Chevron Phillips MarFlex® 7120S LLDPE Blown & Cast Film Resin (discontinued **) price 1727 per MT

Physical Properties
Density
0.918 g/cc
Thickness
31.8 microns
Melt Flow
2.0 g/10 min

Mechanical Properties
Film Elongation at Break, MD
580 %
Film Elongation at Break, TD
780 %
Coefficient of Friction
>= 1.0
Elmendorf Tear Strength, MD
11.8 g/micron
Elmendorf Tear Strength, TD
21.7 g/micron
Dart Drop
4.41 g/micron
Film Tensile Strength at Break, MD
42.7 MPa
Film Tensile Strength at Break, TD
33.1 MPa
1% Secant Modulus, MD
200 MPa
1% Secant Modulus, TD
214 MPa

Optical Properties
Haze
3.0 %
Gloss
84 %
Gloss
140 %

Processing Properties
Processing Temperature
270 °C
Die Opening
0.0640 cm
Extruder Size
6.35 cm

Descriptive Properties
Color
Natural

Alternative products

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 74%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

LyondellBasell Petrothene® NA373244 Low Density Polyethylene, Cast/Blown Film Grade accurate 62%

$ 1457/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Thickness: 31.8 microns
Melt Flow: 3.0 g/10 min
Antiblock Level: 6000 ppm

LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade accurate 62%

$ 1612/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Thickness: 31.8 microns
Melt Flow: 3.0 g/10 min
Antiblock Level: 0.000 ppm

Chevron Phillips MarFlex® 7120B LLDPE Blown & Cast Film Resin accurate 99%

$ 1450/MT

Density: 0.918 g/cc
Thickness: 31.8 microns
Melt Flow: 2.0 g/10 min
Film Elongation at Break, MD: 580 %
Film Elongation at Break, TD: 780 %

S&E Specialty Polymers TufFlex™ GF 1831 PVC/Nitrile Alloy accurate 74%

$ 1631/MT

Specific Gravity: 1.14 g/cc
Hardness, Shore A: 58.0
Hardness, Shore A: 50.0 @Time 15.0 sec
Tensile Strength: 8.48 MPa
Elongation at Break: 575 %

Thermal Ceramics Cerafelt accurate 74%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

Chevron Phillips MarFlex® 7120X Polyethylene; LLDPE accurate 62%

$ 1896/MT

Density: 0.918 g/cc
Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Antiblock Level: 0.00 ppm
Slip Level: 0.00 ppm
Film Elongation at Break, MD: 580 %

Thermal Ceramics Kaowool Blanket accurate 62%

$ 1501/MT

Density: 0.0480 g/cc
Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Density: 0.192 g/cc

Chevron Phillips MarFlex® 7120 LLDPE Blown & Cast Film Resin (discontinued **) accurate 99%

$ 1576/MT

Density: 0.918 g/cc
Thickness: 31.8 microns
Melt Flow: 2.0 g/10 min
Film Elongation at Break, MD: 580 %
Film Elongation at Break, TD: 780 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, luxury ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Chevron Phillips MarFlex® 7120S LLDPE Blown & Cast Film Resin (discontinued **)

Seller from Chicago – 2021-06-12:

Seller from Chicago work with company: Solvay, RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $1939 per MT

Seller from Phoenix – 2021-04-19:

Seller from Phoenix work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1727 per MT