Arkema Group LOTADER® 4720 Terpolymer Ethylene - Acrylic Ester

Physical Properties
Density
0.940 g/cc @Temperature 23.0 °C
Melt Index of Compound
7.0 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Hardness, Shore D
19
Tensile Strength at Break
6.00 MPa
Elongation at Break
800 %
Flexural Modulus
<= 0.0300 GPa

Thermal Properties
Melting Point
65.0 °C
Vicat Softening Point
<= 40.0 °C @Load 0.999 kg
Ring & Ball Softening Point
145 °C

Chemical Properties
Acid Value
2.5

Descriptive Properties
Ethyl Acrylate Content (%)
29
Maleic Anhydride Content (%)
0.3

Alternative products

NuSil MED-4535 One-Part Standard High Consistency Elastomer - Unrestricted Medical Use accurate 66%

$ 1856/MT

Specific Gravity: 1.10 g/cc
Hardness, Shore A: 35
Hardness, Shore A: 30 - 40
Tensile Strength at Break: 5.50 MPa
Tensile Strength at Break: 8.60 MPa

NuSil MED-4815 Liquid Silicone Rubber - Unrestricted Medical Use accurate 66%

$ 1642/MT

Specific Gravity: 1.10 g/cc
Hardness, Shore A: 15
Hardness, Shore A: 13 - 18
Tensile Strength at Break: 5.20 MPa
Tensile Strength at Break: 6.40 MPa

NuSil MED-4735 Two-Part Standard High Consistency Elastomers - Unrestricted Medical Use accurate 66%

$ 1644/MT

Specific Gravity: 1.11 g/cc
Hardness, Shore A: 35
Hardness, Shore A: 30 - 40
Tensile Strength at Break: 6.20 MPa
Tensile Strength at Break: 10.3 MPa

Teknor Apex Monprene® MP-1518C Thermoplastic Elastomer accurate 66%

$ 1673/MT

Specific Gravity: 0.890 g/cc
Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore A: 44
Tensile Strength at Break: 6.89 MPa
Tensile Stress: 2.76 MPa @Strain 300 %

ExxonMobil Santoprene® 281-64MED Thermoplastic Elastomer (discontinued **) accurate 66%

$ 1767/MT

Specific Gravity: 0.970 g/cc
Hardness, Shore A: 64
Tensile Strength at Break: 6.420 MPa
Tensile Strength at Break: 6.69 MPa
Tensile Strength, Ultimate: 2.48 MPa

Arkema Group LOTADER® 4700 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride accurate 99%

$ 1496/MT

Density: 0.940 g/cc @Temperature 23.0 °C
Melt Index of Compound: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore D: 14
Tensile Strength at Break: 5.50 MPa
Elongation at Break: 800 %

Teknor Apex Telcar® TL-2470A Thermoplastic Elastomer accurate 66%

$ 2132/MT

Specific Gravity: 1.04 g/cc
Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore A: 65
Hardness, Shore A: 70
Tensile Strength at Break: 6.55 MPa

3M Scotchkote™ 60RG 537 Urethane Elastomer accurate 66%

$ 1464/MT

Solids Content: 100 %
Volatile Organic Compounds (VOC) Content: 0.00 g/l
Thickness: 6100 microns
Hardness, Shore A: 60
Tensile Strength at Break: 6.21 MPa

Teknor Apex Telcar® TL-2555A Thermoplastic Elastomer accurate 66%

$ 1595/MT

Specific Gravity: 0.890 g/cc
Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Shore A: 55
Tensile Strength at Break: 6.89 MPa
Elongation at Break: 800 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships forsale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Arkema Group LOTADER® 4720 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Seller from Xi’an – 2021-04-21:

Seller from Xi’an work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2186 per MT