Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC price 1651 per MT

Physical Properties
Density
8.40 g/cc

Mechanical Properties
Tensile Strength, Ultimate
1262 MPa
Tensile Strength, Ultimate
1055 MPa @Temperature 538 °C
Tensile Strength, Ultimate
1069 MPa @Temperature 649 °C
Tensile Strength, Ultimate
1069 MPa @Temperature 427 °C
Tensile Strength, Ultimate
1104 MPa @Temperature 316 °C
Tensile Strength, Ultimate
1152 MPa @Temperature 232 °C
Tensile Strength, Ultimate
1186 MPa @Temperature 177 °C
Tensile Strength, Yield
883 MPa @Strain 0.200 %
Tensile Strength, Yield
773 MPa @Strain 0.200 %, Temperature 649 °C
Tensile Strength, Yield
787 MPa @Strain 0.200 %, Temperature 316 °C
Tensile Strength, Yield
787 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
787 MPa @Strain 0.200 %, Temperature 427 °C
Tensile Strength, Yield
800 MPa @Strain 0.200 %, Temperature 232 °C
Tensile Strength, Yield
821 MPa @Strain 0.200 %, Temperature 177 °C
Elongation at Break
33 %
Elongation at Break
25 % @Temperature 649 °C
Elongation at Break
31 % @Temperature 538 °C
Elongation at Break
32 % @Temperature 316 °C
Elongation at Break
32 % @Temperature 427 °C
Elongation at Break
34 % @Temperature 232 °C
Elongation at Break
34 % @Temperature 177 °C
Reduction of Area
56 %
Reduction of Area
31 % @Temperature 649 °C
Reduction of Area
52 % @Temperature 538 °C
Reduction of Area
54 % @Temperature 427 °C
Reduction of Area
59 % @Temperature 316 °C
Reduction of Area
59 % @Temperature 177 °C
Reduction of Area
60 % @Temperature 232 °C
Modulus of Elasticity
207 GPa @Temperature 23.0 °C

Thermal Properties
CTE, linear
12.6 µm/m-°C @Temperature 25.0 - 100 °C
CTE, linear
13.4 µm/m-°C @Temperature 25.0 - 300 °C
CTE, linear
14.0 µm/m-°C @Temperature 25.0 - 500 °C
Specific Heat Capacity
0.418 J/g-°C
Melting Point
1257 - 1356 °C
Solidus
1257 °C
Liquidus
1356 °C

Component Elements Properties
Aluminum, Al
<= 0.35 %
Carbon, C
<= 0.030 %
Chromium, Cr
19 - 22 %
Iron, Fe
5.0 %
Manganese, Mn
<= 0.20 %
Molybdenum, Mo
7.0 - 9.5 %
Nickel, Ni
59 - 63 %
Niobium, Nb (Columbium, Cb)
2.75 - 4.0 %
Phosphorous, P
<= 0.015 %
Silicon, Si
<= 0.20 %
Sulfur, S
<= 0.010 %
Titanium, Ti
1.0 - 1.6 %

Electrical Properties
Electrical Resistivity
0.0001299 ohm-cm

Alternative products

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 99%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 16) accurate 99%

$ 1714/MT

Particle Size: 8.4 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 420 Stainless Steel Powder (Grade 80% - 22) accurate 79%

$ 2559/MT

Particle Size: 12 µm
Carbon, C: >= 0.15 %
Carbon, C: 0.50 %
Chromium, Cr: 12 - 14 %
Iron, Fe: 85 %

Osprey Metals 430L Stainless Steel Powder (Grade 90% - 22) accurate 79%

$ 1750/MT

Particle Size: 10 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.030 %
Chromium, Cr: 16 - 18 %
Iron, Fe: 81.79 %

Osprey Metals 420 Stainless Steel Powder (Grade 90% - 22) accurate 79%

$ 2111/MT

Particle Size: 10 µm
Carbon, C: >= 0.15 %
Carbon, C: 0.50 %
Chromium, Cr: 12 - 14 %
Iron, Fe: 85 %

Osprey Metals 17-4 PH Stainless Steel Powder (Grade 95% - 16) accurate 79%

$ 1460/MT

Particle Size: 6.7 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.070 %
Chromium, Cr: 15.5 - 17.5 %
Copper, Cu: 3.0 - 5.0 %

Osprey Metals 17-4 PH Stainless Steel Powder (Grade 95% - 16) accurate 79%

$ 1655/MT

Particle Size: 6.7 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.070 %
Chromium, Cr: 15.5 - 17.5 %
Copper, Cu: 3.0 - 5.0 %

Osprey Metals 420 Stainless Steel Powder (Grade 90% - 16) accurate 79%

$ 2241/MT

Particle Size: 8.4 µm
Carbon, C: >= 0.15 %
Carbon, C: 0.50 %
Chromium, Cr: 12 - 14 %
Iron, Fe: 85 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 99%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tankers for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC

Seller from Barcelona – 2021-04-27:

Seller from Barcelona work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), BASF

Price: $1651 per MT

Seller from Riyadh – 2021-04-13:

Seller from Riyadh work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2303 per MT