Chevron Phillips Marlex® C513UV HDPE Blow Molding Resin (discontinued **) price 1890 per MT

Physical Properties
Density
0.945 g/cc
ESCR 100% Igepal®
>= 2000 hour
Melt Flow
6.2 g/10 min

Mechanical Properties
Hardness, Shore D
61
Tensile Strength, Yield
24.0 MPa
Elongation at Break
700 %
Flexural Modulus
1.07 GPa
Tensile Impact Strength
580 kJ/m²

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
66.0 °C
Vicat Softening Point
123 °C
Brittleness Temperature
<= -75.0 °C

Alternative products

Celanese RITEFLEX 655A TPC, Unfilled accurate 82%

$ 1571/MT

Specific Gravity: 1.19 g/cc
Density: 0.000689 g/cc
Density: 1.19 g/cc
Density of Compound: 1.19 g/cc
Water Absorption: 0.400 % @Temperature 22.8 °C

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 99%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

SABIC Innovative Plastics LNP LUBRICOMP FL003 PE accurate 82%

$ 1506/MT

Specific Gravity: 1.03 g/cc
Density: 1.03 g/cc
Moisture Absorption: 0.0400 %
Moisture Absorption: 0.0400 %
Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec

Total Lacqtene® 2001 TBK 46 HDPE pipe (discontinued **) accurate 82%

$ 2552/MT

Density: 0.955 g/cc
Viscosity: 1.60e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
Environmental Stress Crack Resistance: >= 700 hour
Oxidative Induction Time (OIT): >= 20 min
Oxidative Induction Time (OIT): >= 30 min

Thermal Ceramics Cerafelt accurate 99%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

DuPont Elvax® 670 Ethylene-Vinyl Acetate Copolymer Resin accurate 82%

$ 1717/MT

Density: 0.933 g/cc
Vinyl Acetate Content: 12 %
Melt Index of Compound: 0.30 g/10 min
Hardness, Shore A: 96
Hardness, Shore D: 45

Chevron Phillips Marlex® C513UV High Density Polyethylene, Blow Molding accurate 82%

$ 1453/MT

Specific Gravity: 0.945 g/cc
ESCR 100% Igepal®: >= 2000 hour
ESCR 100% Igepal®: >= 2000 hour
Melt Flow: 5.5 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore D: 61

SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) accurate 99%

$ 1895/MT

Density: 1.43 g/cc
Density: 1.43 g/cc
Moisture Absorption: 0.200 %
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Time 86400 sec

Chevron Phillips Marlex® C513 High density polyethylene (discontinued **) accurate 82%

$ 1884/MT

Density: 0.945 g/cc
Environmental Stress Crack Resistance: >= 2000 hour @Temperature 50.0 °C
High Load Melt Index: 6.2 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore D: 66
Tensile Strength, Yield: 23.7 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Chevron Phillips Marlex® C513UV HDPE Blow Molding Resin (discontinued **)

Seller from Dallas – 2021-04-23:

Seller from Dallas work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1890 per MT