Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 900 (Age-Hardened 482°C/1hr/AC) price 2174 per MT

Physical Properties
Density
7.80 g/cc

Mechanical Properties
Hardness, Brinell
420
Hardness, Knoop
450
Hardness, Rockwell C
44
Hardness, Vickers
430
Tensile Strength, Ultimate
1365 MPa
Tensile Strength, Ultimate
793 MPa @Temperature 538 °C
Tensile Strength, Ultimate
952 MPa @Temperature 482 °C
Tensile Strength, Ultimate
1103 MPa @Temperature 427 °C
Tensile Strength, Ultimate
1186 MPa @Temperature 316 °C
Tensile Strength, Yield
1262 MPa @Strain 0.200 %
Tensile Strength, Yield
643 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
814 MPa @Strain 0.200 %, Temperature 482 °C
Tensile Strength, Yield
910 MPa @Strain 0.200 %, Temperature 427 °C
Tensile Strength, Yield
1000 MPa @Strain 0.200 %, Temperature 316 °C
Elongation at Break
15 %
Elongation at Break
13 % @Temperature 427 °C
Elongation at Break
13 % @Temperature 316 °C
Elongation at Break
13 % @Temperature 482 °C
Elongation at Break
17 % @Temperature 538 °C
Reduction of Area
52 %
Reduction of Area
46 % @Temperature 316 °C
Reduction of Area
51 % @Temperature 427 °C
Reduction of Area
52 % @Temperature 538 °C
Reduction of Area
55 % @Temperature 482 °C
Modulus of Elasticity
197 GPa
Poissons Ratio
0.272
Shear Modulus
77.4 GPa
Charpy Impact
21.0 J

Thermal Properties
CTE, linear
10.8 µm/m-°C @Temperature 21.0 - 93.0 °C
CTE, linear
11.3 µm/m-°C @Temperature 21.0 - 316 °C
CTE, linear
11.7 µm/m-°C @Temperature 21.0 - 427 °C
Specific Heat Capacity
0.419 J/g-°C @Temperature 0.000 - 100 °C
Thermal Conductivity
17.9 W/m-K @Temperature 149 °C
Thermal Conductivity
22.6 W/m-K @Temperature 482 °C

Component Elements Properties
Carbon, C
<= 0.070 %
Chromium, Cr
15 - 17.5 %
Copper, Cu
3.0 - 5.0 %
Iron, Fe
73 %
Manganese, Mn
<= 1.0 %
Nb + Ta
0.15 - 0.45 %
Nickel, Ni
3.0 - 5.0 %
Niobium, Nb (Columbium, Cb)
<= 0.45 %
Phosphorous, P
<= 0.040 %
Silicon, Si
<= 1.0 %
Sulfur, S
<= 0.030 %
Tantalum, Ta
<= 0.45 %

Electrical Properties
Electrical Resistivity
0.0000770 ohm-cm

Alternative products

Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel accurate 91%

$ 1709/MT

Density: 7.75 g/cc
Density: 7.86 g/cc
Hardness, Brinell: 302
Hardness, Brinell: 332
Hardness, Brinell: 409

Crucible Steel 15-5 Precipitation Hardening Stainless Steel accurate 91%

$ 1974/MT

Density: 7.75 g/cc
Density: 7.86 g/cc
Hardness, Brinell: 302
Hardness, Brinell: 332
Hardness, Brinell: 409

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 84%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Special Metals NIMONIC® Alloy 901 accurate 76%

$ 1514/MT

Density: 8.14 g/cc
Tensile Strength, Ultimate: 1030 MPa @Temperature 550 °C
Tensile Strength, Ultimate: 1200 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 875 MPa @Strain 0.200 %
Tensile Strength, Yield: 800 MPa @Strain 0.200 %, Temperature 550 °C

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 16) accurate 84%

$ 1714/MT

Particle Size: 8.4 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel accurate 84%

$ 2294/MT

Density: 7.75 g/cc
Density: 7.86 g/cc
Hardness, Brinell: 302
Hardness, Brinell: 332
Hardness, Brinell: 409

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 84%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 84%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 33%, Aged 565°C/4hr/AC accurate 84%

$ 1547/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1565 MPa
Tensile Strength, Ultimate: 1269 MPa @Temperature 316 °C
Tensile Strength, Ultimate: 1282 MPa @Temperature 371 °C
Tensile Strength, Ultimate: 1289 MPa @Temperature 426 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 900 (Age-Hardened 482°C/1hr/AC)

Seller from Chengdu – 2021-07-20:

Seller from Chengdu work with company: Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2174 per MT