CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWUVCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, UV Stabilized, Heat Stabilized, Dry price 1512 per MT

Physical Properties
Density
1.38 g/cc
Moisture Absorption at Equilibrium
1.8 - 2.3 %
Linear Mold Shrinkage
0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse
0.0070 cm/cm @Thickness 4.00 mm

Mechanical Properties
Tensile Strength at Break
110 MPa
Elongation at Break
3.5 %
Tensile Modulus
6.20 GPa
Flexural Modulus
5.10 GPa
Charpy Impact Unnotched
4.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.500 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear
25.0 µm/m-°C @Temperature 23.0 - 80.0 °C
Melting Point
215 °C
Deflection Temperature at 0.46 MPa (66 psi)
215 °C
Deflection Temperature at 1.8 MPa (264 psi)
180 °C
Vicat Softening Point
200 °C
Flammability, UL94
HB @Thickness 1.60 mm
Flammability, UL94
HB @Thickness 3.20 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+12 ohm
Dielectric Constant
4.0 @Frequency 1e+6 Hz
Dielectric Strength
35.0 kV/mm
Dielectric Loss Index
0.020
Comparative Tracking Index
450 V

Processing Properties
Melt Temperature
250 - 280 °C
Mold Temperature
60.0 - 90.0 °C

Descriptive Properties
Back Pressure
Low
Holding Pressure
High
Injection Speed
High
Screw Speed
High

Alternative products

CP-Polymer-Technik Wellamid® 6000 GVS 10/30 HWCP 10% Glass Fiber and 30% Glass Sphere Nylon 6, Heat Stabilized, Dry accurate 75%

$ 1827/MT

Density: 1.46 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 115 MPa

CP-Polymer-Technik Wellamid® 6000 MR 409 HWCP Mineral Nylon 6, Heat Stabilized, Dry accurate 75%

$ 1681/MT

Density: 1.46 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 5.5 %

CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 75%

$ 1704/MT

Density: 1.47 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 120 MPa

CP-Polymer-Technik Wellamid® 6000 MRGV 20/10 HWCP 20% Mineral and 10% Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 93%

$ 1704/MT

Density: 1.38 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 110 MPa

CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWUVCP 25% Mineral and 15% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Dry accurate 75%

$ 1644/MT

Density: 1.47 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 120 MPa

CP-Polymer-Technik Wellamid® 6000 GS 50 HWCP 50% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 75%

$ 1545/MT

Density: 1.55 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 85.0 MPa
Elongation at Break: 6.5 %

CP-Polymer-Technik Wellamid® 6000 GV 15 HWCP 15% Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 75%

$ 1642/MT

Density: 1.23 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 125 MPa

CP-Polymer-Technik Wellamid® 6000 GS 50 HWUVCP 50% Glass Sphere Filled Nylon 6, UV Stabilized, Heat Stabilized, Dry accurate 75%

$ 1470/MT

Density: 1.55 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 85.0 MPa
Elongation at Break: 6.5 %

SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific) accurate 81%

$ 1957/MT

Specific Gravity: 1.50 g/cc
Density: 1.46 g/cc
Density: 1.46 g/cc
Linear Mold Shrinkage, Flow: 0.0055 cm/cm
Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Time 86400 sec

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWUVCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, UV Stabilized, Heat Stabilized, Dry

Seller from Shanghai – 2021-04-04:

Seller from Shanghai work with company: ChevronTexaco Corp, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1645 per MT

Seller from Montréal – 2021-04-11:

Seller from Montréal work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1512 per MT

Seller from Guangzhou – 2021-08-17:

Seller from Guangzhou work with company: 3M, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2377 per MT

Would you like to sell CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWUVCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, UV Stabilized, Heat Stabilized, Dry?