ExxonMobil Escorene® LD-314 EVA Packaging Film Resin (discontinued **) price 2407 per MT

Physical Properties
Density
0.925 g/cc
Thickness
31.8 microns
Melt Flow
2.2 g/10 min

Mechanical Properties
Film Tensile Strength at Yield, MD
8.30 MPa
Film Tensile Strength at Yield, TD
8.30 MPa
Film Elongation at Break, MD
200 %
Film Elongation at Break, TD
600 %
Secant Modulus, MD
0.150 GPa
Secant Modulus, TD
0.180 GPa
Elmendorf Tear Strength MD
375 g
Elmendorf Tear Strength TD
100 g
Elmendorf Tear Strength, MD
11.8 g/micron
Elmendorf Tear Strength, TD
3.15 g/micron
Dart Drop
3.15 g/micron
Dart Drop Test
100 g
Film Tensile Strength at Break, MD
24.0 MPa
Film Tensile Strength at Break, TD
19.0 MPa

Thermal Properties
Melting Point
106 °C

Optical Properties
Haze
5.0 %
Gloss
75 %

Alternative products

Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding accurate 59%

$ 1788/MT

Density: 0.0150 g/cc
Density: 0.0180 g/cc
Density: 0.0180 g/cc
Density: 0.0185 g/cc
Density: 0.0200 g/cc

LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade accurate 59%

$ 1612/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Thickness: 31.8 microns
Melt Flow: 3.0 g/10 min
Antiblock Level: 0.000 ppm

Thermal Ceramics Cerafelt accurate 59%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

ExxonMobil Escorene® LD-306 EVA Film Resin, High Clarity, Very High Impact (discontinued **) accurate 59%

$ 1914/MT

Density: 0.926 g/cc
Thickness: 31.8 microns
Melt Flow: 2.0 g/10 min
Film Tensile Strength at Yield, MD: 8.30 MPa
Film Tensile Strength at Yield, TD: 6.90 MPa

Westlake EF378 Low Density Polyethylene accurate 59%

$ 2043/MT

Density: 0.922 g/cc
Thickness: 31.8 microns
Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Elongation at Break, MD: 350 %
Film Elongation at Break, TD: 700 %

ExxonMobil Escorene® LD-302 EVA Film Resin, High Clarity, High Impact (discontinued **) accurate 79%

$ 1561/MT

Density: 0.925 g/cc
Thickness: 31.8 microns
Melt Flow: 1.3 g/10 min
Film Tensile Strength at Yield, MD: 8.30 MPa
Film Tensile Strength at Yield, TD: 8.90 MPa

Westlake EF421 Low Density Polyethylene accurate 59%

$ 1569/MT

Density: 0.923 g/cc
Thickness: 31.8 microns
Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Elongation at Break, MD: 350 %
Film Elongation at Break, TD: 700 %

LyondellBasell Petrothene® NA442051 Low Density Polyethylene accurate 59%

$ 1895/MT

Density: 0.927 g/cc
Vinyl Acetate Content: 5.0 %
Thickness: 31.8 microns
Melt Flow: 5.0 g/10 min
Film Elongation at Break, MD: 320 %

ExxonMobil Escorene® LD-138 LDPE Packaging Film Resin (discontinued **) accurate 59%

$ 1598/MT

Density: 0.924 g/cc
Thickness: 31.8 microns
Melt Flow: 1.3 g/10 min
Film Tensile Strength at Yield, MD: 11.0 MPa
Film Tensile Strength at Yield, TD: 12.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, luxury cruise ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for ExxonMobil Escorene® LD-314 EVA Packaging Film Resin (discontinued **)

Seller from Singapore – 2021-04-08:

Seller from Singapore work with company: 3M, Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $2407 per MT