DuPont™ Surlyn® 1652-1 Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating (discontinued **) price 1690 per MT

Physical Properties
Density
0.940 g/cc
Melt Flow
4.5 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Film Elongation at Break, MD
500 %
Film Elongation at Break, TD
400 %
Secant Modulus, MD
0.160 GPa
Secant Modulus, TD
0.0450 GPa
Impact
220
Elmendorf Tear Strength, MD
3.50 g/micron
Elmendorf Tear Strength, TD
3.70 g/micron
Dart Drop
7.90 g/micron
Seal Strength
<= 2700 g/25 mm
Hot Tack Strength
<= 2000 g/25 mm
Film Tensile Strength at Break, MD
30.0 MPa
Film Tensile Strength at Break, TD
30.0 MPa

Thermal Properties
Melting Point
100 °C
Vicat Softening Point
79.0 °C

Optical Properties
Haze
3.5 %
Gloss
60 %

Processing Properties
Melt Temperature
177 °C

Alternative products

Chevron Phillips 7109CLT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) accurate 43%

$ 1660/MT

Density: 0.920 g/cc
Melt Flow: 0.90 g/10 min
Film Elongation at Break, MD: 440 %
Film Elongation at Break, TD: 580 %
Secant Modulus, MD: 0.260 GPa

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 66%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

Thermal Ceramics Pyro-Log R Fiber accurate 43%

$ 1536/MT

Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.240 g/cc
Thermal Conductivity: 0.0706 W/m-K @Temperature 260 °C

Borealis Bormed™ RD808CF Polypropylene Random Copolymer accurate 43%

$ 1948/MT

Density: 0.905 g/cc
Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Modulus: 0.400 GPa
Flexural Modulus: 0.700 GPa
Dart Drop, Total Energy: 30.0 J @Thickness 0.0500 mm

Thermal Ceramics Cerafelt accurate 66%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

DuPont™ Surlyn® 1652 Zinc Ionomer Resin for Flexible Packaging accurate 55%

$ 2060/MT

Density: 0.940 g/cc
Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Elongation at Break, MD: 400 %
Film Elongation at Break, TD: 400 %
Secant Modulus, MD: 0.160 GPa

Thermal Ceramics Kaowool Blanket accurate 55%

$ 1501/MT

Density: 0.0480 g/cc
Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Density: 0.192 g/cc

Braskem LH537 LLDPE Cast Film Extrusion Polyethylene accurate 43%

$ 1684/MT

Density: 0.937 g/cc
Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Elongation at Break, MD: 1320 %
Film Elongation at Break, TD: 1400 %
Elmendorf Tear Strength MD: 20 g

Thermal Ceramics Pyro-Bloc R T-Bar Module accurate 43%

$ 1576/MT

Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.240 g/cc
Thickness: 3000 - 12000 microns

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, shipsforsale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont™ Surlyn® 1652-1 Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating (discontinued **)

Seller from Manila – 2021-05-31:

Seller from Manila work with company: RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co.

Price: $1690 per MT