Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced  (Unverified Data**)

Seller in Shenyang price: $1642 per MT

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced  (Unverified Data**) in Polymer, Thermoplastic, Polyphenylene Sulfide (PPS), Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler

  • Physical Properties
  • Specific Gravity
  • 1.60 g/cc
  • Specific Gravity
  • 1.66 g/cc
  • Density
  • 1.64 g/cc
  • Density
  • 1.64 g/cc
  • Density
  • 1.65 g/cc
  • Water Absorption
  • 0.020 %
  • Water Absorption
  • 0.020 %
  • Thickness
  • 3180 microns
  • Linear Mold Shrinkage, Flow
  • 0.0020 - 0.0030 cm/cm
  • Linear Mold Shrinkage, Flow
  • 0.0020 - 0.0060 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0040 - 0.0060 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0050 - 0.0070 cm/cm

  • Mechanical Properties
  • Hardness, Rockwell M
  • 100
  • Hardness, Rockwell M
  • 100
  • Tensile Strength at Break
  • 195 MPa
  • Tensile Strength at Break
  • 200 MPa
  • Elongation at Break
  • 1.9 %
  • Elongation at Break
  • 1.7 % @Temperature 22.8 °C
  • Tensile Modulus
  • 14.7 GPa
  • Tensile Modulus
  • 3.24 GPa @Temperature 200 °C
  • Tensile Modulus
  • 4.27 GPa @Temperature 150 °C
  • Tensile Modulus
  • 11.9 GPa @Temperature 167 °C
  • Tensile Modulus
  • 14.5 GPa @Temperature -40.0 °C
  • Flexural Strength
  • 1.97 MPa
  • Flexural Strength
  • 241 MPa
  • Flexural Modulus
  • 14.5 GPa
  • Flexural Modulus
  • 13.1 GPa @Temperature 22.8 °C
  • Izod Impact, Notched
  • 0.854 J/cm
  • Izod Impact, Unnotched
  • 5.87 J/cm
  • Izod Impact, Notched (ISO)
  • 10.0 kJ/m²
  • Izod Impact, Notched (ISO)
  • 10.0 kJ/m² @Temperature -30.0 °C
  • Izod Impact, Unnotched (ISO)
  • 34.0 kJ/m²
  • Charpy Impact Unnotched
  • 5.30 J/cm²
  • Charpy Impact Unnotched
  • 5.30 J/cm² @Temperature -30.0 °C
  • Charpy Impact, Notched
  • 1.00 J/cm²
  • Charpy Impact, Notched
  • 1.00 J/cm² @Temperature -30.0 °C

  • Thermal Properties
  • CTE, linear
  • 26.0 µm/m-°C
  • CTE, linear, Transverse to Flow
  • 42.0 µm/m-°C
  • Specific Heat Capacity
  • 1.50 J/g-°C
  • Melting Point
  • 280 °C
  • Transformation Temperature, Tg
  • 90.0 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 280 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 265 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 270 °C
  • Deflection Temperature at 8.0 MPa
  • 215 °C
  • Flammability, UL94
  • V-0 @Thickness 1.60 mm
  • Flammability, UL94
  • V-0 @Thickness 0.380 mm
  • Flammability, UL94
  • 5VA @Thickness 3.00 mm
  • Oxygen Index
  • 47 %

  • Electrical Properties
  • Volume Resistivity
  • >= 1.00e+15 ohm-cm
  • Volume Resistivity
  • 1.00e+16 ohm-cm
  • Surface Resistance
  • >= 1.00e+15 ohm
  • Dielectric Constant
  • 3.5 @Frequency 1000 Hz
  • Dielectric Constant
  • 3.5 @Frequency 1.00e+6 Hz
  • Dielectric Constant
  • 4.6 @Frequency 1.00e+6 Hz
  • Dielectric Strength
  • 28.0 kV/mm
  • Dissipation Factor
  • 0.0010 @Frequency 1000 Hz
  • Dissipation Factor
  • 0.0010 @Frequency 1.00e+6 Hz
  • Dissipation Factor
  • 0.0062 @Frequency 1.00e+6 Hz
  • Arc Resistance
  • 134 sec
  • Comparative Tracking Index
  • 125 V

  • Processing Properties
  • Processing Temperature
  • 20.0 - 30.0 °C
  • Processing Temperature
  • 140 - 160 °C
  • Feed Temperature
  • 60.0 - 80.0 °C
  • Zone 1
  • 290 - 300 °C
  • Zone 2
  • 310 - 320 °C
  • Zone 3
  • 330 - 340 °C
  • Zone 4
  • 330 - 340 °C

Alternative products

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

1 prices for Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced  (Unverified Data**)

Seller from Shenyang – 2021-07-10:

Seller from Shenyang work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1642 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced  (Unverified Data**)?

Plastic warehouse