Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides price 1668 per MT

Physical Properties
Density
2.78 g/cc

Mechanical Properties
Hardness, Brinell
125 @Thickness 7.90 - 25.0 mm
Hardness, Brinell
125 @Thickness 25.0 - 60.0 mm
Hardness, Brinell
125 @Thickness 60.0 - 155 mm
Tensile Strength
>= 370 MPa @Thickness 60.0 - 80.0 mm
Tensile Strength
>= 385 MPa @Thickness 40.0 - 60.0 mm
Tensile Strength
>= 390 MPa @Thickness 7.90 - 12.5 mm
Tensile Strength
>= 390 MPa @Thickness 12.5 - 40.0 mm
Tensile Strength
415 MPa @Thickness 7.90 - 25.0 mm
Tensile Strength
415 MPa @Thickness 25.0 - 60.0 mm
Tensile Strength
415 MPa @Thickness 60.0 - 155 mm
Tensile Strength
>= 495 MPa @Thickness 80.0 - 115 mm
Tensile Strength, Yield
>= 240 MPa @Strain 0.200 %, Thickness 60.0 - 80.0 mm
Tensile Strength, Yield
>= 245 MPa @Strain 0.200 %, Thickness 40.0 - 60.0 mm
Tensile Strength, Yield
>= 250 MPa @Strain 0.200 %, Thickness 12.5 - 40.0 mm
Tensile Strength, Yield
>= 260 MPa @Strain 0.200 %, Thickness 7.90 - 12.5 mm
Tensile Strength, Yield
265 MPa @Strain 0.200 %, Thickness 25.0 - 60.0 mm
Tensile Strength, Yield
265 MPa @Strain 0.200 %, Thickness 60.0 - 155 mm
Tensile Strength, Yield
270 MPa @Strain 0.200 %, Thickness 7.90 - 25.0 mm
Tensile Strength, Yield
>= 420 MPa @Strain 0.200 %, Thickness 80.0 - 115 mm
Elongation at Break
>= 6.0 % @Thickness 80.0 - 115 mm
Elongation at Break
>= 7.0 % @Thickness 60.0 - 80.0 mm
Elongation at Break
>= 12 % @Thickness 12.5 - 40.0 mm
Elongation at Break
>= 12 % @Thickness 40.0 - 60.0 mm
Elongation at Break
>= 13 % @Thickness 7.90 - 12.5 mm
Elongation at Break
17 % @Thickness 60.0 - 155 mm
Elongation at Break
20 % @Thickness 7.90 - 25.0 mm
Elongation at Break
20 % @Thickness 25.0 - 60.0 mm
Modulus of Elasticity
72.0 GPa

Thermal Properties
CTE, linear
23.6 µm/m-°C @Temperature 20.0 - 100 °C
Thermal Conductivity
125 - 140 W/m-K

Component Elements Properties
Aluminum, Al
91.4 - 95.5 %
Chromium, Cr
<= 0.10 %
Copper, Cu
3.5 - 4.5 %
Iron, Fe
<= 0.70 %
Magnesium, Mg
0.40 - 1.0 %
Manganese, Mn
0.40 - 1.0 %
Silicon, Si
0.20 - 0.80 %
Zinc, Zn
<= 0.25 %
Zr+Ti
<= 0.25 %

Electrical Properties
Electrical Resistivity
0.00000360 - 0.00000420 ohm-cm

Alternative products

Indium Corp. Ga2O3 Gallium Sesquioxide accurate 99%

$ 1605/MT

Bulk Density: 0.700 g/cc
Density: 6.44 g/cc
Loss On Ignition: <= 0.10 % @Temperature 800 °C
Particle Mesh Size: -325 Mesh
Particle Mesh Size: -100 Mesh

Universal Wire Works 112 Nickel Alloy Welding Wire accurate 49%

$ 1750/MT

Tensile Strength, Ultimate: 758 MPa
Elongation at Break: 30 %
Carbon, C: <= 0.10 %
Chromium, Cr: 20 - 23 %
Cobalt, Co: <= 0.12 %

Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours accurate 49%

$ 1541/MT

Density: 8.75 g/cc
Hardness, Rockwell A: 52
Tensile Strength, Ultimate: 875 MPa
Tensile Strength, Yield: 383 MPa @Strain 0.200 %
Elongation at Break: 60 %

Indium Corp. Germanium Corporation® GeCl4 Germanium Tetrachloride accurate 99%

$ 1866/MT

Specific Gravity: 1.875 g/cc @Temperature 20.0 °C
Molecular Weight: 214.45 g/mol
Vapor Pressure: 0.101 bar @Temperature 20.0 °C
Boiling Point: 83.0 °C
Aluminum, Al: <= 1.0e-7 %

Special Metals NIMONIC® Alloy PK33 accurate 49%

$ 1586/MT

Density: 8.21 g/cc
Tensile Strength, Ultimate: 1020 MPa @Temperature 650 °C
Tensile Strength, Ultimate: 1150 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 750 MPa @Strain 0.200 %
Tensile Strength, Yield: 720 MPa @Strain 0.200 %, Temperature 650 °C

H.C. Starck Pure Molybdenum GME Glass Melting Electrodes accurate 49%

$ 1741/MT

Aluminum, Al: <= 0.0020 %
Calcium, Ca: <= 0.0030 %
Carbon, C: <= 0.0050 %
Chromium, Cr: <= 0.0050 %
Copper, Cu: <= 0.0020 %

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 99%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

Indium Corp. Germanium Corporation® Germanium Metal accurate 99%

$ 2337/MT

Specific Gravity: 5.323 g/cc @Temperature 20.0 °C
Molecular Weight: 72.61 g/mol
Heat of Fusion: 508.2 J/g
Heat of Vaporization: 4600 J/g
Specific Heat Capacity: 0.320 J/g-°C

Haynes Hastelloy® S alloy, weld metal, aged 16000 hours accurate 49%

$ 2158/MT

Density: 8.75 g/cc
Hardness, Rockwell A: 58
Tensile Strength, Ultimate: 760 MPa
Tensile Strength, Yield: 458 MPa @Strain 0.200 %
Elongation at Break: 19 %

H.C. Starck 4202 Pure Tungsten WS-3, Sheet accurate 49%

$ 1682/MT

Aluminum, Al: <= 0.0020 %
Calcium, Ca: <= 0.0030 %
Carbon, C: <= 0.0050 %
Chromium, Cr: <= 0.0020 %
Copper, Cu: <= 0.0020 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale japan. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides

Seller from Singapore – 2021-05-22:

Seller from Singapore work with company: Solvay, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1668 per MT

Seller from Dallas – 2021-06-06:

Seller from Dallas work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2138 per MT