Physical Properties
Density
1.64 g/cc
Water Absorption
0.10 % @Thickness 1.00 mm, Temperature 23.0 °C
Water Absorption
0.75 % @Thickness 1.00 mm, Temperature 23.0 °C
Linear Mold Shrinkage, Flow
0.0020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.0070 cm/cm @Thickness 2.00 mm
Melt Index of Compound
10 g/10 min @Load 5.00 kg, Temperature 280 °C

Mechanical Properties
Tensile Strength at Break
110 MPa @Temperature 23.0 °C
Elongation at Break
2.0 % @Temperature 23.0 °C
Tensile Modulus
12.0 GPa @Temperature 23.0 °C
Charpy Impact Unnotched
3.00 J/cm² @Temperature -30.0 °C
Charpy Impact Unnotched
3.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.600 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
60.0 µm/m-°C @Temperature 23.0 - 55.0 °C
Melting Point
250 °C
Deflection Temperature at 0.46 MPa (66 psi)
240 °C
Deflection Temperature at 1.8 MPa (264 psi)
220 °C

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm @Temperature 23.0 °C
Surface Resistance
1.00e+14 ohm @Temperature 23.0 °C
Dielectric Constant
3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Constant
3.8 @Frequency 100 Hz, Temperature 23.0 °C
Dielectric Strength
38.0 kV/mm @Temperature 23.0 °C
Dissipation Factor
0.0070 @Frequency 100 Hz, Temperature 23.0 °C
Dissipation Factor
0.015 @Frequency 1.00e+6 Hz, Temperature 23.0 °C

Processing Properties
Melt Temperature
285 °C
Melt Temperature
280 - 300 °C
Mold Temperature
>= 95.0 °C
Mold Temperature
110 °C
Drying Temperature
120 °C
Dry Time
4.00 hour
Moisture Content
<= 0.020 %

Descriptive Properties
Drying Recommended
Yes
Generic
PET
Heat Stabilized
Yes
Part Marking Code
>PET-(GF+MD)40<
Polymer Family
Polyester
Polymer Type
PET
Product Category
Glass/Mineral Reinforced Resins
Product Category
Low Warp Resins
Region Available - Global
Yes
Resin Identification
PET-(GF+MD)40
Ultrasonic Weldable
Yes

Alternative products

DuPont Performance Polymers Rynite® 408 BK515 PET accurate 49%

$ 1711/MT

Density: 1.49 g/cc
Filler Content: 30 %
Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
Tensile Strength at Break: 71.0 MPa @Temperature 90.0 °C
Tensile Strength at Break: 127 MPa @Temperature 23.0 °C

DuPont Performance Polymers Rynite® 545 BK504 PET (Unverified Data**) accurate 74%

$ 2143/MT

Density: 1.70 g/cc
Filler Content: 45 %
Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 175 MPa @Temperature 23.0 °C

DuPont Performance Polymers Zytel® PLUS PLSFR95G15DH2 BK269 Nylon (Unverified Data**) accurate 49%

$ 1692/MT

Density: 1.48 g/cc
Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 138 MPa @Temperature 23.0 °C
Elongation at Break: 2.6 % @Temperature 23.0 °C

DuPont Performance Polymers Zytel® FG42A NC010 Nylon 66 (Unverified Data**) accurate 57%

$ 2087/MT

Density: 1.14 g/cc
Water Absorption: 2.6 % @Temperature 23.0 °C
Water Absorption: 8.5 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.015 cm/cm @Thickness 3.20 mm
Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Zytel® FN718 NC010A Nylon 66 accurate 49%

$ 2278/MT

Density: 1.04 g/cc
Tensile Strength at Break: 40.0 MPa @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Break: 125 % @Temperature 23.0 °C
Elongation at Break: 150 % @Temperature 23.0 °C

DuPont Performance Polymers Zytel® FN718 BK230A Nylon 66 (Unverified Data**) accurate 49%

$ 1521/MT

Density: 1.04 g/cc
Tensile Strength at Break: 36.0 MPa @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Break: 170 % @Temperature 23.0 °C
Elongation at Break: 200 % @Temperature 23.0 °C

DuPont Performance Polymers Zytel® FN714 NC010A Nylon 66 accurate 74%

$ 2532/MT

Density: 1.02 g/cc
Tensile Strength at Break: 29.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 29.0 MPa @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Break: 190 % @Temperature 23.0 °C

DuPont Performance Polymers Rynite® 415HP BK503 PET (Unverified Data**) accurate 49%

$ 1674/MT

Density: 1.39 g/cc
Filler Content: 15 %
Tensile Strength at Break: 80.0 MPa @Temperature 23.0 °C
Elongation at Break: 5.0 % @Temperature 23.0 °C
Tensile Modulus: 4.50 GPa @Temperature 23.0 °C

Celanese Impet® 340R PET, 45% Glass Reinforced (Unverified Data**) accurate 49%

$ 2031/MT

Specific Gravity: 1.70 g/cc
Density: 1.73 g/cc
Water Absorption: 0.060 %
Linear Mold Shrinkage, Flow: 0.0020 cm/cm
Linear Mold Shrinkage, Flow: 0.0060 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale australia. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Rynite® 940 NC010 PET (Unverified Data**)

Seller from Alexandria – 2021-08-05:

Seller from Alexandria work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2581 per MT