Carpenter Custom 455® Stainless Steel, Condition H950 (Age Hardened 510°C) price 1845 per MT

Physical Properties
Density
7.76 g/cc

Mechanical Properties
Hardness, Brinell
459
Hardness, Knoop
504
Hardness, Rockwell C
48
Hardness, Vickers
482
Tensile Strength, Ultimate
1586 MPa
Tensile Strength, Ultimate
896 MPa @Temperature 538 °C
Tensile Strength, Ultimate
1207 MPa @Temperature 427 °C
Tensile Strength, Ultimate
1345 MPa @Temperature 316 °C
Tensile Strength, Ultimate
1689 MPa @Temperature -73.0 °C
Tensile Strength, Ultimate
1931 MPa @Temperature -184 °C
Tensile Strength, Yield
1517 MPa @Strain 0.200 %
Tensile Strength, Yield
758 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
1124 MPa @Strain 0.200 %, Temperature 427 °C
Tensile Strength, Yield
1276 MPa @Strain 0.200 %, Temperature 316 °C
Elongation at Break
12 %
Elongation at Break
5.0 % @Temperature -184 °C
Elongation at Break
11 % @Temperature -73.0 °C
Elongation at Break
12 % @Temperature 316 °C
Elongation at Break
14 % @Temperature 427 °C
Elongation at Break
18 % @Temperature 538 °C
Reduction of Area
50 %
Reduction of Area
20 % @Temperature -184 °C
Reduction of Area
45 % @Temperature -73.0 °C
Reduction of Area
50 % @Temperature 316 °C
Reduction of Area
60 % @Temperature 427 °C
Reduction of Area
70 % @Temperature 538 °C
Modulus of Elasticity
200 GPa @Temperature 23.0 °C
Notched Tensile Strength
793 MPa
Notched Tensile Strength
1931 MPa
Notched Tensile Strength
2068 MPa
Poissons Ratio
0.30 @Temperature 23.0 °C
Fatigue Strength
680 MPa @# of Cycles 1.00e+7
Shear Modulus
76.9 GPa @Temperature 23.0 °C
Charpy Impact
20.0 J
Charpy Impact
4.00 J @Temperature -184 °C
Charpy Impact
14.0 J @Temperature -73.0 °C

Thermal Properties
CTE, linear
10.6 µm/m-°C @Temperature 22.0 - 93.0 °C
CTE, linear
11.2 µm/m-°C @Temperature 22.0 - 260 °C
CTE, linear
12.0 µm/m-°C @Temperature 22.0 - 482 °C

Component Elements Properties
Carbon, C
<= 0.050 %
Chromium, Cr
11 - 12.5 %
Copper, Cu
1.5 - 2.5 %
Iron, Fe
75 %
Manganese, Mn
<= 0.50 %
Molybdenum, Mo
<= 0.50 %
Nb + Ta
0.10 - 0.50 %
Nickel, Ni
7.5 - 9.5 %
Niobium, Nb (Columbium, Cb)
<= 0.50 %
Phosphorous, P
<= 0.040 %
Silicon, Si
<= 0.50 %
Sulfur, S
<= 0.030 %
Tantalum, Ta
<= 0.50 %
Titanium, Ti
0.80 - 1.4 %

Electrical Properties
Electrical Resistivity
0.0000758 ohm-cm @Temperature 23.0 °C

Alternative products

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 55% Cold Reduction accurate 72%

$ 1920/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1827 MPa
Tensile Strength, Yield: 1413 MPa @Strain 0.200 %
Elongation at Break: 12 %
Reduction of Area: 50 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 72%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

ATI Allegheny Ludlum AL 13-8™ H 1025 Precipitation Hardening Alloy accurate 72%

$ 1669/MT

Density: 7.76 g/cc
Tensile Strength, Ultimate: 1276 MPa
Tensile Strength, Yield: 1207 MPa @Strain 0.200 %
Elongation at Break: 11 %
Reduction of Area: 45 %

ATI Allegheny Ludlum AL 13-8™ H 1000 Precipitation Hardening Alloy accurate 72%

$ 1599/MT

Density: 7.76 g/cc
Hardness, Rockwell C: 45
Tensile Strength, Ultimate: 1413 MPa
Tensile Strength, Yield: 1310 MPa @Strain 0.200 %
Elongation at Break: 10 %

ATI Allegheny Ludlum AL 13-8™ H 1100 Precipitation Hardening Alloy accurate 86%

$ 1713/MT

Density: 7.76 g/cc
Hardness, Rockwell C: 35
Tensile Strength, Ultimate: 1034 MPa
Tensile Strength, Yield: 931 MPa @Strain 0.200 %
Elongation at Break: 14 %

ATI Allegheny Ludlum AL 13-8™ H 1050 Precipitation Hardening Alloy, Heat Treated at 1150°F accurate 86%

$ 1459/MT

Density: 7.76 g/cc
Hardness, Rockwell C: 33
Tensile Strength, Ultimate: 931 MPa
Tensile Strength, Yield: 621 MPa @Strain 0.200 %
Elongation at Break: 14 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 72%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 72%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

ATI Allegheny Ludlum AL 13-8™ H 1050 Precipitation Hardening Alloy, Heat Treated at 1050°F accurate 86%

$ 2086/MT

Density: 7.76 g/cc
Hardness, Rockwell C: 43
Tensile Strength, Ultimate: 1207 MPa
Tensile Strength, Yield: 1138 MPa @Strain 0.200 %
Elongation at Break: 12 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, used cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Carpenter Custom 455® Stainless Steel, Condition H950 (Age Hardened 510°C)

Seller from Beijing – 2021-05-26:

Seller from Beijing work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2413 per MT

Seller from Shenzhen – 2021-06-29:

Seller from Shenzhen work with company: ChevronTexaco Corp, 3M, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1845 per MT

Seller from Santiago – 2021-06-13:

Seller from Santiago work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2157 per MT