ExxonMobil Escorene® LD-103 LDPE Industrial Film Resin (discontinued **) price 2143 per MT

Physical Properties
Density
0.921 g/cc
Thickness
31.8 microns
Melt Flow
1.0 g/10 min

Mechanical Properties
Film Tensile Strength at Yield, MD
17.0 MPa
Film Tensile Strength at Yield, TD
12.0 MPa
Film Elongation at Break, MD
500 %
Film Elongation at Break, TD
600 %
Secant Modulus, MD
0.200 GPa
Secant Modulus, TD
0.220 GPa
Elmendorf Tear Strength MD
100 g
Elmendorf Tear Strength TD
250 g
Elmendorf Tear Strength, MD
3.15 g/micron
Elmendorf Tear Strength, TD
7.87 g/micron
Dart Drop
2.36 g/micron
Dart Drop Test
75.0 g
Film Tensile Strength at Break, MD
40.0 MPa
Film Tensile Strength at Break, TD
18.0 MPa

Thermal Properties
Melting Point
109 °C

Optical Properties
Haze
15 %
Gloss
40 %

Alternative products

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 59%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

LyondellBasell Petrothene® NA373244 Low Density Polyethylene, Cast/Blown Film Grade accurate 49%

$ 1457/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Thickness: 31.8 microns
Melt Flow: 3.0 g/10 min
Antiblock Level: 6000 ppm

LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade accurate 49%

$ 1612/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Thickness: 31.8 microns
Melt Flow: 3.0 g/10 min
Antiblock Level: 0.000 ppm

Bapolene® 200F Polyethylene, Film Grade accurate 49%

$ 1613/MT

Density: 0.920 g/cc
Thickness: 32.0 microns
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, MD: 15.2 MPa
Film Tensile Strength at Yield, TD: 12.4 MPa

LyondellBasell Petrothene® NA285003 Medium Density Polyethylene accurate 49%

$ 1503/MT

Density: 0.930 g/cc
Thickness: 31.8 microns
Melt Flow: 6.2 g/10 min
Film Elongation at Break, MD: 500 %
Film Elongation at Break, TD: 600 %

ExxonMobil Escorene® LD-317 EVA Film Resin, FMI (discontinued **) accurate 49%

$ 1468/MT

Density: 0.928 g/cc
Thickness: 31.8 microns
Melt Flow: 0.30 g/10 min
Film Tensile Strength at Yield, MD: 8.20 MPa
Film Tensile Strength at Yield, TD: 6.80 MPa

Thermal Ceramics Cerafelt accurate 59%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

Thermal Ceramics Kaowool Blanket accurate 49%

$ 1501/MT

Density: 0.0480 g/cc
Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Density: 0.192 g/cc

ExxonMobil Escorene® LD-138 LDPE Packaging Film Resin (discontinued **) accurate 49%

$ 1598/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Melt Flow: 1.3 g/10 min
Film Tensile Strength at Yield, MD: 11.0 MPa
Film Tensile Strength at Yield, TD: 12.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, retired cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for ExxonMobil Escorene® LD-103 LDPE Industrial Film Resin (discontinued **)

Seller from Kinshasa – 2021-06-06:

Seller from Kinshasa work with company: Solvay, Fainplast Compounds, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2143 per MT