DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer  (Unverified Data**)

Seller in Melbourne price: $1826 per MT

DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer  (Unverified Data**) in Polymer, Thermoplastic, Acetal (POM)

  • Physical Properties
  • Specific Gravity
  • 1.39 g/cc
  • Density
  • 1.39 g/cc
  • Linear Mold Shrinkage
  • 0.017 - 0.020 cm/cm @Thickness 3.20 mm
  • Linear Mold Shrinkage
  • 0.017 - 0.020 cm/cm @Thickness 3.20 mm
  • Linear Mold Shrinkage, Flow
  • 0.018 cm/cm @Thickness 2.00 mm
  • Linear Mold Shrinkage, Flow
  • 0.019 cm/cm @Thickness 4.00 mm
  • Linear Mold Shrinkage, Transverse
  • 0.017 cm/cm @Thickness 2.00 mm
  • Linear Mold Shrinkage, Transverse
  • 0.019 cm/cm @Thickness 4.00 mm
  • Melt Flow
  • 6.0 g/10 min @Load 1.05 kg, Temperature 190 °C
  • Melt Flow
  • 14 g/10 min @Load 2.16 kg, Temperature 190 °C
  • Melt Index of Compound
  • 12 g/10 min @Load 2.16 kg, Temperature 190 °C
  • Mechanical Properties
  • Tensile Strength
  • 66.0 MPa @Temperature 23.0 °C
  • Tensile Strength, Yield
  • 65.0 MPa @Temperature 23.0 °C
  • Tensile Strength, Yield
  • 66.0 MPa @Temperature 23.0 °C
  • Elongation at Break
  • 23 % @Temperature 23.0 °C
  • Elongation at Break
  • 30 % @Temperature 23.0 °C
  • Elongation at Break
  • 35 % @Temperature 23.0 °C
  • Elongation at Yield
  • 10 % @Temperature 23.0 °C
  • Elongation at Yield
  • 11 % @Temperature 23.0 °C
  • Tensile Modulus
  • 3.00 GPa @Temperature 23.0 °C
  • Tensile Modulus
  • 3.17 GPa @Temperature 23.0 °C
  • Flexural Strength
  • 88.0 MPa @Strain 5.00 %, Temperature 23.0 °C
  • Flexural Modulus
  • 2.80 GPa @Temperature 23.0 °C
  • Flexural Modulus
  • 2.97 GPa @Temperature 23.0 °C
  • Izod Impact, Notched
  • 0.580 J/cm @Temperature 23.0 °C
  • Izod Impact, Notched (ISO)
  • 5.00 kJ/m² @Temperature -40.0 °C
  • Izod Impact, Notched (ISO)
  • 6.00 kJ/m² @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 13.0 J/cm² @Temperature -30.0 °C
  • Charpy Impact Unnotched
  • 16.0 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 0.600 J/cm² @Temperature -30.0 °C
  • Charpy Impact, Notched
  • 0.700 J/cm² @Temperature 23.0 °C
  • Tensile Creep Modulus, 1 hour
  • 2400 MPa @Temperature 23.0 °C
  • Tensile Creep Modulus, 1000 hours
  • 1600 MPa @Temperature 23.0 °C
  • Thermal Properties
  • CTE, linear, Parallel to Flow
  • 500 µm/m-°C @Temperature 23.0 - 55.0 °C
  • CTE, linear, Parallel to Flow
  • 500 µm/m-°C @Temperature -40.0 - 23.0 °C
  • CTE, linear, Parallel to Flow
  • 500 µm/m-°C @Temperature 23.0 - 55.0 °C
  • CTE, linear, Parallel to Flow
  • 500 µm/m-°C @Temperature 55.0 - 100 °C
  • CTE, linear, Transverse to Flow
  • 100 µm/m-°C @Temperature -40.0 - 23.0 °C
  • CTE, linear, Transverse to Flow
  • 116 µm/m-°C @Temperature 23.0 - 55.0 °C
  • CTE, linear, Transverse to Flow
  • 120 µm/m-°C @Temperature 23.0 - 55.0 °C
  • CTE, linear, Transverse to Flow
  • 170 µm/m-°C @Temperature 55.0 - 100 °C
  • Melting Point
  • 178 °C
  • Melting Point
  • 178 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 164 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 169 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 97.0 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 108 °C
  • UL RTI, Electrical
  • 50.0 °C @Thickness 0.750 mm
  • UL RTI, Electrical
  • 110 °C @Thickness 1.50 mm
  • UL RTI, Electrical
  • 110 °C @Thickness 3.00 mm
  • UL RTI, Mechanical with Impact
  • 50.0 °C @Thickness 0.750 mm
  • UL RTI, Mechanical with Impact
  • 85.0 °C @Thickness 1.50 mm
  • UL RTI, Mechanical with Impact
  • 90.0 °C @Thickness 3.00 mm
  • UL RTI, Mechanical without Impact
  • 50.0 °C @Thickness 0.750 mm
  • UL RTI, Mechanical without Impact
  • 90.0 °C @Thickness 1.50 mm
  • UL RTI, Mechanical without Impact
  • 95.0 °C @Thickness 3.00 mm
  • Flammability, UL94
  • HB @Thickness 1.50 mm
  • Flammability, UL94
  • HB @Thickness 3.00 mm
  • Electrical Properties
  • Volume Resistivity
  • 7.00e+14 ohm-cm @Temperature 23.0 °C
  • Surface Resistance
  • 4.00e+15 ohm @Temperature 23.0 °C
  • Dielectric Constant
  • 3.6 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
  • Dielectric Strength
  • 17.7 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C
  • Dissipation Factor
  • 0.0060 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
  • Comparative Tracking Index
  • 600 V @Thickness 3.00 mm, Temperature 23.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer  (Unverified Data**)

Seller from Melbourne – 2021-07-16:

Seller from Melbourne work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1826 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit