Physical Properties
Density
1.07 g/cc
Water Absorption
1.1 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow
0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.017 cm/cm @Thickness 2.00 mm

Mechanical Properties
Tensile Stress
44.0 MPa @Strain 50.0 %, Temperature 23.0 °C
Tensile Stress
49.0 MPa @Strain 50.0 %, Temperature 23.0 °C
Tensile Strength, Yield
43.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield
48.0 MPa @Temperature 23.0 °C
Elongation at Break
>= 50 % @Temperature 23.0 °C
Elongation at Break
50 % @Temperature 23.0 °C
Elongation at Yield
20 % @Temperature 23.0 °C
Elongation at Yield
>= 50 % @Temperature 23.0 °C
Tensile Modulus
0.900 GPa @Temperature 23.0 °C
Tensile Modulus
2.00 GPa @Temperature 23.0 °C
Flexural Modulus
0.682 GPa @Temperature 23.0 °C
Flexural Modulus
1.80 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
15.0 kJ/m² @Temperature -30.0 °C
Izod Impact, Notched (ISO)
15.0 kJ/m² @Temperature -30.0 °C
Izod Impact, Notched (ISO)
17.0 kJ/m² @Temperature -40.0 °C
Izod Impact, Notched (ISO)
20.0 kJ/m² @Temperature -40.0 °C
Izod Impact, Notched (ISO)
22.0 kJ/m² @Temperature -20.0 °C
Izod Impact, Notched (ISO)
23.0 kJ/m² @Temperature -20.0 °C
Izod Impact, Notched (ISO)
73.0 kJ/m² @Temperature 23.0 °C
Izod Impact, Notched (ISO)
93.0 kJ/m² @Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
800 MPa @Temperature 23.0 °C
Tensile Creep Modulus, 1000 hours
700 MPa @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
110 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Parallel to Flow
110 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Parallel to Flow
120 µm/m-°C @Temperature -30.0 - 30.0 °C
CTE, linear, Parallel to Flow
120 µm/m-°C @Temperature -30.0 - 30.0 °C
CTE, linear, Parallel to Flow
140 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
140 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
160 µm/m-°C @Temperature 55.0 - 160 °C
CTE, linear, Parallel to Flow
160 µm/m-°C @Temperature 55.0 - 160 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature -30.0 - 30.0 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature -30.0 - 30.0 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Transverse to Flow
130 µm/m-°C @Temperature 55.0 - 160 °C
CTE, linear, Transverse to Flow
130 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
130 µm/m-°C @Temperature 55.0 - 160 °C
CTE, linear, Transverse to Flow
130 µm/m-°C @Temperature 23.0 - 55.0 °C
Melting Point
262 °C
Deflection Temperature at 0.46 MPa (66 psi)
157 °C
Deflection Temperature at 1.8 MPa (264 psi)
63.0 °C
Glass Transition Temp, Tg
75.0 °C
UL RTI, Electrical
125 °C @Thickness 0.810 mm
UL RTI, Mechanical with Impact
75.0 °C @Thickness 0.810 mm
UL RTI, Mechanical without Impact
85.0 °C @Thickness 0.810 mm
Flammability, UL94
HB @Thickness 0.810 mm
Flammability, UL94
HB @Thickness 0.810 mm

Electrical Properties
Volume Resistivity
8.70e+12 ohm-cm @Temperature 23.0 °C
Volume Resistivity
3.70e+16 ohm-cm @Temperature 23.0 °C
Surface Resistance
1.00e+12 ohm @Temperature 23.0 °C
Surface Resistance
1.20e+16 ohm @Temperature 23.0 °C
Dielectric Constant
3.3 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Constant
3.5 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Constant
3.5 @Frequency 100 Hz, Temperature 23.0 °C
Dielectric Constant
5.9 @Frequency 100 Hz, Temperature 23.0 °C
Dielectric Strength
25.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C
Dielectric Strength
26.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C
Dissipation Factor
0.0050 @Frequency 100 Hz, Temperature 23.0 °C
Dissipation Factor
0.010 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dissipation Factor
0.038 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dissipation Factor
0.158 @Frequency 100 Hz, Temperature 23.0 °C
Comparative Tracking Index
600 V @Temperature 23.0 °C
Comparative Tracking Index
>= 600 V @Thickness 3.00 mm, Temperature 23.0 °C

Alternative products

LG Chemical B120 EPS, Non-Flame Retardant accurate 56%

$ 1731/MT

Water Absorption: 0.24 %
Water Absorption: 0.25 %
Water Absorption: 0.30 %
Water Absorption: 0.30 %
Flexural Yield Strength: 0.161 MPa

LG Chemical B240 EPS, Non-Flame Retardant accurate 56%

$ 1551/MT

Water Absorption: 0.45 %
Water Absorption: 0.50 %
Water Absorption: 0.75 %
Water Absorption: 0.83 %
Flexural Yield Strength: 0.186 MPa

SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopolymer accurate 56%

$ 2046/MT

Density: 1.47 g/cc
Density: 1.47 g/cc
Moisture Absorption: 0.300 %
Linear Mold Shrinkage, Flow: 0.024 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.024 cm/cm @Time 86400 sec

DuPont Performance Polymers Zytel® ST801AHS NC010 Nylon 66 (Unverified Data**) accurate 70%

$ 1479/MT

Density: 1.08 g/cc
Water Absorption: 1.1 % @Temperature 23.0 °C
Water Absorption: 6.7 % @Temperature 23.0 °C
Water Absorption: 2.0 % @Thickness 1.00 mm, Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm

Thermal Ceramics Cerafelt accurate 85%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

SABIC Innovative Plastics LNP Lubricomp KI001A Acetal accurate 56%

$ 1451/MT

Density: 1.40 g/cc
Density: 1.40 g/cc
Moisture Absorption at Equilibrium: 0.47 %
Moisture Absorption at Equilibrium: 0.33 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**) accurate 56%

$ 1463/MT

Density: 1.01 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.60 % @Thickness 2.00 mm
Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C

Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite accurate 70%

$ 2111/MT

Density: 0.920 g/cc
Density: 0.920 g/cc
Water Absorption: <= 0.10 %
Water Absorption: <= 0.10 %
Water Absorption: <= 0.10 %

LG Chemical R320 EPS, Flame Retardant accurate 56%

$ 1862/MT

Water Absorption: 0.65 %
Water Absorption: 0.65 %
Water Absorption: 0.80 %
Water Absorption: 1.0 %
Flexural Yield Strength: 0.172 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, retired cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for DuPont Performance Polymers Zytel® ST801A NC010A Nylon 66 (Unverified Data**)

Seller from Montréal – 2021-06-14:

Seller from Montréal work with company: PolyOne Corporation, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1727 per MT

Seller from Karachi – 2021-03-13:

Seller from Karachi work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1896 per MT

Seller from Los Angeles – 2021-06-18:

Seller from Los Angeles work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2580 per MT

Seller from Washington – 2021-07-18:

Seller from Washington work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2132 per MT

Seller from Chicago – 2021-08-06:

Seller from Chicago work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2074 per MT