Amco PRIMATOP HDPE 003946HP Blow Molding Polyethylene price 2566 per MT

Physical Properties
Density
0.946 g/cc
ESCR 100% Igepal®
>= 1000 hour
ESCR 100% Igepal®
>= 1000 hour
Melt Index of Compound
0.31 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength, Yield
24.8 MPa
Elongation at Break
>= 500 %
Flexural Modulus
1.07 GPa

Thermal Properties
Brittleness Temperature
<= -75.0 °C

Alternative products

Chevron Phillips Marlex® C101 Polyethylene; Enhanced accurate 74%

$ 1450/MT

Density: 0.916 g/cc
ESCR 100% Igepal®: >= 1000 hour
ESCR 100% Igepal®: >= 1000 hour
Melt Index of Compound: 1.4 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 10.0 MPa

Thermal Ceramics Cerafelt accurate 74%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

NOVA Chemicals Novapol® HB-W646-U HDPE Blow Molding Resin accurate 87%

$ 1499/MT

Density: 0.946 g/cc
ESCR 100% Igepal®: >= 1000 hour
ESCR 100% Igepal®: >= 1000 hour
Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 24.0 MPa

Chevron Phillips Marlex® 9503H HDPE Blow Molding Resin accurate 74%

$ 1669/MT

Density: 0.946 g/cc
ESCR 100% Igepal®: >= 1000 hour
Melt Index of Compound: 0.31 g/10 min
Tensile Strength, Yield: 24.0 MPa
Elongation at Break: 500 %

Formosa Plastics Formolene® HP4306 Pipe HDPE (discontinued **) accurate 87%

$ 1478/MT

Density: 0.944 g/cc
Density: 0.955 g/cc
ESCR 100% Igepal®: >= 1000 hour
Melt Flow: 0.060 g/10 min @Load 2.16 kg, Temperature 190 °C
High Load Melt Index: 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C

SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) accurate 74%

$ 1895/MT

Density: 1.43 g/cc
Density: 1.43 g/cc
Moisture Absorption: 0.200 %
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Time 86400 sec

Chevron Phillips Marlex® C100 Polyethylene; Enhanced accurate 74%

$ 1992/MT

Density: 0.918 g/cc
ESCR 100% Igepal®: >= 1000 hour
ESCR 100% Igepal®: >= 1000 hour
Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 10.0 MPa

Formosa Plastics Formolene® HP4000 Pipe HDPE accurate 74%

$ 1556/MT

Density: 0.944 g/cc
ESCR 100% Igepal®: >= 1000 hour
Melt Flow: 0.16 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 34.5 MPa
Tensile Strength, Yield: 22.1 MPa

Chevron Phillips Marlex® C300 Polyethylene; Enhanced accurate 74%

$ 2112/MT

Density: 0.933 g/cc
ESCR 100% Igepal®: >= 1000 hour
ESCR 100% Igepal®: >= 1000 hour
Melt Index of Compound: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 18.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, container ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Amco PRIMATOP HDPE 003946HP Blow Molding Polyethylene

Seller from Shenyang – 2021-08-14:

Seller from Shenyang work with company: 3M, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2566 per MT