DuPont Performance Polymers Crastin® HR5330HF BK503 PBT (Unverified Data**) price 1488 per MT

Physical Properties
Density
1.50 g/cc
Filler Content
30 %
Linear Mold Shrinkage, Flow
0.0030 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.010 cm/cm @Thickness 2.00 mm

Mechanical Properties
Tensile Strength at Break
120 MPa @Temperature 23.0 °C
Elongation at Break
3.5 % @Temperature 23.0 °C
Tensile Modulus
8.40 GPa @Temperature 23.0 °C
Flexural Modulus
7.50 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
8.00 kJ/m² @Temperature -40.0 °C
Izod Impact, Notched (ISO)
12.0 kJ/m² @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
50.0 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
6.50 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.900 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
1.10 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
221 °C
Deflection Temperature at 1.8 MPa (264 psi)
207 °C
Flammability, UL94
HB @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 0.750 mm

Processing Properties
Melt Temperature
250 °C
Melt Temperature
240 - 260 °C
Mold Temperature
80.0 °C
Mold Temperature
30.0 - 130 °C
Drying Temperature
110 - 130 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.040 %

Descriptive Properties
Additive
Hydrolysis Resistant
Additive
Lubricant
Appearance
Black Color
Drying Recommended
Yes
Features
Chemical Resistance, Good
Features
Dimensional Stability, Good
Features
Flow, High
Features
Hydrolysis Resistant
Features
Moisture Absorption, Low
Features
Processability, Good
Features
Viscosity, Low
Filler
Glass fiber reinforcement
Forms
Pellets
Generic
PBT
Material Status
Current
Part Marking Code
>PBT-IGF30<
Polymer Family
Polyester
Polymer Type
PBT
Processing Method
Injection Molding
Product Category
Glass Reinforced Resins
Product Category
Hydrolysis Resistant Resins
Region Available - Global
Yes
Resin Identification
PBT-IGF30
RoHS Compliance
Contact Manufacturer
Uses
Automotive Applications
Uses
Connectors
Uses
Electrical/Electronic Applications
Uses
Industrial Applications
Uses
Parts, Engineering
Uses
Parts, Industrial
Uses
Parts, Machine/Mechanical

Alternative products

DuPont Performance Polymers Crastin® FG6129 NC010 PBT (Unverified Data**) accurate 72%

$ 1581/MT

Density: 1.30 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.015 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® HR5315HF BK503 PBT (Unverified Data**) accurate 72%

$ 1689/MT

Density: 1.37 g/cc
Filler Content: 15 %
Water Absorption: 0.080 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® LW9030 BK851 PBT (Unverified Data**) accurate 79%

$ 2170/MT

Density: 1.44 g/cc
Filler Content: 30 %
Tensile Strength at Break: 125 MPa @Temperature 23.0 °C
Elongation at Break: 2.0 % @Temperature 23.0 °C
Tensile Modulus: 9.20 GPa @Temperature 23.0 °C

DuPont Performance Polymers Crastin® SK615SF BK591 PBT (Unverified Data**) accurate 72%

$ 2381/MT

Density: 1.54 g/cc
Filler Content: 30 %
Linear Mold Shrinkage, Flow: 0.0030 cm/cm
Linear Mold Shrinkage, Transverse: 0.011 cm/cm
Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 250 °C

DuPont Performance Polymers Crastin® S600F40 BK851 PBT (Unverified Data**) accurate 72%

$ 1695/MT

Density: 1.31 g/cc
Tensile Strength, Yield: 58.0 MPa @Temperature 23.0 °C
Elongation at Break: 20 % @Temperature 23.0 °C
Elongation at Break: 30 % @Temperature 23.0 °C
Elongation at Yield: 6.0 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® SK605 BK851 PBT (Unverified Data**) accurate 79%

$ 1559/MT

Density: 1.52 g/cc
Filler Content: 30 %
Tensile Strength at Break: 130 MPa @Temperature 23.0 °C
Elongation at Break: 2.5 % @Temperature 23.0 °C
Tensile Modulus: 9.60 GPa @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S600LF NC010 PBT accurate 72%

$ 1448/MT

Density: 1.32 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.022 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® S620F20 BK851 PBT (Unverified Data**) accurate 72%

$ 1519/MT

Density: 1.31 g/cc
Tensile Strength, Yield: 59.0 MPa @Temperature 23.0 °C
Elongation at Break: 30 % @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Yield: 8.0 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® SK603 BK851 PBT (Unverified Data**) accurate 72%

$ 1647/MT

Density: 1.45 g/cc
Filler Content: 20 %
Tensile Strength at Break: 113 MPa @Temperature 23.0 °C
Elongation at Break: 3.0 % @Temperature 23.0 °C
Tensile Modulus: 6.90 GPa @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Crastin® HR5330HF BK503 PBT (Unverified Data**)

Seller from Bangkok – 2021-07-21:

Seller from Bangkok work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1488 per MT