DuPont Performance Polymers Zytel® 73G30HSL BK416 Nylon 6 (Unverified Data**) price 1494 per MT

Physical Properties
Density
1.36 g/cc
Filler Content
30 %
Linear Mold Shrinkage
0.0010 cm/cm @Thickness 1.60 mm
Linear Mold Shrinkage
0.0020 cm/cm @Thickness 3.20 mm
Linear Mold Shrinkage
0.0030 cm/cm @Thickness 6.40 mm
Linear Mold Shrinkage
0.0070 cm/cm @Thickness 1.60 mm
Linear Mold Shrinkage
0.0080 cm/cm @Thickness 3.20 mm
Linear Mold Shrinkage
0.0080 cm/cm @Thickness 6.40 mm
Linear Mold Shrinkage, Flow
0.0020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.0060 cm/cm @Thickness 2.00 mm

Mechanical Properties
Tensile Strength at Break
115 MPa @Temperature 23.0 °C
Tensile Strength at Break
190 MPa @Temperature 23.0 °C
Elongation at Break
3.5 % @Temperature 23.0 °C
Elongation at Break
6.0 % @Temperature 23.0 °C
Tensile Modulus
5.80 GPa @Temperature 23.0 °C
Tensile Modulus
9.80 GPa @Temperature 23.0 °C
Flexural Modulus
8.20 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
11.0 kJ/m² @Temperature -40.0 °C
Izod Impact, Notched (ISO)
15.0 kJ/m² @Temperature 23.0 °C
Izod Impact, Notched (ISO)
20.0 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
9.50 J/cm² @Temperature 23.0 °C
Charpy Impact Unnotched
9.50 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
1.60 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
2.30 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 55.0 - 160 °C
CTE, linear, Transverse to Flow
76.0 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Transverse to Flow
99.0 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
125 µm/m-°C @Temperature 55.0 - 160 °C
Melting Point
221 °C
Deflection Temperature at 0.46 MPa (66 psi)
220 °C
Deflection Temperature at 1.8 MPa (264 psi)
204 °C
UL RTI, Electrical
65.0 °C @Thickness 0.800 mm
UL RTI, Electrical
65.0 °C @Thickness 1.50 mm
UL RTI, Electrical
65.0 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
65.0 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
65.0 °C @Thickness 0.800 mm
UL RTI, Mechanical with Impact
65.0 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
65.0 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
65.0 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
65.0 °C @Thickness 0.800 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 0.800 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 0.800 mm

Processing Properties
Melt Temperature
270 °C
Melt Temperature
260 - 280 °C
Mold Temperature
70.0 - 120 °C
Mold Temperature
100 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.20 %

Descriptive Properties
Additive
Heat Stabilizer
Additive
Lubricant
Appearance
Black Color
Drying Recommended
Yes, if moisture content of resin exceeds recommended level
Features
Weather Resistance, Good
Filler
Glass fiber reinforcement
Forms
Pellets
Generic
Nylon 6
Heat Stabilized
Yes
Material Status
Current
Part Marking Code
>PA6-GF30<
Polymer Family
Polyamide
Polymer Type
PA6
Processing Method
Blow Molding
Processing Method
Injection Molding
Product Category
Glass Reinforced Resins
Region Available - Global
Yes
Resin Identification
PA6-GF30
RoHS Compliance
Contact Manufacturer
Ultrasonic Weldable
Yes
Uses
Appliance Components
Uses
Automotive Applications
Uses
Parts, Engineering
Uses
Parts, Machine/Mechanical

Alternative products

DuPont Performance Polymers Zytel® 73G30HSL BK261 Nylon 6 (Unverified Data**) accurate 85%

$ 1758/MT

Density: 1.36 g/cc
Filler Content: 30 %
Tensile Strength at Break: 110 MPa @Temperature 23.0 °C
Tensile Strength at Break: 180 MPa @Temperature 23.0 °C
Elongation at Break: 3.0 % @Temperature 23.0 °C

DuPont Performance Polymers Zytel® FG7301 NC010 Nylon 6 (Unverified Data**) accurate 63%

$ 1715/MT

Density: 1.13 g/cc
Water Absorption: 3.0 % @Temperature 23.0 °C
Water Absorption: 9.5 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.010 cm/cm @Thickness 3.00 mm
Tensile Strength, Yield: 50.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Zytel® ST7301 BK356 Nylon 6 (Unverified Data**) accurate 63%

$ 1467/MT

Density: 1.06 g/cc
Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 2.00 mm
Tensile Strength, Yield: 30.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 48.0 MPa @Temperature 23.0 °C
Elongation at Break: 45 % @Temperature 23.0 °C

DuPont Performance Polymers Zytel® 73G30HSL NC010 Nylon 6 (Unverified Data**) accurate 85%

$ 2093/MT

Density: 1.36 g/cc
Filler Content: 30 %
Water Absorption: 1.9 % @Temperature 23.0 °C
Water Absorption: 6.3 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Zytel® 73G35HSL BK262 Nylon 6 (Unverified Data**) accurate 78%

$ 1606/MT

Density: 1.41 g/cc
Filler Content: 35 %
Water Absorption: 1.8 % @Thickness 1.00 mm, Temperature 23.0 °C
Water Absorption: 5.8 % @Thickness 1.00 mm, Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Zytel® BM73G15THS BK317 Nylon 6 (Unverified Data**) accurate 63%

$ 1711/MT

Density: 1.18 g/cc
Filler Content: 15 %
Linear Mold Shrinkage, Flow: 0.0028 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 65.0 MPa @Temperature 23.0 °C
Tensile Strength at Break: 107 MPa @Temperature 23.0 °C

DuPont Performance Polymers Zytel® 7304 NC010 Nylon 6 (Unverified Data**) accurate 63%

$ 1446/MT

Specific Gravity: 1.13 g/cc
Water Absorption: 3.0 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.012 cm/cm @Thickness 3.20 mm
Tensile Strength, Yield: 50.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 80.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Zytel® 73G45 BK263 Nylon 6 (Unverified Data**) accurate 70%

$ 1652/MT

Density: 1.51 g/cc
Filler Content: 45 %
Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 145 MPa @Temperature 23.0 °C

DuPont Performance Polymers Zytel® ST7301 NC010 Nylon 6 (Unverified Data**) accurate 63%

$ 1727/MT

Density: 1.06 g/cc
Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 2.00 mm
Tensile Strength, Yield: 29.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 48.0 MPa @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for DuPont Performance Polymers Zytel® 73G30HSL BK416 Nylon 6 (Unverified Data**)

Seller from Ankara – 2021-03-10:

Seller from Ankara work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), BASF

Price: $2585 per MT

Seller from Xi’an – 2021-04-21:

Seller from Xi’an work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2217 per MT

Seller from Dallas – 2021-04-01:

Seller from Dallas work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1494 per MT