CP-Polymer-Technik Wellamid® 6000/505 GS 30 HWCP 30% Impact Modified Glass Sphere Filled Nylon 6, Heat Stabilized, Dry price 1652 per MT

Physical Properties
Density
1.32 g/cc
Moisture Absorption at Equilibrium
1.5 - 2.0 %
Linear Mold Shrinkage
0.0080 - 0.010 cm/cm @Thickness 4.00 mm

Mechanical Properties
Tensile Strength at Break
65.0 MPa
Elongation at Break
10.5 %
Tensile Modulus
3.60 GPa
Flexural Modulus
3.00 GPa
Charpy Impact Unnotched
7.50 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear
35.0 µm/m-°C @Temperature 23.0 - 80.0 °C
Melting Point
215 °C
Deflection Temperature at 0.46 MPa (66 psi)
215 °C
Deflection Temperature at 1.8 MPa (264 psi)
70.0 °C
Vicat Softening Point
200 °C
Flammability, UL94
HB @Thickness 1.60 mm
Flammability, UL94
HB @Thickness 3.20 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+12 ohm
Dielectric Constant
4.0 @Frequency 1e+6 Hz
Dielectric Strength
35.0 kV/mm
Dielectric Loss Index
0.020
Comparative Tracking Index
450 V

Processing Properties
Melt Temperature
250 - 270 °C
Mold Temperature
60.0 - 90.0 °C

Descriptive Properties
Back Pressure
Low
Holding Pressure
High
Injection Speed
Medium
Screw Speed
High

Alternative products

CP-Polymer-Technik Wellamid® 6000 GS 15 HWCP 15% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 87%

$ 2182/MT

Density: 1.23 g/cc
Moisture Absorption at Equilibrium: 2.2 - 3.0 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 70.0 MPa
Elongation at Break: 9.0 %

CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 70%

$ 1704/MT

Density: 1.47 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 120 MPa

CP-Polymer-Technik Wellamid® 6000 MRGV 20/10 HWCP 20% Mineral and 10% Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 70%

$ 1704/MT

Density: 1.38 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 110 MPa

CP-Polymer-Technik Wellamid® 6000 GS 20 HWCP 20% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 87%

$ 1789/MT

Density: 1.29 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 75.0 MPa
Elongation at Break: 8.5 %

CP-Polymer-Technik Wellamid® 6000 MR 209 HWCP Mineral Nylon 6, Heat Stabilized, Dry accurate 87%

$ 2331/MT

Density: 1.27 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 75.0 MPa
Elongation at Break: 7.0 %

CP-Polymer-Technik Wellamid® 6000 GS 25 HWCP 25% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 81%

$ 1882/MT

Density: 1.31 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 78.0 MPa
Elongation at Break: 8.5 %

CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWUVCP 25% Mineral and 15% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Dry accurate 70%

$ 1644/MT

Density: 1.47 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 120 MPa

CP-Polymer-Technik Wellamid® 6000 GS 30 HWCP 30% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry accurate 70%

$ 1612/MT

Density: 1.35 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 80.0 MPa
Elongation at Break: 8.5 %

CP-Polymer-Technik Wellamid® 6000 GX 350 HWCP Combination Nylon 6, Heat Stabilized, Dry accurate 75%

$ 1728/MT

Density: 1.36 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 70.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale vessel. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for CP-Polymer-Technik Wellamid® 6000/505 GS 30 HWCP 30% Impact Modified Glass Sphere Filled Nylon 6, Heat Stabilized, Dry

Seller from Guadalajara – 2021-05-15:

Seller from Guadalajara work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2272 per MT

Seller from Hyderabad – 2021-03-11:

Seller from Hyderabad work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1814 per MT

Seller from Kinshasa – 2021-05-23:

Seller from Kinshasa work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2330 per MT

Seller from Mexico City – 2021-05-18:

Seller from Mexico City work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2501 per MT

Seller from Guangzhou – 2021-03-31:

Seller from Guangzhou work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1652 per MT