CP-Polymer-Technik Wellamid® 6000 MR 309 HWCP Mineral Nylon 6, Heat Stabilized, Dry price 1733 per MT

Physical Properties
Density
1.35 g/cc
Moisture Absorption at Equilibrium
1.8 - 2.3 %
Linear Mold Shrinkage
0.0080 - 0.010 cm/cm @Thickness 4.00 mm

Mechanical Properties
Tensile Strength at Break
80.0 MPa
Elongation at Break
6.0 %
Tensile Modulus
5.10 GPa
Flexural Modulus
4.00 GPa
Charpy Impact Unnotched
NB @Temperature 23.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear
65.0 µm/m-°C @Temperature 23.0 - 80.0 °C
Melting Point
215 °C
Deflection Temperature at 0.46 MPa (66 psi)
190 °C
Deflection Temperature at 1.8 MPa (264 psi)
70.0 °C
Vicat Softening Point
200 °C
Flammability, UL94
HB @Thickness 1.60 mm
Flammability, UL94
HB @Thickness 3.20 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+12 ohm
Dielectric Constant
4.0 @Frequency 1e+6 Hz
Dielectric Strength
35.0 kV/mm
Dielectric Loss Index
0.020
Comparative Tracking Index
450 V

Processing Properties
Melt Temperature
260 - 290 °C
Mold Temperature
70.0 - 100 °C

Descriptive Properties
Back Pressure
Low
Holding Pressure
High
Injection Speed
High
Screw Speed
High

Alternative products

CP-Polymer-Technik Wellamid® 6000 GS 20 HWCP 20% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 77%

$ 1789/MT

Density: 1.29 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 75.0 MPa
Elongation at Break: 8.5 %

CP-Polymer-Technik Wellamid® 6000 MR 209 HWCP Mineral Nylon 6, Heat Stabilized, Dry accurate 82%

$ 2331/MT

Density: 1.27 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 75.0 MPa
Elongation at Break: 7.0 %

CP-Polymer-Technik Wellamid® 6000 GS 25 HWCP 25% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 82%

$ 1882/MT

Density: 1.31 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 78.0 MPa
Elongation at Break: 8.5 %

CP-Polymer-Technik Wellamid® 6000 GS 50 HWCP 50% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 77%

$ 1545/MT

Density: 1.55 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 85.0 MPa
Elongation at Break: 6.5 %

CP-Polymer-Technik Wellamid® 6000 GS 30 HWUVCP 30% Glass Sphere Filled Nylon 6, UV Stabilized, Heat Stabilized, Dry accurate 88%

$ 2029/MT

Density: 1.35 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 80.0 MPa
Elongation at Break: 8.5 %

CP-Polymer-Technik Wellamid® 6000 GS 50 HWUVCP 50% Glass Sphere Filled Nylon 6, UV Stabilized, Heat Stabilized, Dry accurate 77%

$ 1470/MT

Density: 1.55 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 85.0 MPa
Elongation at Break: 6.5 %

CP-Polymer-Technik Wellamid® 6000 GS 40 HWCP 40% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 82%

$ 1892/MT

Density: 1.46 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 82.0 MPa
Elongation at Break: 7.0 %

CP-Polymer-Technik Wellamid® 6000 GS 30 HWCP 30% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 88%

$ 1612/MT

Density: 1.35 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 80.0 MPa
Elongation at Break: 8.5 %

CP-Polymer-Technik Wellamid® 6000 GX 350 HWCP Combination Nylon 6, Heat Stabilized, Dry accurate 77%

$ 1728/MT

Density: 1.36 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 70.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, bulk ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for CP-Polymer-Technik Wellamid® 6000 MR 309 HWCP Mineral Nylon 6, Heat Stabilized, Dry

Seller from Hong Kong – 2021-05-23:

Seller from Hong Kong work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1733 per MT