Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 53%, Aged 565°C/4hr/AC price 2358 per MT

Physical Properties
Density
8.43 g/cc

Mechanical Properties
Tensile Strength, Ultimate
2027 MPa
Tensile Strength, Ultimate
1655 MPa @Temperature 426 °C
Tensile Strength, Ultimate
1689 MPa @Temperature 371 °C
Tensile Strength, Ultimate
1724 MPa @Temperature 316 °C
Tensile Strength, Ultimate
1744 MPa @Temperature 260 °C
Tensile Strength, Ultimate
1793 MPa @Temperature 204 °C
Tensile Strength, Ultimate
1834 MPa @Temperature 149 °C
Tensile Strength, Yield
1965 MPa @Strain 0.200 %
Tensile Strength, Yield
1551 MPa @Strain 0.200 %, Temperature 426 °C
Tensile Strength, Yield
1586 MPa @Strain 0.200 %, Temperature 371 °C
Tensile Strength, Yield
1627 MPa @Strain 0.200 %, Temperature 316 °C
Tensile Strength, Yield
1662 MPa @Strain 0.200 %, Temperature 260 °C
Tensile Strength, Yield
1710 MPa @Strain 0.200 %, Temperature 204 °C
Tensile Strength, Yield
1758 MPa @Strain 0.200 %, Temperature 149 °C
Elongation at Break
10 %
Elongation at Break
4.0 % @Temperature 426 °C
Elongation at Break
7.0 % @Temperature 371 °C
Elongation at Break
8.0 % @Temperature 149 °C
Elongation at Break
8.0 % @Temperature 316 °C
Elongation at Break
8.0 % @Temperature 260 °C
Elongation at Break
8.0 % @Temperature 204 °C
Reduction of Area
46 %
Reduction of Area
8.0 % @Temperature 426 °C
Reduction of Area
22 % @Temperature 371 °C
Reduction of Area
41 % @Temperature 316 °C
Reduction of Area
43 % @Temperature 260 °C
Reduction of Area
44 % @Temperature 204 °C
Reduction of Area
45 % @Temperature 149 °C
Modulus of Elasticity
234.8 GPa
Shear Modulus
80.95 GPa

Thermal Properties
CTE, linear
12.8 µm/m-°C @Temperature 21.0 - 93.0 °C
CTE, linear
14.8 µm/m-°C @Temperature 21.0 - 316 °C
CTE, linear
15.7 µm/m-°C @Temperature 21.0 - 538 °C
Thermal Conductivity
11.2 W/m-K @Temperature 23.0 °C
Thermal Conductivity
17.0 W/m-K @Temperature 316 °C
Thermal Conductivity
23.4 W/m-K @Temperature 649 °C
Melting Point
1315 - 1440 °C
Solidus
1315 °C
Liquidus
1440 °C

Component Elements Properties
Boron, B
0.010 %
Carbon, C
<= 0.025 %
Chromium, Cr
19 - 21 %
Cobalt, Co
33 %
Iron, Fe
<= 1.0 %
Manganese, Mn
<= 0.15 %
Molybdenum, Mo
9.0 - 10.5 %
Nickel, Ni
33 - 37 %
Phosphorous, P
<= 0.015 %
Silicon, Si
<= 0.15 %
Sulfur, S
<= 0.010 %
Titanium, Ti
<= 1.0 %

Electrical Properties
Electrical Resistivity
0.0001033 ohm-cm @Temperature 23.0 °C
Electrical Resistivity
0.0001154 ohm-cm @Temperature 538 °C

Alternative products

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 55% Cold Reduction accurate 68%

$ 1920/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1827 MPa
Tensile Strength, Yield: 1413 MPa @Strain 0.200 %
Elongation at Break: 12 %
Reduction of Area: 50 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction accurate 68%

$ 1553/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1172 MPa
Tensile Strength, Yield: 1034 MPa @Strain 0.200 %
Elongation at Break: 28 %
Reduction of Area: 65 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 35% Cold Reduction accurate 68%

$ 2577/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1336 MPa
Tensile Strength, Yield: 1062 MPa @Strain 0.200 %
Elongation at Break: 22 %
Reduction of Area: 67 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 15% Cold Reduction + Aged 538°C (1000°F)/4hr/AC accurate 68%

$ 1802/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1089 MPa
Tensile Strength, Yield: 862 MPa @Strain 0.200 %
Elongation at Break: 39 %
Reduction of Area: 70 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 0% Cold Reduction + Aged 538°C (1000°F)/4hr/AC accurate 68%

$ 1534/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 931 MPa
Tensile Strength, Yield: 414 MPa @Strain 0.200 %
Elongation at Break: 68 %
Reduction of Area: 77 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction + Aged 538°C (1000°F)/4hr/AC accurate 68%

$ 1550/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1282 MPa
Tensile Strength, Yield: 1207 MPa @Strain 0.200 %
Elongation at Break: 24 %
Reduction of Area: 65 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 53% Cold Reduction + Aged 538°C (1000°F)/4hr/AC accurate 84%

$ 1503/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 2068 MPa
Tensile Strength, Yield: 1999 MPa @Strain 0.200 %
Elongation at Break: 10 %
Reduction of Area: 48 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction accurate 68%

$ 2233/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1572 MPa
Tensile Strength, Yield: 1303 MPa @Strain 0.200 %
Elongation at Break: 17 %
Reduction of Area: 62 %

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 33%, Aged 565°C/4hr/AC accurate 68%

$ 1547/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1565 MPa
Tensile Strength, Ultimate: 1269 MPa @Temperature 316 °C
Tensile Strength, Ultimate: 1282 MPa @Temperature 371 °C
Tensile Strength, Ultimate: 1289 MPa @Temperature 426 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, chemical tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 53%, Aged 565°C/4hr/AC

Seller from Buenos Aires – 2021-07-09:

Seller from Buenos Aires work with company: 3M, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2358 per MT