Chevron Phillips MarFlex® 7109S LLDPE Blown Film Resin (discontinued **) price 1818 per MT

Physical Properties
Density
0.918 g/cc
Thickness
31.8 microns
Melt Flow
0.90 g/10 min

Mechanical Properties
Film Elongation at Break, MD
560 %
Film Elongation at Break, TD
770 %
Coefficient of Friction
1.0
Elmendorf Tear Strength, MD
16.5 g/micron
Elmendorf Tear Strength, TD
33.1 g/micron
Dart Drop
4.72 g/micron
Film Tensile Strength at Break, MD
52.4 MPa
Film Tensile Strength at Break, TD
42.7 MPa
1% Secant Modulus, MD
241 MPa
1% Secant Modulus, TD
310 MPa

Optical Properties
Haze
11 %
Gloss
60 %
Gloss
100 %

Processing Properties
Processing Temperature
204 °C
Die Opening
0.0762 cm
Extruder Size
6.35 cm

Descriptive Properties
Color
Natural

Alternative products

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 85%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

Chevron Phillips 7105GLT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) accurate 70%

$ 2136/MT

Density: 0.920 g/cc
Melt Flow: 0.50 g/10 min
Coefficient of Friction: 0.10
Dart Drop: 5.70 g/micron
Haze: 11 %

S&E Specialty Polymers TufFlex™ GF 1831 PVC/Nitrile Alloy accurate 85%

$ 1631/MT

Specific Gravity: 1.14 g/cc
Hardness, Shore A: 58.0
Hardness, Shore A: 50.0 @Time 15.0 sec
Tensile Strength: 8.48 MPa
Elongation at Break: 575 %

Eastman E6838-997F Polyethylene (discontinued **) accurate 70%

$ 1515/MT

Density: 0.921 g/cc
Moisture Vapor Transmission: 18.6 cc-mm/m²-24hr-atm
Oxygen Transmission: 200 cc-mm/m²-24hr-atm
Thickness: 32.0 microns
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C

Thermal Ceramics Cerafelt accurate 85%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

Eastman D4036-F Polyethylene (discontinued **) accurate 70%

$ 1556/MT

Density: 0.921 g/cc
Moisture Vapor Transmission: 18.6 cc-mm/m²-24hr-atm
Oxygen Transmission: 200 cc-mm/m²-24hr-atm
Thickness: 32.0 microns
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C

Thermal Ceramics Kaowool Blanket accurate 70%

$ 1501/MT

Density: 0.0480 g/cc
Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Density: 0.192 g/cc

Chevron Phillips 7109DT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) accurate 70%

$ 1618/MT

Density: 0.920 g/cc
Melt Flow: 0.90 g/10 min
Film Elongation at Break, MD: 560 %
Film Elongation at Break, TD: 770 %
Secant Modulus, MD: 0.250 GPa

Chevron Phillips MarFlex® 7109DJ LLDPE Blown Film Resin accurate 85%

$ 2460/MT

Density: 0.918 g/cc
Thickness: 31.8 microns
Melt Flow: 0.90 g/10 min
Film Elongation at Break, MD: 520 %
Film Elongation at Break, TD: 700 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ships sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Chevron Phillips MarFlex® 7109S LLDPE Blown Film Resin (discontinued **)

Seller from Shenyang – 2021-07-10:

Seller from Shenyang work with company: 3M, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $1818 per MT