speed
average to high
Isopropanol
Pass
Kerosene
Pass
Methanol
Pass
Petrol
Pass
Phenol
Fail
Rate acc. FMVSS 302 (
Passed
Rate acc. FMVSS 302,(
FMVSS 302, >1 [mm] Thickness
Silicone oil
Pass
Sulphuric acid
Fail
Toluene
Pass
Urea, aqueous
Pass
Water
Pass
Xylene
Pass
Zinc chloride, aqueous
Pass

Alternative products

Lanxess Durethan® AKV 40 H2.0 901510 Nylon 66, Glass Fiber Reinforced accurate 57%

$ 2262/MT

Specific Gravity: 1.46 g/cc
Moisture Absorption at Equilibrium: 1.7 %
Water Absorption at Saturation: 4.5 %
Linear Mold Shrinkage, Flow: 0.00030 cm/cm
Linear Mold Shrinkage, Flow: 0.00050 cm/cm

Akro-Plastic Akromid® T6 GF30 (3501) PPA Dry, 30% Glass Filled accurate 62%

$ 1891/MT

Density: 1.50 g/cc @Temperature 23.0 °C
Filler Content: 30 %
Water Absorption: 1.35 % @Temperature 70.0 °C
Tensile Strength at Break: 200 MPa
Tensile Strength at Break: 100 MPa @Temperature 150 - 160 °C, Time 1.80e+7 sec

Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA) (Unverified Data**) accurate 78%

$ 1789/MT

Density: 1.44 g/cc
Filler Content: 33 %
Water Absorption: 0.21 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00 cm/cm
Linear Mold Shrinkage, Flow: 0.0040 cm/cm

Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer accurate 57%

$ 1773/MT

Density: 1.45 g/cc
Water Absorption: 0.29 %
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.010 cm/cm
Tensile Strength at Break: 79.3 MPa @Temperature 175 °C

Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA) (Unverified Data**) accurate 62%

$ 1478/MT

Specific Gravity: 1.45 g/cc
Density: 1.45 g/cc
Filler Content: 33 %
Water Absorption: 0.29 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 cm/cm

Akro-Plastic Akromid® T1 GF 40 (3464) PPA Dry, 40% Glass Filled accurate 57%

$ 1562/MT

Density: 1.50 g/cc @Temperature 23.0 °C
Filler Content: 40 %
Water Absorption: 1.1 % @Temperature 70.0 °C
Linear Mold Shrinkage, Flow: 0.0020 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA) (Unverified Data**) accurate 73%

$ 2159/MT

Density: 1.48 g/cc
Filler Content: 33 %
Water Absorption: 0.21 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0040 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Akro-Plastic Akromid® T1 GF 30 9 (3498) PPA Dry, 30% Glass Filled accurate 83%

$ 1738/MT

Density: 1.42 g/cc @Temperature 23.0 °C
Filler Content: 30 %
Water Absorption: 1.3 % @Temperature 23.0 °C
Ball Indentation Hardness: 270 MPa
Tensile Strength at Break: 210 MPa

Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA) (Unverified Data**) accurate 67%

$ 1937/MT

Density: 1.45 g/cc
Filler Content: 35 %
Water Absorption: 0.29 % @Temperature 23.0 °C, Time 86400 sec
Water Absorption: 0.30 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships on sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Akro-Plastic Akromid® T1 GF 30 (3466) PPA Dry, 30% Glass Filled

Seller from Tianjin – 2021-06-15:

Seller from Tianjin work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2376 per MT

Seller from Lima – 2021-05-03:

Seller from Lima work with company: DuPont Performance Polymers, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2425 per MT