CLAL-MSX CUPROROR® TL1 1/4 hard, Copper Alloy price 1550 per MT

Physical Properties
Density
8.90 g/cc

Mechanical Properties
Hardness, Vickers
100 - 125
Hardness, Vickers
108 @Temperature 500 °C, Time 180 sec
Hardness, Vickers
108 @Temperature 500 °C, Time 600 sec
Hardness, Vickers
108 @Temperature 500 °C, Time 1800 sec
Hardness, Vickers
109 @Temperature 500 °C, Time 60.0 sec
Hardness, Vickers
109.5 @Temperature 350 °C, Time 1800 sec
Hardness, Vickers
110 @Temperature 350 °C, Time 180 sec
Hardness, Vickers
110 @Temperature 350 °C, Time 600 sec
Hardness, Vickers
110 @Temperature 500 °C, Time 30.0 sec
Hardness, Vickers
110.5 @Temperature 500 °C, Time 10.0 sec
Hardness, Vickers
110.5 @Temperature 350 °C, Time 60.0 sec
Hardness, Vickers
111 @Temperature 350 °C, Time 30.0 sec
Hardness, Vickers
111 @Temperature 500 °C, Time 0.000 sec
Hardness, Vickers
112 @Temperature 350 °C, Time 0.000 sec
Hardness, Vickers
112 @Temperature 350 °C, Time 10.0 sec
Tensile Strength, Ultimate
320 - 400 MPa
Tensile Strength, Yield
>= 220 MPa @Strain 0.200 %
Elongation at Break
>= 15 %
Modulus of Elasticity
140 GPa

Thermal Properties
CTE, linear
16.3 µm/m-°C @Temperature 0.000 - 500 °C
CTE, linear
16.4 µm/m-°C @Temperature 0.000 - 250 °C
CTE, linear
16.7 µm/m-°C @Temperature 0.000 - 100 °C
Specific Heat Capacity
0.383 J/g-°C
Thermal Conductivity
338 W/m-K
Melting Point
1080 °C

Component Elements Properties
Cobalt, Co
0.080 %
Phosphorous, P
0.080 %

Electrical Properties
Electrical Resistivity
0.00000181 - 0.00000229 ohm-cm

Alternative products

Special Metals NIMONIC® Alloy 901 accurate 99%

$ 1514/MT

Density: 8.14 g/cc
Tensile Strength, Ultimate: 1030 MPa @Temperature 550 °C
Tensile Strength, Ultimate: 1200 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 875 MPa @Strain 0.200 %
Tensile Strength, Yield: 800 MPa @Strain 0.200 %, Temperature 550 °C

Bohler-Uddeholm BeCu Alloy 172 Mold Material accurate 66%

$ 1462/MT

Density: 8.36 g/cc
Density: 8.22 g/cc @Temperature 299 °C
Density: 8.28 g/cc @Temperature 199 °C
Hardness, Rockwell C: 30 - 40
Tensile Strength, Ultimate: 1170 MPa

Haynes Hastelloy® W alloy, gas metal arc welds, aged 1000 hours at 650°C (1200°F) accurate 99%

$ 1759/MT

Density: 9.00 g/cc
Tensile Strength, Ultimate: 1055 MPa
Tensile Strength, Ultimate: 565 MPa @Temperature 760 °C
Tensile Strength, Yield: 755 MPa
Tensile Strength, Yield: 400 MPa @Temperature 760 °C

BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Dry) accurate 99%

$ 1809/MT

Density: 1.41 g/cc
Water Absorption: 4.9 %
Moisture Absorption at Equilibrium: 1.4 %
Linear Mold Shrinkage: 0.010 cm/cm
Hardness, Rockwell R: 119

Special Metals INCOLOY® Alloy 909 accurate 99%

$ 1449/MT

Density: 8.30 g/cc
Tensile Strength, Ultimate: 1160 MPa @Temperature 550 °C
Tensile Strength, Ultimate: 1300 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 1140 MPa @Strain 0.200 %
Tensile Strength, Yield: 950 MPa @Strain 0.200 %, Temperature 550 °C

BASF Capron® 5202 HS Blend Nylon 66 (Dry) (discontinued **) accurate 66%

$ 1685/MT

Density: 1.14 g/cc
Moisture Absorption at Equilibrium: 2.5 %
Water Absorption at Saturation: 8.5 %
Viscosity Measurement: 55
Linear Mold Shrinkage: 0.015 cm/cm

SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 (Asia Pacific) accurate 66%

$ 1502/MT

Density: 1.18 g/cc
Density: 1.18 g/cc
Moisture Absorption: 0.100 %
Linear Mold Shrinkage, Flow: 0.017 - 0.019 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Time 86400 sec

Ampco Metal AMPCOLOY® 35 Tin Bronze, Castings accurate 66%

$ 1773/MT

Density: 8.80 g/cc
Hardness, Brinell: 65
Tensile Strength, Ultimate: 240 MPa
Tensile Strength, Yield: 120 MPa @Strain 0.200 %
Elongation at Break: 15 %

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet accurate 66%

$ 1643/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Tensile Strength, Ultimate: 799 MPa @Thickness 3.20 mm, Temperature 25.0 °C
Tensile Strength, Ultimate: 1088 MPa @Thickness 3.20 mm, Temperature 25.0 °C
Tensile Strength, Yield: 451 MPa @Strain 0.200 %, Thickness 3.20 mm

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 33%, Aged 565°C/4hr/AC accurate 99%

$ 1547/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 1565 MPa
Tensile Strength, Ultimate: 1269 MPa @Temperature 316 °C
Tensile Strength, Ultimate: 1282 MPa @Temperature 371 °C
Tensile Strength, Ultimate: 1289 MPa @Temperature 426 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for CLAL-MSX CUPROROR® TL1 1/4 hard, Copper Alloy

Seller from Hanoi – 2021-03-18:

Seller from Hanoi work with company: RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2441 per MT

Seller from Shanghai – 2021-07-12:

Seller from Shanghai work with company: RTP Company, MV Laboratories, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2154 per MT

Seller from Phoenix – 2021-07-04:

Seller from Phoenix work with company: Solvay, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1550 per MT