Celanese Hostaform® C 9021 AW POM, Tribological  (Unverified Data**)

Seller in Kolkata price: $1815 per MT

Celanese Hostaform® C 9021 AW POM, Tribological  (Unverified Data**) in Polymer, Thermoplastic, Acetal (POM)

  • Physical Properties
  • Density
  • 1.38 g/cc
  • Water Absorption
  • 0.65 %
  • Linear Mold Shrinkage, Flow
  • 0.021 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.019 cm/cm
  • Melt Flow
  • 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
  • Mechanical Properties
  • Tensile Strength, Yield
  • 58.0 MPa
  • Elongation at Break
  • 20 %
  • Elongation at Yield
  • 8.0 %
  • Tensile Modulus
  • 2.60 GPa
  • Charpy Impact Unnotched
  • 15.0 J/cm²
  • Charpy Impact Unnotched
  • 13.0 J/cm² @Temperature -30.0 °C
  • Charpy Impact, Notched
  • 0.600 J/cm²
  • Charpy Impact, Notched
  • 0.500 J/cm² @Temperature -30.0 °C
  • Tensile Creep Modulus, 1 hour
  • 2300 MPa
  • Tensile Creep Modulus, 1000 hours
  • 1200 MPa
  • Thermal Properties
  • CTE, linear
  • 110 µm/m-°C
  • Melting Point
  • 166 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 88.0 °C
  • Flammability, UL94
  • HB @Thickness 1.60 mm
  • Flammability, UL94
  • HB @Thickness 3.00 mm
  • Flame Spread
  • <= 100 mm/min
  • Electrical Properties
  • Volume Resistivity
  • 1.00e+14 ohm-cm
  • Surface Resistance
  • 1.00e+14 ohm
  • Dielectric Constant
  • 3.8 @Frequency 100 Hz
  • Dielectric Constant
  • 3.8 @Frequency 1.00e+6 Hz
  • Dielectric Strength
  • 35.0 kV/mm
  • Dissipation Factor
  • 0.0020 @Frequency 100 Hz
  • Dissipation Factor
  • 0.0050 @Frequency 1.00e+6 Hz
  • Comparative Tracking Index
  • 600 V
  • Processing Properties
  • Processing Temperature
  • 20.0 - 30.0 °C
  • Processing Temperature
  • 80.0 - 120 °C
  • Feed Temperature
  • 60.0 - 80.0 °C
  • Zone 1
  • 170 - 180 °C
  • Zone 2
  • 180 - 190 °C
  • Zone 3
  • 190 - 200 °C
  • Zone 4
  • 190 - 210 °C
  • Die Temperature
  • 190 - 210 °C
  • Melt Temperature
  • 190 - 230 °C
  • Mold Temperature
  • 80.0 - 120 °C
  • Drying Temperature
  • 100 - 120 °C
  • Dry Time
  • 3.00 - 4.00 hour
  • Moisture Content
  • 0.15 %
  • Injection Pressure
  • 60.0 - 120 MPa
  • Hold Pressure
  • 60.0 - 120 MPa
  • Back Pressure
  • 2.00 MPa
  • Screw Speed
  • 70 rpm @Diameter 55.0 mm
  • Screw Speed
  • 100 rpm @Diameter 40.0 mm
  • Screw Speed
  • 150 rpm @Diameter 25.0 mm
  • Hot-Working Temperature
  • 190 - 210 °C
  • Descriptive Properties
  • Injection molding
  • Yes
  • Injection Speed
  • slow
  • Longer pre-drying times/storage
  • The product can then be stored in standard conditions until processed.
  • Pre-drying
  • Drying is not normally required with proper storage
  • Processing conditions
  • ISO 9988

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Celanese Hostaform® C 9021 AW POM, Tribological  (Unverified Data**)

Seller from Kolkata – 2021-08-19:

Seller from Kolkata work with company: 3M, Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics)

Price: $1815 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Celanese Hostaform® C 9021 AW POM, Tribological  (Unverified Data**)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Tesla showroom in Singapore open-nearme.com