CP-Polymer-Technik Wellamid® 6600/50 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Conditioned price 1739 per MT

Physical Properties
Density
1.29 g/cc
Moisture Absorption at Equilibrium
1.8 - 2.3 %
Linear Mold Shrinkage
0.0020 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse
0.0070 cm/cm @Thickness 4.00 mm

Mechanical Properties
Tensile Strength at Break
90.0 MPa
Elongation at Break
8.0 %
Tensile Modulus
6.00 GPa
Charpy Impact Unnotched
10.0 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
3.20 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
255 °C

Electrical Properties
Volume Resistivity
1.00e+12 ohm-cm
Surface Resistance
1.00e+10 ohm
Dielectric Constant
6.0 @Frequency 1e+6 Hz
Dielectric Strength
35.0 kV/mm
Dielectric Loss Index
0.15

Processing Properties
Melt Temperature
265 - 295 °C
Mold Temperature
70.0 - 100 °C

Descriptive Properties
Back Pressure
Low
Holding Pressure
High
Injection Speed
High
Screw Speed
Medium

Alternative products

EMS-Grivory Grivory® HT2VZ-15H PA6T/66-GF15 accurate 79%

$ 1507/MT

Density: 1.24 g/cc
Water Absorption: 5.5 %
Moisture Absorption: 2.00 %
Linear Mold Shrinkage, Flow: 0.0040 cm/cm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm

CP-Polymer-Technik Wellamid® 6600 GV 25 DCHP 25% Glass Fiber Nylon 66, Special Heat Ageing Stabilization, Conditioned accurate 79%

$ 2062/MT

Density: 1.32 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 120 MPa

CP-Polymer-Technik Wellamid® 6000/51 GV 30 HWCP 30% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Conditioned accurate 79%

$ 1484/MT

Density: 1.29 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 90.0 MPa

CP-Polymer-Technik Wellamid® 6600 GVS 20/10 HWCP 20% Glass Fiber and 10% Glass Sphere Nylon 66, Heat Stabilized, Conditioned accurate 89%

$ 1780/MT

Density: 1.35 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.5 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 95.0 MPa

CP-Polymer-Technik Wellamid® 6600 MRGV 20/20 HWCP 20% Mineral and 20% Glass Fiber Nylon 66, Heat Stabilized, Conditioned accurate 89%

$ 2177/MT

Density: 1.48 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 90.0 MPa

CP-Polymer-Technik Wellamid® 6600 GV 30 HW 30% Glass Fiber Nylon 66, Heat Stabilized, Conditioned accurate 79%

$ 2577/MT

Density: 1.36 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 115 MPa

CP-Polymer-Technik Wellamid® 6600 MF30 HWCP 30% Milled Glass Fiber Nylon 66, Heat Stabilized, Conditioned accurate 89%

$ 2353/MT

Density: 1.36 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 90.0 MPa

CP-Polymer-Technik Wellamid® 6600 MZ 315 CP Combination Nylon 66, Conditioned accurate 79%

$ 1887/MT

Density: 1.35 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.5 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 95.0 MPa

CP-Polymer-Technik Wellamid® 6600 GV 25 HWCP 25% Glass Fiber Nylon 66, Heat Stabilized, Conditioned accurate 79%

$ 1796/MT

Density: 1.32 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 120 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, passenger catamarans for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: a.kutuzov@plastic-price.com

Work with plastics from August, 2015

3 prices for CP-Polymer-Technik Wellamid® 6600/50 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Conditioned

Seller from Shenzhen – 2021-05-31:

Seller from Shenzhen work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2509 per MT

Seller from Bengalūru – 2021-08-01:

Seller from Bengalūru work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1739 per MT

Seller from Brasília – 2021-05-20:

Seller from Brasília work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1906 per MT

Would you like to sell CP-Polymer-Technik Wellamid® 6600/50 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Conditioned?