Covestro Apec® DP9-9354 High-Heat Polycarbonate, Flame-Retardant (discontinued **) price 1581 per MT

Physical Properties
Density
1.15 g/cc
Water Absorption
0.20 %
Linear Mold Shrinkage
0.0080 - 0.0090 cm/cm
Melt Flow
8.0 g/10 min @Load 2.16 kg, Temperature 330 °C

Mechanical Properties
Tensile Strength, Ultimate
62.0 MPa
Tensile Strength, Yield
66.0 MPa
Elongation at Break
30 %
Elongation at Yield
6.0 %
Tensile Modulus
2.20 GPa
Flexural Yield Strength
86.0 MPa
Flexural Modulus
2.28 GPa
Izod Impact, Notched
1.00 J/cm @Thickness 3.17 mm
Izod Impact, Unnotched
NB
Izod Impact, Unnotched
NB @Temperature -40.0 °C
Impact Test
58.0 J @Thickness 3.20 mm

Thermal Properties
CTE, linear
70.0 µm/m-°C @Temperature 20.0 °C
Thermal Conductivity
0.210 W/m-K
Deflection Temperature at 0.46 MPa (66 psi)
174 °C @Thickness 3.20 mm
Deflection Temperature at 1.8 MPa (264 psi)
162 °C @Thickness 3.17 mm
Vicat Softening Point
185 °C
UL RTI, Electrical
140 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
120 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
140 °C @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Oxygen Index
35 %

Optical Properties
Transmission, Visible
0.00 %

Electrical Properties
Electrical Resistivity
>= 1.00e+16 ohm-cm
Surface Resistance
4.00e+15 ohm
Dielectric Constant
2.9 @Frequency 60 Hz
Dielectric Constant
2.9 @Frequency 1e+6 Hz
Dielectric Strength
>= 16.0 kV/mm @Thickness 3.17 mm
Dissipation Factor
0.0010 @Frequency 60 Hz
Dissipation Factor
0.010 @Frequency 1e+6 Hz
Arc Resistance
60 - 120 sec @Thickness 3.00 mm
Comparative Tracking Index
>= 600 V @Thickness 3.00 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness 1.50 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Voltage Arc-Tracking Rate, HVTR
25.4 - 80.0 mm/min @Thickness 3.00 mm

Alternative products

Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant (discontinued **) accurate 92%

$ 1645/MT

Density: 1.15 g/cc
Water Absorption: 0.20 %
Linear Mold Shrinkage: 0.0080 - 0.0090 cm/cm
Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C
Tensile Strength, Ultimate: 62.0 MPa

BASF Styrodur® 3035 CN Extruded Rigid Polystyrene Foam (Europe) accurate 79%

$ 1548/MT

Density: 0.0300 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 3.0 %
Water Vapor Transmission: 100 - 150 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

Covestro Apec® DP9-9353 High-Heat Polycarbonate, UV Stabilized (discontinued **) accurate 79%

$ 2450/MT

Density: 1.15 g/cc
Water Absorption: 0.20 %
Linear Mold Shrinkage: 0.0080 - 0.0090 cm/cm
Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C
Hardness, Rockwell M: 84

SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC accurate 86%

$ 1548/MT

Density: 1.37 g/cc
Density: 1.37 g/cc
Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Transverse: 0.0096 cm/cm @Time 86400 sec

BASF Styrodur® 2800 C Extruded Rigid Polystyrene Foam (Europe) accurate 79%

$ 2010/MT

Density: 0.0300 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 5.0 %
Water Vapor Transmission: 80.0 - 200 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 72%

$ 2169/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 72%

$ 2396/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

BASF Styrodur® 4000 CS Extruded Rigid Polystyrene Foam (Europe) accurate 79%

$ 2342/MT

Density: 0.0350 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 3.0 %
Water Vapor Transmission: 80.0 - 150 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

BASF Styrodur® 3035 CS Extruded Rigid Polystyrene Foam (Europe) accurate 79%

$ 2271/MT

Density: 0.0330 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 3.0 %
Water Vapor Transmission: 50.0 - 150 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, crude oil tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: a.kutuzov@plastic-price.com

Work with plastics from August, 2015

3 prices for Covestro Apec® DP9-9354 High-Heat Polycarbonate, Flame-Retardant (discontinued **)

Seller from Monterrey – 2021-03-26:

Seller from Monterrey work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1581 per MT

Seller from Dongguan – 2021-05-09:

Seller from Dongguan work with company: PolyOne Corporation, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2097 per MT

Seller from Sūrat – 2021-04-24:

Seller from Sūrat work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2490 per MT