Constellium Fortal® Aluminum Alloy price 1990 per MT

Physical Properties
Density
2.81 g/cc

Mechanical Properties
Tensile Strength
>= 450 MPa @Thickness 180 - 200 mm
Tensile Strength
>= 470 MPa @Thickness 140 - 160 mm
Tensile Strength
>= 480 MPa @Thickness 120 - 140 mm
Tensile Strength
>= 480 MPa @Thickness 160 - 180 mm
Tensile Strength
>= 485 MPa @Thickness 100 - 120 mm
Tensile Strength
>= 495 MPa @Thickness 80.0 - 100 mm
Tensile Strength
>= 500 MPa @Thickness 60.0 - 80.0 mm
Tensile Strength
505 MPa @Thickness 180 - 200 mm
Tensile Strength
510 MPa @Thickness 160 - 180 mm
Tensile Strength
515 MPa @Thickness 140 - 160 mm
Tensile Strength
520 MPa @Thickness 120 - 140 mm
Tensile Strength
525 MPa @Thickness 60.0 - 80.0 mm
Tensile Strength
530 MPa @Thickness 100 - 120 mm
Tensile Strength
>= 530 MPa @Thickness 50.0 - 60.0 mm
Tensile Strength
535 MPa @Thickness 80.0 - 100 mm
Tensile Strength
>= 540 MPa @Thickness 40.0 - 50.0 mm
Tensile Strength
>= 550 MPa @Thickness 25.0 - 40.0 mm
Tensile Strength
>= 555 MPa @Thickness 6.50 - 12.0 mm
Tensile Strength
>= 555 MPa @Thickness 12.0 - 25.0 mm
Tensile Strength
560 MPa @Thickness 50.0 - 60.0 mm
Tensile Strength
570 MPa @Thickness 40.0 - 50.0 mm
Tensile Strength
580 MPa @Thickness 25.0 - 40.0 mm
Tensile Strength
590 MPa @Thickness 6.50 - 12.0 mm
Tensile Strength
590 MPa @Thickness 12.0 - 25.0 mm
Tensile Strength, Yield
>= 380 MPa @Strain 0.200 %, Thickness 180 - 200 mm
Tensile Strength, Yield
>= 390 MPa @Strain 0.200 %, Thickness 160 - 180 mm
Tensile Strength, Yield
>= 400 MPa @Strain 0.200 %, Thickness 140 - 160 mm
Tensile Strength, Yield
>= 405 MPa @Strain 0.200 %, Thickness 120 - 140 mm
Tensile Strength, Yield
>= 410 MPa @Strain 0.200 %, Thickness 100 - 120 mm
Tensile Strength, Yield
>= 415 MPa @Strain 0.200 %, Thickness 80.0 - 100 mm
Tensile Strength, Yield
>= 420 MPa @Strain 0.200 %, Thickness 60.0 - 80.0 mm
Tensile Strength, Yield
>= 445 MPa @Strain 0.200 %, Thickness 50.0 - 60.0 mm
Tensile Strength, Yield
445 MPa @Strain 0.200 %, Thickness 60.0 - 80.0 mm
Tensile Strength, Yield
445 MPa @Strain 0.200 %, Thickness 180 - 200 mm
Tensile Strength, Yield
450 MPa @Strain 0.200 %, Thickness 160 - 180 mm
Tensile Strength, Yield
455 MPa @Strain 0.200 %, Thickness 140 - 160 mm
Tensile Strength, Yield
465 MPa @Strain 0.200 %, Thickness 120 - 140 mm
Tensile Strength, Yield
>= 470 MPa @Strain 0.200 %, Thickness 40.0 - 50.0 mm
Tensile Strength, Yield
>= 475 MPa @Strain 0.200 %, Thickness 25.0 - 40.0 mm
Tensile Strength, Yield
475 MPa @Strain 0.200 %, Thickness 100 - 120 mm
Tensile Strength, Yield
480 MPa @Strain 0.200 %, Thickness 80.0 - 100 mm
Tensile Strength, Yield
>= 480 MPa @Strain 0.200 %, Thickness 6.50 - 12.0 mm
Tensile Strength, Yield
>= 480 MPa @Strain 0.200 %, Thickness 12.0 - 25.0 mm
Tensile Strength, Yield
485 MPa @Strain 0.200 %, Thickness 50.0 - 60.0 mm
Tensile Strength, Yield
500 MPa @Strain 0.200 %, Thickness 40.0 - 50.0 mm
Tensile Strength, Yield
520 MPa @Strain 0.200 %, Thickness 25.0 - 40.0 mm
Tensile Strength, Yield
525 MPa @Strain 0.200 %, Thickness 6.50 - 12.0 mm
Tensile Strength, Yield
525 MPa @Strain 0.200 %, Thickness 12.0 - 25.0 mm
Elongation at Break
>= 2.0 % @Thickness 180 - 200 mm
Elongation at Break
>= 3.0 % @Thickness 160 - 180 mm
Elongation at Break
>= 4.0 % @Thickness 120 - 140 mm
Elongation at Break
>= 4.0 % @Thickness 140 - 160 mm
Elongation at Break
>= 5.0 % @Thickness 60.0 - 80.0 mm
Elongation at Break
>= 5.0 % @Thickness 80.0 - 100 mm
Elongation at Break
>= 5.0 % @Thickness 100 - 120 mm
Elongation at Break
5.0 % @Thickness 160 - 180 mm
Elongation at Break
5.0 % @Thickness 180 - 200 mm
Elongation at Break
6.0 % @Thickness 140 - 160 mm
Elongation at Break
>= 6.0 % @Thickness 25.0 - 40.0 mm
Elongation at Break
>= 6.0 % @Thickness 40.0 - 50.0 mm
Elongation at Break
>= 6.0 % @Thickness 50.0 - 60.0 mm
Elongation at Break
>= 7.0 % @Thickness 12.0 - 25.0 mm
Elongation at Break
7.0 % @Thickness 120 - 140 mm
Elongation at Break
8.0 % @Thickness 60.0 - 80.0 mm
Elongation at Break
8.0 % @Thickness 80.0 - 100 mm
Elongation at Break
>= 8.0 % @Thickness 6.50 - 12.0 mm
Elongation at Break
8.0 % @Thickness 100 - 120 mm
Elongation at Break
9.0 % @Thickness 25.0 - 40.0 mm
Elongation at Break
9.0 % @Thickness 40.0 - 50.0 mm
Elongation at Break
9.0 % @Thickness 50.0 - 60.0 mm
Elongation at Break
10 % @Thickness 12.0 - 25.0 mm
Elongation at Break
11 % @Thickness 6.50 - 12.0 mm
Modulus of Elasticity
72.0 GPa

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale listing. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Constellium Fortal® Aluminum Alloy

Seller from Philadelphia – 2021-07-11:

Seller from Philadelphia work with company: 3M, Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $2199 per MT

Seller from Chicago – 2021-03-31:

Seller from Chicago work with company: Solvay, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $1990 per MT