Chevron Phillips Marlex® HMN TR-945/945G Polyethylene; HDPE price 1829 per MT

Physical Properties
Density
0.945 g/cc
ESCR 100% Igepal®
70 hour
ESCR 10% Igepal®
25 hour
Melt Index of Compound
6.0 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Hardness, Shore D
63
Tensile Strength, Yield
20.0 MPa
Elongation at Break
460 %
Flexural Modulus
0.740 GPa
Flexural Modulus
0.910 GPa
Impact Test
92.0 J @Thickness 3.17 mm, Temperature -40.0 °C
Impact Test
224 J @Thickness 6.35 mm, Temperature -40.0 °C

Thermal Properties
Melting Point
130 °C
Crystallization Temperature
113 °C
Deflection Temperature at 0.46 MPa (66 psi)
64.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
44.0 °C
Vicat Softening Point
118 °C
Brittleness Temperature
-75.0 °C

Alternative products

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 85%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

SABIC Innovative Plastics LNP Stat-kon FX97333 PE accurate 70%

$ 1626/MT

Density: 0.990 g/cc
Density: 0.994 g/cc
Moisture Absorption at Equilibrium: 0.99 %
Moisture Absorption at Equilibrium: 0.020 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.020 - 0.040 cm/cm @Time 86400 sec

Celanese RITEFLEX 663 TPC, Unfilled accurate 56%

$ 2042/MT

Specific Gravity: 1.24 g/cc
Density: 1.24 g/cc
Water Absorption: 0.300 % @Temperature 22.8 °C
Linear Mold Shrinkage, Flow: 0.0170 - 0.0200 cm/cm
Linear Mold Shrinkage, Flow: 0.0190 cm/cm

Thermal Ceramics Cerafelt accurate 85%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

Jackon JACKOCELL® R311 Expanded Polystyrene Packaging and Shape Molding accurate 56%

$ 1711/MT

Density: 0.0140 g/cc
Density: 0.0170 g/cc
Density: 0.0200 g/cc
Density: 0.0280 g/cc
Water Absorption: 4.6 %

Thermal Ceramics Cerablanket Blanket accurate 56%

$ 1758/MT

Density: 0.0480 g/cc
Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Thickness: 6250 - 50000 microns

Thermal Ceramics Kaowool Blanket accurate 70%

$ 1501/MT

Density: 0.0480 g/cc
Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Density: 0.192 g/cc

Polimeri Europa Extir® CM Giotto 5 AE Expandable Polystyrene - Continuous Mass/Flame Retardant accurate 56%

$ 2492/MT

Bulk Density: 0.590 - 0.630 g/cc
Density: >= 0.0100 g/cc
Density: >= 0.0130 g/cc
Density: >= 0.0150 g/cc
Density: 0.0110 - 0.0200 g/cc
Particle Size: 900 - 1600 µm

Phillips Sumika Marlex® CHP-370 Thermoplastic Polyolefin (discontinued **) accurate 56%

$ 2349/MT

Density: 1.00 g/cc
Density: 1.00 g/cc
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
Melt Flow: 30 g/10 min @Temperature 230 °C
Melt Flow: 30 g/10 min @Temperature 230 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Chevron Phillips Marlex® HMN TR-945/945G Polyethylene; HDPE

Seller from London – 2021-05-24:

Seller from London work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1829 per MT