Covestro Makroblend® DP UT6007 Polycarbonate + PBT, Impact Grade price 2178 per MT

Physical Properties
Density
1.20 g/cc
Density
1.02 g/cc @Temperature 260 °C
Water Absorption
0.50 %
Moisture Absorption at Equilibrium
0.20 %
Melt Flow
18 g/10 min @Load 5.00 kg, Temperature 260 °C

Mechanical Properties
Tensile Strength, Yield
60.0 MPa
Elongation at Break
>= 50 %
Elongation at Yield
5.0 %
Tensile Modulus
2.20 GPa
Charpy Impact Unnotched
NB
Charpy Impact Unnotched
NB @Temperature -30.0 °C
Charpy Impact, Notched
6.00 J/cm²
Charpy Impact, Notched
4.00 J/cm² @Temperature -30.0 °C
Impact
3800
Impact
5000 @Temperature -30.0 °C
Puncture Energy
47.0 J
Puncture Energy
58.0 J @Temperature -30.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
90.0 µm/m-°C
CTE, linear, Transverse to Flow
90.0 µm/m-°C
Specific Heat Capacity
1.82 J/g-°C
Thermal Conductivity
0.179 W/m-K
Deflection Temperature at 0.46 MPa (66 psi)
110 °C
Deflection Temperature at 1.8 MPa (264 psi)
85.0 °C
Flammability, UL94
HB @Thickness 1.60 mm
Oxygen Index
21 %

Electrical Properties
Volume Resistivity
>= 1.00e+13 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
3.0 @Frequency 1.00e+6 Hz
Dielectric Constant
3.2 @Frequency 100 Hz
Dielectric Strength
30.0 kV/mm
Dissipation Factor
0.00070 @Frequency 100 Hz
Dissipation Factor
0.0045 @Frequency 1.00e+6 Hz
Comparative Tracking Index
600 V

Processing Properties
Melt Temperature
250 - 270 °C
Melt Temperature
260 °C
Mold Temperature
60.0 - 80.0 °C
Mold Temperature
70.0 °C
Ejection Temperature
170 °C
Injection Velocity
200 mm/sec

Descriptive Properties
Availability
Asia Pacific
Availability
Europe
Availability
India
Availability
Near East/Africa
Availability
North America
Availability
South and Central America
Eff. thermal diffusivity (m²/s)
9.64E-08
Feature
Release agent
Form
Pellets
Process
Injection Molding

Alternative products

Covestro Makroblend® DP UT6003 Polycarbonate + PBT, Impact Grade accurate 99%

$ 1844/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® DP UT3905 Polycarbonate + PBT, Impact Grade accurate 90%

$ 1832/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® DP UT6000 Polycarbonate + PBT, Impact Grade accurate 99%

$ 1449/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® DP UT3907 Polycarbonate + PBT, Impact Grade accurate 90%

$ 1489/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® DP UT6005 Polycarbonate + PBT, Impact Grade accurate 99%

$ 1557/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® KU 2-7912/4 Polycarbonate + PBT, Impact Grade accurate 77%

$ 1557/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® DP UT5007 Polycarbonate + PBT, Impact Grade accurate 83%

$ 2090/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Melt Flow: 29 g/10 min @Load 5.00 kg, Temperature 260 °C
Tensile Strength, Yield: 60.0 MPa
Elongation at Break: >= 50 %

Covestro Makroblend® KU 2-7915 Polycarbonate + PBT, Impact Grade accurate 90%

$ 2043/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® DP UT5005 Polycarbonate + PBT, Impact Grade accurate 83%

$ 2174/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Melt Flow: 29 g/10 min @Load 5.00 kg, Temperature 260 °C
Tensile Strength, Yield: 60.0 MPa
Elongation at Break: >= 50 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Covestro Makroblend® DP UT6007 Polycarbonate + PBT, Impact Grade

Seller from Lima – 2021-08-14:

Seller from Lima work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2178 per MT